Lead-free low melting glasses,ZnO-CuO-Bi_(2)O_(3)-B_(2)O_(3)-SiO_(2)system,with fixed contents of 15 mol%CuO and 20 mol%Bi_(2)O_(3),were prepared by using melt cooling method.Structure and thermal properties of the gl...Lead-free low melting glasses,ZnO-CuO-Bi_(2)O_(3)-B_(2)O_(3)-SiO_(2)system,with fixed contents of 15 mol%CuO and 20 mol%Bi_(2)O_(3),were prepared by using melt cooling method.Structure and thermal properties of the glasses were studied by using X-ray diffractometer(XRD),infrared spectrometer(FIT-IR),thermal dilatometer and differential thermal analyzer(DTA).Chemical durability of the glasses was studied by using dissolution rate method.Wettability of glasses on substrate was tested by using button sintering experiment.It is found that alkaline resistance of the glass solders is lower than that of plate glass and the water resistance is comparable with that of plate glass.The sealing temperatures are Ts=445-490℃,while the average thermal expansion coefficient from room temperature to 300℃is in the range of(65-82)×10^(−7)℃^(−1).At sealing temperature,the glass solders have good wettability on plate glass or alumina substrate.They are not crystallized even sintered at the sealing temperature for 30 min.The solder glasses are suitable for sealing plate glass,alumina and other inorganic non-metallic materials.展开更多
基于商业智能的学生评教决策支持系统,是对高校现有相关业务管理信息系统的数据进行抽取、清理、转化和加载,建立数据仓库,根据系统设计目标和业务需求分析,确立系统总体设计框架和分析的主题,进行概念、逻辑和物理模型设计,给出了基于...基于商业智能的学生评教决策支持系统,是对高校现有相关业务管理信息系统的数据进行抽取、清理、转化和加载,建立数据仓库,根据系统设计目标和业务需求分析,确立系统总体设计框架和分析的主题,进行概念、逻辑和物理模型设计,给出了基于微软SQL SERVER 2005商业智能解决方案的系统应用。展开更多
基金National Natural Science Foundation of China(52172070)Jiangxi Provincial Natural Science Foundation(20242BAB25222)Jiangxi Provincial Graduate Innovation Special Fund Project(YC2022-S882 and YC2023-S808).
文摘Lead-free low melting glasses,ZnO-CuO-Bi_(2)O_(3)-B_(2)O_(3)-SiO_(2)system,with fixed contents of 15 mol%CuO and 20 mol%Bi_(2)O_(3),were prepared by using melt cooling method.Structure and thermal properties of the glasses were studied by using X-ray diffractometer(XRD),infrared spectrometer(FIT-IR),thermal dilatometer and differential thermal analyzer(DTA).Chemical durability of the glasses was studied by using dissolution rate method.Wettability of glasses on substrate was tested by using button sintering experiment.It is found that alkaline resistance of the glass solders is lower than that of plate glass and the water resistance is comparable with that of plate glass.The sealing temperatures are Ts=445-490℃,while the average thermal expansion coefficient from room temperature to 300℃is in the range of(65-82)×10^(−7)℃^(−1).At sealing temperature,the glass solders have good wettability on plate glass or alumina substrate.They are not crystallized even sintered at the sealing temperature for 30 min.The solder glasses are suitable for sealing plate glass,alumina and other inorganic non-metallic materials.