The effect of the Y spacer layer on the phase composition,coercivity,and magnetization reversal processes of La-Nd-Fe-B films has been investigated.The addition of a 10 nm Y spacer layer increases the coercivity of th...The effect of the Y spacer layer on the phase composition,coercivity,and magnetization reversal processes of La-Nd-Fe-B films has been investigated.The addition of a 10 nm Y spacer layer increases the coercivity of the film to 1.36 T at 300 K and remains 0.938 T at 380 K.As the thickness of the Y spacer layer increases,Y participates in the formation of the main phase in the film,and further regulates the formation of La-B phases.The results of the first-order reversal curve(FORC)and micromagnetic fitting show that the coercivity of all the films is dominated by nucleation mechanism.The c-axis preferred orientation,good magnetic microstructure parameters and the largest dipole interaction enhance the coercivity.Therefore,the introduction of the Y spacer layer can be an effective way to improve the coercivity of La-Nd-Fe-B film over a wide temperature range of 150 K-380 K.展开更多
基金Project supported by the National Key Research and Development Program of China(Grant No.2021YFB3500303)the National Natural Science Foundation of China(Grant Nos.52031014 and 51971219).
文摘The effect of the Y spacer layer on the phase composition,coercivity,and magnetization reversal processes of La-Nd-Fe-B films has been investigated.The addition of a 10 nm Y spacer layer increases the coercivity of the film to 1.36 T at 300 K and remains 0.938 T at 380 K.As the thickness of the Y spacer layer increases,Y participates in the formation of the main phase in the film,and further regulates the formation of La-B phases.The results of the first-order reversal curve(FORC)and micromagnetic fitting show that the coercivity of all the films is dominated by nucleation mechanism.The c-axis preferred orientation,good magnetic microstructure parameters and the largest dipole interaction enhance the coercivity.Therefore,the introduction of the Y spacer layer can be an effective way to improve the coercivity of La-Nd-Fe-B film over a wide temperature range of 150 K-380 K.