The supported catalysts for propylene polymerization were prepared by milling Mg (OEt)_2 with EB (ethylbenzoate) and treating with TiCl_4 solution. When TiCl_4/(Mg(OEt)_2/EB) (mol.) ratio was increased, decrease in co...The supported catalysts for propylene polymerization were prepared by milling Mg (OEt)_2 with EB (ethylbenzoate) and treating with TiCl_4 solution. When TiCl_4/(Mg(OEt)_2/EB) (mol.) ratio was increased, decrease in contents of-OEt and Ti of the catalysts was observed, while the content of EB increased. It is proved by analyses of IR, X-ray and XPS that during co-milling Mg(OEt)_2 with EB no reactions have taken place. But after treatment with TiCl_4 solution, Mg(OEt)_2 converts into MgCl_2 and EB coordinates on the resulting MgCl_2 carrier, a surface complex forms.The activity of catalysts,isotacticity and vicosimetric molecular weight of polypropylene increase with the decrease of the content of ethoxyl group. The kinetic curves of propene polymerization obtained with present catalysts system display decay curves. It is found from the triad tacticity calculated from the expanded spectra of methyl carbon region that, ethoxyl group in catalyst has an effect on the configuration of polymer chain.展开更多
Copolymerization of ethylene/1-octene was carried out in toluene withvarious concentrations of comonomer in the feed using Et(Ind)_2ZrCl_2/MAO (methyl alu-minoxane) as catalyst. It was found that with the increase of ...Copolymerization of ethylene/1-octene was carried out in toluene withvarious concentrations of comonomer in the feed using Et(Ind)_2ZrCl_2/MAO (methyl alu-minoxane) as catalyst. It was found that with the increase of 1-octene concentration in thefeed the content of 1-octene in the copolymer increases, while the density, melting point,crystallinity and intrinsic viscosity of copolymer decrease. A copolymer with very lowdensity, containing 11.5 mol% of 1-octene (VLLDPE) can be produced with this catalystsystem. The effect of temperature and zirconium aluminum mole ratio of the catalyst onthe copolymerization was also investigated. The results of ^(13)C NMR determination of thecopolymer showed that the 1-octene units in the copolymer are principally isolated.展开更多
文摘The supported catalysts for propylene polymerization were prepared by milling Mg (OEt)_2 with EB (ethylbenzoate) and treating with TiCl_4 solution. When TiCl_4/(Mg(OEt)_2/EB) (mol.) ratio was increased, decrease in contents of-OEt and Ti of the catalysts was observed, while the content of EB increased. It is proved by analyses of IR, X-ray and XPS that during co-milling Mg(OEt)_2 with EB no reactions have taken place. But after treatment with TiCl_4 solution, Mg(OEt)_2 converts into MgCl_2 and EB coordinates on the resulting MgCl_2 carrier, a surface complex forms.The activity of catalysts,isotacticity and vicosimetric molecular weight of polypropylene increase with the decrease of the content of ethoxyl group. The kinetic curves of propene polymerization obtained with present catalysts system display decay curves. It is found from the triad tacticity calculated from the expanded spectra of methyl carbon region that, ethoxyl group in catalyst has an effect on the configuration of polymer chain.
文摘Copolymerization of ethylene/1-octene was carried out in toluene withvarious concentrations of comonomer in the feed using Et(Ind)_2ZrCl_2/MAO (methyl alu-minoxane) as catalyst. It was found that with the increase of 1-octene concentration in thefeed the content of 1-octene in the copolymer increases, while the density, melting point,crystallinity and intrinsic viscosity of copolymer decrease. A copolymer with very lowdensity, containing 11.5 mol% of 1-octene (VLLDPE) can be produced with this catalystsystem. The effect of temperature and zirconium aluminum mole ratio of the catalyst onthe copolymerization was also investigated. The results of ^(13)C NMR determination of thecopolymer showed that the 1-octene units in the copolymer are principally isolated.