Suspended emulsion polymerization of vinyl chloride was carried out in a 5 L autoclave. The influence of agitation, polymerization conversion, dispersant and surfactant on the average particle size (PS) and particle s...Suspended emulsion polymerization of vinyl chloride was carried out in a 5 L autoclave. The influence of agitation, polymerization conversion, dispersant and surfactant on the average particle size (PS) and particle size distribution (PSD), particle morphology and porosity of polyvinyl chloride (PVC) resin was investigated. It showed that the agitator had great influence on the smooth operation of polymerization, PS and PSD. The PS increased and PSD became narrow as polymerization conversion became high. The porosity decreased with the increase of conversion. A convenient choice of additives, both dispersants and non-ionic surfactants, allows one to adjust PS and PSD. The PS decreased with the addition of polyvinyl alcohol or hydroxypropyl methylcellulose dispersants,and increased with the addition of Span surfactants. The addition of dispersants or surfactants also affected the morphology and porosity of resin, and PVC resin with looser agglomeration and homogeneous distribution of primary particles was prepared.展开更多
基金Supported by the National Natural Science Foundation of China (No. 29906009).
文摘Suspended emulsion polymerization of vinyl chloride was carried out in a 5 L autoclave. The influence of agitation, polymerization conversion, dispersant and surfactant on the average particle size (PS) and particle size distribution (PSD), particle morphology and porosity of polyvinyl chloride (PVC) resin was investigated. It showed that the agitator had great influence on the smooth operation of polymerization, PS and PSD. The PS increased and PSD became narrow as polymerization conversion became high. The porosity decreased with the increase of conversion. A convenient choice of additives, both dispersants and non-ionic surfactants, allows one to adjust PS and PSD. The PS decreased with the addition of polyvinyl alcohol or hydroxypropyl methylcellulose dispersants,and increased with the addition of Span surfactants. The addition of dispersants or surfactants also affected the morphology and porosity of resin, and PVC resin with looser agglomeration and homogeneous distribution of primary particles was prepared.