Three kinds of different phases of Mg-xLi-1Al alloys with x=5 （full α LA51）, 9 （dual-phase LA91）, and 14 （rich-βLA141） were prepared by vacuum melting method. Their microstructure and damping capacities were i...Three kinds of different phases of Mg-xLi-1Al alloys with x=5 （full α LA51）, 9 （dual-phase LA91）, and 14 （rich-βLA141） were prepared by vacuum melting method. Their microstructure and damping capacities were investigated by optical microscopy, X-ray diffractometry, and dynamic mechanical analysis. The results show that the addition of Li changes the crystal structure of the alloys and causes new damping mechanisms to emerge. And the appearance of BCC structure makes the damping performance improved remarkably. The lower the elastic modulus is, the smaller the strain is and even the slower the acceleration is. The dual-phase alloy shows a better damping capacity while the temperature changes. Furthermore, all three alloys have two significant peaks：P1 caused by the movement of dislocations on the basal planes and P2 caused by the sliding of grain boundaries.展开更多
The effects of Zn addition on the microstructure and mechanical properties of Mg.10Gd.3Y.0.6Zr(wt.%)alloys in the as-cast,solution-treated,and peak-aged conditions were investigated.Experimental results reveal that th...The effects of Zn addition on the microstructure and mechanical properties of Mg.10Gd.3Y.0.6Zr(wt.%)alloys in the as-cast,solution-treated,and peak-aged conditions were investigated.Experimental results reveal that the microstructure of the as-cast alloy without Zn consists ofα-Mg and Mg24(Gd,Y)5 phases,and the alloy with 0.5 wt.%Zn consists ofα-Mg,(Mg,Zn)3(Gd,Y)and Mg24(Gd,Y,Zn)5 phases.With the addition of Zn increasing to 1 wt.%,the Mg24(Gd,Y,Zn)5 phase disappears and some needle-like stacking faults distribute along the grain boundaries.Moreover,the 18R long-period stacking ordered(LPSO)phase is observed in the as-cast alloy with 2 wt.%Zn.After solution treatment,the Mg24(Gd,Y)5 and Mg24(Gd,Y,Zn)5 eutectic phases are completely dissolved,and the(Mg,Zn)3(Gd,Y)phase,needle-like stacking faults and 18R LPSO phase all transform into 14H LPSO phase.Both the suitable volume fraction of 14H LPSO phases and the fine ellipsoidal-shapedβ′phases make the peak-aged alloy with 0.5 wt.%Zn exhibit excellent comprehensive mechanical properties and the UTS,YS and elongation are 338 MPa,201 MPa and 6.8%,respectively.展开更多
Magnesium alloys possess lots of unique advantages as one of the most promising materials. However, relatively poor mechanical properties limit the application of Mg alloys. As a relatively excellent strengthing phase...Magnesium alloys possess lots of unique advantages as one of the most promising materials. However, relatively poor mechanical properties limit the application of Mg alloys. As a relatively excellent strengthing phase, icosahedral quasicrystal phased-phase） has great influence on Mg-Zn-Y-（Zr） alloys. The yield strength of Mg-Zn-Y-（Zr） alloys could reach 150 - 450 MPa at room temperature with different I-phase volume fractions, therefore the formation of I-phase has been regared as an effective method to improve the performance of Mg alloys. In this review paper, a series of researches about the Mg-Zn-Y-（Zr） alloys containing I-phase have been discussed, mainly including the current understandings about formation mechanism and I- phase structure, its orientation relationship with a-Mg matrix, and the effect of I-phase on Mg-Zn-Y-（Zr） alloys.展开更多
The microstructure and damping capacities of MgZnxYi.33x(x=l-4at.%)alloys were discussed and researched.The main phase composition of the alloys consists of a_Mg and long-period stacking ordered(LPSO)phase.Due to incr...The microstructure and damping capacities of MgZnxYi.33x(x=l-4at.%)alloys were discussed and researched.The main phase composition of the alloys consists of a_Mg and long-period stacking ordered(LPSO)phase.Due to increasedLPSO phase,grain size was refined.LPSO phase was advantageous to the damping properties of the Mg-Zn-Y alloys.Mg-7%Zn-12.8%Y has the highest damping capacity up to0.04.Due to stacking fault probability,the LPSO phase in the Mg-Zn-Yalloys could be new damping source to dissipate energy so as to contribute to the improvement of damping capacities.展开更多
The effects of two different casting methods on the microstructures and mechanical properties of as-cast and T6-cast states of Mg-10Gd-3Y-0.6Zr alloy were studied by using metal mold casting and squeeze casting.The re...The effects of two different casting methods on the microstructures and mechanical properties of as-cast and T6-cast states of Mg-10Gd-3Y-0.6Zr alloy were studied by using metal mold casting and squeeze casting.The results show that the microstructure of Mg-10Gd-3Y-0.6Zr alloy is mainly composed ofα-Mg primary phase and Mg 24(Gd,Y)5 eutectic phase.The squeeze cast grains are small with a dendrite like morphology,and the tensile strength of the alloy in T6 state can reach 285 MPa.While the metal grains are coarse,the eutectic phases are distributed in the grain boundary,and the tensile strength of the alloy in T6 state is only 250 MPa.展开更多
基金Project(NCET-11-0554)supported by the Program for New Century Excellent Talents in University,ChinaProject(2011BAE22B04)supported by the National Key Technology R&D Program,ChinaProject(51271206)supported by the National Natural Science Foundation of China
文摘Three kinds of different phases of Mg-xLi-1Al alloys with x=5 （full α LA51）, 9 （dual-phase LA91）, and 14 （rich-βLA141） were prepared by vacuum melting method. Their microstructure and damping capacities were investigated by optical microscopy, X-ray diffractometry, and dynamic mechanical analysis. The results show that the addition of Li changes the crystal structure of the alloys and causes new damping mechanisms to emerge. And the appearance of BCC structure makes the damping performance improved remarkably. The lower the elastic modulus is, the smaller the strain is and even the slower the acceleration is. The dual-phase alloy shows a better damping capacity while the temperature changes. Furthermore, all three alloys have two significant peaks：P1 caused by the movement of dislocations on the basal planes and P2 caused by the sliding of grain boundaries.
基金Projects(51774254,51774253,51701187,U1610123,51674226,51574207,51574206)supported by the National Natural Science Foundation of ChinaProject(MC2016-06)supported by the Science and Technology Major Project of Shanxi Province,ChinaProject(201601D021062)supported by Shanxi Province Science Foundation for Youths,China
文摘The effects of Zn addition on the microstructure and mechanical properties of Mg.10Gd.3Y.0.6Zr(wt.%)alloys in the as-cast,solution-treated,and peak-aged conditions were investigated.Experimental results reveal that the microstructure of the as-cast alloy without Zn consists ofα-Mg and Mg24(Gd,Y)5 phases,and the alloy with 0.5 wt.%Zn consists ofα-Mg,(Mg,Zn)3(Gd,Y)and Mg24(Gd,Y,Zn)5 phases.With the addition of Zn increasing to 1 wt.%,the Mg24(Gd,Y,Zn)5 phase disappears and some needle-like stacking faults distribute along the grain boundaries.Moreover,the 18R long-period stacking ordered(LPSO)phase is observed in the as-cast alloy with 2 wt.%Zn.After solution treatment,the Mg24(Gd,Y)5 and Mg24(Gd,Y,Zn)5 eutectic phases are completely dissolved,and the(Mg,Zn)3(Gd,Y)phase,needle-like stacking faults and 18R LPSO phase all transform into 14H LPSO phase.Both the suitable volume fraction of 14H LPSO phases and the fine ellipsoidal-shapedβ′phases make the peak-aged alloy with 0.5 wt.%Zn exhibit excellent comprehensive mechanical properties and the UTS,YS and elongation are 338 MPa,201 MPa and 6.8%,respectively.
基金National Natural Science Foundation of China(Nos.U1610123,51674226,51574207)International Cooperation project of the Ministry of Science and Technology of China(No.2014DFA50320)Science and Technology Major Project of Shanxi Province(No.MC2016-06)
文摘Magnesium alloys possess lots of unique advantages as one of the most promising materials. However, relatively poor mechanical properties limit the application of Mg alloys. As a relatively excellent strengthing phase, icosahedral quasicrystal phased-phase） has great influence on Mg-Zn-Y-（Zr） alloys. The yield strength of Mg-Zn-Y-（Zr） alloys could reach 150 - 450 MPa at room temperature with different I-phase volume fractions, therefore the formation of I-phase has been regared as an effective method to improve the performance of Mg alloys. In this review paper, a series of researches about the Mg-Zn-Y-（Zr） alloys containing I-phase have been discussed, mainly including the current understandings about formation mechanism and I- phase structure, its orientation relationship with a-Mg matrix, and the effect of I-phase on Mg-Zn-Y-（Zr） alloys.
基金National Natural Science Foundation of China(Nos.U1610123,51674226,51574207,51574206,51274175)International Cooperation project of the Ministry of Science and Technology of China(No.2014DFA50320)+4 种基金The Science and Technology Major Project of Shanxi Province(No.MC2016-06)International Science and Technology Cooperation Project of Shanxi Province(No.2015081041)Research Project Supported by Shanxi Scholarship Council of China(No.2016-Key 2)Transformation of Scientific and Technological Achievements Special Guide Project of Shanxi Province(No.201604D131029)Shanxi Province Science Foundation for Youths(No.201601D021062)
文摘The microstructure and damping capacities of MgZnxYi.33x(x=l-4at.%)alloys were discussed and researched.The main phase composition of the alloys consists of a_Mg and long-period stacking ordered(LPSO)phase.Due to increasedLPSO phase,grain size was refined.LPSO phase was advantageous to the damping properties of the Mg-Zn-Y alloys.Mg-7%Zn-12.8%Y has the highest damping capacity up to0.04.Due to stacking fault probability,the LPSO phase in the Mg-Zn-Yalloys could be new damping source to dissipate energy so as to contribute to the improvement of damping capacities.
基金International Cooperation Project of the Ministry of Science and Technology of China(No.2014DFA50320)National Natural Science Foundation of China(Nos.51674226,51574207,51574206,51204147,51274175)International Science and Technology Cooperation Project of Shanxi Province(Nos.2013081017,2012081013)
文摘The effects of two different casting methods on the microstructures and mechanical properties of as-cast and T6-cast states of Mg-10Gd-3Y-0.6Zr alloy were studied by using metal mold casting and squeeze casting.The results show that the microstructure of Mg-10Gd-3Y-0.6Zr alloy is mainly composed ofα-Mg primary phase and Mg 24(Gd,Y)5 eutectic phase.The squeeze cast grains are small with a dendrite like morphology,and the tensile strength of the alloy in T6 state can reach 285 MPa.While the metal grains are coarse,the eutectic phases are distributed in the grain boundary,and the tensile strength of the alloy in T6 state is only 250 MPa.