To prevent dense chromium oxide covers from cracking during firing,such as internal cracking,surface cracking and fracture,the firing process of dense chromium oxide products was simulated,and the performance paramete...To prevent dense chromium oxide covers from cracking during firing,such as internal cracking,surface cracking and fracture,the firing process of dense chromium oxide products was simulated,and the performance parameters at several specific temperatures before and after densification of chromium oxide green bodies were tested.The temperature difference and the stress difference of chromium oxide green bodies were calculated by Finite Element Software at heating and cooling rates of 10,20,30 and 40℃·h^(-1),respectively.The results show that large temperature difference and thermal stress difference are the main causes of internal cracking,surface cracking and fracture of the brick.Suitable heating rates reduce or avoid internal cracking of the brick.When the heating rate is 30℃·h^(-1) below 1450℃and 10℃·h^(-1) above 1450℃,the temperature difference and the thermal stress difference in the brick are below 4℃and 4 MPa,respectively,and there is no internal crack in the brick after firing.The initial cooling stage is the key stage that causes cracking or fracture of bricks.When the cooling rate is 20℃·h^(-1) above 1450℃,the thermal stress difference in the brick is less than 4 MPa,which can significantly reduce the surface cracks and fracture of the brick.展开更多
Commercial high purity corundum brick,corundum-mullite brick,mullite brick,calcium hexaaluminate brick and calcium hexaaluminate-corundum brick were studied to investigate their reaction state and alkali vapor corrosi...Commercial high purity corundum brick,corundum-mullite brick,mullite brick,calcium hexaaluminate brick and calcium hexaaluminate-corundum brick were studied to investigate their reaction state and alkali vapor corrosion mechanism at 1370 and 1500℃.The results show that:(1)served in hot alkali vapor,the high-purity corundum brick has no obvious slag layer but expands dramatically;(2)the corundum-mullite brick shows obvious reactive expansion at 1370℃and melting corrosion happens at 1500℃;(3)at 1370℃alkali vapor and mullite brick react and form a slag layer without volume effect;when the temperature increases to 1500℃,the reaction melting corrosion intensifies;(4)the calcium hexaaluminate brick and the calcium hexaaluminate-corundum brick form a thin slag layer in alkali vapor,and the sample surface absorbs Na+to form a dense layer with small volume effect.展开更多
文摘To prevent dense chromium oxide covers from cracking during firing,such as internal cracking,surface cracking and fracture,the firing process of dense chromium oxide products was simulated,and the performance parameters at several specific temperatures before and after densification of chromium oxide green bodies were tested.The temperature difference and the stress difference of chromium oxide green bodies were calculated by Finite Element Software at heating and cooling rates of 10,20,30 and 40℃·h^(-1),respectively.The results show that large temperature difference and thermal stress difference are the main causes of internal cracking,surface cracking and fracture of the brick.Suitable heating rates reduce or avoid internal cracking of the brick.When the heating rate is 30℃·h^(-1) below 1450℃and 10℃·h^(-1) above 1450℃,the temperature difference and the thermal stress difference in the brick are below 4℃and 4 MPa,respectively,and there is no internal crack in the brick after firing.The initial cooling stage is the key stage that causes cracking or fracture of bricks.When the cooling rate is 20℃·h^(-1) above 1450℃,the thermal stress difference in the brick is less than 4 MPa,which can significantly reduce the surface cracks and fracture of the brick.
文摘Commercial high purity corundum brick,corundum-mullite brick,mullite brick,calcium hexaaluminate brick and calcium hexaaluminate-corundum brick were studied to investigate their reaction state and alkali vapor corrosion mechanism at 1370 and 1500℃.The results show that:(1)served in hot alkali vapor,the high-purity corundum brick has no obvious slag layer but expands dramatically;(2)the corundum-mullite brick shows obvious reactive expansion at 1370℃and melting corrosion happens at 1500℃;(3)at 1370℃alkali vapor and mullite brick react and form a slag layer without volume effect;when the temperature increases to 1500℃,the reaction melting corrosion intensifies;(4)the calcium hexaaluminate brick and the calcium hexaaluminate-corundum brick form a thin slag layer in alkali vapor,and the sample surface absorbs Na+to form a dense layer with small volume effect.