Elucidation of a reaction mechanism is the most critical aspect for designing electrodes for highperformance secondary batteries.Herein,we investigate the sodium insertion/extraction into an iron fluoride hydrate(FeF_...Elucidation of a reaction mechanism is the most critical aspect for designing electrodes for highperformance secondary batteries.Herein,we investigate the sodium insertion/extraction into an iron fluoride hydrate(FeF_(3)·0.5H_(2)O)electrode for sodium-ion batteries(SIBs).The electrode material is prepared by employing an ionic liquid 1-butyl-3-methylimidazolium-tetrafluoroborate,which serves as a reaction medium and precursor for F^(-)ions.The crystal structure of FeF_(3)·0.5H_(2)O is observed as pyrochlore type with large open 3-D tunnels and a unit cell volume of 1129A^(3).The morphology of FeF_(3)·0.5H_(2)O is spherical shape with a mesoporous structure.The microstructure analysis reveals primary particle size of around 10 nm.The FeF_(3)·0.5H_(2)O cathode exhibits stable discharge capacities of 158,210,and 284 mA h g^(-1) in three different potential ranges of 1.5-4.5,1.2-4.5,and 1.0-4.5 V,respectively at 0.05 C rate.The specific capacities remained stable in over 50 cycles in all three potential ranges,while the rate capability was best in the potential range of 1.5-4.5 V.The electrochemical sodium storage mechanism is studied using X-ray absorption spectroscopy,indicating higher conversion at a more discharged state.Ex-situ M?ssbauer spectroscopy strengthens the results for reversible reduction/oxidation of Fe.These results will be favorable to establish high-performance cathode materials with selective voltage window for SIBs.展开更多
基金supported by the Basic Science Research Program of the National Research Foundation(NRF)of South Koreafunded by the Ministry of Science&ICT and Future Planning(NRF-2020M3H4A3081889)KIST Institutional Program of South Korea(Project Nos.2E31860)。
文摘Elucidation of a reaction mechanism is the most critical aspect for designing electrodes for highperformance secondary batteries.Herein,we investigate the sodium insertion/extraction into an iron fluoride hydrate(FeF_(3)·0.5H_(2)O)electrode for sodium-ion batteries(SIBs).The electrode material is prepared by employing an ionic liquid 1-butyl-3-methylimidazolium-tetrafluoroborate,which serves as a reaction medium and precursor for F^(-)ions.The crystal structure of FeF_(3)·0.5H_(2)O is observed as pyrochlore type with large open 3-D tunnels and a unit cell volume of 1129A^(3).The morphology of FeF_(3)·0.5H_(2)O is spherical shape with a mesoporous structure.The microstructure analysis reveals primary particle size of around 10 nm.The FeF_(3)·0.5H_(2)O cathode exhibits stable discharge capacities of 158,210,and 284 mA h g^(-1) in three different potential ranges of 1.5-4.5,1.2-4.5,and 1.0-4.5 V,respectively at 0.05 C rate.The specific capacities remained stable in over 50 cycles in all three potential ranges,while the rate capability was best in the potential range of 1.5-4.5 V.The electrochemical sodium storage mechanism is studied using X-ray absorption spectroscopy,indicating higher conversion at a more discharged state.Ex-situ M?ssbauer spectroscopy strengthens the results for reversible reduction/oxidation of Fe.These results will be favorable to establish high-performance cathode materials with selective voltage window for SIBs.
