Wide-bandgap(>1.7 eV)perovskites suffer from severe light-induced phase segregation due to high bromine content,causing irreversible damage to devices stability.However,the strategies of suppressing photoinduced ph...Wide-bandgap(>1.7 eV)perovskites suffer from severe light-induced phase segregation due to high bromine content,causing irreversible damage to devices stability.However,the strategies of suppressing photoinduced phase segregation and related mechanisms have not been fully disclosed.Here,we report a new passivation agent 4-aminotetrahydrothiopyran hydrochloride(4-ATpHCl)with multifunctional groups for the interface treatment of a 1.77-eV wide-bandgap perovskite film.4-ATpH^(+)impeded halogen ion migration by anchoring on the perovskite surface,leading to the inhibition of phase segregation and thus the passivation of defects,which is ascribed to the interaction of 4-ATpH^(+)with perovskite and the formation of low-dimensional perovskites.Finally,the champion device achieved an efficiency of 19.32%with an open-circuit voltage(V_(OC))of 1.314 V and a fill factor of 83.32%.Moreover,4-ATpHCl modified device exhibited significant improved stability as compared with control one.The target device maintained 80%of its initial efficiency after 519 h of maximum power output(MPP)tracking under 1 sun illumination,however,the control device showed a rapid decrease in efficiency after 267 h.Finally,an efficiency of 27.38%of the champion 4-terminal all-perovskite tandem solar cell was achieved by mechanically stacking this wide-bandgap top subcell with a 1.25-eV low-bandgap perovskite bottom subcell.展开更多
基金financially supported by the National Key R&D Program of China (2022YFB4200304)the National Natural Science Foundation of China (52303347)+3 种基金the Fundamental Research Funds for the Central Universities (YJ2021157)the Engineering Featured Team Fund of Sichuan University (2020SCUNG102)open foundation of Guangxi Key Laboratory of Processing for Non-Ferrous Metals and Featured Materials, Guangxi University (2022GXYSOF05)the support from the National Natural Science Foundation of China (E30853YM19)
文摘Wide-bandgap(>1.7 eV)perovskites suffer from severe light-induced phase segregation due to high bromine content,causing irreversible damage to devices stability.However,the strategies of suppressing photoinduced phase segregation and related mechanisms have not been fully disclosed.Here,we report a new passivation agent 4-aminotetrahydrothiopyran hydrochloride(4-ATpHCl)with multifunctional groups for the interface treatment of a 1.77-eV wide-bandgap perovskite film.4-ATpH^(+)impeded halogen ion migration by anchoring on the perovskite surface,leading to the inhibition of phase segregation and thus the passivation of defects,which is ascribed to the interaction of 4-ATpH^(+)with perovskite and the formation of low-dimensional perovskites.Finally,the champion device achieved an efficiency of 19.32%with an open-circuit voltage(V_(OC))of 1.314 V and a fill factor of 83.32%.Moreover,4-ATpHCl modified device exhibited significant improved stability as compared with control one.The target device maintained 80%of its initial efficiency after 519 h of maximum power output(MPP)tracking under 1 sun illumination,however,the control device showed a rapid decrease in efficiency after 267 h.Finally,an efficiency of 27.38%of the champion 4-terminal all-perovskite tandem solar cell was achieved by mechanically stacking this wide-bandgap top subcell with a 1.25-eV low-bandgap perovskite bottom subcell.
