The classification, characteristics and current situation of aluminum melt hydrogen-removal methods and technologies have been summarized. The latest studies and research results of aluminum melt degassing technology ...The classification, characteristics and current situation of aluminum melt hydrogen-removal methods and technologies have been summarized. The latest studies and research results of aluminum melt degassing technology have been summed up. The tendency and prospect of aluminum degassing technology was discussed.展开更多
Mg-content cored-wire was used to desulphurize and spheroidize ductile iron melt in industrial experiments. The optimal feeding speed and suitable treatment temperature were determined in the experiments. And cored-wi...Mg-content cored-wire was used to desulphurize and spheroidize ductile iron melt in industrial experiments. The optimal feeding speed and suitable treatment temperature were determined in the experiments. And cored-wire method and pouring method were compared. Conclusions have been drawn that, under these conditions in the experiments, the optimal feeding speed is 15m/min, treatment temperature should be as low as possible, 1400-1450℃ generally; and cored-wire method can act more effective in ductile iron melt desulphurization and spheroid than pouring method.展开更多
文摘The classification, characteristics and current situation of aluminum melt hydrogen-removal methods and technologies have been summarized. The latest studies and research results of aluminum melt degassing technology have been summed up. The tendency and prospect of aluminum degassing technology was discussed.
基金the High Technology Research and Development Program of China(No.2002A4336072)
文摘Mg-content cored-wire was used to desulphurize and spheroidize ductile iron melt in industrial experiments. The optimal feeding speed and suitable treatment temperature were determined in the experiments. And cored-wire method and pouring method were compared. Conclusions have been drawn that, under these conditions in the experiments, the optimal feeding speed is 15m/min, treatment temperature should be as low as possible, 1400-1450℃ generally; and cored-wire method can act more effective in ductile iron melt desulphurization and spheroid than pouring method.