The TiB2 coatings deposited over nickel substrate by electroplating was investigated, which is in molten salt of a fluoride mixture involving KF, NaF, K2 TiF6 and KBF4. Effects of temperature, cathodic current density...The TiB2 coatings deposited over nickel substrate by electroplating was investigated, which is in molten salt of a fluoride mixture involving KF, NaF, K2 TiF6 and KBF4. Effects of temperature, cathodic current density (Jc) and duration on the coating's formation were examined. The composition, morphology and structure of the coatings were characterized by scanning electron microscopy (SEM), energy dispersive X-ray detector (EDS) and X-ray diffraction (XRD). The results show that the coatings, with black, smooth and uniform appearance, are composed of predominating TiB2 and small amounts of nickel titanium oxide (Ni0.75 Ti0.125 O). The coatings show a nodular morphology and the grain size is dependent on the Jc and ranges about 1 - 10 μm. There is a linear relationship between the coating's thickness and the time of electrolysis within certain duration range. The reduction of the potassium can take place simultaneously with the electrochemical synthesis of TiB2 as the Jc is in excess of certain level. The hardness of the TiB2 coatings is likely to be deteriorated due to the presence of potassium and Ni0.75Ti0.125 O in the coatings.展开更多
文摘The TiB2 coatings deposited over nickel substrate by electroplating was investigated, which is in molten salt of a fluoride mixture involving KF, NaF, K2 TiF6 and KBF4. Effects of temperature, cathodic current density (Jc) and duration on the coating's formation were examined. The composition, morphology and structure of the coatings were characterized by scanning electron microscopy (SEM), energy dispersive X-ray detector (EDS) and X-ray diffraction (XRD). The results show that the coatings, with black, smooth and uniform appearance, are composed of predominating TiB2 and small amounts of nickel titanium oxide (Ni0.75 Ti0.125 O). The coatings show a nodular morphology and the grain size is dependent on the Jc and ranges about 1 - 10 μm. There is a linear relationship between the coating's thickness and the time of electrolysis within certain duration range. The reduction of the potassium can take place simultaneously with the electrochemical synthesis of TiB2 as the Jc is in excess of certain level. The hardness of the TiB2 coatings is likely to be deteriorated due to the presence of potassium and Ni0.75Ti0.125 O in the coatings.