Nd-Fe-B sintered magnet sludge wastes are one kind of typical commodity of recyclable rare-earth permanent magnet resources,and recycling such kind of wastes with economical and environmentally friendly techniques is ...Nd-Fe-B sintered magnet sludge wastes are one kind of typical commodity of recyclable rare-earth permanent magnet resources,and recycling such kind of wastes with economical and environmentally friendly techniques is crucial to the sustainable rare-earth industry.However,the current multistage wet process recycling technique for the sludge wastes involves high fabrication cost,excessive energy consumption,and heavy environmental burden.Therefore,short-process recycling techniques for Nd-Fe-B sintered magnet wastes have drawn increasing attention in the past decades.In this paper,we review recent efforts into short-process recycling Nd-Fe-B sintered magnet sludge wastes with emphasis on in-situ recycling techniques.展开更多
In this work,the recycled Nd-Fe-B powders and regenerated Nd-Fe-B sintered magnets with low impurity content were successfully prepared from Nd-Fe-B magnet sludge via reduction diffusion(RD)method followed by a chemo-...In this work,the recycled Nd-Fe-B powders and regenerated Nd-Fe-B sintered magnets with low impurity content were successfully prepared from Nd-Fe-B magnet sludge via reduction diffusion(RD)method followed by a chemo-selective dissolution washing proc ess.The chemo-selective dissolution effect of various solution(deionized water,dilute acetic acid solution,NH_(4)Cl-methanol solution) was evaluated by impurity content and magnetic properties of the recycled Nd-Fe-B powder.The NH_(4)Cl-methanol solution can selectively remove impurities with minimal damage to the magnetic phase.Besides,the optimal NH_(4)Cl concentration and liquid-to-solid ratio were investigated.As a consequence,the contents of Ca,O,and H after optimal washing process are reduced to 0.07 wt%,0.31 wt% and 0.22 wt%,respectively.Hence,M_(3) Tis increased to 146.72 emu/g,which is 33% higher than that of the initial sludge.Then,the regenerated Nd-Fe-B sintered magnets with properties of B_(r)=11.66 kG,H_(cj)=16.49 kOe,and(BH)_(m)=31.78 MGOe were successfully prepared by mixing with 40 wt% Nd4Fe14B alloy powders.Compared with the corresponding regenerated magnets washed with deionized water,the remanence and coercivity are increased by 18% and 59%,respectively.展开更多
基金the National Key R&D Project(2021YFB3500800,2020YFC1909004)Science and Technology Program ofAnhui Province(201903a07020002)+1 种基金Program of Top DisciplinesConstruction in Beijing(PXM2019_014204_500031)State Key Laboratoryof Rare Earth Permanent Magnetic Materials Opening Foundation(SKLREPM17OF02)。
文摘Nd-Fe-B sintered magnet sludge wastes are one kind of typical commodity of recyclable rare-earth permanent magnet resources,and recycling such kind of wastes with economical and environmentally friendly techniques is crucial to the sustainable rare-earth industry.However,the current multistage wet process recycling technique for the sludge wastes involves high fabrication cost,excessive energy consumption,and heavy environmental burden.Therefore,short-process recycling techniques for Nd-Fe-B sintered magnet wastes have drawn increasing attention in the past decades.In this paper,we review recent efforts into short-process recycling Nd-Fe-B sintered magnet sludge wastes with emphasis on in-situ recycling techniques.
基金Project supported by the National Key R&D Program of China (2021YFB3500801)the National Natural Science Foundation of China(52271161)+5 种基金the Science and Technology Program of Anhui Province(201903a07020002)General Program of Science and Technology Development Project of Beijing Municipal Education Commission (KM202010005009)"QiHang Programme"for Faculty of Materials and Manufacturing,BJUT (QH202211)Program of Top Disciplines Construction in Beijing (PXM2019_014204_500031)Key Laboratory of Ionic Rare Earth Resources and Environment,Ministry of Natural Resources of the People’s Republic of China (2022IRERE302)the State Key Laboratory of Rare Earth Permanent Magnetic Materials Opening Foundation(SKLREPM170F02)。
文摘In this work,the recycled Nd-Fe-B powders and regenerated Nd-Fe-B sintered magnets with low impurity content were successfully prepared from Nd-Fe-B magnet sludge via reduction diffusion(RD)method followed by a chemo-selective dissolution washing proc ess.The chemo-selective dissolution effect of various solution(deionized water,dilute acetic acid solution,NH_(4)Cl-methanol solution) was evaluated by impurity content and magnetic properties of the recycled Nd-Fe-B powder.The NH_(4)Cl-methanol solution can selectively remove impurities with minimal damage to the magnetic phase.Besides,the optimal NH_(4)Cl concentration and liquid-to-solid ratio were investigated.As a consequence,the contents of Ca,O,and H after optimal washing process are reduced to 0.07 wt%,0.31 wt% and 0.22 wt%,respectively.Hence,M_(3) Tis increased to 146.72 emu/g,which is 33% higher than that of the initial sludge.Then,the regenerated Nd-Fe-B sintered magnets with properties of B_(r)=11.66 kG,H_(cj)=16.49 kOe,and(BH)_(m)=31.78 MGOe were successfully prepared by mixing with 40 wt% Nd4Fe14B alloy powders.Compared with the corresponding regenerated magnets washed with deionized water,the remanence and coercivity are increased by 18% and 59%,respectively.