Material flow and phase transformation were studied at the interface of dissimilar joint between Al 6013 and Mg, produced by stir friction welding （FSW） experiments. Defect-free weld was obtained when aluminum and m...Material flow and phase transformation were studied at the interface of dissimilar joint between Al 6013 and Mg, produced by stir friction welding （FSW） experiments. Defect-free weld was obtained when aluminum and magnesium were placed in the advancing side and retreating side respectively and the tool was placed 1 mm off the weld centerline into the aluminum side. In order to understand the material flow during FSW, steel shots were implanted as indexes into the welding path. After welding, using X-ray images, secondary positions of the steel shots were evaluated. It was revealed that steel shots implanted in advancing side were penetrated from the advancing side into the retreating side, whereas the shots implanted in the retreating side remained in the retreating side, without penetrating into the advancing side. The welded specimens were also heat treated. The effects of heat treatment on the mechanical properties of the welds and the formation of new intermetallic layers were investigated. Two intermetallic compounds, Al3Mg2 and Al12Mg17, were formed sequentially at Al6013/Mg interface.展开更多
Aluminum and silver strips were cold welded by rolling and a bimetallic strip was produced. To create cold weld between A1 and Ag, mating surfaces were specially prepared and various rolling thickness reductions were ...Aluminum and silver strips were cold welded by rolling and a bimetallic strip was produced. To create cold weld between A1 and Ag, mating surfaces were specially prepared and various rolling thickness reductions were applied. The minimum critical thickness reduction to begin cold weld was specified as 70% which equals 0.1630 critical rolling shape factors. The bimetallic strips were treated by diffusion annealing at 400 ~C and various annealing time. The A1/Ag interface of strips was observed by scanning electron microscope to investigate the formation of hard and brittle probable phases. The effect of anneal time on diffusion distance and phase transformation was also analysed by EDS analysis and line scan. A diffusion region along the interface in the Ag side was observed and its width increased with prolonging annealing time. Some 8 phases were detected close to the interface after anneal treating for 3 h and 8 phase was thicker and more continuous by increasing annealing time. The microhardness measurement showed that in spite of formation of 8 phase due to diffusion annealing, the interface hardness was reduced.展开更多
文摘Material flow and phase transformation were studied at the interface of dissimilar joint between Al 6013 and Mg, produced by stir friction welding （FSW） experiments. Defect-free weld was obtained when aluminum and magnesium were placed in the advancing side and retreating side respectively and the tool was placed 1 mm off the weld centerline into the aluminum side. In order to understand the material flow during FSW, steel shots were implanted as indexes into the welding path. After welding, using X-ray images, secondary positions of the steel shots were evaluated. It was revealed that steel shots implanted in advancing side were penetrated from the advancing side into the retreating side, whereas the shots implanted in the retreating side remained in the retreating side, without penetrating into the advancing side. The welded specimens were also heat treated. The effects of heat treatment on the mechanical properties of the welds and the formation of new intermetallic layers were investigated. Two intermetallic compounds, Al3Mg2 and Al12Mg17, were formed sequentially at Al6013/Mg interface.
文摘Aluminum and silver strips were cold welded by rolling and a bimetallic strip was produced. To create cold weld between A1 and Ag, mating surfaces were specially prepared and various rolling thickness reductions were applied. The minimum critical thickness reduction to begin cold weld was specified as 70% which equals 0.1630 critical rolling shape factors. The bimetallic strips were treated by diffusion annealing at 400 ~C and various annealing time. The A1/Ag interface of strips was observed by scanning electron microscope to investigate the formation of hard and brittle probable phases. The effect of anneal time on diffusion distance and phase transformation was also analysed by EDS analysis and line scan. A diffusion region along the interface in the Ag side was observed and its width increased with prolonging annealing time. Some 8 phases were detected close to the interface after anneal treating for 3 h and 8 phase was thicker and more continuous by increasing annealing time. The microhardness measurement showed that in spite of formation of 8 phase due to diffusion annealing, the interface hardness was reduced.
