Magnetization roasting is one of the most effective way of utilizing low-grade refractory iron ore.However,the reduction roasting of siderite(FeCO3)generates weakly magnetic wüstite,thus reducing iron recovery vi...Magnetization roasting is one of the most effective way of utilizing low-grade refractory iron ore.However,the reduction roasting of siderite(FeCO3)generates weakly magnetic wüstite,thus reducing iron recovery via weak magnetic separation.We systematically studied and proposed the fluidized preoxidation-low-temperature reduction magnetization roasting process for siderite.We found that the maghemite generated during the air oxidation roasting of siderite would be further reduced into wüstite at 500 and 550℃due to the unstable intermediate product magnetite(Fe_(3)O_(4)).Stable magnetite can be obtained through maghemite reduction only at low temperature.The optimal fluidized magnetization roasting parameters included preoxidation at 610℃for 2.5 min,followed by reduction at 450℃for 5 min.For roasted ore,weak magnetic separation yielded an iron ore concentrate grade of 62.0wt%and an iron recovery rate of 88.36%.Compared with that of conventional direct reduction magnetization roasting,the iron recovery rate of weak magnetic separation had greatly improved by 34.33%.The proposed fluidized preoxidation-low-temperature reduction magnetization roasting process can realize the efficient magnetization roasting utilization of low-grade refractory siderite-containing iron ore without wüstite generation and is unlimited by the proportion of siderite and hematite in iron ore.展开更多
The correlation between phase structures and surface acidity of Al2O3 supports calcined at different temperatures and the catalytic performance of Ni/Al2O3 catalysts in the production of synthetic natural gas(SNG) via...The correlation between phase structures and surface acidity of Al2O3 supports calcined at different temperatures and the catalytic performance of Ni/Al2O3 catalysts in the production of synthetic natural gas(SNG) via CO methanation was systematically investigated. A series of 10 wt% NiO/Al2O3 catalysts were prepared by the conventional impregnation method, and the phase structures and surface acidity of Al2O3 supports were adjusted by calcining the commercial γ-Al2O3 at different temperatures(600–1200 C). CO methanation reaction was carried out in the temperature range of 300–600 C at different weight hourly space velocities(WHSV = 30000 and 120000 mL·g-1h-1) and pressures(0.1 and 3.0 MPa). It was found that high calcination temperature not only led to the growth in Ni particle size, but also weakened the interaction between Ni nanoparticles and Al2O3 supports due to the rapid decrease of the specific surface area and acidity of Al2O3 supports. Interestingly, Ni catalysts supported on Al2O3 calcined at 1200 C(Ni/Al2O3-1200) exhibited the best catalytic activity for CO methanation under different reaction conditions. Lifetime reaction tests also indicated that Ni/Al2O3-1200 was the most active and stable catalyst compared with the other three catalysts, whose supports were calcined at lower temperatures(600, 800 and 1000 C). These findings would therefore be helpful to develop Ni/Al2O3 methanation catalyst for SNG production.展开更多
Ultrafine or nano-sized of tungsten carbide(WC)is the key material to prepare ultrafine grained cemented carbides.In this paper,nano-sized WC powders were directly prepared by using industrial nano-needle violet tungs...Ultrafine or nano-sized of tungsten carbide(WC)is the key material to prepare ultrafine grained cemented carbides.In this paper,nano-sized WC powders were directly prepared by using industrial nano-needle violet tungsten oxide(WO2.72)as the raw material,a fluidized bed as the reactor,and CO as the carbonization gas.The relationship between particle sizes and reaction temperatures,residence times,atmospheres has been investigated systematically.In addition,the physical–chemical indexes(such as residual oxygen,total carbon and free carbon)of the products were measured.The results indicated that the particle size of WC increased with the increase of temperature from 800 to 950°C.As the residence time increased,the particle size decreased gradually,and then increased due to slight sintering.The introduction of hydrogen reduced the carbonization rate,and is not beneficial to obtaining nano-sized WC.Products that satisfy the standard were obtained when WO2.72 reacted with CO at 850°C,900°C and 950°C for 3.0 h,2.5 h and 2.0 h,respectively.The particle sizes of the three samples calculated from the specific surface area were 46.4 nm,53.2 nm and 52.1 nm,respectively.展开更多
基金the National Natural Science Foundation of China(Nos.51974287 and 21736010)Innovation Academy for Green Manufacture,Chinese Academy of Sciences(No.IAGM-2019-A11).
文摘Magnetization roasting is one of the most effective way of utilizing low-grade refractory iron ore.However,the reduction roasting of siderite(FeCO3)generates weakly magnetic wüstite,thus reducing iron recovery via weak magnetic separation.We systematically studied and proposed the fluidized preoxidation-low-temperature reduction magnetization roasting process for siderite.We found that the maghemite generated during the air oxidation roasting of siderite would be further reduced into wüstite at 500 and 550℃due to the unstable intermediate product magnetite(Fe_(3)O_(4)).Stable magnetite can be obtained through maghemite reduction only at low temperature.The optimal fluidized magnetization roasting parameters included preoxidation at 610℃for 2.5 min,followed by reduction at 450℃for 5 min.For roasted ore,weak magnetic separation yielded an iron ore concentrate grade of 62.0wt%and an iron recovery rate of 88.36%.Compared with that of conventional direct reduction magnetization roasting,the iron recovery rate of weak magnetic separation had greatly improved by 34.33%.The proposed fluidized preoxidation-low-temperature reduction magnetization roasting process can realize the efficient magnetization roasting utilization of low-grade refractory siderite-containing iron ore without wüstite generation and is unlimited by the proportion of siderite and hematite in iron ore.
基金supported by the Hundred Talents Program of the Chinese Academy of Sciences (CAS),State Key Laboratory of Multiphase Complex Systems of China (No.MPCS-2009-C-01)the National Key Technology R&D Program of China (No.2010BAC66B01)the Knowledge Innovation Program of the CAS (No.KGCX2-YW-396)
文摘The correlation between phase structures and surface acidity of Al2O3 supports calcined at different temperatures and the catalytic performance of Ni/Al2O3 catalysts in the production of synthetic natural gas(SNG) via CO methanation was systematically investigated. A series of 10 wt% NiO/Al2O3 catalysts were prepared by the conventional impregnation method, and the phase structures and surface acidity of Al2O3 supports were adjusted by calcining the commercial γ-Al2O3 at different temperatures(600–1200 C). CO methanation reaction was carried out in the temperature range of 300–600 C at different weight hourly space velocities(WHSV = 30000 and 120000 mL·g-1h-1) and pressures(0.1 and 3.0 MPa). It was found that high calcination temperature not only led to the growth in Ni particle size, but also weakened the interaction between Ni nanoparticles and Al2O3 supports due to the rapid decrease of the specific surface area and acidity of Al2O3 supports. Interestingly, Ni catalysts supported on Al2O3 calcined at 1200 C(Ni/Al2O3-1200) exhibited the best catalytic activity for CO methanation under different reaction conditions. Lifetime reaction tests also indicated that Ni/Al2O3-1200 was the most active and stable catalyst compared with the other three catalysts, whose supports were calcined at lower temperatures(600, 800 and 1000 C). These findings would therefore be helpful to develop Ni/Al2O3 methanation catalyst for SNG production.
基金the financial support from the National Natural Science Foundation of China(Grant No.21878305)。
文摘Ultrafine or nano-sized of tungsten carbide(WC)is the key material to prepare ultrafine grained cemented carbides.In this paper,nano-sized WC powders were directly prepared by using industrial nano-needle violet tungsten oxide(WO2.72)as the raw material,a fluidized bed as the reactor,and CO as the carbonization gas.The relationship between particle sizes and reaction temperatures,residence times,atmospheres has been investigated systematically.In addition,the physical–chemical indexes(such as residual oxygen,total carbon and free carbon)of the products were measured.The results indicated that the particle size of WC increased with the increase of temperature from 800 to 950°C.As the residence time increased,the particle size decreased gradually,and then increased due to slight sintering.The introduction of hydrogen reduced the carbonization rate,and is not beneficial to obtaining nano-sized WC.Products that satisfy the standard were obtained when WO2.72 reacted with CO at 850°C,900°C and 950°C for 3.0 h,2.5 h and 2.0 h,respectively.The particle sizes of the three samples calculated from the specific surface area were 46.4 nm,53.2 nm and 52.1 nm,respectively.