The porosity, pore size and softening of 6063 aluminum alloy CMT MIX + Synchropulse welded joint with different welding speeds were studied. The results show that with the increase of welding speed(from 55 to 65 cm/mi...The porosity, pore size and softening of 6063 aluminum alloy CMT MIX + Synchropulse welded joint with different welding speeds were studied. The results show that with the increase of welding speed(from 55 to 65 cm/min), the porosity increases dramatically(from 0.1% to 3.9%) and large pores(341.1 μm) appear. The pore size distributions are mainly concentrated at 87.8 and 20.6 μm in the joints produced from weld speeds of 65 and 55 cm/min, respectively. The dissolution and transformation of the β′′ phase in the base metal(BM) result in a significant softening of both the fusion zone and heat-affected zone, and the latter was more serious. The effects of welding speed on the average tensile strength of the full penetration welded joints are minor, which was about 155 MPa(67.4% that of the BM).展开更多
基金financially supported by the Major Program of the National Natural Science Foundation of China (No. U1864209)the “Qinglan” Project of Jiangsu Province, China。
文摘The porosity, pore size and softening of 6063 aluminum alloy CMT MIX + Synchropulse welded joint with different welding speeds were studied. The results show that with the increase of welding speed(from 55 to 65 cm/min), the porosity increases dramatically(from 0.1% to 3.9%) and large pores(341.1 μm) appear. The pore size distributions are mainly concentrated at 87.8 and 20.6 μm in the joints produced from weld speeds of 65 and 55 cm/min, respectively. The dissolution and transformation of the β′′ phase in the base metal(BM) result in a significant softening of both the fusion zone and heat-affected zone, and the latter was more serious. The effects of welding speed on the average tensile strength of the full penetration welded joints are minor, which was about 155 MPa(67.4% that of the BM).