AZ31B magnesium alloy and nano-composite were manufactured by hybrid casting process and hot extruded at 350 °C. The sliding wear behaviour of alloy and nano-composite was estimated at room temperature using the ...AZ31B magnesium alloy and nano-composite were manufactured by hybrid casting process and hot extruded at 350 °C. The sliding wear behaviour of alloy and nano-composite was estimated at room temperature using the standard pin-on-disc wear test equipment. The tests were conducted under a normal load of 10 N at different sliding speeds ranging from 0.60 to 1.2 m/s for distance up to 2000 m. The wear mechanisms of the worn out surface were studied using SEM analysis. The influence of test parameters on wear rate of the pins was established using a linear regression model statistically. Compared with the AZ31B magnesium alloy, the nano-composite shows lower wear rates due to higher hardness improvement caused by the reinforcement. The wear mechanism appears to be a mix-up of ploughing, rows of furrows, delamination and oxidation.展开更多
Achieving not only high mechanical strengths but also high ductility is recently established using an additive manufacturing technique called selective laser melting. In the present study, stainless steel 304 L fully ...Achieving not only high mechanical strengths but also high ductility is recently established using an additive manufacturing technique called selective laser melting. In the present study, stainless steel 304 L fully dense samples were successfully printed using the 3 D systems – ProX 300 printing machine. The ductility and tensile yield strength were almost two and three times higher compared to those of ASTM cast's alloy. Honey comb like nano-cellular structure with different orientation was observed in the fine grains(~4μm) due to fast cooling rate. In addition, the formation of martensite phase in random grains is also a contributor to the strengths. Furthermore, negative residual stresses in the build and horizontal directions were detected and assisted further increase in the tensile strength. Fractography revealed the ductile feature of plastic deformation and the crack openings at unmelted particles or pores.展开更多
文摘AZ31B magnesium alloy and nano-composite were manufactured by hybrid casting process and hot extruded at 350 °C. The sliding wear behaviour of alloy and nano-composite was estimated at room temperature using the standard pin-on-disc wear test equipment. The tests were conducted under a normal load of 10 N at different sliding speeds ranging from 0.60 to 1.2 m/s for distance up to 2000 m. The wear mechanisms of the worn out surface were studied using SEM analysis. The influence of test parameters on wear rate of the pins was established using a linear regression model statistically. Compared with the AZ31B magnesium alloy, the nano-composite shows lower wear rates due to higher hardness improvement caused by the reinforcement. The wear mechanism appears to be a mix-up of ploughing, rows of furrows, delamination and oxidation.
基金support from A*STAR Industrial Additive Manufacturing Facilities with the research grant number 142680088
文摘Achieving not only high mechanical strengths but also high ductility is recently established using an additive manufacturing technique called selective laser melting. In the present study, stainless steel 304 L fully dense samples were successfully printed using the 3 D systems – ProX 300 printing machine. The ductility and tensile yield strength were almost two and three times higher compared to those of ASTM cast's alloy. Honey comb like nano-cellular structure with different orientation was observed in the fine grains(~4μm) due to fast cooling rate. In addition, the formation of martensite phase in random grains is also a contributor to the strengths. Furthermore, negative residual stresses in the build and horizontal directions were detected and assisted further increase in the tensile strength. Fractography revealed the ductile feature of plastic deformation and the crack openings at unmelted particles or pores.