High strength abrasion resistant steel plates are widely used in mining,construction and agricultural machineries.The plates are,however,usually poor in impact toughness.An attempt is made to improve the impact toughn...High strength abrasion resistant steel plates are widely used in mining,construction and agricultural machineries.The plates are,however,usually poor in impact toughness.An attempt is made to improve the impact toughness of HB400 grade abrasion resistant steel by controlling quenching and tempering of the plates.Optimized combination of the strength and the toughness has been achieved by choosing best fit set of quenching and tempering condition.Mechanism underlying the achievement has been investigated in terms of the microstructure consisting of tempered lath martensite,retained austenite and precipitated carbides.展开更多
The weldability of 12MnNiVR was examined in terms of the simulated HAZ continuous cooling transformation (SH-CCT) diagram,microstructure and mechanical properties of the simulated coarse grain heat-affected zone (CGHA...The weldability of 12MnNiVR was examined in terms of the simulated HAZ continuous cooling transformation (SH-CCT) diagram,microstructure and mechanical properties of the simulated coarse grain heat-affected zone (CGHAZ).When t 8/5 is shorter,the microstructure mainly consists of lath bainite.When t 8/5 is 60 s,the microstructure becomes coarser bainite.Some acicular ferrite appears beside lath bainite when t 8/5 =100s.Finally,a microstructure composed of polygonal ferrite,acicular ferrite,and small amount pearlite is obtained with a small amount of bainite at t 8/5 】100s.With the increase of t 8/5,the hardness of CGHAZ decreases considerably.The minimum impact toughness of CGHAZ appears at t 8/5 =100s.The hardness and the toughness of CGHAZ remain above the specified values for steel 12MnNiVR.展开更多
文摘High strength abrasion resistant steel plates are widely used in mining,construction and agricultural machineries.The plates are,however,usually poor in impact toughness.An attempt is made to improve the impact toughness of HB400 grade abrasion resistant steel by controlling quenching and tempering of the plates.Optimized combination of the strength and the toughness has been achieved by choosing best fit set of quenching and tempering condition.Mechanism underlying the achievement has been investigated in terms of the microstructure consisting of tempered lath martensite,retained austenite and precipitated carbides.
文摘The weldability of 12MnNiVR was examined in terms of the simulated HAZ continuous cooling transformation (SH-CCT) diagram,microstructure and mechanical properties of the simulated coarse grain heat-affected zone (CGHAZ).When t 8/5 is shorter,the microstructure mainly consists of lath bainite.When t 8/5 is 60 s,the microstructure becomes coarser bainite.Some acicular ferrite appears beside lath bainite when t 8/5 =100s.Finally,a microstructure composed of polygonal ferrite,acicular ferrite,and small amount pearlite is obtained with a small amount of bainite at t 8/5 】100s.With the increase of t 8/5,the hardness of CGHAZ decreases considerably.The minimum impact toughness of CGHAZ appears at t 8/5 =100s.The hardness and the toughness of CGHAZ remain above the specified values for steel 12MnNiVR.