To prevent dense chromium oxide covers from cracking during firing,such as internal cracking,surface cracking and fracture,the firing process of dense chromium oxide products was simulated,and the performance paramete...To prevent dense chromium oxide covers from cracking during firing,such as internal cracking,surface cracking and fracture,the firing process of dense chromium oxide products was simulated,and the performance parameters at several specific temperatures before and after densification of chromium oxide green bodies were tested.The temperature difference and the stress difference of chromium oxide green bodies were calculated by Finite Element Software at heating and cooling rates of 10,20,30 and 40℃·h^(-1),respectively.The results show that large temperature difference and thermal stress difference are the main causes of internal cracking,surface cracking and fracture of the brick.Suitable heating rates reduce or avoid internal cracking of the brick.When the heating rate is 30℃·h^(-1) below 1450℃and 10℃·h^(-1) above 1450℃,the temperature difference and the thermal stress difference in the brick are below 4℃and 4 MPa,respectively,and there is no internal crack in the brick after firing.The initial cooling stage is the key stage that causes cracking or fracture of bricks.When the cooling rate is 20℃·h^(-1) above 1450℃,the thermal stress difference in the brick is less than 4 MPa,which can significantly reduce the surface cracks and fracture of the brick.展开更多
The main characteristics of high chrome refractories for coal water slurry gasifiers were introduced. The damage mechanism of the refractories was analyzed by observing the microstructure of the used high chrome refra...The main characteristics of high chrome refractories for coal water slurry gasifiers were introduced. The damage mechanism of the refractories was analyzed by observing the microstructure of the used high chrome refractories with the aid of SEM. The main influencing factors on the service life of the refractories were summarized.展开更多
文摘To prevent dense chromium oxide covers from cracking during firing,such as internal cracking,surface cracking and fracture,the firing process of dense chromium oxide products was simulated,and the performance parameters at several specific temperatures before and after densification of chromium oxide green bodies were tested.The temperature difference and the stress difference of chromium oxide green bodies were calculated by Finite Element Software at heating and cooling rates of 10,20,30 and 40℃·h^(-1),respectively.The results show that large temperature difference and thermal stress difference are the main causes of internal cracking,surface cracking and fracture of the brick.Suitable heating rates reduce or avoid internal cracking of the brick.When the heating rate is 30℃·h^(-1) below 1450℃and 10℃·h^(-1) above 1450℃,the temperature difference and the thermal stress difference in the brick are below 4℃and 4 MPa,respectively,and there is no internal crack in the brick after firing.The initial cooling stage is the key stage that causes cracking or fracture of bricks.When the cooling rate is 20℃·h^(-1) above 1450℃,the thermal stress difference in the brick is less than 4 MPa,which can significantly reduce the surface cracks and fracture of the brick.
文摘The main characteristics of high chrome refractories for coal water slurry gasifiers were introduced. The damage mechanism of the refractories was analyzed by observing the microstructure of the used high chrome refractories with the aid of SEM. The main influencing factors on the service life of the refractories were summarized.