Wetting phenomena between MgO C and CaO SiO2 slags were investigated by varying carbon content.A sessile drop technique was adopted to study the wetting phenomena in conjunction with a high speed camera for the observ...Wetting phenomena between MgO C and CaO SiO2 slags were investigated by varying carbon content.A sessile drop technique was adopted to study the wetting phenomena in conjunction with a high speed camera for the observation of intrinsic wetting phenomena.The results show that the high content of SiO2 and the presence of Al2O3 in slags enhance the diffusion of Mg2+,leading to the promotion of reactive wetting.The carbon in MgO C refractory impedes the penetration of slags by repelling the slag and slowing the diffusion of Mg2+.This accounts for the non-wetting behavior of the slag on MgO C refractory with 17% (mass fraction) carbon similar to that of graphite.展开更多
基金supported by the R&D Center for Valuable Recycling(Global-Top Environmental Technology Development Program)funded by the Ministry of Environment(Project No.:11-C22-ID)
文摘Wetting phenomena between MgO C and CaO SiO2 slags were investigated by varying carbon content.A sessile drop technique was adopted to study the wetting phenomena in conjunction with a high speed camera for the observation of intrinsic wetting phenomena.The results show that the high content of SiO2 and the presence of Al2O3 in slags enhance the diffusion of Mg2+,leading to the promotion of reactive wetting.The carbon in MgO C refractory impedes the penetration of slags by repelling the slag and slowing the diffusion of Mg2+.This accounts for the non-wetting behavior of the slag on MgO C refractory with 17% (mass fraction) carbon similar to that of graphite.