The mechanical properties and microstructure of two low carbon high manganese steels with 23.8% （No. 1） and 33% （No. 2） （mass percent） of manganese were investigated. The results showed that No. 1 steel possesse...The mechanical properties and microstructure of two low carbon high manganese steels with 23.8% （No. 1） and 33% （No. 2） （mass percent） of manganese were investigated. The results showed that No. 1 steel possesses high strength and high plasticity, and No. 2 steel has a relatively high strength and extraordinary plasticity. The No. 1 steel exhibits both TRIP （transformation induced plasticity） and TWIP （twin induced plasticity） effects during the deformation; while only TWIP effect appeared under the same deformation condition for No. 2 steel. The comparison between the microstructures and mechanical properties of two steels was made, and the strengthening mechanisms were also analyzed.展开更多
In order to control retained austenite, the effect of hot deformation in the intercritical region on the microstructure of hot-rolled transformation-induced plasticity （TRIP） steel was studied on a Gleeble 1500 hot ...In order to control retained austenite, the effect of hot deformation in the intercritical region on the microstructure of hot-rolled transformation-induced plasticity （TRIP） steel was studied on a Gleeble 1500 hot simulator. Compressive strains varying in amounts from 0 to 60% were imposed inthe intercritical region, and effects on the formation of polygonal ferrite, carbide-free bainite and retained austenite were determined. With increasing the hot deformation amount and the ferrite content and decreasing the carbide-free bainite content, the volume fraction of retained austenite decreases. Increased dislocation density, grain refinement of ferrite and carbon enrichment are the main factors which control retained austenite stability.展开更多
After 2% predeformation,the baking treatment with different schedule was carried out for low silicon TRIP steel sheet with niobium.The effects of baking temperature and time on microstructures and mechanical propertie...After 2% predeformation,the baking treatment with different schedule was carried out for low silicon TRIP steel sheet with niobium.The effects of baking temperature and time on microstructures and mechanical properties were investigated.The results showed that with increasing the baking temperature and time,the volume fraction of retained austenite decreases,and the volume fraction of tempered martensite increases; as baking temperature ranges from 80 ℃ to 170 ℃,the bake-hardening（BH）value increases obviously,while from 170 ℃ to 230 ℃,the variation of BH value is very slight; as baking time ranges from 2 min to 20 min,the BH value increases significantly,while the BH value decreases when baking time exceeds 20 min.So that when the baking temperature is 170 ℃ and the baking time is 20 min,the low silicon TRIP steel sheet exhibits good bake-hardening behavior,and the highest BH value is above 70 MPa.展开更多
Paint baking treatment was carried out in a silicon oil bath at 170℃ for 20 min for Si-Al-Mn TRIP Steel sheet with different prestrains, and effect of prestrain on microstructures and properties was studied before an...Paint baking treatment was carried out in a silicon oil bath at 170℃ for 20 min for Si-Al-Mn TRIP Steel sheet with different prestrains, and effect of prestrain on microstructures and properties was studied before and after baking. The results show that with the increasing of prestrain amount during prestraining and baking, the volume fraction of retained austenite decreases, and the volume fraction of martensite and bainite increases as well as yield strength increases; as prestrain ranges from 0 to 4%, the baking-hardening （BH） value increases; while the prestrain ranges from 4% to 16%, the BH value decreases; when the prestrain amount is 4%, the highest BH value is about 70 MPa for Si-Al-Mn TRIP steel sheet with niobium, which displays excellent baking-hardening behavior.展开更多
文摘The mechanical properties and microstructure of two low carbon high manganese steels with 23.8% （No. 1） and 33% （No. 2） （mass percent） of manganese were investigated. The results showed that No. 1 steel possesses high strength and high plasticity, and No. 2 steel has a relatively high strength and extraordinary plasticity. The No. 1 steel exhibits both TRIP （transformation induced plasticity） and TWIP （twin induced plasticity） effects during the deformation; while only TWIP effect appeared under the same deformation condition for No. 2 steel. The comparison between the microstructures and mechanical properties of two steels was made, and the strengthening mechanisms were also analyzed.
基金Item Sponsored by National Natural Science Foundation of China (50527402)
文摘In order to control retained austenite, the effect of hot deformation in the intercritical region on the microstructure of hot-rolled transformation-induced plasticity （TRIP） steel was studied on a Gleeble 1500 hot simulator. Compressive strains varying in amounts from 0 to 60% were imposed inthe intercritical region, and effects on the formation of polygonal ferrite, carbide-free bainite and retained austenite were determined. With increasing the hot deformation amount and the ferrite content and decreasing the carbide-free bainite content, the volume fraction of retained austenite decreases. Increased dislocation density, grain refinement of ferrite and carbon enrichment are the main factors which control retained austenite stability.
基金Item Sponsored by National Natural Science Foundation of China(50527402)
文摘After 2% predeformation,the baking treatment with different schedule was carried out for low silicon TRIP steel sheet with niobium.The effects of baking temperature and time on microstructures and mechanical properties were investigated.The results showed that with increasing the baking temperature and time,the volume fraction of retained austenite decreases,and the volume fraction of tempered martensite increases; as baking temperature ranges from 80 ℃ to 170 ℃,the bake-hardening（BH）value increases obviously,while from 170 ℃ to 230 ℃,the variation of BH value is very slight; as baking time ranges from 2 min to 20 min,the BH value increases significantly,while the BH value decreases when baking time exceeds 20 min.So that when the baking temperature is 170 ℃ and the baking time is 20 min,the low silicon TRIP steel sheet exhibits good bake-hardening behavior,and the highest BH value is above 70 MPa.
基金Item Sponsored by National Natural Science Foundation of China(50527402)
文摘Paint baking treatment was carried out in a silicon oil bath at 170℃ for 20 min for Si-Al-Mn TRIP Steel sheet with different prestrains, and effect of prestrain on microstructures and properties was studied before and after baking. The results show that with the increasing of prestrain amount during prestraining and baking, the volume fraction of retained austenite decreases, and the volume fraction of martensite and bainite increases as well as yield strength increases; as prestrain ranges from 0 to 4%, the baking-hardening （BH） value increases; while the prestrain ranges from 4% to 16%, the BH value decreases; when the prestrain amount is 4%, the highest BH value is about 70 MPa for Si-Al-Mn TRIP steel sheet with niobium, which displays excellent baking-hardening behavior.