Effects of welding speed on the microstructure evolution in the stir zone(SZ)and mechanical properties of the friction stir welding(FSW)joints were studied by OM,XRD,SEM,TEM,EBSD and tensile testing.Compared with the ...Effects of welding speed on the microstructure evolution in the stir zone(SZ)and mechanical properties of the friction stir welding(FSW)joints were studied by OM,XRD,SEM,TEM,EBSD and tensile testing.Compared with the base metal(BM),an obviously fine dynamic recrystallization(DRX)microstructure occurs in the SZ and the DRX grain size decreases from 5.6 to 4.4μm with the increasing of welding speed.Fine DRX microstructure is mainly achieved by continuous dynamic recrystallization(CDRX)mechanism,strain induced boundary migration(SIBM)mechanism and particle stimulated nucleation(PSN)mechanism.Meanwhile,the geometric coalescence and the Burke−Turnbull mechanism are the main DRX grain growth mechanisms.Among all the welding speeds,the joint welded at rotation speed of 1500 r/min and welding speed of 75 mm/min has the greatest tensile properties,i.e.ultimate tensile strength(UTS)of(509±2)MPa,yield strength(YS)of(282±4)MPa,elongation(El)of(23±1)%,and the joint efficiency of 73%.展开更多
目的探讨膝关节周围骨折病人术后下肢深静脉血栓形成(deep vein thrombosis,DVT)的危险因素。方法回顾性分析西安交通大学医学院附属红会医院创伤骨科2014年9月至2018年12月收治的497例膝关节周围骨折且术前超声检查未发现DVT的病人的...目的探讨膝关节周围骨折病人术后下肢深静脉血栓形成(deep vein thrombosis,DVT)的危险因素。方法回顾性分析西安交通大学医学院附属红会医院创伤骨科2014年9月至2018年12月收治的497例膝关节周围骨折且术前超声检查未发现DVT的病人的临床资料,根据术后超声检查结果将病人分为血栓组和无血栓组,记录血栓发生部位及发生率,将年龄、性别、骨折部位、骨折侧别、合并外伤、合并内科疾病、美国麻醉医师协会(America Society of Anesthesiologists,ASA)分级、术中失血量、术中输液量、术中输血量、止血带使用时间、手术时间、术后1 d血红蛋白、术后1 d红细胞压积、术后1 d的D-二聚体列为观察指标,先后采用单因素分析和多因素Logistic回归分析确定术后DVT的独立危险因素。结果497例病人中,术后有175例发生DVT,发生率为35.21%,其中发生近端血栓2例(2/175,1.14%),远端血栓162例(162/175,92.57%),混合血栓11例(11/175,6.29%)。单因素分析结果显示两组间年龄、性别、冠状动脉粥样硬化性心脏病(冠心病)、术后1 d D-二聚体的差异均有统计学意义(P均<0.05)。多因素Logistic回归分析结果提示年龄>60岁[OR=1.888,95%CI(1.213,2.930),P=0.005)、女性[OR=1.841,95%CI(1.268,2.673),P=0.001]、冠心病[OR=1.086,95%CI(1.190,3.945),P=0.011]、术后1 d D-二聚体[OR=1.077,95%CI(1.019,1.138),P=0.009]是术后DVT的独立危险因素。结论膝关节周围骨折病人术后DVT发生率较高,以远端DVT为主。对于年龄>60岁、女性、冠心病、术后D-二聚体升高的病人应注意重点预防下肢DVT的发生,防止发生致命性肺栓塞。展开更多
目的探讨髋部骨折病人骨折后24h内下肢深静脉血栓形成(deep vein thrombosis, DVT的发生率及危险因素,并对超过24h住院病人血栓发生率的变化进行分析。方法回顾性分析西安交通大学医学院附属红会医院2014年10月至2018年3月收治的1183例...目的探讨髋部骨折病人骨折后24h内下肢深静脉血栓形成(deep vein thrombosis, DVT的发生率及危险因素,并对超过24h住院病人血栓发生率的变化进行分析。方法回顾性分析西安交通大学医学院附属红会医院2014年10月至2018年3月收治的1183例髋部骨折病人资料,根据受伤时间至入院时间进行分组。分析24h内住院的374例髋部骨折病人资料,根据入院时下肢静脉彩超结果分为DVT组和非DVT组,对两组病人的年龄、性别、身体质量指数(body mass index, BMI)、骨折类型、美国麻醉医师协会(America Society of Anesthesiologists, ASA)分级、入院时的实验室检查、是否多发伤、是否合并内科疾病等可能危险因素进行单因素分析;采用多因素Logistic回归分析确定其独立危险因素;对超过24h住院的病人进行DVT发生率的变化情况分析。结果在髋部骨折后24h内入院的374例髋部骨折病人中,未发生DVT有292例,发生DVT有82例,血栓发生率为21.93%(82/374)。分析DVT组和非DVT组之间的数据,年龄(P=0.005)、骨折部位(P<0.001)、入院时血红蛋白(P=0.002)、入院时红细胞压积(P=0.004)之间的差异有统计学意义;多因素Logistic回归分析结果显示:年龄、骨折部位是髋部骨折24h内形成DVT的独立危险因素。粗隆间骨折[P=0.002,OR=2.510,95%CI:(1.397,4.510)]和粗隆下骨折[P=0.023,OR=4.798,95%CI:(1.237,18.605)]发生DVT的风险分别是股骨颈骨折发生DVT风险的2.51倍、4.80倍。45~59岁、60~75岁、≥75岁年龄段病人分别是<45岁病人发生DVT风险的3.12、3.20、6.45倍。24h内入院的病人DVT发生率最低,延迟住院后DVT发生率逐渐升高,在受伤后8~14d入院的病人DVT发生率最高,达到48.86%。结论髋部骨折后24h内就会发生DVT,DVT的类型以远端血栓为主,也会发生近端血栓,年龄≥75岁、股骨粗隆下骨折的病人发生DVT的风险最高。髋部骨折后,随着入院时间的推迟,DVT的发生率逐渐升高。入院后应当第一时间对DVT进行诊断和预防,防止发生致命性肺栓塞。展开更多
文摘Effects of welding speed on the microstructure evolution in the stir zone(SZ)and mechanical properties of the friction stir welding(FSW)joints were studied by OM,XRD,SEM,TEM,EBSD and tensile testing.Compared with the base metal(BM),an obviously fine dynamic recrystallization(DRX)microstructure occurs in the SZ and the DRX grain size decreases from 5.6 to 4.4μm with the increasing of welding speed.Fine DRX microstructure is mainly achieved by continuous dynamic recrystallization(CDRX)mechanism,strain induced boundary migration(SIBM)mechanism and particle stimulated nucleation(PSN)mechanism.Meanwhile,the geometric coalescence and the Burke−Turnbull mechanism are the main DRX grain growth mechanisms.Among all the welding speeds,the joint welded at rotation speed of 1500 r/min and welding speed of 75 mm/min has the greatest tensile properties,i.e.ultimate tensile strength(UTS)of(509±2)MPa,yield strength(YS)of(282±4)MPa,elongation(El)of(23±1)%,and the joint efficiency of 73%.
文摘目的探讨膝关节周围骨折病人术后下肢深静脉血栓形成(deep vein thrombosis,DVT)的危险因素。方法回顾性分析西安交通大学医学院附属红会医院创伤骨科2014年9月至2018年12月收治的497例膝关节周围骨折且术前超声检查未发现DVT的病人的临床资料,根据术后超声检查结果将病人分为血栓组和无血栓组,记录血栓发生部位及发生率,将年龄、性别、骨折部位、骨折侧别、合并外伤、合并内科疾病、美国麻醉医师协会(America Society of Anesthesiologists,ASA)分级、术中失血量、术中输液量、术中输血量、止血带使用时间、手术时间、术后1 d血红蛋白、术后1 d红细胞压积、术后1 d的D-二聚体列为观察指标,先后采用单因素分析和多因素Logistic回归分析确定术后DVT的独立危险因素。结果497例病人中,术后有175例发生DVT,发生率为35.21%,其中发生近端血栓2例(2/175,1.14%),远端血栓162例(162/175,92.57%),混合血栓11例(11/175,6.29%)。单因素分析结果显示两组间年龄、性别、冠状动脉粥样硬化性心脏病(冠心病)、术后1 d D-二聚体的差异均有统计学意义(P均<0.05)。多因素Logistic回归分析结果提示年龄>60岁[OR=1.888,95%CI(1.213,2.930),P=0.005)、女性[OR=1.841,95%CI(1.268,2.673),P=0.001]、冠心病[OR=1.086,95%CI(1.190,3.945),P=0.011]、术后1 d D-二聚体[OR=1.077,95%CI(1.019,1.138),P=0.009]是术后DVT的独立危险因素。结论膝关节周围骨折病人术后DVT发生率较高,以远端DVT为主。对于年龄>60岁、女性、冠心病、术后D-二聚体升高的病人应注意重点预防下肢DVT的发生,防止发生致命性肺栓塞。
文摘目的探讨髋部骨折病人骨折后24h内下肢深静脉血栓形成(deep vein thrombosis, DVT的发生率及危险因素,并对超过24h住院病人血栓发生率的变化进行分析。方法回顾性分析西安交通大学医学院附属红会医院2014年10月至2018年3月收治的1183例髋部骨折病人资料,根据受伤时间至入院时间进行分组。分析24h内住院的374例髋部骨折病人资料,根据入院时下肢静脉彩超结果分为DVT组和非DVT组,对两组病人的年龄、性别、身体质量指数(body mass index, BMI)、骨折类型、美国麻醉医师协会(America Society of Anesthesiologists, ASA)分级、入院时的实验室检查、是否多发伤、是否合并内科疾病等可能危险因素进行单因素分析;采用多因素Logistic回归分析确定其独立危险因素;对超过24h住院的病人进行DVT发生率的变化情况分析。结果在髋部骨折后24h内入院的374例髋部骨折病人中,未发生DVT有292例,发生DVT有82例,血栓发生率为21.93%(82/374)。分析DVT组和非DVT组之间的数据,年龄(P=0.005)、骨折部位(P<0.001)、入院时血红蛋白(P=0.002)、入院时红细胞压积(P=0.004)之间的差异有统计学意义;多因素Logistic回归分析结果显示:年龄、骨折部位是髋部骨折24h内形成DVT的独立危险因素。粗隆间骨折[P=0.002,OR=2.510,95%CI:(1.397,4.510)]和粗隆下骨折[P=0.023,OR=4.798,95%CI:(1.237,18.605)]发生DVT的风险分别是股骨颈骨折发生DVT风险的2.51倍、4.80倍。45~59岁、60~75岁、≥75岁年龄段病人分别是<45岁病人发生DVT风险的3.12、3.20、6.45倍。24h内入院的病人DVT发生率最低,延迟住院后DVT发生率逐渐升高,在受伤后8~14d入院的病人DVT发生率最高,达到48.86%。结论髋部骨折后24h内就会发生DVT,DVT的类型以远端血栓为主,也会发生近端血栓,年龄≥75岁、股骨粗隆下骨折的病人发生DVT的风险最高。髋部骨折后,随着入院时间的推迟,DVT的发生率逐渐升高。入院后应当第一时间对DVT进行诊断和预防,防止发生致命性肺栓塞。