The hot corrosion behaviour of a modified Ti3Al-based alloy under thin Na2SO4deposit film was investigated at910and950°C in air.The corrosion product was identified by XRD and its morphologies on the surface and ...The hot corrosion behaviour of a modified Ti3Al-based alloy under thin Na2SO4deposit film was investigated at910and950°C in air.The corrosion product was identified by XRD and its morphologies on the surface and cross-section were observed bySEM.The alloy suffered from considerable hot corrosion attack.The mass gain versus time curves obtained by TGA exhibited tworegions of different kinetics.The whole corroded layer consisted of loose and porous mixture oxides of TiO2,Nb2O5and Al2O3.Numerous small nodules of corrosion product were observed.An illustrative schematic was established to describe the formationprocess of such nodules.It seemed that the refractory oxides played a significantly important role in determining the development ofhot corrosion attack.展开更多
基金Projects(51271191,51571205)supported by the National Natural Science Foundation of China
文摘The hot corrosion behaviour of a modified Ti3Al-based alloy under thin Na2SO4deposit film was investigated at910and950°C in air.The corrosion product was identified by XRD and its morphologies on the surface and cross-section were observed bySEM.The alloy suffered from considerable hot corrosion attack.The mass gain versus time curves obtained by TGA exhibited tworegions of different kinetics.The whole corroded layer consisted of loose and porous mixture oxides of TiO2,Nb2O5and Al2O3.Numerous small nodules of corrosion product were observed.An illustrative schematic was established to describe the formationprocess of such nodules.It seemed that the refractory oxides played a significantly important role in determining the development ofhot corrosion attack.