Achieving a high color rendering index(CRI)and luminous stability in single-structured Ce:Y_(3)Al_(5)O_(12)(Ce:YAG)phosphor ceramics(PCs)is crucial for high-power white light-emitting diodes or laser diodes(LEDs/LDs)....Achieving a high color rendering index(CRI)and luminous stability in single-structured Ce:Y_(3)Al_(5)O_(12)(Ce:YAG)phosphor ceramics(PCs)is crucial for high-power white light-emitting diodes or laser diodes(LEDs/LDs).However,cyan valleys and insufficient amounts of the red component in the Ce:YAG emission spectra significantly limit their real applications.In this work,a series of Ce,Mn:Y_(3)(Al,Sc)_(2)Al_(3)O_(12)(Ce,Mn:YSAG)PCs were fabricated by vacuum sintering,and efficient spectral regulation was realized for full-color lighting.The cyan valley was filled by the blueshifted emission peak of Ce^(3+)via Sc^(3+)doping.The orange‒red emission at approximately 580 nm was effectively supplemented via Mn^(2+)doping.In particular,CRI of Ce,Mn:YSAG increased from 56.4 to 85.8,a 52%increase compared with that of Ce:YAG under high-power LED excitation,and the operating temperature was stable at approximately 50℃for long working time.Moreover,CRI of 80.9 could still be obtained for PC-based white LDs.These results indicated that Ce,Mn:YSAG PC,which has excellent CRI and luminous stability,is an extremely promising color convertor for high-power white LEDs/LDs.展开更多
基金financially supported by the National Key R&D Program of China(No.2021YFB3501700)the National Natural Science Foundation of China(Nos.52202135,61975070,and 52302141)+4 种基金the Priority Academic Program Development of Jiangsu Higher Education Institutions(PAPD),the International S&T Cooperation Program of Jiangsu Province(No.BZ2023007)the Key R&D Project of Jiangsu Province(Nos.BE2023050 and BE2021040)Natural Science Foundation of Jiangsu Province(No.BK20221226)the Special Project for Technology Innovation of Xuzhou City(Nos.KC23380,KC21379,KC22461,and KC22497)the Open Project of State Key Laboratory of Crystal Materials(No.KF2205).
文摘Achieving a high color rendering index(CRI)and luminous stability in single-structured Ce:Y_(3)Al_(5)O_(12)(Ce:YAG)phosphor ceramics(PCs)is crucial for high-power white light-emitting diodes or laser diodes(LEDs/LDs).However,cyan valleys and insufficient amounts of the red component in the Ce:YAG emission spectra significantly limit their real applications.In this work,a series of Ce,Mn:Y_(3)(Al,Sc)_(2)Al_(3)O_(12)(Ce,Mn:YSAG)PCs were fabricated by vacuum sintering,and efficient spectral regulation was realized for full-color lighting.The cyan valley was filled by the blueshifted emission peak of Ce^(3+)via Sc^(3+)doping.The orange‒red emission at approximately 580 nm was effectively supplemented via Mn^(2+)doping.In particular,CRI of Ce,Mn:YSAG increased from 56.4 to 85.8,a 52%increase compared with that of Ce:YAG under high-power LED excitation,and the operating temperature was stable at approximately 50℃for long working time.Moreover,CRI of 80.9 could still be obtained for PC-based white LDs.These results indicated that Ce,Mn:YSAG PC,which has excellent CRI and luminous stability,is an extremely promising color convertor for high-power white LEDs/LDs.