Laser multi\|layer cladding experiments were performed on the substrate of DD3 single crystal with FGH95 powder as cladding material.The solidification microstructure in the sample was investigated.It was found that t...Laser multi\|layer cladding experiments were performed on the substrate of DD3 single crystal with FGH95 powder as cladding material.The solidification microstructure in the sample was investigated.It was found that the solidification microstructure was greatly influenced by the crystallography orientation of the substrate and the local solidification conditions.When the angle between the preferred orientation of the single crystal and the direction of heat flow in the cladding layer is less than 30°,single crystal cladding layers were acquired.Otherwise the crystallography orientation of the cladding layer will deviate from the orientation of the substrate and the microstructure with polycrystalline appears.Meanwhile,even when the experiments were performed on the same preferred crystal surface,the solidification microstructures will be different distinctly resulting from the variation of the local solidification conditions.The secondary arms were degenerated and the primary arm spacing was about 10\|20μm.Further investigation shows that the phases of the cladding layer are mainly made up ofγ,γ′,the flower\|likeγ/γ′eutectic and carbide.The morphology ofγ′was cubical and the size is less than 0.1μm.展开更多
A series of single track clads of Inconel 625 alloy were fabricated by laser solid forming.To achieve the high dimensional accuracy and excellent mechanical properties,the effect of processing parameters on the geomet...A series of single track clads of Inconel 625 alloy were fabricated by laser solid forming.To achieve the high dimensional accuracy and excellent mechanical properties,the effect of processing parameters on the geometry,the formation of Laves phase and the residual stress was investigated.The results show that laser power and scanning speed had a dramatical influence on the width and height of single-track clads.According to the columnar to equiaxed transition curve of Inconel 625,the grain morphology can be predicted during the LSF process.With the increasing laser power and the decreasing scanning speed,the segregation degree of Si,Nb,Mo,the volume fraction and size of Laves phase increased.Vickers indentation was used to demonstrate that optimizing processing parameter can achieve the minimum residual tensile stress.展开更多
基金National Key Basic Research Development Program me of china(No.G2000067205-3)
文摘Laser multi\|layer cladding experiments were performed on the substrate of DD3 single crystal with FGH95 powder as cladding material.The solidification microstructure in the sample was investigated.It was found that the solidification microstructure was greatly influenced by the crystallography orientation of the substrate and the local solidification conditions.When the angle between the preferred orientation of the single crystal and the direction of heat flow in the cladding layer is less than 30°,single crystal cladding layers were acquired.Otherwise the crystallography orientation of the cladding layer will deviate from the orientation of the substrate and the microstructure with polycrystalline appears.Meanwhile,even when the experiments were performed on the same preferred crystal surface,the solidification microstructures will be different distinctly resulting from the variation of the local solidification conditions.The secondary arms were degenerated and the primary arm spacing was about 10\|20μm.Further investigation shows that the phases of the cladding layer are mainly made up ofγ,γ′,the flower\|likeγ/γ′eutectic and carbide.The morphology ofγ′was cubical and the size is less than 0.1μm.
基金Project(2018YFB1105804)supported by the National Key R&D Program of ChinaProject(2020-TS-06)supported by the Research Fund of the State Key Laboratory of Solidification Processing(NPU),China。
文摘A series of single track clads of Inconel 625 alloy were fabricated by laser solid forming.To achieve the high dimensional accuracy and excellent mechanical properties,the effect of processing parameters on the geometry,the formation of Laves phase and the residual stress was investigated.The results show that laser power and scanning speed had a dramatical influence on the width and height of single-track clads.According to the columnar to equiaxed transition curve of Inconel 625,the grain morphology can be predicted during the LSF process.With the increasing laser power and the decreasing scanning speed,the segregation degree of Si,Nb,Mo,the volume fraction and size of Laves phase increased.Vickers indentation was used to demonstrate that optimizing processing parameter can achieve the minimum residual tensile stress.