A cordierite was synthesized from calcined bauxite, talcum, and quartz. The properties and microstructure of the cordierite sintered samples were characterized by Archimedes＇ method, thermal dilatometry, X-ray diffra...A cordierite was synthesized from calcined bauxite, talcum, and quartz. The properties and microstructure of the cordierite sintered samples were characterized by Archimedes＇ method, thermal dilatometry, X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and so on. The experimental results showed that calcined bauxite could broaden the range of synthesizing temperature from 1300 ℃ to 1420 ℃ and get pure cordierite. The bulk density and linear thermal expansion coefficient of the sample synthesized at 1420 ℃ for 2 h were 1.97 g·cm^-3 and 2.1×10^-6 ℃^-1, respectively. The XRD analysis showed that the major crystalline phase was a-cordierite with almost no glassy matters, the SEM images illustrated a small vent hole and the size were 5 -100 μm, the well-grown hexagonal and granular cordierite grains had the sizes distributed among 0.1-8 ;xm, and providing high mechanical strength and lower linear thermal expansion coefficient.展开更多
基金Funded by the National Basic Research Program ("973"Program)(2010CB227105)
文摘A cordierite was synthesized from calcined bauxite, talcum, and quartz. The properties and microstructure of the cordierite sintered samples were characterized by Archimedes＇ method, thermal dilatometry, X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and so on. The experimental results showed that calcined bauxite could broaden the range of synthesizing temperature from 1300 ℃ to 1420 ℃ and get pure cordierite. The bulk density and linear thermal expansion coefficient of the sample synthesized at 1420 ℃ for 2 h were 1.97 g·cm^-3 and 2.1×10^-6 ℃^-1, respectively. The XRD analysis showed that the major crystalline phase was a-cordierite with almost no glassy matters, the SEM images illustrated a small vent hole and the size were 5 -100 μm, the well-grown hexagonal and granular cordierite grains had the sizes distributed among 0.1-8 ;xm, and providing high mechanical strength and lower linear thermal expansion coefficient.