Lithium metal anode of lithium batteries,including lithium-ion batteries,has been considered the anode for next-generation batteries with desired high energy densities due to its high theoretical specific capacity(386...Lithium metal anode of lithium batteries,including lithium-ion batteries,has been considered the anode for next-generation batteries with desired high energy densities due to its high theoretical specific capacity(3860 mA h g^(-1))and low standards electrode potential(-3.04 V vs.SHE).However,the highly reactive nature of metallic lithium and its direct contact with the electrolyte could lead to severe chemical reactions,leading to the continuous consumption of the electrolyte and a reduction in the cycle life and Coulombic efficiency.In addition,the solid electrolyte interface formed during battery cycling is mainly inorganic,which is too fragile to withstand the extreme volume change during the plating and stripping of lithium.The uneven flux of lithium ions could lead to excessive lithium deposition at local points,resulting in needle-like lithium dendrites,which could pierce the separator and cause short circuits,battery failure,and safety issues.In the last five years,tremendous efforts have been dedicated to addressing these issues,and the most successful improvements have been related to lithiophilicity optimizations.Thus,this paper comprehensively reviewed the lithiophilicity regulation in lithium metal anode modifications and highlighted the vital effect of lithiophilicity.The remaining challenges faced by the lithiophilicity optimization for lithium metal anodes are discussed with the proposed research directions for overcoming the technical challenges in this subject.展开更多
Charging P2-Na_(2/3)Ni_(1/3)Mn_(2/3)O_(2)to 4.5 V for higher capacity is enticing.However,it leads to severe capacity fading,ascribing to the lattice oxygen evolution and the P2-O2 phase transformation.Here,the Mg Fe_...Charging P2-Na_(2/3)Ni_(1/3)Mn_(2/3)O_(2)to 4.5 V for higher capacity is enticing.However,it leads to severe capacity fading,ascribing to the lattice oxygen evolution and the P2-O2 phase transformation.Here,the Mg Fe_(2)O_(4) coating and Mg,Fe co-doping were constructed simultaneously by Mg,Fe surface treatment to suppress lattice oxygen evolution and P2-O2 phase transformation of P2-Na_(2/3)Ni_(1/3)Mn_(2/3)O_(2)at deep charging.Through ex-situ X-ray diffraction(XRD)tests,we found that the Mg,Fe bulk co-doping could reduce the repulsion between transition metals and Na+/vacancies ordering,thus inhibiting the P2-O2 phase transition and significantly reducing the irreversible volume change of the material.Meanwhile,the internal electric field formed by the dielectric polarization of Mg Fe_(2)O_(4) effectively inhibits the outward migration of oxidized O^(a-)(a<2),thereby suppressing the lattice oxygen evolution at deep charging,confirmed by in situ Raman and ex situ XPS techniques.P2-Na NM@MF-3 shows enhanced high-voltage cycling performance with capacity retentions of 84.8% and 81.3%at 0.1 and 1 C after cycles.This work sheds light on regulating the surface chemistry for Na-layered oxide materials to enhance the high-voltage performance of Na-ion batteries.展开更多
Cost-effective atomically dispersed Fe-N-P-C complex catalysts are promising to catalyze the oxygen reduction reaction(ORR)and replace Pt catalysts in fuel cells and metal-air batteries.However,it remains a challenge ...Cost-effective atomically dispersed Fe-N-P-C complex catalysts are promising to catalyze the oxygen reduction reaction(ORR)and replace Pt catalysts in fuel cells and metal-air batteries.However,it remains a challenge to increase the number of atomically dispersed active sites on these catalysts.Here we report a highly efficient impregnation-pyrolysis method to prepare effective ORR electrocatalysts with large amount of atomically dispersed Fe active sites from biomass.Two types of active catalyst centers were identified,namely atomically dispersed Fe sites and Fe_(x)P particles.The ORR rate of the atomically dispersed Fe sites is three orders of magnitude higher than it of Fe_(x)P particles.A linear correlation between the amount of the atomically dispersed Fe and the ORR activity was obtained,revealing the major contribution of the atomically dispersed Fe to the ORR activity.The number of atomically dispersed Fe increases as the Fe loading increased and reaching the maximum at 1.86 wt%Fe,resulting in the maximum ORR rate.Optimized Fe-N-P-C complex catalyst was used as the cathode catalyst in a homemade Zn-air battery and good performance of an energy density of 771 Wh kgZn^(-1),a power density of 92.9 m W cm^(-2) at 137 m A cm^(-2) and an excellent durability were exhibited.展开更多
Severe infections caused by multidrug-resistant Klebsiella pneumoniae(K.pneumoniae)highlight the need for new therapeutics with activity against this pathogen.Phage therapy is an alternative treatment approach for mul...Severe infections caused by multidrug-resistant Klebsiella pneumoniae(K.pneumoniae)highlight the need for new therapeutics with activity against this pathogen.Phage therapy is an alternative treatment approach for multidrug-resistant K.pneumoniae infections.Here,we report a novel bacteriophage(phage)BUCT631 that can specifically lyse capsule-type K1 K.pneumoniae.Physiological characterization revealed that phage BUCT631 could rapidly adsorb to the surface of K.pneumoniae and form an obvious halo ring,and it had relatively favorable thermal stability(4–50C)and pH tolerance(pH?4–12).In addition,the optimal multiplicity of infection(MOI)of phage BUCT631 was 0.01,and the burst size was approximately 303 PFU/cell.Genomic analysis showed that phage BUCT631 has double-stranded DNA(total length of 44,812 bp)with a G t C content of 54.1%,and the genome contains 57 open reading frames(ORFs)and no virulence or antibiotic resistance related genes.Based on phylogenetic analysis,phage BUCT631 could be assigned to a new species in the genus Drulisvirus of the subfamily Slopekvirinae.In addition,phage BUCT631 could quickly inhibit the growth of K.pneumoniae within 2 h in vitro and significantly elevated the survival rate of K.pneumoniae infected Galleria mellonella larvae from 10%to 90%in vivo.These studies suggest that phage BUCT631 has promising potential for development as a safe alternative for control and treatment of multidrug-resistant K.pneumoniae infection.展开更多
High-perfo rmance anodes of sodium ion batteries(SIBs)largely depends on rational architecture design and binder-free smart hybridization.Herein,we report TiC/C core/shell nanowires arrays prepared by a one-step chemi...High-perfo rmance anodes of sodium ion batteries(SIBs)largely depends on rational architecture design and binder-free smart hybridization.Herein,we report TiC/C core/shell nanowires arrays prepared by a one-step chemical vapor deposition(CVD)method and apply it as the anode of SIBs for the first time.The conductive TiC core is intimately decorated with carbon shell.The as-obtained TiC/C nanowires are homogeneously grown on the substrate and show core/shell heterostructure and porous architecture with high electronic conductivity and reinforced stability.Owing to these merits,the TiC/C electrode displays good rate performance and outstanding cycling performance with a capacity of 135.3 mAh/g at 0.1 A/g and superior capacity retention of 90.14%after 1000 cycles at 2 A/g.The reported strategy would provide a promising way to construct binder-free arrays electrodes for sodium ion storage.展开更多
基金supported by the National Natural Science Foundation of China(52072217,22179071)the Joint Funds of the National Natural Science Foundation of China(U20A20249)the Major Technological Innovation Project of Hubei Science and Technology Department(2019AAA164)。
文摘Lithium metal anode of lithium batteries,including lithium-ion batteries,has been considered the anode for next-generation batteries with desired high energy densities due to its high theoretical specific capacity(3860 mA h g^(-1))and low standards electrode potential(-3.04 V vs.SHE).However,the highly reactive nature of metallic lithium and its direct contact with the electrolyte could lead to severe chemical reactions,leading to the continuous consumption of the electrolyte and a reduction in the cycle life and Coulombic efficiency.In addition,the solid electrolyte interface formed during battery cycling is mainly inorganic,which is too fragile to withstand the extreme volume change during the plating and stripping of lithium.The uneven flux of lithium ions could lead to excessive lithium deposition at local points,resulting in needle-like lithium dendrites,which could pierce the separator and cause short circuits,battery failure,and safety issues.In the last five years,tremendous efforts have been dedicated to addressing these issues,and the most successful improvements have been related to lithiophilicity optimizations.Thus,this paper comprehensively reviewed the lithiophilicity regulation in lithium metal anode modifications and highlighted the vital effect of lithiophilicity.The remaining challenges faced by the lithiophilicity optimization for lithium metal anodes are discussed with the proposed research directions for overcoming the technical challenges in this subject.
基金supported by the Special Project for the Central Government to Guide Local Technological Development (GUIKE ZY20198008)the Guangxi Technology Base and talent Subject (GUIKE AD20238012,AD20297086)+5 种基金the Natural Science Foundation of Guangxi Province (2021GXNSFDA075012)the National Natural Science Foundation of China (51902108,52104298,22169004)the National Natural Science Foundation of China (U20A20249)the Regional Innovation and Development Joint Fundthe Guangxi Innovation Driven Development Subject (GUIKE AA19182020,19254004)the Special Fund for Guangxi Distinguished Expert。
文摘Charging P2-Na_(2/3)Ni_(1/3)Mn_(2/3)O_(2)to 4.5 V for higher capacity is enticing.However,it leads to severe capacity fading,ascribing to the lattice oxygen evolution and the P2-O2 phase transformation.Here,the Mg Fe_(2)O_(4) coating and Mg,Fe co-doping were constructed simultaneously by Mg,Fe surface treatment to suppress lattice oxygen evolution and P2-O2 phase transformation of P2-Na_(2/3)Ni_(1/3)Mn_(2/3)O_(2)at deep charging.Through ex-situ X-ray diffraction(XRD)tests,we found that the Mg,Fe bulk co-doping could reduce the repulsion between transition metals and Na+/vacancies ordering,thus inhibiting the P2-O2 phase transition and significantly reducing the irreversible volume change of the material.Meanwhile,the internal electric field formed by the dielectric polarization of Mg Fe_(2)O_(4) effectively inhibits the outward migration of oxidized O^(a-)(a<2),thereby suppressing the lattice oxygen evolution at deep charging,confirmed by in situ Raman and ex situ XPS techniques.P2-Na NM@MF-3 shows enhanced high-voltage cycling performance with capacity retentions of 84.8% and 81.3%at 0.1 and 1 C after cycles.This work sheds light on regulating the surface chemistry for Na-layered oxide materials to enhance the high-voltage performance of Na-ion batteries.
基金The financial supports from Department of Chemical Engineeringthe support from China Scholarship Council(CSC)for his study at NTNU。
文摘Cost-effective atomically dispersed Fe-N-P-C complex catalysts are promising to catalyze the oxygen reduction reaction(ORR)and replace Pt catalysts in fuel cells and metal-air batteries.However,it remains a challenge to increase the number of atomically dispersed active sites on these catalysts.Here we report a highly efficient impregnation-pyrolysis method to prepare effective ORR electrocatalysts with large amount of atomically dispersed Fe active sites from biomass.Two types of active catalyst centers were identified,namely atomically dispersed Fe sites and Fe_(x)P particles.The ORR rate of the atomically dispersed Fe sites is three orders of magnitude higher than it of Fe_(x)P particles.A linear correlation between the amount of the atomically dispersed Fe and the ORR activity was obtained,revealing the major contribution of the atomically dispersed Fe to the ORR activity.The number of atomically dispersed Fe increases as the Fe loading increased and reaching the maximum at 1.86 wt%Fe,resulting in the maximum ORR rate.Optimized Fe-N-P-C complex catalyst was used as the cathode catalyst in a homemade Zn-air battery and good performance of an energy density of 771 Wh kgZn^(-1),a power density of 92.9 m W cm^(-2) at 137 m A cm^(-2) and an excellent durability were exhibited.
基金This work was supported by the National Key Research and Development Program of China(NO.2018YFA0903000,2020YFC2005405,2020YFA0712100,2020YFC0840805)the Funds for First-class Discipline Construction(NO.XK1805,NO.XK1803-06)the Innovation&Transfer Fund of Peking University Third Hospital BYSYZHKC2022114.
文摘Severe infections caused by multidrug-resistant Klebsiella pneumoniae(K.pneumoniae)highlight the need for new therapeutics with activity against this pathogen.Phage therapy is an alternative treatment approach for multidrug-resistant K.pneumoniae infections.Here,we report a novel bacteriophage(phage)BUCT631 that can specifically lyse capsule-type K1 K.pneumoniae.Physiological characterization revealed that phage BUCT631 could rapidly adsorb to the surface of K.pneumoniae and form an obvious halo ring,and it had relatively favorable thermal stability(4–50C)and pH tolerance(pH?4–12).In addition,the optimal multiplicity of infection(MOI)of phage BUCT631 was 0.01,and the burst size was approximately 303 PFU/cell.Genomic analysis showed that phage BUCT631 has double-stranded DNA(total length of 44,812 bp)with a G t C content of 54.1%,and the genome contains 57 open reading frames(ORFs)and no virulence or antibiotic resistance related genes.Based on phylogenetic analysis,phage BUCT631 could be assigned to a new species in the genus Drulisvirus of the subfamily Slopekvirinae.In addition,phage BUCT631 could quickly inhibit the growth of K.pneumoniae within 2 h in vitro and significantly elevated the survival rate of K.pneumoniae infected Galleria mellonella larvae from 10%to 90%in vivo.These studies suggest that phage BUCT631 has promising potential for development as a safe alternative for control and treatment of multidrug-resistant K.pneumoniae infection.
基金supported by the National Natural Science Foundation of China(Nos.51772272,51728204)Fundamental Research Funds for the Central Universities(No.2018QNA4011)+4 种基金Qianjiang Talents Plan D(No.QJD1602029)Startup Foundation for Hundred-Talent Program of Zhejiang UniversityAnalysis Testing and Commonweal Project of Zhejiang Province(No.GC19E020005)the TEM support from Qiaohong He and Xiaokun DingSEM support from Fang Chen from Department of Chemistry,Zhejiang University。
文摘High-perfo rmance anodes of sodium ion batteries(SIBs)largely depends on rational architecture design and binder-free smart hybridization.Herein,we report TiC/C core/shell nanowires arrays prepared by a one-step chemical vapor deposition(CVD)method and apply it as the anode of SIBs for the first time.The conductive TiC core is intimately decorated with carbon shell.The as-obtained TiC/C nanowires are homogeneously grown on the substrate and show core/shell heterostructure and porous architecture with high electronic conductivity and reinforced stability.Owing to these merits,the TiC/C electrode displays good rate performance and outstanding cycling performance with a capacity of 135.3 mAh/g at 0.1 A/g and superior capacity retention of 90.14%after 1000 cycles at 2 A/g.The reported strategy would provide a promising way to construct binder-free arrays electrodes for sodium ion storage.