Grafting of polystyrene with narrowly dispersed polymer microspheres through surface-initiated atom transferradical polymerization(ATRP)was investigated.Polydivinylbenzene(PDVB)microspheres were prepared by dispersion...Grafting of polystyrene with narrowly dispersed polymer microspheres through surface-initiated atom transferradical polymerization(ATRP)was investigated.Polydivinylbenzene(PDVB)microspheres were prepared by dispersionpolymerization with poly(N-vinyl pyrrolidone)(PVP)as stabilizer.The surfaces of PDVB microspheres werechloromethylated by chloromethyl methyl ether in the presence of zinc chloride as catalyst to form chloromethylbenzeneinitiating core sites for subsequent ATRP grafting of styrene using CuCl/bpy as catalytic system.Polystyrene was found to begrafted not only from the particle surfaces but also from within a thin shell layer,resulting in the formation of particles sizeincreased from 2.38-2.58 μm,which can further grow to 2.93 μm during secondary grafting polymerization of styrene.Thisdemonstrates that grafting polymerization proceeds through a typical ATRP procedure with living nature.All of the preparedmicrospheres have narrow particle size distribution with coefficient of variation around 10%.展开更多
基金This work was supported by the National Natural Science Foundation of China(No.20274018).
文摘Grafting of polystyrene with narrowly dispersed polymer microspheres through surface-initiated atom transferradical polymerization(ATRP)was investigated.Polydivinylbenzene(PDVB)microspheres were prepared by dispersionpolymerization with poly(N-vinyl pyrrolidone)(PVP)as stabilizer.The surfaces of PDVB microspheres werechloromethylated by chloromethyl methyl ether in the presence of zinc chloride as catalyst to form chloromethylbenzeneinitiating core sites for subsequent ATRP grafting of styrene using CuCl/bpy as catalytic system.Polystyrene was found to begrafted not only from the particle surfaces but also from within a thin shell layer,resulting in the formation of particles sizeincreased from 2.38-2.58 μm,which can further grow to 2.93 μm during secondary grafting polymerization of styrene.Thisdemonstrates that grafting polymerization proceeds through a typical ATRP procedure with living nature.All of the preparedmicrospheres have narrow particle size distribution with coefficient of variation around 10%.