Macro-and micro-interface instability of SiO_(x)anode caused by its dramatic volume variation during cycling will result in low Coulombic efficiency and rapid capacity degradation.In this work,an organic-inorganic com...Macro-and micro-interface instability of SiO_(x)anode caused by its dramatic volume variation during cycling will result in low Coulombic efficiency and rapid capacity degradation.In this work,an organic-inorganic composite interfacial layer rich in benzene ring groups,polyisocyanates,and LiF was obtained on SiO_(x)anode by the introduction of 4-fluorophenyl isocyanate(FPI)and fluoroethylene carbonate(FEC)co-additives in electrolyte.The SiO_(x)anode material shows a capacity retention of 69.2%after 100 cycles at a current density of 1 A g^(-1)and rate capacity of 523 m A h g^(-1)at the current density of 3A g^(-1),while the SiO_(x)anode cycling in reference electrolyte has almost no capacity.展开更多
Transition metal cation ordering is essential for controlling the electrochemical performance of cubic spinel LiNi_(0.5)Mn_(1.5)O_(4)(LNMO),which is conventionally adjusted by optimizing the high temperature sintering...Transition metal cation ordering is essential for controlling the electrochemical performance of cubic spinel LiNi_(0.5)Mn_(1.5)O_(4)(LNMO),which is conventionally adjusted by optimizing the high temperature sintering and annealing procedures.In this present work,multiple characterization techniques,including 6,7Li NMR,XRD and HRTEM,have been combined to trace the phase transformation and morphology evolution during synthesis.It has been illustrated that simultaneous formation of LiMn_(2)O_(4)(LMO)and LiNiO_(2)(LNO)binary oxides and their conversion into highly reactive LixNi^(3+)_(y)Mn_(3.5+)_(z)O ternary intermediate is a thermal dynamically difficult but crucial step in the synthesis of LNMO ternary oxide.A new strategy of modifying the intermediates formation pathway from binary mode to ternary mode using thermal regulating agent has been adopted.LNMO synthesized with thermal regulating agent exhibits supreme rate capability,long-cycling performance(even at elevated temperature)and excellent capacity efficiency.At a high rate of 100 C,the assembled battery delivers a discharge capacity of 99 mAh g^(-1).This study provides a way to control the formation pathway of complex oxides using thermal regulating agent.展开更多
基金financially supporting from the Key-Area Research and Development Program of Guangdong Province(2020B090919005)the Fundamental Research Funds for the Central Universities(HIT.OCEF.2021008)+2 种基金the Key Research and Development Program of Heilongjiang Province(GA21A102)the Natural Science Foundation of Chongqing(cstc2021jcyj-msxmX0958)the National Natural Science Foundation of China(51772068)。
文摘Macro-and micro-interface instability of SiO_(x)anode caused by its dramatic volume variation during cycling will result in low Coulombic efficiency and rapid capacity degradation.In this work,an organic-inorganic composite interfacial layer rich in benzene ring groups,polyisocyanates,and LiF was obtained on SiO_(x)anode by the introduction of 4-fluorophenyl isocyanate(FPI)and fluoroethylene carbonate(FEC)co-additives in electrolyte.The SiO_(x)anode material shows a capacity retention of 69.2%after 100 cycles at a current density of 1 A g^(-1)and rate capacity of 523 m A h g^(-1)at the current density of 3A g^(-1),while the SiO_(x)anode cycling in reference electrolyte has almost no capacity.
基金financially supported by the National Natural Science Foundation of China(Grant No.21673065 and 21875057)the Key-Area Research and Development Program of Guangdong Province(No.1934212200002)the Innovation and Entrepreneurship Team Project of Zhuhai(No.ZH01110405170016PWC)。
文摘Transition metal cation ordering is essential for controlling the electrochemical performance of cubic spinel LiNi_(0.5)Mn_(1.5)O_(4)(LNMO),which is conventionally adjusted by optimizing the high temperature sintering and annealing procedures.In this present work,multiple characterization techniques,including 6,7Li NMR,XRD and HRTEM,have been combined to trace the phase transformation and morphology evolution during synthesis.It has been illustrated that simultaneous formation of LiMn_(2)O_(4)(LMO)and LiNiO_(2)(LNO)binary oxides and their conversion into highly reactive LixNi^(3+)_(y)Mn_(3.5+)_(z)O ternary intermediate is a thermal dynamically difficult but crucial step in the synthesis of LNMO ternary oxide.A new strategy of modifying the intermediates formation pathway from binary mode to ternary mode using thermal regulating agent has been adopted.LNMO synthesized with thermal regulating agent exhibits supreme rate capability,long-cycling performance(even at elevated temperature)and excellent capacity efficiency.At a high rate of 100 C,the assembled battery delivers a discharge capacity of 99 mAh g^(-1).This study provides a way to control the formation pathway of complex oxides using thermal regulating agent.