Mg_(3)Sb_(2)-based thermoelectric materials have been the focus of widespread investigations as promising candidates for the harvesting of waste heat.Interface stability and service performance are key points for the ...Mg_(3)Sb_(2)-based thermoelectric materials have been the focus of widespread investigations as promising candidates for the harvesting of waste heat.Interface stability and service performance are key points for the commercial applications of these materials.We utilized Mg_(4.3)Sb_(3)Ni as a barrier layer to improve the thermal stability of Mg 3 Sb 2-based devices.However,its intrinsic high resistivity contributed nega-tively to the desired performance of the device.In this work,we investigated two other Mg-Sb-Ni ternary phases,MgSbNi and MgSbNi_(2),as new barrier layer materials to connect with Mg_(3.2)Sb_(2)Y_(0.05).The results show that the efficiency of the Mg_(1.2)SbNi/Mg_(3.2)Sb_(2)Y_(0.05)/Mg_(1.2)SbNi joint is increased by 33%relative to the higher Mg-content barriers due to lower resistivity.The system exhibited good interfacial compatibility and showed little change with aging at 673 K for 20 days.展开更多
基金supported by the National Science Foundation of China(Grant No.52202277)the Special Project of Science and Technology Cooperation and Exchange of Shanxi Province(Grant No.202104041101007).
文摘Mg_(3)Sb_(2)-based thermoelectric materials have been the focus of widespread investigations as promising candidates for the harvesting of waste heat.Interface stability and service performance are key points for the commercial applications of these materials.We utilized Mg_(4.3)Sb_(3)Ni as a barrier layer to improve the thermal stability of Mg 3 Sb 2-based devices.However,its intrinsic high resistivity contributed nega-tively to the desired performance of the device.In this work,we investigated two other Mg-Sb-Ni ternary phases,MgSbNi and MgSbNi_(2),as new barrier layer materials to connect with Mg_(3.2)Sb_(2)Y_(0.05).The results show that the efficiency of the Mg_(1.2)SbNi/Mg_(3.2)Sb_(2)Y_(0.05)/Mg_(1.2)SbNi joint is increased by 33%relative to the higher Mg-content barriers due to lower resistivity.The system exhibited good interfacial compatibility and showed little change with aging at 673 K for 20 days.