The slag composition corresponding to different coals varies significantly,which directly affects the operation of industrial entrained-flow gasifier and the service life of refractory bricks.In this study,the corrosi...The slag composition corresponding to different coals varies significantly,which directly affects the operation of industrial entrained-flow gasifier and the service life of refractory bricks.In this study,the corrosion resistance of several typical coal slags for gasification on high chromia refractory bricks was comparatively investigated by static laboratory crucible tests and thermodynamic simulations.The results demonstrated that the corrosion degree of high chromia refractory bricks by different coal slags was high-Ca/Na slag>high-Fe slag>high-Si/Al slag.The surface structure of the refractory was relatively flat after corrosion by high-Si/Al slag,and the primary corrosion reaction was the partial dissolution of the matrix by the slag.High-Fe slag was prone to the precipitation of iron phases as well as the formation of(Mg,Fe)(Al,Cr)_(2)O_(4)composite spinel layer at the slag/refractory interface.The high-Ca/Na slag was susceptible to react with the refractory to yield a low melting point phase,which led to the destruction of the matrix structure of the refractory and an isolated distribution of particles.In addition,the monoclinic ZrO_(2) in the refractory reacted with CaO in the slag to formed calcium zirconate,which loosened its phase toughening effect,was the primary factor that aggravated the refractory corrosion.展开更多
Replacing heavy oil with petrol coke can greatly reduce the cost of glass production,but obviously shorten the service life of refractories used in the regenerator checker body of glass tanks.To prolong the service li...Replacing heavy oil with petrol coke can greatly reduce the cost of glass production,but obviously shorten the service life of refractories used in the regenerator checker body of glass tanks.To prolong the service life of the regenerator checker body,the slag chemical composition and alkali-sulfur ratio of glass tanks after using petrol coke and the damage mechanism of the residual magnesia bricks in the regenerator checker body were studied,as well as the corrosion resistance of three magnesia based bricks(direct bonded magnesia chrome bricks,fused rebonded magnesia chrome bricks,and fused rebonded high-purity magnesium aluminate spinel bricks).On this basis,a series of targeted countermeasures were adopted to optimize the configuration of refractories,significantly improving the service life of checker bricks and meeting the requirements of glass industry development.展开更多
Unburned magnesium aluminate spinel refractories were prepared using sintered magnesium aluminate spinel as the main raw material,phenolic resin as the binder,aluminum powder(2%,4%,and 6%by mass)and silicon powder(whe...Unburned magnesium aluminate spinel refractories were prepared using sintered magnesium aluminate spinel as the main raw material,phenolic resin as the binder,aluminum powder(2%,4%,and 6%by mass)and silicon powder(when Al powder addition is 4%,Si powder addition varies:1%and 2%,by mass)as additives.The effects of the Al powder and Si powder additions on the properties and microstructure of the refractories heat treated at different temperatures(1000,1400,and 1600℃for 3 h)were studied.The results show that the Al powder addition can greatly enhance the cold modulus of rupture of the samples fired at 1000 or 1400℃,and meanwhile AlN reinforcement phase forms in the matrix,which greatly improves the hot modulus of rupture of the samples at 1400℃;however,the heat treatment at 1600℃has little influence on the strength;the addition of Al powder and Si powder results in the formation of low melting point phases,greatly reducing the hot modulus of rupture.However,the low melting point phases promote sintering,which enhances the density and the cold modulus of rupture,and decreases the volume change during heating.The samples added with Al and Si all have higher cold modulus of rupture than those added with Al powder only.展开更多
In order to investigate the effect of the catalyst loading mode on the mechanical properties of Si_(3)N_(4) composite MgO-C refractories prepared by nitridation,fused magnesia,flake graphite,silicon powder,and phenoli...In order to investigate the effect of the catalyst loading mode on the mechanical properties of Si_(3)N_(4) composite MgO-C refractories prepared by nitridation,fused magnesia,flake graphite,silicon powder,and phenolic resin were used as the main raw materials,and ferric nitrate as the catalyst to prepare refractories by nitriding at 1350℃.The effects of different catalyst supports(silicon powder,silicon powder+phenolic resin)on the formation of Si_(3)N_(4) in MgO-C refractories and the properties of refractories were studied.The results show that the silicon powder+resin catalyst support promotes the participation ofα-Si_(3)N_(4) in the reaction to generateβ-Si_(3)N_(4) and MgSiN_(2),and generates more SiC.However,this loading mode causes more gas to escape from the refractories and loosens the material structure,which reduces the mechanical properties.On the contrary,MgO-C refractories prepared by nitridation with silicon powder-supported catalysts under the same conditions show higher density and better mechanical properties.展开更多
基金financial support from the Joint Funds of the National Natural Science Foundation of China(U21A20318).
文摘The slag composition corresponding to different coals varies significantly,which directly affects the operation of industrial entrained-flow gasifier and the service life of refractory bricks.In this study,the corrosion resistance of several typical coal slags for gasification on high chromia refractory bricks was comparatively investigated by static laboratory crucible tests and thermodynamic simulations.The results demonstrated that the corrosion degree of high chromia refractory bricks by different coal slags was high-Ca/Na slag>high-Fe slag>high-Si/Al slag.The surface structure of the refractory was relatively flat after corrosion by high-Si/Al slag,and the primary corrosion reaction was the partial dissolution of the matrix by the slag.High-Fe slag was prone to the precipitation of iron phases as well as the formation of(Mg,Fe)(Al,Cr)_(2)O_(4)composite spinel layer at the slag/refractory interface.The high-Ca/Na slag was susceptible to react with the refractory to yield a low melting point phase,which led to the destruction of the matrix structure of the refractory and an isolated distribution of particles.In addition,the monoclinic ZrO_(2) in the refractory reacted with CaO in the slag to formed calcium zirconate,which loosened its phase toughening effect,was the primary factor that aggravated the refractory corrosion.
文摘Replacing heavy oil with petrol coke can greatly reduce the cost of glass production,but obviously shorten the service life of refractories used in the regenerator checker body of glass tanks.To prolong the service life of the regenerator checker body,the slag chemical composition and alkali-sulfur ratio of glass tanks after using petrol coke and the damage mechanism of the residual magnesia bricks in the regenerator checker body were studied,as well as the corrosion resistance of three magnesia based bricks(direct bonded magnesia chrome bricks,fused rebonded magnesia chrome bricks,and fused rebonded high-purity magnesium aluminate spinel bricks).On this basis,a series of targeted countermeasures were adopted to optimize the configuration of refractories,significantly improving the service life of checker bricks and meeting the requirements of glass industry development.
文摘Unburned magnesium aluminate spinel refractories were prepared using sintered magnesium aluminate spinel as the main raw material,phenolic resin as the binder,aluminum powder(2%,4%,and 6%by mass)and silicon powder(when Al powder addition is 4%,Si powder addition varies:1%and 2%,by mass)as additives.The effects of the Al powder and Si powder additions on the properties and microstructure of the refractories heat treated at different temperatures(1000,1400,and 1600℃for 3 h)were studied.The results show that the Al powder addition can greatly enhance the cold modulus of rupture of the samples fired at 1000 or 1400℃,and meanwhile AlN reinforcement phase forms in the matrix,which greatly improves the hot modulus of rupture of the samples at 1400℃;however,the heat treatment at 1600℃has little influence on the strength;the addition of Al powder and Si powder results in the formation of low melting point phases,greatly reducing the hot modulus of rupture.However,the low melting point phases promote sintering,which enhances the density and the cold modulus of rupture,and decreases the volume change during heating.The samples added with Al and Si all have higher cold modulus of rupture than those added with Al powder only.
基金supported by the National Natural Science Foundation of China(U20A20239)the Natural Science Foundation of Hubei Province(2020CFB692)the Scientific Research Fund of Hunan Provincial Education Department(18A428).
文摘In order to investigate the effect of the catalyst loading mode on the mechanical properties of Si_(3)N_(4) composite MgO-C refractories prepared by nitridation,fused magnesia,flake graphite,silicon powder,and phenolic resin were used as the main raw materials,and ferric nitrate as the catalyst to prepare refractories by nitriding at 1350℃.The effects of different catalyst supports(silicon powder,silicon powder+phenolic resin)on the formation of Si_(3)N_(4) in MgO-C refractories and the properties of refractories were studied.The results show that the silicon powder+resin catalyst support promotes the participation ofα-Si_(3)N_(4) in the reaction to generateβ-Si_(3)N_(4) and MgSiN_(2),and generates more SiC.However,this loading mode causes more gas to escape from the refractories and loosens the material structure,which reduces the mechanical properties.On the contrary,MgO-C refractories prepared by nitridation with silicon powder-supported catalysts under the same conditions show higher density and better mechanical properties.