The flow stress behavior and microstructure development of Al-5Zn-2Mg （7005） aluminum alloy were studied by hot compression tests at deformation temperatures between 300-500 ＆#176;C and strain rates between 0.05-50...The flow stress behavior and microstructure development of Al-5Zn-2Mg （7005） aluminum alloy were studied by hot compression tests at deformation temperatures between 300-500 ＆#176;C and strain rates between 0.05-50 s-1. The deformed structures of the samples were observed by optical microscopy （OM）, transmission electron microscopy （TEM） and electron backscattering diffraction （EBSD） analysis. The calculated activation energy is 147 kJ/mol, which is very close to the activation energy for lattice self-diffusion in aluminum （142 kJ/mol）. Dynamic recovery is the dominant restoration mechanism during the deformation. At high strain rate of 50 s-1, temperature rise due to deformation heating leads to a significant flow softening. Microstructure observations indicated that the remaining softening after deformation heating correction at high strain rate and the softening observed at high temperature are associated with grain coarsening induced by grain boundary migration during dynamic recovery process.展开更多
Mechanical behavior of nickel？titanium shape memory alloy（NiTi SMA） under hot deformation was investigated according to the true stress—strain curves of NiTi samples under compression at the strain rates of 0.001-...Mechanical behavior of nickel？titanium shape memory alloy（NiTi SMA） under hot deformation was investigated according to the true stress—strain curves of NiTi samples under compression at the strain rates of 0.001-1 s-1 and at the temperatures of 600？1000℃.Dynamic recovery and dynamic recrystallization of NiTi SMA were systematically investigated by microstructural evolution.The influence of the strain rates,the deformation temperatures and the deformation degree on the dynamic recovery and dynamic recrystallization of NiTi SMA was obtained as well.NiTi SMA was characterized by the combination of dynamic recovery and dynamic recrystallization at 600℃ and 700℃,but the complete dynamic recrystallization occurred at other deformation temperatures.Increasing the deformation temperatures or decreasing the stain rates leads to larger equiaxed grains.The deformation degree has an important influence on the dynamic recrystallization of NiTi SMA.There exists the critical deformation degree during the dynamic recrystallization of NiTi SMA,beyond which the larger deformation degree contributes to obtaining the finer equiaxed grains.展开更多
Dynamic recovery and dynamic recrystallizatin behaviors of AA7005 aluminium alloy (Al - Zn - Mg) during hot compression are investigated by isothermal compression testing.The interdependence of flow stress,stress, s...Dynamic recovery and dynamic recrystallizatin behaviors of AA7005 aluminium alloy (Al - Zn - Mg) during hot compression are investigated by isothermal compression testing.The interdependence of flow stress,stress, strain rate,true strain and deformation temperature for the alloy is analyzed by introduc- ing Zener-Hollomon parameter. A steady - state flow of the 7005 alloy is confirmed to be a thermal- ly activated process.which is governed by rate-controlling mechanisms of dislocations.A hyperbolic sine relationship can satisfactorily correlate temperature, strain rate with flow stress through an Arrhe- nius term that involves thermal activation parameters. The dynamic recovery mechanisms of the alloy are discussed.Cross- slip of jogged screw dislocations is the main dynamic recovery mechanism over the deformation temperatures and strain rates.Subgrains are highly developed in the originally elongat- ed grains.The size of the subgrain increases with decrease of the natural logarithm of Zener- Hol - lomon parameter.Local dynamic recrystallization is operative when the alloy is deformed at temperature of 500℃ and strain rate of 0. 001s - 1.展开更多
Network virtualization is a promising way to overcome the current ossification of the Intemet. It is essential challenge to find effective, efficient and robust embedding algorithms for recovering virtual network. The...Network virtualization is a promising way to overcome the current ossification of the Intemet. It is essential challenge to find effective, efficient and robust embedding algorithms for recovering virtual network. The virtual network mapping algorithm based on integer programming which was proposed months ago. But it did consider the faults of physical network resources, which is so called survivable virtual network embedding （VNE） problem. Previous strategies for enabling survivability in network virtualization focused on providing protection for the physical network or enhancing the virtual networks by providing backup physical resources in advance, and treated all the physical failures as link failures. In the article, a dynamic recovery method is proposed to solve the survivable virtual network embedding problem based on the integer programming VNE algorithm. The dynamic recovery method doesn＇t need to backup physical resources and it makes more substrate resources which can be used in the embedding. The dynamic recovery process will be activated only when physical failures occur. Different algorithms are used to recovery node and link failures. Simulations show that the method helps to recover almost all of physical failures by finding the substitute nodes and paths, and its performance is very close to that of pure VNE method without considering physical failures.展开更多
Dynamic performance is important to the controlling and monitoring of the organic Rankine cycle(ORC) system so to avoid the occurrence of unwanted conditions. A small scale waste heat recovery system with organic Rank...Dynamic performance is important to the controlling and monitoring of the organic Rankine cycle(ORC) system so to avoid the occurrence of unwanted conditions. A small scale waste heat recovery system with organic Rankine cycle was constructed and the dynamic behavior was presented. In the dynamic test, the pump was stopped and then started. In addition, there was a step change of the flue gas volume flow rate and the converter frequency of multistage pump, respectively. The results indicate that the working fluid flow rate has the shortest response time, followed by the expander inlet pressure and the expander inlet temperature.The operation frequency of pump is a key parameter for the ORC system. Due to a step change of pump frequency(39.49-35.24 Hz),the expander efficiency and thermal efficiency drop by 16% and 21% within 2 min, respectively. Besides, the saturated mixture can lead to an increase of the expander rotation speed.展开更多
Based on the dynamic dielectric recovery process in the vacuum gaps in series, investigations were made on post-arc insulation state in double and multi-breaks operation in high voltage power system. From the research...Based on the dynamic dielectric recovery process in the vacuum gaps in series, investigations were made on post-arc insulation state in double and multi-breaks operation in high voltage power system. From the research on the breakdown weak points in high voltage vacuum gaps, their turnout and distribution, some theoretic work were made to set up the models for describing the statistical property of multi-breaks vacuum circuit-breakers' breakdown and post-arc re-strike, which can be used for explaining the mechanism of the improvement in the breaking capacity of multi-breaks units compared with that of single-break ones which have the same equivalent gap length. The advantages of vacuum breakers with multi-breaks are proposed.展开更多
The Al?4.10Cu?1.42Mg?0.57Mn?0.12Zr alloy was compressed to different strains at deformation temperature of 300 oC and strain rate of 10 s?1 on Gleeble?1500 system. The dynamic complex microstructures evolutions were i...The Al?4.10Cu?1.42Mg?0.57Mn?0.12Zr alloy was compressed to different strains at deformation temperature of 300 oC and strain rate of 10 s?1 on Gleeble?1500 system. The dynamic complex microstructures evolutions were investigated by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The true stress?true strain curves exhibited a peak stress at critical strain, after which the flow stresses decreased monotonically, showing a dynamic flow softening. As the strain increased, the dislocation tangled to cell structure and sub-grain structure, which indicated the occurrence of dynamic recovery during deformation. Dynamic precipitations ofS (Al2CuMg),θ (Al2Cu) and Al3Zr phase were accelerated and coarsened by deformation. ContinuousS phases precipitated in the Al matrix and discontinuousS phases were found to be nucleated near the Al3Zr phase and at the sub-grain boundary. The flow softening mechanism was resulted from the reduction of dislocation density which attributed to dynamic recovery and precipitates coarsening.展开更多
The microstructures in the electroformed copper liners of shapedcharges after high-strain-rate plastic deformation were in-vestigated by transmission electron microscopy(TEM). Meanwhile, theorientation distribution of...The microstructures in the electroformed copper liners of shapedcharges after high-strain-rate plastic deformation were in-vestigated by transmission electron microscopy(TEM). Meanwhile, theorientation distribution of the grains in the recovered slug wasexamined by the electron backscattering Kikuchipattern(EBSP)technique. EBSP analysis illustrated that unlike theas-formed electro- formed copper liners of shaped charges the grainorientations in the recovered slug are distributed along randomly allthe directions after undergoing heavily strain deformation athigh-strain rate. Optical microscopy shows a typicalrecrystallization structure, and TEM exam- ination revealsdislocation cells existed in the thin foil specimen. These resultsindicate that dynamic recovery and recrystallization occur duringthis plastic deformation process, and the associated deformationtemperature is considered to be higher than 0.6 times the meltingpoint of copper.展开更多
The hot deformation behavior of a high Ti 6061 aluminum alloy in the temperature range from 350 to 510 ℃ and strain rate range from 0.001 to 10 s^-1 was investigated using stress-strain curve analysis, processing map...The hot deformation behavior of a high Ti 6061 aluminum alloy in the temperature range from 350 to 510 ℃ and strain rate range from 0.001 to 10 s^-1 was investigated using stress-strain curve analysis, processing map, transmission electron microscopy and electron backscatter diffraction analysis. The results show that the peak stress decreases with increasing deformation temperatures and decreasing strain rate. The average deformation activation energy is 185 kJ/mol in the parameter range investigated. The flow stress model was constructed. The main softening mechanism is dynamic recovery. The processing map was obtained using dynamic material model, and the suggested processing window is 400-440℃ and 0.001-0.1 s^-1.展开更多
Hot compression of 7050 aluminum alloy was performed on Gleeble 1500D thermo-mechanical simulator at 350 ℃ and 450 ℃ with a constant strain rate of 0.1 s-1 to different nominal strains of 0.1, 0.3 and 0.7. Microstru...Hot compression of 7050 aluminum alloy was performed on Gleeble 1500D thermo-mechanical simulator at 350 ℃ and 450 ℃ with a constant strain rate of 0.1 s-1 to different nominal strains of 0.1, 0.3 and 0.7. Microstructures of 7050 alloy under various compression conditions were observed by TEM to investigate the microstructure evolution process of the alloy deformed at various temperatures. The microstructure evolves from dislocation tangles to cell structure and subgrain structure when being deformed at 350 ℃, of which dynamic recovery is the softening mechanism. However, continuous dynamic recrystallization (DRX) occurs during hot deformation at 450 ℃, in which the main nucleation mechanisms of DRX are subgrain growth and subgrain coalescence rather than particle-simulated nucleation (PSN).展开更多
The microstructure and mechanical properties of 105 mm thick 5083 aluminum alloy hot rolled plate were investigated by metallurgical microscope, scanning electron microscope and tensile testing machine, and three majo...The microstructure and mechanical properties of 105 mm thick 5083 aluminum alloy hot rolled plate were investigated by metallurgical microscope, scanning electron microscope and tensile testing machine, and three major characteristic problems in mechanical properties inhomogeneity were explained. The results show that the mechanical properties of the rolled plate are inhomogeneous along the thickness direction. From the surface to the center, the strength shows an inverted "N" shape change and the elongation presents a semi "U" shape change. Several similar structural units composed of long fibrous grains(LFG) and short fibrous grains bands(SFGB) exist in a special layer(Layer 2) adjacent to the surface. This alternating layered distribution of LFG and SFGB is conducive to improving the plasticity by dispersing the plastic deformation concentrated on the boundary line(BL) between them. However, their different deformability will cause the alternation of additional stresses during the hot rolling, leading to the strength reduction. The closer the location to the center of the plate is, the more likely the recovery rather than the recrystallization occurs. This is the possible reason for the unnegligible difference in strength near the central region(Layer 4 and Layer 5).展开更多
The hot deformation behavior and microstructures of Al-7055 commercial alloy were investigated by axisymmetric hot compres- sion at temperatures ranging from 300℃ to 450℃ and strain rates from 10^-2 to 10 s^-1, resp...The hot deformation behavior and microstructures of Al-7055 commercial alloy were investigated by axisymmetric hot compres- sion at temperatures ranging from 300℃ to 450℃ and strain rates from 10^-2 to 10 s^-1, respectively. Microstructures of deformed 7055 alloy were investigated by transmission electron microscopy （TEM）. The dependence of peak stress on deformation temperature and strain rate can be expressed by the hyperbolic-sine type equation. The hot deformation activation energy of the alloy is 146 kJ/mol. Moreover, the flow stress curves predicted by the modified constitutive equations are reasonably consistent with the experimental results, which confirms that the proposed deformation constitutive equations can provide evidence for the selection of hot forming parameters. TEM results indicate that dy- namic recovery is the main softening mechanism during hot deformation.展开更多
Hot compression tests of 2050 Al-Li alloy were performed in the deformation temperature range of 340-500°C and strain rate range of 0.001-10 s-1 to investigate the hot deformation behavior of the alloy.The effect...Hot compression tests of 2050 Al-Li alloy were performed in the deformation temperature range of 340-500°C and strain rate range of 0.001-10 s-1 to investigate the hot deformation behavior of the alloy.The effects of friction and temperature difference on flow stress were analyzed and the flow curves were corrected.Based on the dynamic material model,processing map at a strain of 0.5 was established.The grain structure of the compressed samples was observed using optical microscopy.The results show that friction and temperature variation during the hot compression have significant influences on flow stress.The optimum processing domains are in the temperature range from 370 to 430°C with the strain rate range from 0.01 to 0.001 s-1,and in the temperature range from 440 to 500°C with the strain rate range from 0.3 to 0.01 s-1;the flow instable region is located at high strain rates(3-10 s-1)in the entire temperature range.Dynamic recovery(DRV)and dynamic recrystallization(DRX)are the main deformation mechanisms of the 2050 alloy in the stable domains,whereas the alloy exhibits flow localization in the instable region.展开更多
Compression tests of the Al-Zn-Mg-Cu-Zr（7055） alloy were performed at various strains and temperatures from 300 to 450℃ under a con- stant strain rate between 10^-2 s^-1and 1 s^-1. Microstructures during hot deform...Compression tests of the Al-Zn-Mg-Cu-Zr（7055） alloy were performed at various strains and temperatures from 300 to 450℃ under a con- stant strain rate between 10^-2 s^-1and 1 s^-1. Microstructures during hot deformation were studied by transmission electron microscopy （TEM）. Dislocation density, dislocation cells and subgrains of the deformed samples were investigated in detail and compared to make a better understanding of the microstructure evolution. The results showed that stress-strain curves under the experimental conditions belonged to the type of dynamic recovery. When the alloy deformed at various strains and 300℃, the microstructure underwent a process of disordered dislocations to cell structure, subgrain structure and subgrain coarsening. With the temperature increasing, subgrains grew and dislocation density in the interior decreased at a strain rate of 1 s^-1. At the temperature of 350℃, the average diameter of subgrains decreased, sub-boundaries broadened and dislocation density in the interior decreased when the strain rate was increased. The deformed samples of 7055 alloy had smaller subgrains than that of 7005 alloy at the same compression condition because of high alloy content.展开更多
Nickel liner of shaped charge with nano-sized grains was prepared by electroforming technique and the ultra-highstrain-rate deformation was performed by explosive detonation.The as-electroformed and post-deformed micr...Nickel liner of shaped charge with nano-sized grains was prepared by electroforming technique and the ultra-highstrain-rate deformation was performed by explosive detonation.The as-electroformed and post-deformed microstructures of electroformed nickel liner of shaped charge were observed by optical metallography(OM),scanning electron microscopy(SEM) and transmission electron microscopy(TEM) and the orientation distribution of the grains was analyzed by electron backscattering pattern(EBSP) technique.Both melting phenomenon in the jet fragment and recovery and recrystallization in the slug after ultra-high-strain-rate deformation were observed.The research evidence shows that dynamic recovery and recrystallization play an important role in ultra-high-strain-rate deformation for electroformed nickel liner of shaped charge with nano-sized grain.展开更多
The constitutive model was developed to describe the relationship among flow stress,strain,strain rate,and deformation temperature completely,based on the characteristics of flow stress curves for a new kind of metast...The constitutive model was developed to describe the relationship among flow stress,strain,strain rate,and deformation temperature completely,based on the characteristics of flow stress curves for a new kind of metastable β Ti2448 titanium alloy from isothermal hot compression tests,in a wide range of temperatures（1023-1123 K） and strain rates（63-0.001 s-1）.During this process,the adopted hyperbolic sine function based on the unified viscoplasticity theory was used to model the flow behavior of alloy undergoing flow softening caused by dynamic recovery（DRV） at high strain rates（≥1 s-1）.The standard Avrami equation was adopted to represent the softening mechanism attributed to dynamic recrystallization（DRX） at low strain rates（1 s-1）.Additionally,the material constants were determined by optimization strategy,which is a new method to solve the nonlinear constitutive equation.The stress—strain curves predicted by the developed constitutive model agree well with the experimental results,which con-rms that the developed constitutive model can give an accurate estimate of the-ow stress of Ti2448 titanium alloy and provide an effective method to model the flow behavior of metastable β titanium alloys during hot deformation.展开更多
The influence of welding speed on the joint microstructures of an austenitic stainless steel(ASS)produced by friction stir welding(FSW)was investigated.The FSW process was conducted using a rotational speed of 400 r/m...The influence of welding speed on the joint microstructures of an austenitic stainless steel(ASS)produced by friction stir welding(FSW)was investigated.The FSW process was conducted using a rotational speed of 400 r/min and welding speeds of 50 and 150 mm/min.The study was carried out using electron backscattered diffraction(EBSD)technique in different regions of the resultant stir zones(SZs).The results show that the texture of the advancing side(AS)was mainly composed of C{001}〈110〉and cube{001}〈100〉texture components along with partial B/B{112}〈110〉component.Moving from the AS toward the center and the retreating side(RS),the cube texture component disappeared and the A;/A*{111}(112)component developed and predominated the other components.Higher welding speed greatly affected and decreased the intensity of the textures in the resultant SZs.Moreover,higher welding speed(lower heat input)resulted in lower frequency of cube texture in the AS.展开更多
The hot deformation behavior of FGH96 superalloys at 1070-1170℃ and 5×10^-4-2×10^-1 s^-1 were investigated by means of the isothermal compression tests at a Gleeble-1500 thermal mechanical simulator. The re...The hot deformation behavior of FGH96 superalloys at 1070-1170℃ and 5×10^-4-2×10^-1 s^-1 were investigated by means of the isothermal compression tests at a Gleeble-1500 thermal mechanical simulator. The results show that dynamic recovery acts as the main softening mechanism below 2×10^-3 s^-1, whereas dynamic recrystallization acts as the main softening mechanism above 2× 10^-3 s^-1 during deformation; the temperature increase caused by the deformation and the corresponding softening stress is negligible; the thermal-mechanical constitutive model to describe the hot deformation behavior is given, and the value of the apparent deformation activation energy （Qdef） is determined to be 354.93 kJ/mol.展开更多
Hot compression tests were conducted on a Gleeble-1500 simulator to investigate the hot deformation behavior of BT20 Ti alloy （Ti-6Al-2Zr-IMo-1V） in the temperature range from 550 to 1000℃ at constant strain rate i...Hot compression tests were conducted on a Gleeble-1500 simulator to investigate the hot deformation behavior of BT20 Ti alloy （Ti-6Al-2Zr-IMo-1V） in the temperature range from 550 to 1000℃ at constant strain rate in the range of 0.01-1s^-1, and then the optimum spinning temperature range was determined. Moreover, tube spinning experiments were executed to verify the reasonability of the optimum temperature range. The results show that the flow stress declines gradually with increasing deformation temperature and decreasing strain rate. In α＋β phase region the dynamic recrystallization is the main softening mechanism and in β phase region the hot deformation softening is controlled by dynamic recovery. In α＋β phase region with reducing strain rate dynamic recrystallization is fully developed. The optimum temperature of hot spinning is 850-900℃ and that of warm spinning is 600-650℃. Meanwhile, at the temperature above 600℃ tubular workpieces of BT20 Ti alloy have been spun without surface cracks and microstructure inhomogeneity, which proves that the optimum spinning temperature range obtained through hot compression experiments is reasonable.展开更多
To realize numerical simulation of rolling and obtain the hot forming process parameters for X70 HD steel, the flow stress behaviors of X70 HD steel were investigated under different temperatures（820-1100 ℃ and stra...To realize numerical simulation of rolling and obtain the hot forming process parameters for X70 HD steel, the flow stress behaviors of X70 HD steel were investigated under different temperatures（820-1100 ℃ and strain rates（0.01-10 s-1） on a Gleeble-3500 thermo-simulation machine. A new flow stress model was established. The linear and exponential relationship methods were applied to the parameters with respect to temperature and deformation rates. The rise of curve ends under certain conditions was analyzed. The flow stress of X70 HD steel predicted by the proposed model agrees well with the experimental results. So, it greatly improves the precision of the metal thermoplastic processing through finite element method and practical application of engineering.展开更多
基金Project(51075132)supported by the National Natural Science Foundation of ChinaProject(20090161110027)supported by the Doctoral Fund of Ministry of Education of ChinaProject(2011BAG03B02)supported by National Key Technology R&D Program during the 12th Five-Year Plan Period,China
文摘The flow stress behavior and microstructure development of Al-5Zn-2Mg （7005） aluminum alloy were studied by hot compression tests at deformation temperatures between 300-500 ＆#176;C and strain rates between 0.05-50 s-1. The deformed structures of the samples were observed by optical microscopy （OM）, transmission electron microscopy （TEM） and electron backscattering diffraction （EBSD） analysis. The calculated activation energy is 147 kJ/mol, which is very close to the activation energy for lattice self-diffusion in aluminum （142 kJ/mol）. Dynamic recovery is the dominant restoration mechanism during the deformation. At high strain rate of 50 s-1, temperature rise due to deformation heating leads to a significant flow softening. Microstructure observations indicated that the remaining softening after deformation heating correction at high strain rate and the softening observed at high temperature are associated with grain coarsening induced by grain boundary migration during dynamic recovery process.
基金Project(51071056) supported by the National Natural Science Foundation of ChinaProjects(HEUCFR1132,HEUCF121712) supported by the Fundamental Research Funds for the Central Universities of China
文摘Mechanical behavior of nickel？titanium shape memory alloy（NiTi SMA） under hot deformation was investigated according to the true stress—strain curves of NiTi samples under compression at the strain rates of 0.001-1 s-1 and at the temperatures of 600？1000℃.Dynamic recovery and dynamic recrystallization of NiTi SMA were systematically investigated by microstructural evolution.The influence of the strain rates,the deformation temperatures and the deformation degree on the dynamic recovery and dynamic recrystallization of NiTi SMA was obtained as well.NiTi SMA was characterized by the combination of dynamic recovery and dynamic recrystallization at 600℃ and 700℃,but the complete dynamic recrystallization occurred at other deformation temperatures.Increasing the deformation temperatures or decreasing the stain rates leads to larger equiaxed grains.The deformation degree has an important influence on the dynamic recrystallization of NiTi SMA.There exists the critical deformation degree during the dynamic recrystallization of NiTi SMA,beyond which the larger deformation degree contributes to obtaining the finer equiaxed grains.
文摘Dynamic recovery and dynamic recrystallizatin behaviors of AA7005 aluminium alloy (Al - Zn - Mg) during hot compression are investigated by isothermal compression testing.The interdependence of flow stress,stress, strain rate,true strain and deformation temperature for the alloy is analyzed by introduc- ing Zener-Hollomon parameter. A steady - state flow of the 7005 alloy is confirmed to be a thermal- ly activated process.which is governed by rate-controlling mechanisms of dislocations.A hyperbolic sine relationship can satisfactorily correlate temperature, strain rate with flow stress through an Arrhe- nius term that involves thermal activation parameters. The dynamic recovery mechanisms of the alloy are discussed.Cross- slip of jogged screw dislocations is the main dynamic recovery mechanism over the deformation temperatures and strain rates.Subgrains are highly developed in the originally elongat- ed grains.The size of the subgrain increases with decrease of the natural logarithm of Zener- Hol - lomon parameter.Local dynamic recrystallization is operative when the alloy is deformed at temperature of 500℃ and strain rate of 0. 001s - 1.
基金supported by the National Basic Research Programs of China(2012CB315801)
文摘Network virtualization is a promising way to overcome the current ossification of the Intemet. It is essential challenge to find effective, efficient and robust embedding algorithms for recovering virtual network. The virtual network mapping algorithm based on integer programming which was proposed months ago. But it did consider the faults of physical network resources, which is so called survivable virtual network embedding （VNE） problem. Previous strategies for enabling survivability in network virtualization focused on providing protection for the physical network or enhancing the virtual networks by providing backup physical resources in advance, and treated all the physical failures as link failures. In the article, a dynamic recovery method is proposed to solve the survivable virtual network embedding problem based on the integer programming VNE algorithm. The dynamic recovery method doesn＇t need to backup physical resources and it makes more substrate resources which can be used in the embedding. The dynamic recovery process will be activated only when physical failures occur. Different algorithms are used to recovery node and link failures. Simulations show that the method helps to recover almost all of physical failures by finding the substitute nodes and paths, and its performance is very close to that of pure VNE method without considering physical failures.
基金Project(2009Gk2009)supported by the Science and Technology Department Funds of Hunan Province,ChinaProject(12C0379)supported by the Scientific Research Fund of Hunan Province,ChinaProject(13QDZ04)supported by the Scientific Research Foundation for Doctors of Xiang Tan University,China
文摘Dynamic performance is important to the controlling and monitoring of the organic Rankine cycle(ORC) system so to avoid the occurrence of unwanted conditions. A small scale waste heat recovery system with organic Rankine cycle was constructed and the dynamic behavior was presented. In the dynamic test, the pump was stopped and then started. In addition, there was a step change of the flue gas volume flow rate and the converter frequency of multistage pump, respectively. The results indicate that the working fluid flow rate has the shortest response time, followed by the expander inlet pressure and the expander inlet temperature.The operation frequency of pump is a key parameter for the ORC system. Due to a step change of pump frequency(39.49-35.24 Hz),the expander efficiency and thermal efficiency drop by 16% and 21% within 2 min, respectively. Besides, the saturated mixture can lead to an increase of the expander rotation speed.
文摘Based on the dynamic dielectric recovery process in the vacuum gaps in series, investigations were made on post-arc insulation state in double and multi-breaks operation in high voltage power system. From the research on the breakdown weak points in high voltage vacuum gaps, their turnout and distribution, some theoretic work were made to set up the models for describing the statistical property of multi-breaks vacuum circuit-breakers' breakdown and post-arc re-strike, which can be used for explaining the mechanism of the improvement in the breaking capacity of multi-breaks units compared with that of single-break ones which have the same equivalent gap length. The advantages of vacuum breakers with multi-breaks are proposed.
基金Project(2009CB623704)supported by the National Basic Research(973)Program of ChinaProject(20130161110007)supported by the Doctoral Program of the Ministry of Education,ChinaProject(CX2013B128)supported by Hunan Provincial Innovation Foundation for Postgraduate,China
文摘The Al?4.10Cu?1.42Mg?0.57Mn?0.12Zr alloy was compressed to different strains at deformation temperature of 300 oC and strain rate of 10 s?1 on Gleeble?1500 system. The dynamic complex microstructures evolutions were investigated by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The true stress?true strain curves exhibited a peak stress at critical strain, after which the flow stresses decreased monotonically, showing a dynamic flow softening. As the strain increased, the dislocation tangled to cell structure and sub-grain structure, which indicated the occurrence of dynamic recovery during deformation. Dynamic precipitations ofS (Al2CuMg),θ (Al2Cu) and Al3Zr phase were accelerated and coarsened by deformation. ContinuousS phases precipitated in the Al matrix and discontinuousS phases were found to be nucleated near the Al3Zr phase and at the sub-grain boundary. The flow softening mechanism was resulted from the reduction of dislocation density which attributed to dynamic recovery and precipitates coarsening.
基金financially supported by the National Natural Science Foundation of China (No.59971008).
文摘The microstructures in the electroformed copper liners of shapedcharges after high-strain-rate plastic deformation were in-vestigated by transmission electron microscopy(TEM). Meanwhile, theorientation distribution of the grains in the recovered slug wasexamined by the electron backscattering Kikuchipattern(EBSP)technique. EBSP analysis illustrated that unlike theas-formed electro- formed copper liners of shaped charges the grainorientations in the recovered slug are distributed along randomly allthe directions after undergoing heavily strain deformation athigh-strain rate. Optical microscopy shows a typicalrecrystallization structure, and TEM exam- ination revealsdislocation cells existed in the thin foil specimen. These resultsindicate that dynamic recovery and recrystallization occur duringthis plastic deformation process, and the associated deformationtemperature is considered to be higher than 0.6 times the meltingpoint of copper.
文摘The hot deformation behavior of a high Ti 6061 aluminum alloy in the temperature range from 350 to 510 ℃ and strain rate range from 0.001 to 10 s^-1 was investigated using stress-strain curve analysis, processing map, transmission electron microscopy and electron backscatter diffraction analysis. The results show that the peak stress decreases with increasing deformation temperatures and decreasing strain rate. The average deformation activation energy is 185 kJ/mol in the parameter range investigated. The flow stress model was constructed. The main softening mechanism is dynamic recovery. The processing map was obtained using dynamic material model, and the suggested processing window is 400-440℃ and 0.001-0.1 s^-1.
文摘Hot compression of 7050 aluminum alloy was performed on Gleeble 1500D thermo-mechanical simulator at 350 ℃ and 450 ℃ with a constant strain rate of 0.1 s-1 to different nominal strains of 0.1, 0.3 and 0.7. Microstructures of 7050 alloy under various compression conditions were observed by TEM to investigate the microstructure evolution process of the alloy deformed at various temperatures. The microstructure evolves from dislocation tangles to cell structure and subgrain structure when being deformed at 350 ℃, of which dynamic recovery is the softening mechanism. However, continuous dynamic recrystallization (DRX) occurs during hot deformation at 450 ℃, in which the main nucleation mechanisms of DRX are subgrain growth and subgrain coalescence rather than particle-simulated nucleation (PSN).
基金Project(2011DFR50950)supported by the International Science and Technology Cooperation Program of ChinaProject(51971183)supported by the National Natural Science Foundation of ChinaProject(cstc2019jcyj-msxmX0594)supported by the Natural Science Foundation of Chongqing,China。
文摘The microstructure and mechanical properties of 105 mm thick 5083 aluminum alloy hot rolled plate were investigated by metallurgical microscope, scanning electron microscope and tensile testing machine, and three major characteristic problems in mechanical properties inhomogeneity were explained. The results show that the mechanical properties of the rolled plate are inhomogeneous along the thickness direction. From the surface to the center, the strength shows an inverted "N" shape change and the elongation presents a semi "U" shape change. Several similar structural units composed of long fibrous grains(LFG) and short fibrous grains bands(SFGB) exist in a special layer(Layer 2) adjacent to the surface. This alternating layered distribution of LFG and SFGB is conducive to improving the plasticity by dispersing the plastic deformation concentrated on the boundary line(BL) between them. However, their different deformability will cause the alternation of additional stresses during the hot rolling, leading to the strength reduction. The closer the location to the center of the plate is, the more likely the recovery rather than the recrystallization occurs. This is the possible reason for the unnegligible difference in strength near the central region(Layer 4 and Layer 5).
文摘The hot deformation behavior and microstructures of Al-7055 commercial alloy were investigated by axisymmetric hot compres- sion at temperatures ranging from 300℃ to 450℃ and strain rates from 10^-2 to 10 s^-1, respectively. Microstructures of deformed 7055 alloy were investigated by transmission electron microscopy （TEM）. The dependence of peak stress on deformation temperature and strain rate can be expressed by the hyperbolic-sine type equation. The hot deformation activation energy of the alloy is 146 kJ/mol. Moreover, the flow stress curves predicted by the modified constitutive equations are reasonably consistent with the experimental results, which confirms that the proposed deformation constitutive equations can provide evidence for the selection of hot forming parameters. TEM results indicate that dy- namic recovery is the main softening mechanism during hot deformation.
基金Project(2013JSJJ0001)supported by the Teachers’ Research Fund,Central South University,ChinaProject supported by the Nonferrous Metal Oriented Advanced Structural Materials and Manufacturing Cooperative Innovation Center,China
文摘Hot compression tests of 2050 Al-Li alloy were performed in the deformation temperature range of 340-500°C and strain rate range of 0.001-10 s-1 to investigate the hot deformation behavior of the alloy.The effects of friction and temperature difference on flow stress were analyzed and the flow curves were corrected.Based on the dynamic material model,processing map at a strain of 0.5 was established.The grain structure of the compressed samples was observed using optical microscopy.The results show that friction and temperature variation during the hot compression have significant influences on flow stress.The optimum processing domains are in the temperature range from 370 to 430°C with the strain rate range from 0.01 to 0.001 s-1,and in the temperature range from 440 to 500°C with the strain rate range from 0.3 to 0.01 s-1;the flow instable region is located at high strain rates(3-10 s-1)in the entire temperature range.Dynamic recovery(DRV)and dynamic recrystallization(DRX)are the main deformation mechanisms of the 2050 alloy in the stable domains,whereas the alloy exhibits flow localization in the instable region.
文摘Compression tests of the Al-Zn-Mg-Cu-Zr（7055） alloy were performed at various strains and temperatures from 300 to 450℃ under a con- stant strain rate between 10^-2 s^-1and 1 s^-1. Microstructures during hot deformation were studied by transmission electron microscopy （TEM）. Dislocation density, dislocation cells and subgrains of the deformed samples were investigated in detail and compared to make a better understanding of the microstructure evolution. The results showed that stress-strain curves under the experimental conditions belonged to the type of dynamic recovery. When the alloy deformed at various strains and 300℃, the microstructure underwent a process of disordered dislocations to cell structure, subgrain structure and subgrain coarsening. With the temperature increasing, subgrains grew and dislocation density in the interior decreased at a strain rate of 1 s^-1. At the temperature of 350℃, the average diameter of subgrains decreased, sub-boundaries broadened and dislocation density in the interior decreased when the strain rate was increased. The deformed samples of 7055 alloy had smaller subgrains than that of 7005 alloy at the same compression condition because of high alloy content.
基金Project(50671012) supported by the National Natural Science Foundation of China
文摘Nickel liner of shaped charge with nano-sized grains was prepared by electroforming technique and the ultra-highstrain-rate deformation was performed by explosive detonation.The as-electroformed and post-deformed microstructures of electroformed nickel liner of shaped charge were observed by optical metallography(OM),scanning electron microscopy(SEM) and transmission electron microscopy(TEM) and the orientation distribution of the grains was analyzed by electron backscattering pattern(EBSP) technique.Both melting phenomenon in the jet fragment and recovery and recrystallization in the slug after ultra-high-strain-rate deformation were observed.The research evidence shows that dynamic recovery and recrystallization play an important role in ultra-high-strain-rate deformation for electroformed nickel liner of shaped charge with nano-sized grain.
文摘The constitutive model was developed to describe the relationship among flow stress,strain,strain rate,and deformation temperature completely,based on the characteristics of flow stress curves for a new kind of metastable β Ti2448 titanium alloy from isothermal hot compression tests,in a wide range of temperatures（1023-1123 K） and strain rates（63-0.001 s-1）.During this process,the adopted hyperbolic sine function based on the unified viscoplasticity theory was used to model the flow behavior of alloy undergoing flow softening caused by dynamic recovery（DRV） at high strain rates（≥1 s-1）.The standard Avrami equation was adopted to represent the softening mechanism attributed to dynamic recrystallization（DRX） at low strain rates（1 s-1）.Additionally,the material constants were determined by optimization strategy,which is a new method to solve the nonlinear constitutive equation.The stress—strain curves predicted by the developed constitutive model agree well with the experimental results,which con-rms that the developed constitutive model can give an accurate estimate of the-ow stress of Ti2448 titanium alloy and provide an effective method to model the flow behavior of metastable β titanium alloys during hot deformation.
文摘The influence of welding speed on the joint microstructures of an austenitic stainless steel(ASS)produced by friction stir welding(FSW)was investigated.The FSW process was conducted using a rotational speed of 400 r/min and welding speeds of 50 and 150 mm/min.The study was carried out using electron backscattered diffraction(EBSD)technique in different regions of the resultant stir zones(SZs).The results show that the texture of the advancing side(AS)was mainly composed of C{001}〈110〉and cube{001}〈100〉texture components along with partial B/B{112}〈110〉component.Moving from the AS toward the center and the retreating side(RS),the cube texture component disappeared and the A;/A*{111}(112)component developed and predominated the other components.Higher welding speed greatly affected and decreased the intensity of the textures in the resultant SZs.Moreover,higher welding speed(lower heat input)resulted in lower frequency of cube texture in the AS.
基金This work was financially supported by the National Program Committee (No.MKPT-01-127ZD).
文摘The hot deformation behavior of FGH96 superalloys at 1070-1170℃ and 5×10^-4-2×10^-1 s^-1 were investigated by means of the isothermal compression tests at a Gleeble-1500 thermal mechanical simulator. The results show that dynamic recovery acts as the main softening mechanism below 2×10^-3 s^-1, whereas dynamic recrystallization acts as the main softening mechanism above 2× 10^-3 s^-1 during deformation; the temperature increase caused by the deformation and the corresponding softening stress is negligible; the thermal-mechanical constitutive model to describe the hot deformation behavior is given, and the value of the apparent deformation activation energy （Qdef） is determined to be 354.93 kJ/mol.
文摘Hot compression tests were conducted on a Gleeble-1500 simulator to investigate the hot deformation behavior of BT20 Ti alloy （Ti-6Al-2Zr-IMo-1V） in the temperature range from 550 to 1000℃ at constant strain rate in the range of 0.01-1s^-1, and then the optimum spinning temperature range was determined. Moreover, tube spinning experiments were executed to verify the reasonability of the optimum temperature range. The results show that the flow stress declines gradually with increasing deformation temperature and decreasing strain rate. In α＋β phase region the dynamic recrystallization is the main softening mechanism and in β phase region the hot deformation softening is controlled by dynamic recovery. In α＋β phase region with reducing strain rate dynamic recrystallization is fully developed. The optimum temperature of hot spinning is 850-900℃ and that of warm spinning is 600-650℃. Meanwhile, at the temperature above 600℃ tubular workpieces of BT20 Ti alloy have been spun without surface cracks and microstructure inhomogeneity, which proves that the optimum spinning temperature range obtained through hot compression experiments is reasonable.
基金Project(51304171)supported by the National Natural Science Foundation of ChinaProject(E2013203248)supported by Natural Science Foundation of Hebei Province of ChinaProject(NECSR-201209)supported by Open Foundation of the National Engineering Research Center for Equipment and Technology of Cold Rolling Strip,China
文摘To realize numerical simulation of rolling and obtain the hot forming process parameters for X70 HD steel, the flow stress behaviors of X70 HD steel were investigated under different temperatures（820-1100 ℃ and strain rates（0.01-10 s-1） on a Gleeble-3500 thermo-simulation machine. A new flow stress model was established. The linear and exponential relationship methods were applied to the parameters with respect to temperature and deformation rates. The rise of curve ends under certain conditions was analyzed. The flow stress of X70 HD steel predicted by the proposed model agrees well with the experimental results. So, it greatly improves the precision of the metal thermoplastic processing through finite element method and practical application of engineering.