The austenite grain refinement through control of the grain growth during reheating process after thermomechanical controlled process （TMCP） in a vanadium microalloyed steel was achieved. The formation of ultra-fine...The austenite grain refinement through control of the grain growth during reheating process after thermomechanical controlled process （TMCP） in a vanadium microalloyed steel was achieved. The formation of ultra-fine grained austenite was attributed to the high density of austenite nucleation at the ferrite/martensite structure and to the inhibition of austenite growth by （Ti~ V）C particles at the relatively low reheating temperature. Corresponding with the precipitation behavior of （Ti,V）C with temperature, the growth behavior of austenite in the vanadium mi- croalloyed steel could be divided into two regions. At lower reheating temperature, austenite grains grew slowly, and ultra-fine grained austenite smaller than 5 ~m was successfully obtained. By contrast, the austenite grains grew rap- idly at high temperature due to the dissolution of （Ti, V）C particles. According to the measured and predicted results of austenite growth kinetics, two models were developed to describe the growth behavior of austenite grains in two different temperature regions, and the apparent activation energy Qapp for grain growth was estimated to be about 115 and 195 kJ/mol, respectively.展开更多
基金Item Sponsored by National Basic Research Program of China(2010CB630805)National Natural Science Foundation of China(51201036)China Iron and Steel Research Institute Group(12060840A)
文摘The austenite grain refinement through control of the grain growth during reheating process after thermomechanical controlled process （TMCP） in a vanadium microalloyed steel was achieved. The formation of ultra-fine grained austenite was attributed to the high density of austenite nucleation at the ferrite/martensite structure and to the inhibition of austenite growth by （Ti~ V）C particles at the relatively low reheating temperature. Corresponding with the precipitation behavior of （Ti,V）C with temperature, the growth behavior of austenite in the vanadium mi- croalloyed steel could be divided into two regions. At lower reheating temperature, austenite grains grew slowly, and ultra-fine grained austenite smaller than 5 ~m was successfully obtained. By contrast, the austenite grains grew rap- idly at high temperature due to the dissolution of （Ti, V）C particles. According to the measured and predicted results of austenite growth kinetics, two models were developed to describe the growth behavior of austenite grains in two different temperature regions, and the apparent activation energy Qapp for grain growth was estimated to be about 115 and 195 kJ/mol, respectively.