The semiconducting properties of passive films grown on 00Crl3Ni5Mo2 supermartensitic stainless steel were investigated in comparison with conventional 2Cr13 martensitic stainless steel. Cyclic vohammetry and electro-...The semiconducting properties of passive films grown on 00Crl3Ni5Mo2 supermartensitic stainless steel were investigated in comparison with conventional 2Cr13 martensitic stainless steel. Cyclic vohammetry and electro- chemical impedance spectroscopy （EIS） were used for the studies. 00Crl3NiSMo2 steel exhibited a good corrosion resistance performance, attributing to its passive capability. The results of Mott-Schottky analysis demonstrated n- type semiconductors for the passive films with doping densities of about 1020- 1021 cm -3, and the thickness of space- charge layers was also calculated. The experimental results confirmed that Mo plays an important role in improving the corrosion resistance of 00Crl3Ni5Mo2 steel due to its impact on the doping density.展开更多
基金Sponsored by Science and Technology Projects from Xi'an City of China(CX1261⑤)Fund of State Key Laboratory of Solidification Processing in NWPU of China(SKLSP201322)
文摘The semiconducting properties of passive films grown on 00Crl3Ni5Mo2 supermartensitic stainless steel were investigated in comparison with conventional 2Cr13 martensitic stainless steel. Cyclic vohammetry and electro- chemical impedance spectroscopy （EIS） were used for the studies. 00Crl3NiSMo2 steel exhibited a good corrosion resistance performance, attributing to its passive capability. The results of Mott-Schottky analysis demonstrated n- type semiconductors for the passive films with doping densities of about 1020- 1021 cm -3, and the thickness of space- charge layers was also calculated. The experimental results confirmed that Mo plays an important role in improving the corrosion resistance of 00Crl3Ni5Mo2 steel due to its impact on the doping density.