The grown conditions of Acidithiobacillus ferrooxidans and Acidithiobacillus thiooxidans were investigated,and then experiments were conducted to research the bioleaching behaviors of crude ore of copper sulfide and h...The grown conditions of Acidithiobacillus ferrooxidans and Acidithiobacillus thiooxidans were investigated,and then experiments were conducted to research the bioleaching behaviors of crude ore of copper sulfide and hand-picked concentrates of chalcopyrite by Acidithiobacillus ferrooxidans and Acidithiobacillus thiooxidans.The experimental results show that the bacteria grow best when the temperature is(30±1) °C and the pH value is 2.0.The bacteria concentration is 2.24×107 mL-1 in this condition.It is found that the copper extraction yield is affected by the inoculum size and the pulp density and the extraction yield increases as the inoculum size grows.The bioleaching rates reach their highest point in sulfide copper and chalcopyrite with a pulp density of 5% and 10%,respectively.Column flotation experiments of low-grade copper sulfide ores show that the bioleaching recovery reaches nearly 45% after 75 days.展开更多
The corrosion behavior of the acidophilic sulfur-oxidizing microorganism(ASOM)Acidithiobacillusthiooxidans(A.thiooxidans)on mortar was investigated for changes of medium and mortar,as well as for weight lossand surfac...The corrosion behavior of the acidophilic sulfur-oxidizing microorganism(ASOM)Acidithiobacillusthiooxidans(A.thiooxidans)on mortar was investigated for changes of medium and mortar,as well as for weight lossand surface morphology of mortar specimens.Weight loss analysis showed that mortar weight was reduced by(15.1±2.2)%after 56 d.Morphological surface analysis of mortar specimens showed weakly structured fibrous substances with2−100μm in size.The pH variations of the mortar surface and medium indicated that biogenic sulfuric acid had beenproduced by A.thiooxidans.The results prove that A.thiooxidans accelerated concrete corrosion and caused concretefailure.展开更多
基金Project(2012AA061501)supported by the National High-tech Research and Development Program of ChinaProject(20120162120010)supported by the Research Fund for the Doctoral Program of Higher Education of China+2 种基金Project(NCET-13-0595)supported by the program for New Century Excellent Talents in University of ChinaProject(51374248)supported by the National Natural Science Foundation of ChinaProject(2010CB630905)supported by the National Key Basic Research Program of China
文摘The grown conditions of Acidithiobacillus ferrooxidans and Acidithiobacillus thiooxidans were investigated,and then experiments were conducted to research the bioleaching behaviors of crude ore of copper sulfide and hand-picked concentrates of chalcopyrite by Acidithiobacillus ferrooxidans and Acidithiobacillus thiooxidans.The experimental results show that the bacteria grow best when the temperature is(30±1) °C and the pH value is 2.0.The bacteria concentration is 2.24×107 mL-1 in this condition.It is found that the copper extraction yield is affected by the inoculum size and the pulp density and the extraction yield increases as the inoculum size grows.The bioleaching rates reach their highest point in sulfide copper and chalcopyrite with a pulp density of 5% and 10%,respectively.Column flotation experiments of low-grade copper sulfide ores show that the bioleaching recovery reaches nearly 45% after 75 days.
基金Project(42476209)supported by the National Natural Science Foundation of ChinaProject(2023GXNSFBA026252)supported by the Youth Science Foundation of Guangxi Province,China+2 种基金Project(ZR2023MD024)supported by the Natural Science Foundation of Shandong Province,ChinaProject(JC22022104)supported by the Natural Science Foundation of Nantong,ChinaProject(2023VEA0007)supported by the Chinese Academy of Sciences President’s International Fellowship Initiative。
文摘The corrosion behavior of the acidophilic sulfur-oxidizing microorganism(ASOM)Acidithiobacillusthiooxidans(A.thiooxidans)on mortar was investigated for changes of medium and mortar,as well as for weight lossand surface morphology of mortar specimens.Weight loss analysis showed that mortar weight was reduced by(15.1±2.2)%after 56 d.Morphological surface analysis of mortar specimens showed weakly structured fibrous substances with2−100μm in size.The pH variations of the mortar surface and medium indicated that biogenic sulfuric acid had beenproduced by A.thiooxidans.The results prove that A.thiooxidans accelerated concrete corrosion and caused concretefailure.