The Al2O3 abrasion-resistant ceramics is successfully prepared by using waste aluminum sludge as the main raw material with the addition of a little clay, talc and barium carbonate. The crystal structure and microstru...The Al2O3 abrasion-resistant ceramics is successfully prepared by using waste aluminum sludge as the main raw material with the addition of a little clay, talc and barium carbonate. The crystal structure and microstructure of ceramic are characterized by means of XRD, SEM, etc., and the physical and mechanical properties are also tested. The results show that besides the phase of corundum, a little mullite, Mg-Al spinel and hyalophane phases also exist in the product. These phases are produced via reaction in-situ, which can inhibit the overgrowth of Al2O3 grain in grain boundary, and improve the integral property of the material.展开更多
The Al2O3-ZrO2（3Y）-SiC composite ceramics used in solar thermal power were prepared by micrometric Al2O3,nano-ZrO2 and SiC powders under the condition of pressureless sintering.The bulk density and bending strength ...The Al2O3-ZrO2（3Y）-SiC composite ceramics used in solar thermal power were prepared by micrometric Al2O3,nano-ZrO2 and SiC powders under the condition of pressureless sintering.The bulk density and bending strength of samples with 10vol% nano-ZrO2 sintered at 1480℃ were 3.222 g/cm3 and 160.4MPa,respectively.The bending strength of samples after 7 times thermal shock tests （quenching from 1000℃ to 25℃ in air medium） is 132.0MPa,loss rate of bending strength is only 17%.The effect of nano-ZrO2 content on the microstructure and performance of Al2O3-ZrO2（3Y）-SiC composite ceramic was investigated.The experimental results show that the bending strength of samples with above 10vol% nano-ZrO2 content has decreased,because the volume expansion resulting from t-ZrO2 to m-ZrO2 phase transformation is excessive;Adding proper nano-ZrO2 would be contributed to improve the thermal shock resistance of the composite ceramics.The Al2O3-ZrO2（3Y）-SiC composite ceramic has promising potential application in solar thermal power.展开更多
以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO ...以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO 颗粒以 2 2 3 2“晶内型”和晶界型两种形式存在。合理的配方组成及制备工艺有利于 Z r O 以四方亚稳相存在。Z r O 含量为 2 23 0 w t % 时,其四方相含量可达 6 9 %,有利于应力诱导相变增韧,该 Z T A 复相陶瓷的抗弯强度、断裂韧性分别达到 604MPa、6.87MPa·m1/2。展开更多
The thermal shock fatigue behaviors of pure hot-pressed alumina and 30 wt.% TiC/Al2O3 composites were studied. The effect of TiC and Al2O3 starting particle size on the mechanical properties of the composites was disc...The thermal shock fatigue behaviors of pure hot-pressed alumina and 30 wt.% TiC/Al2O3 composites were studied. The effect of TiC and Al2O3 starting particle size on the mechanical properties of the composites was discussed. Indentation-quench test was conducted to evaluate the effect of thermal fatigue temperature difference （ΔT） and number of thermal cycles （Ⅳ） on fatigue crack growth （Δa）. The mechanical properties and thermal fatigue resistance of TiC/Al203 composites are remarkably improved by the addition of TiC. The thermal shock fatigue of monolithic alumina and TiC/Al2O3 composites is due to a ＂true＂ cycling effect （thermal fatigue）. Crack deflection and bridging are the predominant reasons for the improvement of thermal shock fatigue resistance of the composites.展开更多
The effects of Al2O3 addition on both the sintering behavior and microwave dielectric properties of PbO-B203-SiO2 glass ceramics were investigated by Fourier transform infrared spectroscope （FTIR）, differential ther...The effects of Al2O3 addition on both the sintering behavior and microwave dielectric properties of PbO-B203-SiO2 glass ceramics were investigated by Fourier transform infrared spectroscope （FTIR）, differential thermal analysis （DTA）, X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The results show that with the increase of Al2O3 content the bands assigned to [SiO4] nearly disappear. Aluminum replaces silicon in the glass network, which is helpful for the formation of boron-oxygen rings. The increase of the transition temperature Tg and softening temperature Tf of PbO-B2O3-SiO2 glass ceramics leads to the increase of liquid phase precipitation temperature and promotes the structure stability in the glasses, and consequently contributes to the decreasing trend of crystallization. Densification and dielectric constants increase with the increase of Al2O3 content, but the dielectric loss is worsened. By contrast, the 3% （mass fraction） Al2O3-doped glass ceramics sintered at 725℃ have better properties of density p=2.72 g/cm3, dielectric constant Er=6.78, dielectric loss tan8=2.6×10^-3 （measured at 9.8 GHz）, which suggest that the glass ceramics can be applied in multilayer microwave devices requiring low sintering temperatures.展开更多
基金This project was sponsored by "863" Project (No. 2003AA322020)
文摘The Al2O3 abrasion-resistant ceramics is successfully prepared by using waste aluminum sludge as the main raw material with the addition of a little clay, talc and barium carbonate. The crystal structure and microstructure of ceramic are characterized by means of XRD, SEM, etc., and the physical and mechanical properties are also tested. The results show that besides the phase of corundum, a little mullite, Mg-Al spinel and hyalophane phases also exist in the product. These phases are produced via reaction in-situ, which can inhibit the overgrowth of Al2O3 grain in grain boundary, and improve the integral property of the material.
文摘The Al2O3-ZrO2（3Y）-SiC composite ceramics used in solar thermal power were prepared by micrometric Al2O3,nano-ZrO2 and SiC powders under the condition of pressureless sintering.The bulk density and bending strength of samples with 10vol% nano-ZrO2 sintered at 1480℃ were 3.222 g/cm3 and 160.4MPa,respectively.The bending strength of samples after 7 times thermal shock tests （quenching from 1000℃ to 25℃ in air medium） is 132.0MPa,loss rate of bending strength is only 17%.The effect of nano-ZrO2 content on the microstructure and performance of Al2O3-ZrO2（3Y）-SiC composite ceramic was investigated.The experimental results show that the bending strength of samples with above 10vol% nano-ZrO2 content has decreased,because the volume expansion resulting from t-ZrO2 to m-ZrO2 phase transformation is excessive;Adding proper nano-ZrO2 would be contributed to improve the thermal shock resistance of the composite ceramics.The Al2O3-ZrO2（3Y）-SiC composite ceramic has promising potential application in solar thermal power.
文摘以纳米ZrO 、微米Al O 为原料,采用无压烧结方式制备了ZTA 复相陶瓷。结果表明:nano-ZrO 的 2 2 3 2加入有利于制备细晶ZTA 复相陶瓷。此外,nano-ZrO 的加入对 Al O 陶瓷的显微结构也产生影响,ZrO 颗粒以 2 2 3 2“晶内型”和晶界型两种形式存在。合理的配方组成及制备工艺有利于 Z r O 以四方亚稳相存在。Z r O 含量为 2 23 0 w t % 时,其四方相含量可达 6 9 %,有利于应力诱导相变增韧,该 Z T A 复相陶瓷的抗弯强度、断裂韧性分别达到 604MPa、6.87MPa·m1/2。
文摘The thermal shock fatigue behaviors of pure hot-pressed alumina and 30 wt.% TiC/Al2O3 composites were studied. The effect of TiC and Al2O3 starting particle size on the mechanical properties of the composites was discussed. Indentation-quench test was conducted to evaluate the effect of thermal fatigue temperature difference （ΔT） and number of thermal cycles （Ⅳ） on fatigue crack growth （Δa）. The mechanical properties and thermal fatigue resistance of TiC/Al203 composites are remarkably improved by the addition of TiC. The thermal shock fatigue of monolithic alumina and TiC/Al2O3 composites is due to a ＂true＂ cycling effect （thermal fatigue）. Crack deflection and bridging are the predominant reasons for the improvement of thermal shock fatigue resistance of the composites.
基金Project(2007AA03Z0455) supported by the National High Technology Research and Development Program of ChinaProject supported by the Priority Academic Program Development of Jiangsu Higher Education Institution, China
文摘The effects of Al2O3 addition on both the sintering behavior and microwave dielectric properties of PbO-B203-SiO2 glass ceramics were investigated by Fourier transform infrared spectroscope （FTIR）, differential thermal analysis （DTA）, X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The results show that with the increase of Al2O3 content the bands assigned to [SiO4] nearly disappear. Aluminum replaces silicon in the glass network, which is helpful for the formation of boron-oxygen rings. The increase of the transition temperature Tg and softening temperature Tf of PbO-B2O3-SiO2 glass ceramics leads to the increase of liquid phase precipitation temperature and promotes the structure stability in the glasses, and consequently contributes to the decreasing trend of crystallization. Densification and dielectric constants increase with the increase of Al2O3 content, but the dielectric loss is worsened. By contrast, the 3% （mass fraction） Al2O3-doped glass ceramics sintered at 725℃ have better properties of density p=2.72 g/cm3, dielectric constant Er=6.78, dielectric loss tan8=2.6×10^-3 （measured at 9.8 GHz）, which suggest that the glass ceramics can be applied in multilayer microwave devices requiring low sintering temperatures.