Sol-gel derived bismuth cerium titanate (BCT) thin films with different Bi contents in precursor solu- tions were deposited on the Pt/Ti/SiO2/Si substrates. The effect of Bi content in the precursor solutions on the m...Sol-gel derived bismuth cerium titanate (BCT) thin films with different Bi contents in precursor solu- tions were deposited on the Pt/Ti/SiO2/Si substrates. The effect of Bi content in the precursor solutions on the microstructure and ferroelectric properties of the films was investigated. It is found that with Bi content increasing from 90% to 110% of the nominal value in the precursor solutions, the dissipation factor and leakage current density of the BCT films obtained decrease, while the grain sizes, dielectric constant and remanent polarizations (2Pr) increase, and concurrently, a Bi-deficient phase of Bi2Ti2O7 gradually disappears. The film prepared from solution with 110% of the nominal Bi content exhibits pure Bi-layered Aurivillius polycrystalline phase, and the 2Pr value and coercive field value are 67.1 μC/cm2 and 299.7 kV/cm, respectively. Their dielectric constant and the dissipation factor are about 172 and 0.033 at 1 kHz, respectively. Moreover, this film shows no polarization fatigue after 4.46×109 switching cycles.展开更多
The oxygen relief/absorption,superconduc— tivity and structure of(Bi_(1-x)Pb_x)_2Sr_2Ca_2— Cu_3O_y compounds have been studied by TGA, electrical resistance measurement and X-ray diffraction.The amount of oxygen whi...The oxygen relief/absorption,superconduc— tivity and structure of(Bi_(1-x)Pb_x)_2Sr_2Ca_2— Cu_3O_y compounds have been studied by TGA, electrical resistance measurement and X-ray diffraction.The amount of oxygen which can be re- leased and superconductivity of the compounds are correlative to Pb content.The release of oxygen in- creases when x less than 0.2 and decreases when x exceeds 0.2 with increasing x.The appropriate con- tent of Pb for superconductivity is in the range of 0.1<x<0.3,which corresponds to the relative large amount of oxygen that can be released.It is found according to electric resistance measurement that quenching is favourable to form the‘85K’phase and slow cooling the‘110K’phase.The experimen- tal results suggest that a relation exists between the superconductivity and the oxygen content in Bi sys- tem containing Pb.As the T_c of‘85K’phase de- creases and that of‘110K’phase increases with in- creasing oxygen content,it is possible that the effect of oxygen content in‘85K’phase and‘110K’ phase on the superconductivity is different.展开更多
基金Supported by the Hubei Province Natural Science Foundation (Grant No. 2007ABA309)
文摘Sol-gel derived bismuth cerium titanate (BCT) thin films with different Bi contents in precursor solu- tions were deposited on the Pt/Ti/SiO2/Si substrates. The effect of Bi content in the precursor solutions on the microstructure and ferroelectric properties of the films was investigated. It is found that with Bi content increasing from 90% to 110% of the nominal value in the precursor solutions, the dissipation factor and leakage current density of the BCT films obtained decrease, while the grain sizes, dielectric constant and remanent polarizations (2Pr) increase, and concurrently, a Bi-deficient phase of Bi2Ti2O7 gradually disappears. The film prepared from solution with 110% of the nominal Bi content exhibits pure Bi-layered Aurivillius polycrystalline phase, and the 2Pr value and coercive field value are 67.1 μC/cm2 and 299.7 kV/cm, respectively. Their dielectric constant and the dissipation factor are about 172 and 0.033 at 1 kHz, respectively. Moreover, this film shows no polarization fatigue after 4.46×109 switching cycles.
文摘The oxygen relief/absorption,superconduc— tivity and structure of(Bi_(1-x)Pb_x)_2Sr_2Ca_2— Cu_3O_y compounds have been studied by TGA, electrical resistance measurement and X-ray diffraction.The amount of oxygen which can be re- leased and superconductivity of the compounds are correlative to Pb content.The release of oxygen in- creases when x less than 0.2 and decreases when x exceeds 0.2 with increasing x.The appropriate con- tent of Pb for superconductivity is in the range of 0.1<x<0.3,which corresponds to the relative large amount of oxygen that can be released.It is found according to electric resistance measurement that quenching is favourable to form the‘85K’phase and slow cooling the‘110K’phase.The experimen- tal results suggest that a relation exists between the superconductivity and the oxygen content in Bi sys- tem containing Pb.As the T_c of‘85K’phase de- creases and that of‘110K’phase increases with in- creasing oxygen content,it is possible that the effect of oxygen content in‘85K’phase and‘110K’ phase on the superconductivity is different.