Finite element method is used to simulate the high-speed melt spinning process, based on the equation system proposed by Doufas et al. Calculation predicts a neck-like deformation, as well as the related profiles of v...Finite element method is used to simulate the high-speed melt spinning process, based on the equation system proposed by Doufas et al. Calculation predicts a neck-like deformation, as well as the related profiles of velocity, diameter, temperature, chain orientation, and crystallinity in the fiber spinning process. Considering combined effects on the process such as flow-induced crystallization, viscoelasticity, filament cooling, air drag, inertia, surface tension and gravity, the simulated material flow behaviors are consistent with those observed for semi-crystalline polymers under various spinning conditions, The structure change of polymer coils in the necking region described by the evolution of conformation tensor is also investigated. Based on the relaxation mechanism of macromolecules in flow field different types of morphology change of polymer chains before and in the neck are proposed, giving a complete prospect of structure evolution and crystallization of semi-crystalline polymer in the high speed fiber spinning process.展开更多
High modulus low shrinkage (HMLS) fibers have been prepared by using higher viscosity PET chips. The effects of the process conditions on their structure and properties have been studied by various testing techniques....High modulus low shrinkage (HMLS) fibers have been prepared by using higher viscosity PET chips. The effects of the process conditions on their structure and properties have been studied by various testing techniques. The results show that the suitable spinning speed for preparing of HMLS fibers is 2 000 ～ 2 800 m/min. With the increase of the spinning speed, the density, crystallinity, and birefringence of the initial fibers increase obviously, but the shrinkage ratio decreases rapidly. The effects of process technology on properties of the HMLS fibers have also been discussed.展开更多
Calcium alginate fibers were prepared by wet spinning of sodium alginate into a coagulating bath containing calcium chloride.The thermal degradation and flame retardancy of calcium alginate fibers were investigated wi...Calcium alginate fibers were prepared by wet spinning of sodium alginate into a coagulating bath containing calcium chloride.The thermal degradation and flame retardancy of calcium alginate fibers were investigated with thermal gravimetry(TG),X-ray diffraction(XRD),limiting oxygen index(LOI) and cone calorimeter(CONE).The results show that calcium alginate fibers are inherently flame retardant with a LOI value of 34,and the heat release rate(HRR),total heat release(THR),CO and CO_2 concentrations during com...展开更多
基金This work was financially supported by the National Natural Science Foundation of China(Nos.20204007,50390090,20490220,10590355)the Doctoral Foundation of National Education Committee of China(No.20030248008)the 863 Project of China(No.2002AA336120).
文摘Finite element method is used to simulate the high-speed melt spinning process, based on the equation system proposed by Doufas et al. Calculation predicts a neck-like deformation, as well as the related profiles of velocity, diameter, temperature, chain orientation, and crystallinity in the fiber spinning process. Considering combined effects on the process such as flow-induced crystallization, viscoelasticity, filament cooling, air drag, inertia, surface tension and gravity, the simulated material flow behaviors are consistent with those observed for semi-crystalline polymers under various spinning conditions, The structure change of polymer coils in the necking region described by the evolution of conformation tensor is also investigated. Based on the relaxation mechanism of macromolecules in flow field different types of morphology change of polymer chains before and in the neck are proposed, giving a complete prospect of structure evolution and crystallization of semi-crystalline polymer in the high speed fiber spinning process.
文摘High modulus low shrinkage (HMLS) fibers have been prepared by using higher viscosity PET chips. The effects of the process conditions on their structure and properties have been studied by various testing techniques. The results show that the suitable spinning speed for preparing of HMLS fibers is 2 000 ～ 2 800 m/min. With the increase of the spinning speed, the density, crystallinity, and birefringence of the initial fibers increase obviously, but the shrinkage ratio decreases rapidly. The effects of process technology on properties of the HMLS fibers have also been discussed.
基金supported by the Special Program for Key Basic Research of the Ministry of Science and Technology of China(No.2006CB708603)the National Natural Science Foundation of China(No.50673046)Shandong Natural Science Foundation(No.Q2008B04)
文摘Calcium alginate fibers were prepared by wet spinning of sodium alginate into a coagulating bath containing calcium chloride.The thermal degradation and flame retardancy of calcium alginate fibers were investigated with thermal gravimetry(TG),X-ray diffraction(XRD),limiting oxygen index(LOI) and cone calorimeter(CONE).The results show that calcium alginate fibers are inherently flame retardant with a LOI value of 34,and the heat release rate(HRR),total heat release(THR),CO and CO_2 concentrations during com...