Using water soluble organic compound as matrix, Carbon-coated LiMn2O4 was synthesized successfully. Co-doped LiMn2O4 was also synthesized. Physical and electrochemical performances were investigated by XRD, IR, SEM an...Using water soluble organic compound as matrix, Carbon-coated LiMn2O4 was synthesized successfully. Co-doped LiMn2O4 was also synthesized. Physical and electrochemical performances were investigated by XRD, IR, SEM and electrochemical testing. The results showed that due to a better conductivity and stabilization of Co-doped LiMn2O4, the electrochemical performances of LiMn2O4 were improved. And Carbon-coated LiMn2O4 also showed a good property because of the reduction of Mn dissolution. Comparatively speaking, Carbon-coated LiMn2O4 showed a more stable electrochemical performance.展开更多
The cathode material Li 1+ x Mn 2O 4 was prepared by a modified citric acid complexation method. The influences of temperature, sintering time and n (Li)/ n (Mn) ratio on the structure of the products have been explor...The cathode material Li 1+ x Mn 2O 4 was prepared by a modified citric acid complexation method. The influences of temperature, sintering time and n (Li)/ n (Mn) ratio on the structure of the products have been explored, characterized and tested by XRD, TEM, BET measurements. The sample sintered at 750 ℃ for 12 h had greater charge/discharge capacity, better cyclic stability under electric current charge/discharge cycle. The initial capacity reached 120 mA·h/g with the charge/discharge efficieney of 98% and maintained 115 mA·h/g after 50 cycles.展开更多
Li x Mn 2O 4 spinels were prepared by in situ redox precipitation hydrothermal synthesis method, and characterized by XRD, BET, TGA, TEM and SEM etc. , and the effects of many factors on the properties of as prepared ...Li x Mn 2O 4 spinels were prepared by in situ redox precipitation hydrothermal synthesis method, and characterized by XRD, BET, TGA, TEM and SEM etc. , and the effects of many factors on the properties of as prepared Li x Mn 2O 4 samples were investigated. The results demonstrated that Li x Mn 2O 4 spinels can be synthesized under milder conditions by in situ redox precipitation hydrothermal synthesis method. Li x Mn 2O 4 spinels are cubic and symmetrical, and have a better stability at less than 700 ℃, their surface areas and particle sizes were strongly affected by crystallization temperature and time, pH value, calcination temperature and time. The optimal conditions of Li x Mn 2O 4 synthesis were determined as follows: the alkalinity(pH value) was 9; the crystallization temperature and time were more than 240 ℃ and 48 h, respectively; the calcination temperature and time were between 700-750 ℃ and 6-12 h, respectively; the molar ratio of Li to Mn was less than 1.2/2.展开更多
The microstructure evolution of Al-Cu-Li-Mn-Zr-Ti alloy during homogenization was investigated by optical microscopy （OM）, scanning electron microscopy （SEM）, energy dispersive X-ray spectrometry （EDX）, and diff...The microstructure evolution of Al-Cu-Li-Mn-Zr-Ti alloy during homogenization was investigated by optical microscopy （OM）, scanning electron microscopy （SEM）, energy dispersive X-ray spectrometry （EDX）, and differential scanning calorimeter （DSC） methods. The results show that severe dendritic segregation exists in the experimental alloy ingot. Numerous eutectic phases can be observed in the grain boundary, and the distribution of the main elements along the interdendritic region varies periodically. The main secondary phase is Al2Cu. The overburnt temperature of the alloy is 520 °C. The second phases are gradually dissolved into the matrix, and the grain boundaries become spare and thin during homogenization with increasing temperature or prolonging holding time. Homogenization can be described by a constitutive equation in exponential function. The suitable homogenization treatment for the alloy is （510 °C, 18 h）, which agrees well with the results of homogenization kinetic analysis.展开更多
文摘Using water soluble organic compound as matrix, Carbon-coated LiMn2O4 was synthesized successfully. Co-doped LiMn2O4 was also synthesized. Physical and electrochemical performances were investigated by XRD, IR, SEM and electrochemical testing. The results showed that due to a better conductivity and stabilization of Co-doped LiMn2O4, the electrochemical performances of LiMn2O4 were improved. And Carbon-coated LiMn2O4 also showed a good property because of the reduction of Mn dissolution. Comparatively speaking, Carbon-coated LiMn2O4 showed a more stable electrochemical performance.
文摘The cathode material Li 1+ x Mn 2O 4 was prepared by a modified citric acid complexation method. The influences of temperature, sintering time and n (Li)/ n (Mn) ratio on the structure of the products have been explored, characterized and tested by XRD, TEM, BET measurements. The sample sintered at 750 ℃ for 12 h had greater charge/discharge capacity, better cyclic stability under electric current charge/discharge cycle. The initial capacity reached 120 mA·h/g with the charge/discharge efficieney of 98% and maintained 115 mA·h/g after 50 cycles.
文摘Li x Mn 2O 4 spinels were prepared by in situ redox precipitation hydrothermal synthesis method, and characterized by XRD, BET, TGA, TEM and SEM etc. , and the effects of many factors on the properties of as prepared Li x Mn 2O 4 samples were investigated. The results demonstrated that Li x Mn 2O 4 spinels can be synthesized under milder conditions by in situ redox precipitation hydrothermal synthesis method. Li x Mn 2O 4 spinels are cubic and symmetrical, and have a better stability at less than 700 ℃, their surface areas and particle sizes were strongly affected by crystallization temperature and time, pH value, calcination temperature and time. The optimal conditions of Li x Mn 2O 4 synthesis were determined as follows: the alkalinity(pH value) was 9; the crystallization temperature and time were more than 240 ℃ and 48 h, respectively; the calcination temperature and time were between 700-750 ℃ and 6-12 h, respectively; the molar ratio of Li to Mn was less than 1.2/2.
文摘The microstructure evolution of Al-Cu-Li-Mn-Zr-Ti alloy during homogenization was investigated by optical microscopy （OM）, scanning electron microscopy （SEM）, energy dispersive X-ray spectrometry （EDX）, and differential scanning calorimeter （DSC） methods. The results show that severe dendritic segregation exists in the experimental alloy ingot. Numerous eutectic phases can be observed in the grain boundary, and the distribution of the main elements along the interdendritic region varies periodically. The main secondary phase is Al2Cu. The overburnt temperature of the alloy is 520 °C. The second phases are gradually dissolved into the matrix, and the grain boundaries become spare and thin during homogenization with increasing temperature or prolonging holding time. Homogenization can be described by a constitutive equation in exponential function. The suitable homogenization treatment for the alloy is （510 °C, 18 h）, which agrees well with the results of homogenization kinetic analysis.