BaTiO 3 ceramics doped with Nd 2 O 3 (the additive content was respectively 0.001,0.002,0.003,0.005,0.01,0.03mol)were prepared by Sol-Gel method.Effects of Nd 2 O 3 contents on the dielectric constant (ε),the dielect...BaTiO 3 ceramics doped with Nd 2 O 3 (the additive content was respectively 0.001,0.002,0.003,0.005,0.01,0.03mol)were prepared by Sol-Gel method.Effects of Nd 2 O 3 contents on the dielectric constant (ε),the dielectric loss(tanδ),the Curie-temperature(T C )and the resistivity(ρ)of BaTiO 3 ceramic were studied.When Nd 2 O 3 content was 0.001mol and 0.002mol,t he dielectric constant was increase d obviously,but the dielectric loss was also increased.When Nd 2 O 3 content was 0.003mol,the dielectric constant was increased,and the die lectric loss was decreased,which was suitable fo r application in condenser.The resistivity was decreased obviously with the increasing of Nd 2 O 3 contents,the resistivity was the sm allest when Nd 2 O 3 content was 0.001mol.The Curie-temperature was also decreased with the increasing of Nd 2 O 3 contents.展开更多
文摘BaTiO 3 ceramics doped with Nd 2 O 3 (the additive content was respectively 0.001,0.002,0.003,0.005,0.01,0.03mol)were prepared by Sol-Gel method.Effects of Nd 2 O 3 contents on the dielectric constant (ε),the dielectric loss(tanδ),the Curie-temperature(T C )and the resistivity(ρ)of BaTiO 3 ceramic were studied.When Nd 2 O 3 content was 0.001mol and 0.002mol,t he dielectric constant was increase d obviously,but the dielectric loss was also increased.When Nd 2 O 3 content was 0.003mol,the dielectric constant was increased,and the die lectric loss was decreased,which was suitable fo r application in condenser.The resistivity was decreased obviously with the increasing of Nd 2 O 3 contents,the resistivity was the sm allest when Nd 2 O 3 content was 0.001mol.The Curie-temperature was also decreased with the increasing of Nd 2 O 3 contents.