The Ni-Al2O3 catalyst was prepared by the mechanochemical method in combination with a planetary ballmilling machine.Effect of milling time on the crystal structure,the reduction characteristics and the catalytic perf...The Ni-Al2O3 catalyst was prepared by the mechanochemical method in combination with a planetary ballmilling machine.Effect of milling time on the crystal structure,the reduction characteristics and the catalytic performance of Ni-Al2O3 catalyst for hydrogenation of 1,4-butynediol to produce 1,4-butenediol were investigated.The catalysts were characterized by PSD,EDX,XRD,H2-TPR,BET,TEM,and NH3-TPD methods.Results showed that the MCt2.5 catalyst treated at a ball milling time of 2.5 h could form a smallest particle size of 191.0 nm.The evaluation experiments revealed that the activity of the prepared catalyst increased at first and then reached a constant value with the extension of ballmilling time.The BYD conversion,BED selectivity and yield on the MCt2.5 catalyst reached 35.63%,33.48%and 32.46%,respectively,which were higher than those obtained by other samples.The excellent performance of MCt2.5 sample is mainly related to the following three reasons from characterization results.Firstly,it has a smallest particle size of 191.0 nm;and then,the surface acidity(in terms of strong acids)of the catalyst was weaker than other catalysts;and eventually,the loading amount(23.84%)of the active component Ni exceeded the theoretical value(20%).展开更多
The development of efficient systems for the catalytic oxidation of 2-nitro-4-methylsulfonyltoluene(NMST)to 2-nitro-4-methylsulfonyl benzoic acid(NMSBA)with atmospheric air or molecular oxygen in alkaline medium prese...The development of efficient systems for the catalytic oxidation of 2-nitro-4-methylsulfonyltoluene(NMST)to 2-nitro-4-methylsulfonyl benzoic acid(NMSBA)with atmospheric air or molecular oxygen in alkaline medium presents a significant challenge for the chemical industry.Here,we report the synthesis of FeOOH/Fe_(3)O_(4)/metal-organic framework(MOF)polygonal mesopores microflower templated from a MIL-88B(Fe)at room temperature,which exposes polygonal mesopores with atomistic edge steps and lattice defects.The obtained FeOOH/Fe_(3)O_(4)/MOF catalyst was adsorbed onto glass beads and then introduced into the microchannel reactor.In the alkaline environment,oxygen was used as oxidant to catalyze the oxidation of NMST to NMSBA,showing impressive performance.This sustainable system utilizes oxygen as a clean oxidant in an inexpensive and environmentally friendly NaOH/methanol mixture.The position and type of substituent critically affect the products.Additionally,this sustainable protocol enabled gram-scale preparation of carboxylic acid and benzyl alcohol derivatives with high chemoselectivities.Finally,the reactions can be conducted in a pressure reactor,which can conserve oxygen and prevent solvent loss.Moreover,compared with the traditional batch reactor,the self-built microchannel reactor can accelerate the reaction rate,shorten the reaction time,and enhance the selectivity of catalytic oxidation reactions.This approach contributes to environmental protection and holds potential for industrial applications.展开更多
In this study,Ag/γ-Al_(2)O_(3)catalysts were synthesized by an Ar dielectric barrier discharge plasma using silver nitrate as the Ag source andγ-alumina(γ-Al_(2)O_(3))as the support.It is revealed that plasma can r...In this study,Ag/γ-Al_(2)O_(3)catalysts were synthesized by an Ar dielectric barrier discharge plasma using silver nitrate as the Ag source andγ-alumina(γ-Al_(2)O_(3))as the support.It is revealed that plasma can reduce silver ions to generate crystalline silver nanoparticles(Ag NPs)of good dispersion and uniformity on the alumina surface,leading to the formation of Ag/γ-Al_(2)O_(3)catalysts in a green manner without traditional chemical reductants.Ag/γ-Al_(2)O_(3)exhibited good catalytic activity and stability in CO oxidation reactions,and the activity increased with increase in the Ag content.For catalysts with more than 2 wt%Ag,100%CO conversion can be achieved at 300°C.The catalytic activity of the Ag/γ-Al_(2)O_(3)catalysts is also closely related to the size of theγ-alumina,where Ag/nano-γ-Al_(2)O_(3)catalysts demonstrate better performance than Ag/micro-γ-Al_(2)O_(3)catalysts with the same Ag content.In addition,the catalytic properties of plasma-generated Ag/nano-γ-Al_(2)O_(3)(Ag/γ-Al_(2)O_(3)-P)catalysts were compared with those of Ag/nano-γ-Al_(2)O_(3)catalysts prepared by the traditional calcination approach(Ag/γ-Al_(2)O_(3)-C),with the plasma-generated samples demonstrating better overall performance.This simple,rapid and green plasma process is considered to be applicable for the synthesis of diverse noble metal-based catalysts.展开更多
This article reports the production of COx free hydrogen and carbon nanofibers by the catalytic decomposition of methane over Ni-Al2O3-SiO2 catalysts. The influence of reaction temperature, pretreatment temperature, a...This article reports the production of COx free hydrogen and carbon nanofibers by the catalytic decomposition of methane over Ni-Al2O3-SiO2 catalysts. The influence of reaction temperature, pretreatment temperature, and effect of reductive pretreatment on the decomposition of methane activity is investigated. The physico-chemical characteristics of fresh and deactivated samples were characterized using BET-SA, XRD, TPR, SEM/TEM, CHNS analyses and correlated with the methane decomposition results obtained. The Ni-Al-Si （4 ： 0.5 ： 1.5） catalyst reduced with hydrazine hydrate produced better H2 yields of ca. 1815 mol H2/mol Ni than the catalyst reduced with 5% H2/N2.展开更多
A La-modified Al2O3 catalyst was prepared with deposition-precipitation method. The effect of calcination temperature on the reactivity for vapor phase hydrofluorination of acetylene to vinyl fluoride. The catalysts c...A La-modified Al2O3 catalyst was prepared with deposition-precipitation method. The effect of calcination temperature on the reactivity for vapor phase hydrofluorination of acetylene to vinyl fluoride. The catalysts calcined at different temperatures were characterized using NH3-TPD, pyridine-FTIR, X-ray diffraction, and Raman techniques. It was found that the calcination process could not only change the structure of these catalysts but also modify the amount of surface acidity on the catalysts. The catalyst calcined at 400 ℃ exhibited the highest conversion of acetylene （94.6%） and highest selectivity to vinyl fluoride （83.4%） and lower coke deposition selectivity （0.72%）. The highest activity was related to the largest amount of surface acidity on the catalyst, and the coke deposition was also related to the total amount of surface acidic sites.展开更多
基金This work has been supported by the Xinjiang Uygur Autonomous Region Key R&D Program(2017B02012)the Xinjiang University Natural Science Foundation Project(BS160221).
文摘The Ni-Al2O3 catalyst was prepared by the mechanochemical method in combination with a planetary ballmilling machine.Effect of milling time on the crystal structure,the reduction characteristics and the catalytic performance of Ni-Al2O3 catalyst for hydrogenation of 1,4-butynediol to produce 1,4-butenediol were investigated.The catalysts were characterized by PSD,EDX,XRD,H2-TPR,BET,TEM,and NH3-TPD methods.Results showed that the MCt2.5 catalyst treated at a ball milling time of 2.5 h could form a smallest particle size of 191.0 nm.The evaluation experiments revealed that the activity of the prepared catalyst increased at first and then reached a constant value with the extension of ballmilling time.The BYD conversion,BED selectivity and yield on the MCt2.5 catalyst reached 35.63%,33.48%and 32.46%,respectively,which were higher than those obtained by other samples.The excellent performance of MCt2.5 sample is mainly related to the following three reasons from characterization results.Firstly,it has a smallest particle size of 191.0 nm;and then,the surface acidity(in terms of strong acids)of the catalyst was weaker than other catalysts;and eventually,the loading amount(23.84%)of the active component Ni exceeded the theoretical value(20%).
基金supported by the National Natural Science Foundation of China(22078251)Hubei Province Key Research and Development Program(2023DJC167)the research project of Hubei Provincial Department of Education(D20191504).
文摘The development of efficient systems for the catalytic oxidation of 2-nitro-4-methylsulfonyltoluene(NMST)to 2-nitro-4-methylsulfonyl benzoic acid(NMSBA)with atmospheric air or molecular oxygen in alkaline medium presents a significant challenge for the chemical industry.Here,we report the synthesis of FeOOH/Fe_(3)O_(4)/metal-organic framework(MOF)polygonal mesopores microflower templated from a MIL-88B(Fe)at room temperature,which exposes polygonal mesopores with atomistic edge steps and lattice defects.The obtained FeOOH/Fe_(3)O_(4)/MOF catalyst was adsorbed onto glass beads and then introduced into the microchannel reactor.In the alkaline environment,oxygen was used as oxidant to catalyze the oxidation of NMST to NMSBA,showing impressive performance.This sustainable system utilizes oxygen as a clean oxidant in an inexpensive and environmentally friendly NaOH/methanol mixture.The position and type of substituent critically affect the products.Additionally,this sustainable protocol enabled gram-scale preparation of carboxylic acid and benzyl alcohol derivatives with high chemoselectivities.Finally,the reactions can be conducted in a pressure reactor,which can conserve oxygen and prevent solvent loss.Moreover,compared with the traditional batch reactor,the self-built microchannel reactor can accelerate the reaction rate,shorten the reaction time,and enhance the selectivity of catalytic oxidation reactions.This approach contributes to environmental protection and holds potential for industrial applications.
基金financial support from National Natural Science Foundation of China(Nos.52004102 and 22078125)Postdoctoral Science Foundation of China(No.2021M690068)+2 种基金Fundamental Research Funds for the Central Universities(Nos.JUSRP221018 and JUSRP622038)Key Laboratory of Green Cleaning Technology and Detergent of Zhejiang Province(No.Q202204)Open Project of Key Laboratory of Green Chemical Engineering Process of Ministry of Education(No.GCP202112)。
文摘In this study,Ag/γ-Al_(2)O_(3)catalysts were synthesized by an Ar dielectric barrier discharge plasma using silver nitrate as the Ag source andγ-alumina(γ-Al_(2)O_(3))as the support.It is revealed that plasma can reduce silver ions to generate crystalline silver nanoparticles(Ag NPs)of good dispersion and uniformity on the alumina surface,leading to the formation of Ag/γ-Al_(2)O_(3)catalysts in a green manner without traditional chemical reductants.Ag/γ-Al_(2)O_(3)exhibited good catalytic activity and stability in CO oxidation reactions,and the activity increased with increase in the Ag content.For catalysts with more than 2 wt%Ag,100%CO conversion can be achieved at 300°C.The catalytic activity of the Ag/γ-Al_(2)O_(3)catalysts is also closely related to the size of theγ-alumina,where Ag/nano-γ-Al_(2)O_(3)catalysts demonstrate better performance than Ag/micro-γ-Al_(2)O_(3)catalysts with the same Ag content.In addition,the catalytic properties of plasma-generated Ag/nano-γ-Al_(2)O_(3)(Ag/γ-Al_(2)O_(3)-P)catalysts were compared with those of Ag/nano-γ-Al_(2)O_(3)catalysts prepared by the traditional calcination approach(Ag/γ-Al_(2)O_(3)-C),with the plasma-generated samples demonstrating better overall performance.This simple,rapid and green plasma process is considered to be applicable for the synthesis of diverse noble metal-based catalysts.
文摘This article reports the production of COx free hydrogen and carbon nanofibers by the catalytic decomposition of methane over Ni-Al2O3-SiO2 catalysts. The influence of reaction temperature, pretreatment temperature, and effect of reductive pretreatment on the decomposition of methane activity is investigated. The physico-chemical characteristics of fresh and deactivated samples were characterized using BET-SA, XRD, TPR, SEM/TEM, CHNS analyses and correlated with the methane decomposition results obtained. The Ni-Al-Si （4 ： 0.5 ： 1.5） catalyst reduced with hydrazine hydrate produced better H2 yields of ca. 1815 mol H2/mol Ni than the catalyst reduced with 5% H2/N2.
基金ACKNOWLEDGMENT This work was supported by the National Natural Science Foundation of China （No.20873125）,
文摘A La-modified Al2O3 catalyst was prepared with deposition-precipitation method. The effect of calcination temperature on the reactivity for vapor phase hydrofluorination of acetylene to vinyl fluoride. The catalysts calcined at different temperatures were characterized using NH3-TPD, pyridine-FTIR, X-ray diffraction, and Raman techniques. It was found that the calcination process could not only change the structure of these catalysts but also modify the amount of surface acidity on the catalysts. The catalyst calcined at 400 ℃ exhibited the highest conversion of acetylene （94.6%） and highest selectivity to vinyl fluoride （83.4%） and lower coke deposition selectivity （0.72%）. The highest activity was related to the largest amount of surface acidity on the catalyst, and the coke deposition was also related to the total amount of surface acidic sites.