The magnetic properties and anisotropy of amor- phous(Fe_(80)Ni_(20))_(78)Si_xB_(22-x).alloys have been investigated systematically.The maximum permeability,coercive force and remanence have been determined for as-pre...The magnetic properties and anisotropy of amor- phous(Fe_(80)Ni_(20))_(78)Si_xB_(22-x).alloys have been investigated systematically.The maximum permeability,coercive force and remanence have been determined for as-prepared and annealed samples,The results on the technical magnetic properties of this alloy system have been discussed and compared with Masumoto's.展开更多
L1_(0)-FeNi hard magnetic alloy with coercivity reaching 861 Oe was synthesized through annealing Fe_(42)Ni_(41.3)Si_8 B_(4)P_(4)Cu_(0.7)amorphous alloy,and the L1_(0)-FeNi formation mechanism has been studied.It is f...L1_(0)-FeNi hard magnetic alloy with coercivity reaching 861 Oe was synthesized through annealing Fe_(42)Ni_(41.3)Si_8 B_(4)P_(4)Cu_(0.7)amorphous alloy,and the L1_(0)-FeNi formation mechanism has been studied.It is found the L1_(0)-FeNi in annealed samples at 400℃mainly originated from the residual amorphous phase during the second stage of crystallization which could take place over 600 C lower than the measured onset temperature of the second stage with a50 C/min heating rate.Annealing at 4000 C after fully crystallization still caused a slight increase of coercivity,which was probably contributed by the limited transformation from other high temperature crystalline phases towards L1_(0)phase,or the removal of B from L1_(0)lattice and improvement of the ordering quality of L1_(0)phase due to the reduced temperature from520℃to 400℃.The first stage of crystallization has hardly direct contribution to L1_(0)-FeNi formation.Ab initio simulations show that the addition of Si or Co in L1_(0)-FeNi has the effect of enhancing the thermal stability of L1_(0)phase without seriously deteriorating its magnetic hardness.The non-monotonic feature of direction dependent coercivity in ribbon segments resulted from the combination of domain wall pinning and demagnetization effects.The approaches of synthesizing L1_(0)-FeNi magnets by adding Si or Co and decreasing the onset crystallization temperature have been discussed in detail.展开更多
Mg-based amorphous alloys exhibit efficient catalytic performance and excellent biocompatibility with a promising application probability,specifically in the field of azo dye wastewater degradation.However,the problem...Mg-based amorphous alloys exhibit efficient catalytic performance and excellent biocompatibility with a promising application probability,specifically in the field of azo dye wastewater degradation.However,the problems like difficulty in preparation and poor cycling stability need to be solved.At present,Mg-based amorphous alloys applied in wastewater degradation are available in powder and ribbon.The amorphous alloy powder fabricated by ball milling has a high specific surface area,and its reactivity is thousands of times better than that of gas atomized alloy powder.But the development is limited due to the high energy consumption,difficult and costly process of powder recycling.The single roller melt-spinning method is a new manufacturing process of amorphous alloy ribbon.Compared to amorphous powder,the specific surface area of amorphous ribbon is relatively lower,therefore,it is necessary to carry out surface modification to enhance it.Dealloying is a way that can form a pore structure on the surface of the amorphous alloys,increasing the specific surface area and providing more reactive sites,which all contribute to the catalytic performance.Exploring the optimal conditions for Mg-based amorphous alloys in wastewater degradation by adjusting amorphous alloy composition,choosing suitable method to preparation and surface modification,reducing cost,expanding the pH range will advance the steps to put Mg-based amorphous alloys in industrial environments into practice.展开更多
To date,there is still a lack of a comprehensive explanation for caged dynamics which is regarded as one of the intricate dynamic behaviors in amorphous alloys.This study focuses on Pd_(82)Si_(18)as the research objec...To date,there is still a lack of a comprehensive explanation for caged dynamics which is regarded as one of the intricate dynamic behaviors in amorphous alloys.This study focuses on Pd_(82)Si_(18)as the research object to further elucidate the underlying mechanism of caged dynamics from multiple perspectives,including the cage's lifetime,atomic local environment,and atomic potential energy.The results reveal that Si atoms exhibit a pronounced cage effect due to the hindrance of Pd atoms,resulting in an anomalous peak in the non-Gaussian parameters.An in-depth investigation was conducted on the caged dynamics differences between fast and slow Si atoms.In comparison to fast Si atoms,slow Si atoms were surrounded by more Pd atoms and occupied lower potential energy states,resulting in smaller diffusion displacements for the slow Si atoms.Concurrently,slow Si atoms tend to be in the centers of smaller clusters with coordination numbers of 9 and 10.During the isothermal relaxation process,clusters with coordination numbers 9 and 10 have longer lifetimes,suggesting that the escape of slow Si atoms from their cages is more challenging.The findings mentioned above hold significant implications for understanding the caged dynamics.展开更多
The PrMg12-type composite alloy of PrMg_(11)Ni + x wt% Ni (x=100,200) with an amorphous and nanocrystalline microstructure were synthesized through the mechanical milling.Effects of milling duration and Ni content on ...The PrMg12-type composite alloy of PrMg_(11)Ni + x wt% Ni (x=100,200) with an amorphous and nanocrystalline microstructure were synthesized through the mechanical milling.Effects of milling duration and Ni content on the microstructures and electrochemical hydrogen storage performances of the ball-milled alloys were methodically studied.The ball-milled alloys obtain the optimum discharge capacities at the first cycle.Increasing Ni content dramatically enhances the electrochemical property of alloys.Milling time varying may obviously impact the electrochemical performance of these alloys.The discharge capacities show a significant upward trend with milling duration prolonging,but milling for a longer time more than 40 h induces a slight decrease in the discharge capacity of the x=200 alloy.As milling duration increases,the cycle stability clearly lowers,while it first declines and then augments under the same condition for the x=200 alloy.The high-rate discharge abilities of the ball-milled alloys show the optimum values with milling time varying.展开更多
We describe a novel mechanism for the synthesis of a stable high-entropy alloy powder from an otherwise immiscible Mg-Ti rich metallic mixture by employing high-energy mechanical milling.The presented methodology expe...We describe a novel mechanism for the synthesis of a stable high-entropy alloy powder from an otherwise immiscible Mg-Ti rich metallic mixture by employing high-energy mechanical milling.The presented methodology expedites the synthesis of amorphous alloy powder by strategically injecting entropic disorder through the inclusion of multi-principal elements in the alloy composition.Predictions from first principles and materials theory corroborate the results from microscopic characterizations that reveal a transition of the amorphous phase from a precursor intermetallic structure.This transformation,characterized by the emergence of antisite disorder,lattice expansion,and the presence of nanograin boundaries,signifies a departure from the precursor intermetallic structure.Additionally,this phase transformation is accelerated by the presence of multiple principal elements that induce severe lattice distortion and a higher configurational entropy.The atomic size mismatch of the dissimilar elements present in the alloy produces a stable amorphous phase that resists reverting to an ordered lattice even on annealing.展开更多
Development of an electrocatalyst that is cheap and has good properties to replace conventional noble metals is important for H_(2) applications.In this study,dealloying of an amorphous Ti_(37)Cu_(60)Ru_(3) alloy was ...Development of an electrocatalyst that is cheap and has good properties to replace conventional noble metals is important for H_(2) applications.In this study,dealloying of an amorphous Ti_(37)Cu_(60)Ru_(3) alloy was performed to prepare a freestanding nanostructured hydrogen evolution reaction(HER)catalyst.The effect of dealloying and addition of Ru to TiCu alloys on the microstructure and HER properties under alkaline conditions was investigated.3 at.%Ru addition in Ti_(40)Cu_(60) decreases the overpotential to reach a current density of 10mA cm^(-2) and Tafel slope of the dealloyed samples to 35 and 34mV dec−1.The improvement of electrocatalytic properties was attributed to the formation of a nanostructure and the modification of the electronic structure of the catalyst.First-principles calculations based on density function theory indicate that Ru decreases the Gibbs free energy of water dissociation.This work presents a method to prepare an efficient electrocatalyst via dealloying of amorphous alloys.展开更多
Separated preparation of prealloys and amorphous alloys results in severe solidification-remelting and beneficial element removal-readdition contradictions,which markedly increase energy consumption and emissions.This...Separated preparation of prealloys and amorphous alloys results in severe solidification-remelting and beneficial element removal-readdition contradictions,which markedly increase energy consumption and emissions.This study offered a novel strategy for the direct production of FePC amorphous soft magnetic alloys via smelting reduction of high-phosphorus iron ore(HPIO)and apatite.First,the thermodynamic conditions and equilibrium states of the carbothermal reduction reactions in HPIO were calculated,and the element content in reduced alloys was theoretically determined.The phase and structural evolutions,as well as element migration and enrichment behaviors during the smelting reduction of HPIO and Ca_(3)(PO_(4))_(2),were then experimentally verified.The addition of Ca_(3)(PO_(4))_(2)in HPIO contributes to the enrichment of the P element in reduced alloys and the subsequent development of Fe_(3)P and Fe_(2)P phases.The content of P and C elements in the range of 1.52 wt% -14.63 wt% and 0.62 wt% -2.47 wt%,respectively,can be well tailored by adding 0-50 g Ca_(3)(PO_(4))_(2)and controlling the C/O mole ratio of 0.8-1.1,which is highly consistent with the calculated results.These FePC alloys were then successfully formed into amorphous ribbons and rods.The energy consumption of the proposed strategy was estimated to be 2.00×10^(8) kJ/t,which is reduced by 30% when compared with the conventional production process.These results are critical for the comprehensive utilization of mineral resources and pave the way for the clean production of Fe-based amorphous soft magnetic alloys.展开更多
Ni-based alloy was transient liquid phase bonded using a BNi-2 interlayer. The effect of bonding parameters on the microstructures and mechanical properties of the joints was investigated. With the increase of bonding...Ni-based alloy was transient liquid phase bonded using a BNi-2 interlayer. The effect of bonding parameters on the microstructures and mechanical properties of the joints was investigated. With the increase of bonding temperature or time, the number of Ni-rich and Cr-rich borides and the grain size of precipitation zone decrease. Higher bonding temperature or longer bonding time is beneficial to the diffusion of melting point depressant elements （B and Si） from the PZ to the base metal and atomic interdiffusion between the base metal and the joint. The chemical composition and microstructure of the joints bonded at 1170 ℃ for 24 h are comparable to the base metal. The shear test results show that both the room and elevated temperature shear-strengths of the joints increase with increasing bonding time. However, the effect of bonding time on elevated temperature tensile-shear strength is greater than on room temperature tensile-shear strength.展开更多
Reactive brazing of TiAl-based intermetallics and Ni-based alloy with Ti foil as interlayer was investigated. The interfacial microstructure and shear strength of the joints were studied. According to the experimental...Reactive brazing of TiAl-based intermetallics and Ni-based alloy with Ti foil as interlayer was investigated. The interfacial microstructure and shear strength of the joints were studied. According to the experimental observations, the molten interlayer reacts vigorously with base metals, forming several continuous reaction layers. The typical interfacial microstructure of the joint can be expressed as GH99/（Ni,Cr）ss（γ）/TiNi（β2）＋TiNi2Al（τ4）＋Ti2Ni（δ）/δ＋Ti3Al（α2）＋Al3NiTi2（τ3）/α2＋τ3/TiAl. The maximum shear strength is 258 MPa for the specimen brazed at 1000°C for 10 min. Higher brazing temperature or longer brazing time causes coarsening of the phases in the brazing seam and formation of brittle intermetallic layer, which greatly depresses the shear strength of the joints.展开更多
Based on the local canning compression,severe plastic deformation（SPD） is able to lead to the almost complete amorphous nickel-titanium shape memory alloy（NiTi SMA）,in which a small amount of retained nanocrystall...Based on the local canning compression,severe plastic deformation（SPD） is able to lead to the almost complete amorphous nickel-titanium shape memory alloy（NiTi SMA）,in which a small amount of retained nanocrystalline phase is embedded in the amorphous matrix.Crystallization of amorphous NiTi alloy annealed at 573,723 and 873 K was investigated,respectively.The crystallization kinetics of the amorphous NiTi alloy can be mathematically described by the Johnson-MehlAvrami-Kolmogorov（JMAK） equation.NiTi SMA with a complete nanocrystalline phase is obtained in the case of annealing at 573 K and 723 K,where martensite phase transformation is suppressed due to the constraint of the grain boundaries.Crystallization of amorphous NiTi alloy at 873 K leads to the coarse-grained NiTi sample,where（001） martensite compound twin is observed at room temperature.It can be found that the martensitic twins preferentially nucleate at the grain boundary and they grow up towards the two different grains.SPD based on the local canning compression and subsequent annealing provides a new approach to obtain the nanocrystalline NiTi SMA.展开更多
The Ni-based alloy composite coatings reinforced by nanostructured Al2O3-40%TiO2 multiphase ceramic particles were prepared on the surface of 7005 aluminum alloy by plasma spray technology. The microstructure and trib...The Ni-based alloy composite coatings reinforced by nanostructured Al2O3-40%TiO2 multiphase ceramic particles were prepared on the surface of 7005 aluminum alloy by plasma spray technology. The microstructure and tribological properties of the composite coatings were researched. The results show that the composite coatings mainly consist of γ-Ni, α-Al2O3, γ-Al2O3 and rutile-TiO2 etc, and exhibit lower friction coefficients and wear losses than the Ni-based alloy coatings at different loads and speeds. The composite coating bears low contact stress at 3 N and its wear mechanism is micro-cutting wear. As loads increase to 6-12 N, the contact stress is higher than the elastic limit stress of worn surface, and the wear mechanisms change into multi-plastic deformation wear, micro-brittle fracture wear and abrasive wear. With the increase of speeds, the contact temperature of worn surface increases. The composite coating experiences multi-plastic deformation wear, fatigue wear and adhesive wear.展开更多
Bulk Cu50Zr40Ti10 amorphous alloy composites reinforced with carbon nanotube （CNT） were successfully fabricated by hot pressing technique. Their density, thermal conductivity, and mechanical properties were systemic...Bulk Cu50Zr40Ti10 amorphous alloy composites reinforced with carbon nanotube （CNT） were successfully fabricated by hot pressing technique. Their density, thermal conductivity, and mechanical properties were systemically investigated. The density and the compression strength of the compacts both decrease with increasing CNT content. The thermal conductivity of the compacts decreases when the CNT content is less than 0.10% or exceeds 0.60% （mass fraction）, while increases when the CNT content is in the range of 0.1%-0.6%. The strain limit and the modulus of the compacts are obviously improved when the CNT content is less than 1.0% and then decrease significantly when the CNT content exceeds 1.00%. The optimum CNT addition is less than 0.20% at the comprehensive properties point of view.展开更多
Mg65Cu25Y10 bulk amorphous alloy specimens prepared by conventional copper mould method were heated at 200 °C for different time and the phase contents as well as microstructure were studied.The XRD results show ...Mg65Cu25Y10 bulk amorphous alloy specimens prepared by conventional copper mould method were heated at 200 °C for different time and the phase contents as well as microstructure were studied.The XRD results show that the crystallization of Mg65Cu25Y10 bulk amorphous alloy specimen becomes complete as the treating time increases and Mg2Cu,Mg24Y5 and HCP-Mg crystalline phases are found.Snowflake-like morphology is found in different specimens through SEM observation.The EDS patterns show that the composition of the snowflake-like structure is close to that of the as-cast alloy.Laminated structures are observed from the TEM images of the snowflake-like structure.From the electron diffraction patterns,it is seen that the snowflake-like structure is the combination of Mg24Y5 and amorphous matrix.The FCC-Mg phase in the matrix transforms into HCP-Mg during the heat-treating process.展开更多
Cu50Zr40Ti10 bulk amorphous alloys were fabricated by hot pressing gas-atomized Cu50Zr40Ti10 amorphous powder under different consolidation conditions without vacuum and inert gas protection. The consolidation conditi...Cu50Zr40Ti10 bulk amorphous alloys were fabricated by hot pressing gas-atomized Cu50Zr40Ti10 amorphous powder under different consolidation conditions without vacuum and inert gas protection. The consolidation conditions of the Cu50Zr40Ti10 amorphous powder were investigated based on an L9（34） orthogonal design. The compression strength and strain limit of the Cu50Zr40Ti10 bulk amorphous alloys can reach up to 1090.4 MPa and 11.9 %, respectively. The consolidation pressure significantly influences the strain limit and compression strength of the compact. But the mechanical properties are not significantly influenced by the consolidation temperature. In addition, the preforming pressure significantly influences not the compression strength but the strain limit. The optimum consolidation condition for the Cu50Zr40Ti10 amorphous powder is first precompacted under the pressure of 150 MPa, and then consolidated under the pressure of 450 MPa and the temperature of 380 °C.展开更多
In order to minimize the crystal phase in Al-Cu-Ti amorphous powder,Al65Cu35-xTix amorphous powders were optimized via ball milling through adjusting the amount of Cu and Ti elements and the ball milling time.The resu...In order to minimize the crystal phase in Al-Cu-Ti amorphous powder,Al65Cu35-xTix amorphous powders were optimized via ball milling through adjusting the amount of Cu and Ti elements and the ball milling time.The results show that increasing the mole fraction of Ti can decrease the amount of Al Cu2Ti,Cu9Al4,and Al2Cu intermetallics formed during the process of ball milling;and prolonging the ball milling time can reduce the element crystalline phase to almost none.The optimal composition is determined to be Al65Cu16.5Ti18.5.TiH2 forms in all selected Al65Cu35-xTix amorphous powders during the process of optimization.H atom is decomposed from toluene and reacts with Ti during ball milling,leading to the formation of TiH2.The volume fraction of TiH2 in Al65Cu16.5Ti18.5 amorphous powder is measured to be 4.30%.展开更多
The mean hyper fine field at the Fe nuclei in amorphous alloys Fe80-xTxB20(T=Co,Ni,Mn,V,Ti) by fitting the Moessbauer spectra is displayed. The behaviors of both the hyperfine field and the atomic magnetic moment in t...The mean hyper fine field at the Fe nuclei in amorphous alloys Fe80-xTxB20(T=Co,Ni,Mn,V,Ti) by fitting the Moessbauer spectra is displayed. The behaviors of both the hyperfine field and the atomic magnetic moment in these amorphous alloys and the relation between both the properties are discussed.展开更多
Shock wave and annealing crystallization of amorphous alloys FeSiB, FeMoSiB and FeCuNbSiB were studied by isothermal and non-isothermal DSC technique. It was found that the shock wave crystallization is very perfect, ...Shock wave and annealing crystallization of amorphous alloys FeSiB, FeMoSiB and FeCuNbSiB were studied by isothermal and non-isothermal DSC technique. It was found that the shock wave crystallization is very perfect, the fraction crystallized is very close to 100%, though the period of crystallization is very short, only about 10-4-10-6s. Their produced phases differ from the parent phase in structure and composition. The high velocity of the transformation is very difficult to explain by the diffusion theory of solid state phase transition.展开更多
A new technique of electroplating amorphous Fe-Ni-W alloy deposits was proposed.The structure and morphology o Fe-Ni-W alloy deposit were detected by XRD and SEM.The friction and wear behavior of Fe-Ni-W alloy deposit...A new technique of electroplating amorphous Fe-Ni-W alloy deposits was proposed.The structure and morphology o Fe-Ni-W alloy deposit were detected by XRD and SEM.The friction and wear behavior of Fe-Ni-W alloy deposit were studied and compared with that of chromium deposit.The corrosion properties against 5% sodium chloride,5% sulfuric acid and 5% sodium hydroxide were also discussed.The experimental results indicate that Fe-Ni-W alloy deposits have superior properties against wea than hard chromium deposits under dry sliding condition.Under oil sliding condition,except their better wear resistance,the deposits can protect their counterparts against wear.The deposits plated on brass and AISI 1045 steel show good behavior against corrosion o 5% sodium chloride,5% sulfuric acid and 5% sodium hydroxide.The bath of electroplating amorphous Fe-Ni-W alloy deposits is environmentally friendly and would find widely use in industry.展开更多
Mg86.33Ni13.67-xYx(x=0, 1, 3, 6, 10) amorphous alloys were obtained by single-roller melt-spinning technique and the effect of Y addition on the glass forming ability(GFA), crystallization and micro-hardness of Mg-Ni ...Mg86.33Ni13.67-xYx(x=0, 1, 3, 6, 10) amorphous alloys were obtained by single-roller melt-spinning technique and the effect of Y addition on the glass forming ability(GFA), crystallization and micro-hardness of Mg-Ni alloys were studied. The results show that the GFA of Mg86.33Ni13.67-xYx(x=0, 1, 3, 6, 10) is improved successfully with the Y addition. The highest GFA appeares at x=6, while the reduced glass transition temperature (Trg) is 0.5225 and the supercooled liquid region(ΔTx) is 42.06 K; the position of the main diffraction halo is different for the alloys, and the maximum of the main diffraction halo of alloys with x=0, 1, 3 corresponds to the main peaks of a metastable fcc-Mg6Ni or fcc-Mg6Ni + Ni-Y intermetallic phases, and for the alloys with x=6, 10, it corresponds to Mg-Y and Ni-Y intermetallic phases; the micro-hardness of the alloys is improved with Y additions, and the highest micro-hardness is obtained at x=6 at.%, which is 960 MPa.展开更多
文摘The magnetic properties and anisotropy of amor- phous(Fe_(80)Ni_(20))_(78)Si_xB_(22-x).alloys have been investigated systematically.The maximum permeability,coercive force and remanence have been determined for as-prepared and annealed samples,The results on the technical magnetic properties of this alloy system have been discussed and compared with Masumoto's.
基金supported by the National Natural Science Foundation of China(Grant Nos.51971179 and 51971180)the Natural Science Foundation of Chongqing,China(Grant No.cstc2019jcyj-msxmX0328)+3 种基金Shaanxi Provincial Natural Science Foundation,China(Grant No.2020JM-112)Guangdong Provincial Science and Technology Program,China(Grant No.2019B090905009)the Fundamental Research Funds for the Central Universities of China(Grant No.D5000210731)Shaanxi Provincial Key R&D Program,China(Grant No.2021KWZ-13)。
文摘L1_(0)-FeNi hard magnetic alloy with coercivity reaching 861 Oe was synthesized through annealing Fe_(42)Ni_(41.3)Si_8 B_(4)P_(4)Cu_(0.7)amorphous alloy,and the L1_(0)-FeNi formation mechanism has been studied.It is found the L1_(0)-FeNi in annealed samples at 400℃mainly originated from the residual amorphous phase during the second stage of crystallization which could take place over 600 C lower than the measured onset temperature of the second stage with a50 C/min heating rate.Annealing at 4000 C after fully crystallization still caused a slight increase of coercivity,which was probably contributed by the limited transformation from other high temperature crystalline phases towards L1_(0)phase,or the removal of B from L1_(0)lattice and improvement of the ordering quality of L1_(0)phase due to the reduced temperature from520℃to 400℃.The first stage of crystallization has hardly direct contribution to L1_(0)-FeNi formation.Ab initio simulations show that the addition of Si or Co in L1_(0)-FeNi has the effect of enhancing the thermal stability of L1_(0)phase without seriously deteriorating its magnetic hardness.The non-monotonic feature of direction dependent coercivity in ribbon segments resulted from the combination of domain wall pinning and demagnetization effects.The approaches of synthesizing L1_(0)-FeNi magnets by adding Si or Co and decreasing the onset crystallization temperature have been discussed in detail.
基金supported by the National Natural Science Foundation of China(Grant No.52071276)the Natural Science Foundation of Chongqing,China(Grant No.CSTB2022NSCQ-MSX0440)the Fundamental Research Funds for the Central Universities(Grant No.SWUXDJH202313,SWU-KQ22083).
文摘Mg-based amorphous alloys exhibit efficient catalytic performance and excellent biocompatibility with a promising application probability,specifically in the field of azo dye wastewater degradation.However,the problems like difficulty in preparation and poor cycling stability need to be solved.At present,Mg-based amorphous alloys applied in wastewater degradation are available in powder and ribbon.The amorphous alloy powder fabricated by ball milling has a high specific surface area,and its reactivity is thousands of times better than that of gas atomized alloy powder.But the development is limited due to the high energy consumption,difficult and costly process of powder recycling.The single roller melt-spinning method is a new manufacturing process of amorphous alloy ribbon.Compared to amorphous powder,the specific surface area of amorphous ribbon is relatively lower,therefore,it is necessary to carry out surface modification to enhance it.Dealloying is a way that can form a pore structure on the surface of the amorphous alloys,increasing the specific surface area and providing more reactive sites,which all contribute to the catalytic performance.Exploring the optimal conditions for Mg-based amorphous alloys in wastewater degradation by adjusting amorphous alloy composition,choosing suitable method to preparation and surface modification,reducing cost,expanding the pH range will advance the steps to put Mg-based amorphous alloys in industrial environments into practice.
基金Project supported by the National Natural Science Foundation of China (Grant No.51701071)the Natural Science Foundation of Hunan Province,China (Grant Nos.2022JJ50115 and 2021JJ30179)the Research Foundation of the Education Bureau of Hunan Province,China (Grant No.22A0522)。
文摘To date,there is still a lack of a comprehensive explanation for caged dynamics which is regarded as one of the intricate dynamic behaviors in amorphous alloys.This study focuses on Pd_(82)Si_(18)as the research object to further elucidate the underlying mechanism of caged dynamics from multiple perspectives,including the cage's lifetime,atomic local environment,and atomic potential energy.The results reveal that Si atoms exhibit a pronounced cage effect due to the hindrance of Pd atoms,resulting in an anomalous peak in the non-Gaussian parameters.An in-depth investigation was conducted on the caged dynamics differences between fast and slow Si atoms.In comparison to fast Si atoms,slow Si atoms were surrounded by more Pd atoms and occupied lower potential energy states,resulting in smaller diffusion displacements for the slow Si atoms.Concurrently,slow Si atoms tend to be in the centers of smaller clusters with coordination numbers of 9 and 10.During the isothermal relaxation process,clusters with coordination numbers 9 and 10 have longer lifetimes,suggesting that the escape of slow Si atoms from their cages is more challenging.The findings mentioned above hold significant implications for understanding the caged dynamics.
基金Funded by National Natural Science Foundation of China(Nos.51871125,51901105 and 51761032)Inner Mongolia Natural Science Foundation(No.2019BS05005)。
文摘The PrMg12-type composite alloy of PrMg_(11)Ni + x wt% Ni (x=100,200) with an amorphous and nanocrystalline microstructure were synthesized through the mechanical milling.Effects of milling duration and Ni content on the microstructures and electrochemical hydrogen storage performances of the ball-milled alloys were methodically studied.The ball-milled alloys obtain the optimum discharge capacities at the first cycle.Increasing Ni content dramatically enhances the electrochemical property of alloys.Milling time varying may obviously impact the electrochemical performance of these alloys.The discharge capacities show a significant upward trend with milling duration prolonging,but milling for a longer time more than 40 h induces a slight decrease in the discharge capacity of the x=200 alloy.As milling duration increases,the cycle stability clearly lowers,while it first declines and then augments under the same condition for the x=200 alloy.The high-rate discharge abilities of the ball-milled alloys show the optimum values with milling time varying.
基金supported in part by the National Science Foundation(NSF)award#CMMI-1944040。
文摘We describe a novel mechanism for the synthesis of a stable high-entropy alloy powder from an otherwise immiscible Mg-Ti rich metallic mixture by employing high-energy mechanical milling.The presented methodology expedites the synthesis of amorphous alloy powder by strategically injecting entropic disorder through the inclusion of multi-principal elements in the alloy composition.Predictions from first principles and materials theory corroborate the results from microscopic characterizations that reveal a transition of the amorphous phase from a precursor intermetallic structure.This transformation,characterized by the emergence of antisite disorder,lattice expansion,and the presence of nanograin boundaries,signifies a departure from the precursor intermetallic structure.Additionally,this phase transformation is accelerated by the presence of multiple principal elements that induce severe lattice distortion and a higher configurational entropy.The atomic size mismatch of the dissimilar elements present in the alloy produces a stable amorphous phase that resists reverting to an ordered lattice even on annealing.
基金National Natural Science Foundation of China,Grant/Award Number:52071217。
文摘Development of an electrocatalyst that is cheap and has good properties to replace conventional noble metals is important for H_(2) applications.In this study,dealloying of an amorphous Ti_(37)Cu_(60)Ru_(3) alloy was performed to prepare a freestanding nanostructured hydrogen evolution reaction(HER)catalyst.The effect of dealloying and addition of Ru to TiCu alloys on the microstructure and HER properties under alkaline conditions was investigated.3 at.%Ru addition in Ti_(40)Cu_(60) decreases the overpotential to reach a current density of 10mA cm^(-2) and Tafel slope of the dealloyed samples to 35 and 34mV dec−1.The improvement of electrocatalytic properties was attributed to the formation of a nanostructure and the modification of the electronic structure of the catalyst.First-principles calculations based on density function theory indicate that Ru decreases the Gibbs free energy of water dissociation.This work presents a method to prepare an efficient electrocatalyst via dealloying of amorphous alloys.
基金financially supported by the National Natural Science Foundation of China(Nos.52174217 and 52304354)the China Postdoctoral Science Foundation(No.2020M682495)。
文摘Separated preparation of prealloys and amorphous alloys results in severe solidification-remelting and beneficial element removal-readdition contradictions,which markedly increase energy consumption and emissions.This study offered a novel strategy for the direct production of FePC amorphous soft magnetic alloys via smelting reduction of high-phosphorus iron ore(HPIO)and apatite.First,the thermodynamic conditions and equilibrium states of the carbothermal reduction reactions in HPIO were calculated,and the element content in reduced alloys was theoretically determined.The phase and structural evolutions,as well as element migration and enrichment behaviors during the smelting reduction of HPIO and Ca_(3)(PO_(4))_(2),were then experimentally verified.The addition of Ca_(3)(PO_(4))_(2)in HPIO contributes to the enrichment of the P element in reduced alloys and the subsequent development of Fe_(3)P and Fe_(2)P phases.The content of P and C elements in the range of 1.52 wt% -14.63 wt% and 0.62 wt% -2.47 wt%,respectively,can be well tailored by adding 0-50 g Ca_(3)(PO_(4))_(2)and controlling the C/O mole ratio of 0.8-1.1,which is highly consistent with the calculated results.These FePC alloys were then successfully formed into amorphous ribbons and rods.The energy consumption of the proposed strategy was estimated to be 2.00×10^(8) kJ/t,which is reduced by 30% when compared with the conventional production process.These results are critical for the comprehensive utilization of mineral resources and pave the way for the clean production of Fe-based amorphous soft magnetic alloys.
基金Projects (50975062, 51105107, 51275135, 51021002) supported by the National Natural Science Foundation of ChinaProject (QC2011C044) supported by the Natural Science Foundation of Heilongjiang Province, China+1 种基金Project (20112302130005) supported by Specialized Research Fund for the Doctoral Program of Higher Education, ChinaProject (20100471027) supported by the Postdoctoral Science Foundation of China
文摘Ni-based alloy was transient liquid phase bonded using a BNi-2 interlayer. The effect of bonding parameters on the microstructures and mechanical properties of the joints was investigated. With the increase of bonding temperature or time, the number of Ni-rich and Cr-rich borides and the grain size of precipitation zone decrease. Higher bonding temperature or longer bonding time is beneficial to the diffusion of melting point depressant elements （B and Si） from the PZ to the base metal and atomic interdiffusion between the base metal and the joint. The chemical composition and microstructure of the joints bonded at 1170 ℃ for 24 h are comparable to the base metal. The shear test results show that both the room and elevated temperature shear-strengths of the joints increase with increasing bonding time. However, the effect of bonding time on elevated temperature tensile-shear strength is greater than on room temperature tensile-shear strength.
基金Projects (50975062, 51105107, 51021002) supported by the National Natural Science Foundation of ChinaProjects (QC2011C044) supported by the Natural Science Foundation of Heilongjiang Province,China+1 种基金Project (20112302130005) supported by the Specialized Research Fund for the Doctoral Program of Higher Education,ChinaProject (CUGA4130902510) supported by the China Postdoctoral Science Foundation Funded
文摘Reactive brazing of TiAl-based intermetallics and Ni-based alloy with Ti foil as interlayer was investigated. The interfacial microstructure and shear strength of the joints were studied. According to the experimental observations, the molten interlayer reacts vigorously with base metals, forming several continuous reaction layers. The typical interfacial microstructure of the joint can be expressed as GH99/（Ni,Cr）ss（γ）/TiNi（β2）＋TiNi2Al（τ4）＋Ti2Ni（δ）/δ＋Ti3Al（α2）＋Al3NiTi2（τ3）/α2＋τ3/TiAl. The maximum shear strength is 258 MPa for the specimen brazed at 1000°C for 10 min. Higher brazing temperature or longer brazing time causes coarsening of the phases in the brazing seam and formation of brittle intermetallic layer, which greatly depresses the shear strength of the joints.
基金Project (51071056) supported by the National Natural Science Foundation of ChinaProject (HEUCF201317002) supported by the Fundamental Research Funds for the Central Universities of China
文摘Based on the local canning compression,severe plastic deformation（SPD） is able to lead to the almost complete amorphous nickel-titanium shape memory alloy（NiTi SMA）,in which a small amount of retained nanocrystalline phase is embedded in the amorphous matrix.Crystallization of amorphous NiTi alloy annealed at 573,723 and 873 K was investigated,respectively.The crystallization kinetics of the amorphous NiTi alloy can be mathematically described by the Johnson-MehlAvrami-Kolmogorov（JMAK） equation.NiTi SMA with a complete nanocrystalline phase is obtained in the case of annealing at 573 K and 723 K,where martensite phase transformation is suppressed due to the constraint of the grain boundaries.Crystallization of amorphous NiTi alloy at 873 K leads to the coarse-grained NiTi sample,where（001） martensite compound twin is observed at room temperature.It can be found that the martensitic twins preferentially nucleate at the grain boundary and they grow up towards the two different grains.SPD based on the local canning compression and subsequent annealing provides a new approach to obtain the nanocrystalline NiTi SMA.
文摘The Ni-based alloy composite coatings reinforced by nanostructured Al2O3-40%TiO2 multiphase ceramic particles were prepared on the surface of 7005 aluminum alloy by plasma spray technology. The microstructure and tribological properties of the composite coatings were researched. The results show that the composite coatings mainly consist of γ-Ni, α-Al2O3, γ-Al2O3 and rutile-TiO2 etc, and exhibit lower friction coefficients and wear losses than the Ni-based alloy coatings at different loads and speeds. The composite coating bears low contact stress at 3 N and its wear mechanism is micro-cutting wear. As loads increase to 6-12 N, the contact stress is higher than the elastic limit stress of worn surface, and the wear mechanisms change into multi-plastic deformation wear, micro-brittle fracture wear and abrasive wear. With the increase of speeds, the contact temperature of worn surface increases. The composite coating experiences multi-plastic deformation wear, fatigue wear and adhesive wear.
基金Project (50874045) supported by the National Natural Science Foundation of ChinaProjects (200902472, 20080431021) supported by the China Postdoctoral Science FoundationProject (10A044) supported by the Research Foundation of Education Bureau of Hunan Province of China
文摘Bulk Cu50Zr40Ti10 amorphous alloy composites reinforced with carbon nanotube （CNT） were successfully fabricated by hot pressing technique. Their density, thermal conductivity, and mechanical properties were systemically investigated. The density and the compression strength of the compacts both decrease with increasing CNT content. The thermal conductivity of the compacts decreases when the CNT content is less than 0.10% or exceeds 0.60% （mass fraction）, while increases when the CNT content is in the range of 0.1%-0.6%. The strain limit and the modulus of the compacts are obviously improved when the CNT content is less than 1.0% and then decrease significantly when the CNT content exceeds 1.00%. The optimum CNT addition is less than 0.20% at the comprehensive properties point of view.
基金Project (2008-04) supported by the Top Talent Plan of Jiangsu University, ChinaProject (10KJA430008) supported by the Natural Science Foundation of Jiangsu Higher Education Institutions,China
文摘Mg65Cu25Y10 bulk amorphous alloy specimens prepared by conventional copper mould method were heated at 200 °C for different time and the phase contents as well as microstructure were studied.The XRD results show that the crystallization of Mg65Cu25Y10 bulk amorphous alloy specimen becomes complete as the treating time increases and Mg2Cu,Mg24Y5 and HCP-Mg crystalline phases are found.Snowflake-like morphology is found in different specimens through SEM observation.The EDS patterns show that the composition of the snowflake-like structure is close to that of the as-cast alloy.Laminated structures are observed from the TEM images of the snowflake-like structure.From the electron diffraction patterns,it is seen that the snowflake-like structure is the combination of Mg24Y5 and amorphous matrix.The FCC-Mg phase in the matrix transforms into HCP-Mg during the heat-treating process.
基金Project (50874045) supported by the National Natural Science Foundation of ChinaProjects (200902472, 20080431021) supported by the China Postdoctoral Science FoundationProject (10A044) supported by the Research Foundation of Education Bureau of Hunan Province of China
文摘Cu50Zr40Ti10 bulk amorphous alloys were fabricated by hot pressing gas-atomized Cu50Zr40Ti10 amorphous powder under different consolidation conditions without vacuum and inert gas protection. The consolidation conditions of the Cu50Zr40Ti10 amorphous powder were investigated based on an L9（34） orthogonal design. The compression strength and strain limit of the Cu50Zr40Ti10 bulk amorphous alloys can reach up to 1090.4 MPa and 11.9 %, respectively. The consolidation pressure significantly influences the strain limit and compression strength of the compact. But the mechanical properties are not significantly influenced by the consolidation temperature. In addition, the preforming pressure significantly influences not the compression strength but the strain limit. The optimum consolidation condition for the Cu50Zr40Ti10 amorphous powder is first precompacted under the pressure of 150 MPa, and then consolidated under the pressure of 450 MPa and the temperature of 380 °C.
基金Projects(51271036,51471035,51101018)supported by the National Natural Science Foundation of ChinaProject supported by the Program of"One Hundred Talented People"of the Chinese Academy of Sciences
文摘In order to minimize the crystal phase in Al-Cu-Ti amorphous powder,Al65Cu35-xTix amorphous powders were optimized via ball milling through adjusting the amount of Cu and Ti elements and the ball milling time.The results show that increasing the mole fraction of Ti can decrease the amount of Al Cu2Ti,Cu9Al4,and Al2Cu intermetallics formed during the process of ball milling;and prolonging the ball milling time can reduce the element crystalline phase to almost none.The optimal composition is determined to be Al65Cu16.5Ti18.5.TiH2 forms in all selected Al65Cu35-xTix amorphous powders during the process of optimization.H atom is decomposed from toluene and reacts with Ti during ball milling,leading to the formation of TiH2.The volume fraction of TiH2 in Al65Cu16.5Ti18.5 amorphous powder is measured to be 4.30%.
文摘The mean hyper fine field at the Fe nuclei in amorphous alloys Fe80-xTxB20(T=Co,Ni,Mn,V,Ti) by fitting the Moessbauer spectra is displayed. The behaviors of both the hyperfine field and the atomic magnetic moment in these amorphous alloys and the relation between both the properties are discussed.
文摘Shock wave and annealing crystallization of amorphous alloys FeSiB, FeMoSiB and FeCuNbSiB were studied by isothermal and non-isothermal DSC technique. It was found that the shock wave crystallization is very perfect, the fraction crystallized is very close to 100%, though the period of crystallization is very short, only about 10-4-10-6s. Their produced phases differ from the parent phase in structure and composition. The high velocity of the transformation is very difficult to explain by the diffusion theory of solid state phase transition.
基金Project(04GK1007) supported by the Science and Technology Office of Hunan Province,China
文摘A new technique of electroplating amorphous Fe-Ni-W alloy deposits was proposed.The structure and morphology o Fe-Ni-W alloy deposit were detected by XRD and SEM.The friction and wear behavior of Fe-Ni-W alloy deposit were studied and compared with that of chromium deposit.The corrosion properties against 5% sodium chloride,5% sulfuric acid and 5% sodium hydroxide were also discussed.The experimental results indicate that Fe-Ni-W alloy deposits have superior properties against wea than hard chromium deposits under dry sliding condition.Under oil sliding condition,except their better wear resistance,the deposits can protect their counterparts against wear.The deposits plated on brass and AISI 1045 steel show good behavior against corrosion o 5% sodium chloride,5% sulfuric acid and 5% sodium hydroxide.The bath of electroplating amorphous Fe-Ni-W alloy deposits is environmentally friendly and would find widely use in industry.
基金supported by the Award Fund for Outstanding Young Scientist in Shandong Province, China (No. BS2011CL004)
文摘Mg86.33Ni13.67-xYx(x=0, 1, 3, 6, 10) amorphous alloys were obtained by single-roller melt-spinning technique and the effect of Y addition on the glass forming ability(GFA), crystallization and micro-hardness of Mg-Ni alloys were studied. The results show that the GFA of Mg86.33Ni13.67-xYx(x=0, 1, 3, 6, 10) is improved successfully with the Y addition. The highest GFA appeares at x=6, while the reduced glass transition temperature (Trg) is 0.5225 and the supercooled liquid region(ΔTx) is 42.06 K; the position of the main diffraction halo is different for the alloys, and the maximum of the main diffraction halo of alloys with x=0, 1, 3 corresponds to the main peaks of a metastable fcc-Mg6Ni or fcc-Mg6Ni + Ni-Y intermetallic phases, and for the alloys with x=6, 10, it corresponds to Mg-Y and Ni-Y intermetallic phases; the micro-hardness of the alloys is improved with Y additions, and the highest micro-hardness is obtained at x=6 at.%, which is 960 MPa.