To study the anti-explosion protection effect of polyurea coating on reinforced concrete box girder,two segmental girder specimens were made at a scale of 1:3,numbered as G(without polyurea coating)and PCG(with polyur...To study the anti-explosion protection effect of polyurea coating on reinforced concrete box girder,two segmental girder specimens were made at a scale of 1:3,numbered as G(without polyurea coating)and PCG(with polyurea coating).The failure characteristics and dynamic responses of the specimens were compared through conducting explosion tests.The reliability of the numerical simulation using LS-DYNA software was verified by the test results.The effects of different scaled distances,reinforcement ratios,concrete strengths,coating thicknesses and ranges of polyurea were studied.The results show that the polyurea coating can effectively enhance the anti-explosion performance of the girder.The top plate of middle chamber in specimen G forms an elliptical penetrating hole,while that in specimen PCG only shows a very slight local dent.The peak vertical displacement and residual displacement of PCG decrease by 74.8% and 73.7%,respectively,compared with those of specimen G.For the TNT explosion with small equivalent,the polyurea coating has a more significant protective effect on reducing the size of fracture.With the increase of TNT equivalent,the protective effect of polyurea on reducing girder displacement becomes more significant.The optimal reinforcement ratio,concrete strength,thickness and range of polyurea coating were also drawn.展开更多
By using 6,6-((sulfonylbis(4,1-phenylene)bis(azanediyl))bis(thiophen-2-ylm-ethylene))bis6H-di-benzo[c,e][1,2]oxaphosphinine 6-oxide(DOPO-N)as phosphorus-nitrogen flame retardant,the polyurea(PUA)with flame retardant p...By using 6,6-((sulfonylbis(4,1-phenylene)bis(azanediyl))bis(thiophen-2-ylm-ethylene))bis6H-di-benzo[c,e][1,2]oxaphosphinine 6-oxide(DOPO-N)as phosphorus-nitrogen flame retardant,the polyurea(PUA)with flame retardant properties(PUA/DOPO-N)was prepared.In addition,organically modified montmorillonite(OMMT)and magnesium hydroxide(MH)were used as co-effectors respectively,and the flame retardant PUA(PUA/DOPO-N/OMMT and PUA/DOPO-N/MH)were also prepared.Thermal properties,flame retardant properties,flame retardant mechanism and mechanical properties of PUA/DOPO-N,PUA/DOPO-N/OMMT and PUA/DOPO-N/MH were investigated by thermogravimetric(TG)analysis,limiting oxygen index(LOI),UL 94,cone calorimeter test,scanning electron microscopy(SEM),and tensile test.The results show that the LOI value of PUA/20%DOPO-N,PUA/18%DOPO-N/2%OMMT and PUA/15%DOPO-N/5%MH are 27.1%,27.7%,and 28.3%,respectively,and UL 94 V-0 rating is attained.Compared with PUA,the peak heat release rate(pk-HRR),total heat release(THR)and average effective heat combustion(av-EHC)of PUA/20%DOPO-N,PUA/18%DOPO-N/2%OMMT and PUA/15%DOPO-N/5%MH decrease significantly.SEM results indicate that the residual chars of PUA/20%DOPO-N,PUA/18%DOPO-N/2%OMMT and PUA/15%DOPO-N/5%MH are completer and more compact.The complex of DOPO-N/OMMT and DOPO-N/MH have synergistic flame retardancy.The mechanical properties of PUA can be improved by the addition of DOPO-N,DOPO-N/OMMT and DOPO-N/MH,respectively.The insulation performance test shows that the volume resistivity of PUA/20%DOPO-N is 6.25×10^(16)Ω.cm.Furthermore,by using modified boron nitride(MBN)as heat dissipating material,the complex of PUA/MBN was prepared,and the thermal conductivity of PUA/MBN was investigated.The thermal conductivity of PUA/8%MBN complex coating at room temperature is 0.166 W/(M·K),which is a 163%improvement over pure PUA.展开更多
In recent years,explosion shock wave has been considered as a signature injury of the current military conflicts.Although strong shock wave is lethal to the human body,weak shock wave can cause many more lasting conse...In recent years,explosion shock wave has been considered as a signature injury of the current military conflicts.Although strong shock wave is lethal to the human body,weak shock wave can cause many more lasting consequences.To investigate the protection ability and characteristics of flexible materials and structures under weak shock wave loading,the blast wave produced by TNT explosive is loaded on the polyurethane foam with the density of 200.0 kg/m3(F-200)and 400.0 kg/m3(F-400),polyurea with the density of 1100.0 kg/m^(3)(P-1100)and structures composed of the two materials,which are intended for individual protection.Experimental results indicate that the shock wave is attenuated to weak pressure disturbance after interacting with the flexible materials which are not damaged.The shock wave protective capability of single-layer materials is dependent on their thickness,density and microscopic characteristics.The overpressure,maximum pressure rise rate and impulse of transmitted wave decrease exponentially with increase in sample thickness.For the same thickness,F-400 provides better protective capability than F-200 while P-1100 shows the best protective capability among the three materials.In this study,as the materials are not destroyed,F-200 with a thickness more than10.0 mm,F-400 with a thickness more than 4.0 mm,and P-1100 with a thickness more than 1.0 mm can attenuate the overpressure amplitude more than 90.0%.Further,multi-layer flexible composites are designed.Different layer layouts of designed structures and layer thickness of the single-layer materials can affect the protective performance.Within the research range,the structure in which polyurea is placed on the impact side shows the optimal shock wave protective performance,and the thicknesses of polyurea and polyurethane foam are 1.0 mm and 4.0 mm respectively.The overpressure attenuation rate reached maximum value of 93.3%and impulse attenuation capacity of this structure are better than those of single-layer polyurea and polyurethane foam with higher areal density.展开更多
[Objectives] This study was conducted to develop a polyurea elastomer which can be sprayed on the surface of expanded polystyrene (EPS) floating balls, so as to improve the surface strength and service life of the flo...[Objectives] This study was conducted to develop a polyurea elastomer which can be sprayed on the surface of expanded polystyrene (EPS) floating balls, so as to improve the surface strength and service life of the floating balls. [Methods] The effects of the types and amounts of isocyanate, chain extenders and polyether polyols on the gelation rate, adhesion and wear resistance of polyurea elastomer were investigated, and it was finally determined the preparation process of polyurea elastomer using liquid isophorone diisocyanate (IPDI) and amino-terminated polyether (D2000) as the main raw materials, dimethylthiotoluene diamine (E300) as the chain extender and silica as the wear resistance modifier through two-step solution polymerization of prepolymerization and chain extension. [Results] The physical properties and chemical resistance tests of spray polyurea elastomer showed that it had good physical properties and acid and alkali resistance, and could meet the requirements of spraying and protection of EPS floating ball surface in marine environment. [Conclusions] Polyurea elastomer coating can improve the aging resistance, wear resistance and acid and alkali resistance of EPS floating balls, and prevent them from being fragile and floating randomly to form marine floating garbage which results in "white pollution".展开更多
Fragments and blast waves generated by explosions pose a serious threat to protective structures.In this paper,the impact resistance of polyurea-coated steel plate under complex dynamic loading is analyzed and designe...Fragments and blast waves generated by explosions pose a serious threat to protective structures.In this paper,the impact resistance of polyurea-coated steel plate under complex dynamic loading is analyzed and designed for improving comprehensive ballistic and blast resistance using the newly established computational evaluating model.Firstly,according to the thickness and placement effects of the coating on the impact resistance,the steel-core sandwich plates are designed,which are proved to own outstanding comprehensive ballistic and blast resistance.Besides,the distribution diagram of ballistic and blast resistance for different polyurea-coated steel plates is given to guide the design of protective structures applying in different explosion scenarios.Furthermore,the dynamic response of designed plates under two scenarios with combined fragments and blast loading is studied.The results show that the synergistic effect of the combined loading reduces both the ballistic and blast resistance of the polyurea-coated steel plate.Besides,the acting sequence of the fragments and blast affects the structural protective performance heavily.It is found that the first loading inducing structural large deformation or damage is dominant.When fragments impact first,the excellent unit-thickness ballistic performance of the structural front part is strongly needed for improving the comprehensive ballistic and blast resistance.展开更多
Five types of polyurea elastomers were synthesized by changing the isocyanate component and the mechanical properties of polyurea materials were measured. Fiber-reinforced cement boards(FRCB)strengthened by polyurea w...Five types of polyurea elastomers were synthesized by changing the isocyanate component and the mechanical properties of polyurea materials were measured. Fiber-reinforced cement boards(FRCB)strengthened by polyurea with different formulations were processed, and a series of experiments were carried out on the specimens with gas explosion devices. The results showed that the conventional mechanical properties of different types of polyureas had their own advantages. Based on the gas explosion overpressure criterion, the blast resistances of reinforced plates were quantitatively evaluated,and the best polyurea was selected to guide the formulation design. The three typical failure modes of polyurea-reinforced FRCBs were flexural, shear, and flexural-shear failure. Dynamic thermodynamics and shock wave spectral analysis revealed that the polyurea did not undergo a glass transition in the gas explosion tests but retained its elastic properties, allowing it to effectively wrap the fragments formed by the brittle substrates.展开更多
Microcapsules with chlorpyrifos cores and polyurea walls were synthesized with 2,4-tolylene diisocyanate as an oil-soluble monomer and ethylenediamine as a water-soluble monomer via an interracial polycondensation rea...Microcapsules with chlorpyrifos cores and polyurea walls were synthesized with 2,4-tolylene diisocyanate as an oil-soluble monomer and ethylenediamine as a water-soluble monomer via an interracial polycondensation reaction. The products were characterized by means of Fourier transform infrared spectrometry, ^13C NMR spectrometry and ^31p NMR spectrometry. The morphology, the particle size and the particle size distribution, and the thermal properties were also evaluated. The prepared microcapsules exhibit clear and smooth surfaces and have a mean diameter of 28. 13 μm. These microcapsules also have a good thermal stability for long-term use, and have potential applications in minimizing the toxicity of chlorpyrifos through controlled release.展开更多
Polyurea is widely employed as a protective coating in many fields because of its superior ability to improve the anti-blast and anti-impact capability of structures.In this study,the mechanical properties of polyurea...Polyurea is widely employed as a protective coating in many fields because of its superior ability to improve the anti-blast and anti-impact capability of structures.In this study,the mechanical properties of polyurea XS-350 were investigated via systematic experimentation over a wide range of strain rates(0.001-7000 s^-1)by using an MTS,Instron VHS,and split-Hopkinson bars.The stress-strain behavior of polyurea was obtained for various strain rates,and the effects of strain rate on the primary mechanical properties were analyzed.Additionally,a modified rate-dependent constitutive model is proposed based on the nine-parameter Mooney-Rivlin model.The results show that the stress-strain curves can be divided into three distinct regions:the linear-elastic stage,the highly elastic stage,and an approximate linear region terminating in fracture.The mechanical properties of the polyurea material were found to be highly dependent on the strain rate.Furthermore,a comparison between model predictions and the experimental stress-strain curves demonstrated that the proposed model can characterize the mechanical properties of polyurea over a wide range of strain rates.展开更多
Autoclaved aerated concrete(AAC) panels have ultra-light weight,excellent thermal insulation and energy absorption,so it is an ideal building material for protective structures.To improve the blast resistance of the A...Autoclaved aerated concrete(AAC) panels have ultra-light weight,excellent thermal insulation and energy absorption,so it is an ideal building material for protective structures.To improve the blast resistance of the AAC panels,three schemes are applied to strengthen the AAC panels through spraying 4 mm thick polyurea coating from top,bottom and double-sides.In three-point bending tests,the polyurea-coated AAC panels have much higher ultimate loads than the un-coated panels,but slightly lower than those strengthened by the carbon fiber reinforced plastics(CEFRPs).Close-in explosion experiments reveal the dynamic strengthening effect of the polyurea coating.Critical scaled distances of the strengthened AAC panels are acquired,which are valuable for the engineering application of the AAC panels in the extreme loading conditions.Polyurea coatings efficiently enhance the blast resistance of the bottom and double-sided polyurea-coated AAC panels.It is interesting that the polyurea-coated AAC panels have much more excellent blast resistance than the CFRP reinforced AAC panels,although the latter have better static mechanical properties.展开更多
The present experimental study investigates shock wave mitigation capability of potentially new personal protective equipment(PPE) suspension pads made from polyurea and shear thickening fluid(STF).The shock tube test...The present experimental study investigates shock wave mitigation capability of potentially new personal protective equipment(PPE) suspension pads made from polyurea and shear thickening fluid(STF).The shock tube test results show that when placed behind Twaron fabric systems with thickness ranging from 2 mm to 18 mm, the replacement of conventional flexible foam pad with STF and STF-infused foam pads with the same thickness of 20 mm greatly reduces the normalized peak pressure(by about 72% for each pad). However, this benefit is partially offset by a large increase in the normalized impulse(by about78% for the STF pad and 131% for the STF-infused foam pad) which may cause the shock wave mitigation performance of these two pads to become less effective. Interestingly, the use of 4 mm thick polyurea pad can greatly reduce the normalized peak pressure and impulse as well(by about 74% and 49%, respectively). These results reveal that among the potentially new suspension pads tested, the polyurea pad displays the best shock wave mitigation performance. Therefore, polyurea has potential for use as a suspension pad in personal protective equipment requiring shock wave mitigation capability such as fabric ballistic vests, bomb suits and combat helmets.展开更多
This paper gives a brief report of the preparation of hexadecane microcapsule with polyurea-melamine formaldehyde resin shell materials(HMPM).The sealing performance and thermal stability of HMPM was enhanced much mor...This paper gives a brief report of the preparation of hexadecane microcapsule with polyurea-melamine formaldehyde resin shell materials(HMPM).The sealing performance and thermal stability of HMPM was enhanced much more effectively than that of microcapsule with polyurea shell material(HPM).The results of microscopical imaging analysis system,DSC,TG,and laser particle analyzer were briefly introduced.展开更多
Polyurea is an elastomeric material that can be applied to enhance the protection ability of structures under blast and impact loading.In order to study the compressive mechanical properties of SiC/polyurea nanocompos...Polyurea is an elastomeric material that can be applied to enhance the protection ability of structures under blast and impact loading.In order to study the compressive mechanical properties of SiC/polyurea nanocomposites under quasi-static and dynamic loading,a universal testing machine and split Hopkinson pressure bar(SHPB)apparatus were used respectively.The stress-strain curves were obtained on polyurea and its composites at strain rates of 0.001e8000 s1.The results of the experiment suggested that increase in the strain rates led to the rise of the flow stress,compressive strength,strain rate sensitivity and strain energy.This indicates that all of the presented materials were dependent on strain rate.Moreover,these mechanical characters were enhanced by incorporating a small amount of SiC into polyurea matrix.The relation between yield stress and strain rates were established using the power law functions.Finally,in order to investigate the fracture surfaces and inside information of failed specimens,scanning electron microscopy(SEM)and micro X-ray computed tomography(micro-CT)were used respectively.Multiple voids,crazes,micro-cracks and cracking were observed in fracture surfaces.On the other hand,the cracking propagation was found in the micro-CT slice images.It is essential to understand the deformation and failure mechanisms in all the polyurea materials.展开更多
Nowadays, the mitigation of damage to a ship caused by the underwater explosion attracts more and more attention from the modern ship designers. In this study, two kinds of scale tests were conducted to investigate th...Nowadays, the mitigation of damage to a ship caused by the underwater explosion attracts more and more attention from the modern ship designers. In this study, two kinds of scale tests were conducted to investigate the effects of polyurea coatings on the blast resistance of hulls subjected to underwater explosion. Firstly, small-scale model tests with different polyurea coatings were carried out. Results indicate that polyurea has a better blast resistance performance when coated on the front face, which can effectively reduce the maximum deflection of the steel plate by more than 20% and reduce the deformation energy by 35.7%-45.4%. Next, a full-scale ship(approximately 50 m × 9 m) under loadings produced by the detonation of 33 kg of spherical TNT charges was tested, where a part of the ship was coated with polyurea on the front face(8 mm + 24 mm) and not on the contrast area. Damage characteristics on the bottom were statistically analyzed based on a 3D scanning technology, indicating that polyurea contributes to enhancing the blast protection of the ship. However, damage results of this test were different from those of the small-scale tests. Moreover, the deformation area of the bottom with polyurea was greatly increased by 40.1% to disperse explosion energy, a conclusion that cannot be drown from the small-scale tests.展开更多
In this study,the anti-penetration performance of polyurea/ASTM1405-steel composite plate subjected to high velocity projectile was analyzed.Two kinds of modified polyurea material(AMMT-053 and AMMT-055)were selected ...In this study,the anti-penetration performance of polyurea/ASTM1405-steel composite plate subjected to high velocity projectile was analyzed.Two kinds of modified polyurea material(AMMT-053 and AMMT-055)were selected and a ballistic impact testing system including speed measuring target system and high-speed camera was designed.This experiment was conducted with a rifle and 5.8 mm projectile to explore the effects by the polyurea coating thickness,the polyurea coating position and the glass-fiber cloth on the anti-penetration performance of polyurea/ASTM1405-steel composite plate.The result showed that the effects of polyurea coating position were different between two types of polyurea,and that the effects of glass-fiber position were disparate between two types of polyurea as well.For AMMT-053 polyurea material,it was better to be on front face than on rear face;whereas for AMMT-055 polyurea,it was better to be on rear surface although the difference was very subtle.Additionally,formulas had been given to describe the relationship between the effectiveness of polyurea and the thickness of polyurea coating.In general,AMMT-055 had better anti-penetration performance than AMMT-053.Furthermore,five typical damage modes including self-healing,crack,local bulge,spallation and local fragmentation were defined and the failure mechanism was analyzed with the results of SHPB test.Additionally,the bonding strength played an important role in the anti-penetration performance of polyurea/steel composite plate.展开更多
A series of novel polysiloxane polyurea-urethane blockcopolymers based on methylene bis(p-phenylisocyanate (MDI), sodium-s-1,2-dihydroxy propyl sulphonate (SDPS) and aminopropyl-terminated polydimethylsiloxane (ATPS) ...A series of novel polysiloxane polyurea-urethane blockcopolymers based on methylene bis(p-phenylisocyanate (MDI), sodium-s-1,2-dihydroxy propyl sulphonate (SDPS) and aminopropyl-terminated polydimethylsiloxane (ATPS) was synthesized with varying length of soft segments and neutralizing cation. The effect of the chemical composition and the cation on the morphology and mechanical properties of the samples were studied. It was found that the SDPS chain extender based samples have definite chemical structure (-MDI-SDPS-MDI-ATPS-). As the length of the soft segment increases, an improvement of phase separation was observed. In addition, when SO3Na was translated into SO3H or the sulphonic acid groups were neutralized with different charge cations (Na+, Zn2+ and Al3+), the morphology and mechanical properties changed greatly.展开更多
Clay brick masonry unit(CBMU) walls are widely used in building structures,and its damage and protection under explosion loads have been a matter of concern in the field of engineering protection.In this paper,a serie...Clay brick masonry unit(CBMU) walls are widely used in building structures,and its damage and protection under explosion loads have been a matter of concern in the field of engineering protection.In this paper,a series of full-scale experiments of the response characteristics of 24 cm CMBU walls unreinforced and reinforced with polyurea elastomer subjected to blast loading were carried out.Through setting 5.0 kg TNT charges at different stand-off distances,the damage characteristics of masonry walls at different scaled distances were obtained.The reinforcement effect of different polyurea coating thicknesses and methods on the blast resistance performance of masonry walls under single and repeated loads were also explored.Five failure grades were summarized according to the dynamic response features of masonry walls.Based on the stress wave propagation pattern in multi-media composite structures,the internal stress distribution of masonry walls were analyzed,and the division basis of the masonry walls’ failure grades was then quantified.Combined with Scanning Electron Microscope(SEM)images,the deformation characteristics of soft and hard segments of polyurea and effects of detonation products on microstructures were revealed respectively,which provides an important reference for the design and application of polyurea in the blast resistance of clay brick masonry walls.展开更多
Activation and transformation of CO_2 is one of the important issues in the field of green and sustainable chemistry. Herein, CO_2 as a carbonoxygen resource was converted to CO_2-polyurea with 1,6-hexanediamine throu...Activation and transformation of CO_2 is one of the important issues in the field of green and sustainable chemistry. Herein, CO_2 as a carbonoxygen resource was converted to CO_2-polyurea with 1,6-hexanediamine through a two-step polymerization. The reaction parameters such as temperature, pressure and reaction time were examined; and several kinds of catalysts were screened in the absence and presence of NMP solvent. The formed oligomer and the final polyurea were characterized by FT-IR, VT-DRIFTS, NMR, XRD, AFM and their thermal properties were examined by TGA and DSC. It was confirmed that the final polyurea has a high thermal stability; the melting temperature is 269℃ and the decomposition temperature is above 300℃. It is a brittle polymer with a tensile strength of 18.35 MPa at break length of 1.64%. The polyurea has a stronger solvent resistance due to the ordered hydrogen bond in structure. The average molecular weight should be enhanced in the postpolymerization as the appearance, hydrogen bond intensity, crystallinity, melting point and the thermal stability changed largely compared to the oligomer. The present work provides a new kind of polyurea, it is expected to have a wide application in the field of polymer materials.展开更多
Polyurea coating and carbon fibre reinforced polymer reinforcing techniques were applied to retrofit a severely damaged urban utility tunnel(UUT).The blast responses of the retrofitted UUT were investigated through in...Polyurea coating and carbon fibre reinforced polymer reinforcing techniques were applied to retrofit a severely damaged urban utility tunnel(UUT).The blast responses of the retrofitted UUT were investigated through in-filed explosion experimental tests,and the displacements,strains,accelerations,and damage were compared.The retrofitted UUT exhibited comparable or even better blast resistance than the intact UUT.Although the polyurea coating was flexible,it exhibited excellent performance in improving the blast resistance of the damaged UUT.As the UUT reinforced with basalt fibre reinforce polymer(BFRP)bars has smaller damage compared with the UUT reinforced with steel bars,its retrofitting is simple,and the cost is low.The roof was simplified as an elastically simple support one-way slab.Euler beam theory was adopted to analyse the dynamic responses of UUT roof considering the interaction between soil and structure,which agree well with the experiments in the first three cases.展开更多
An essential oil is the volatile lipophilic component extracted from plants. Microencapsulation systems protect the essential oil from degradation and evaporation, and, at the same time, allow a sustained release. Thi...An essential oil is the volatile lipophilic component extracted from plants. Microencapsulation systems protect the essential oil from degradation and evaporation, and, at the same time, allow a sustained release. This work analyses and characterizes the oregano and sage essential oil microcapsules prepared by interfacial polymerization technique, using polyurea as wall material. Several instrumental techniques are used: optical microscopy, size particle, Fourier transform infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), Termo gravimetric analysis (TGA), spectrophotometry, antimicrobial test and chromatography. Results show that oregano and sage oil have antimicrobial properties, and their microencapsulation allows knowing that these properties remain inside the microcapsules.展开更多
The use of CO_(2) as monomer to synthesize polymer materials is an important and potential applications topic from the viewpoint of green and sustainable chemistry.A new kind of CO_(2)-based polyurea(PUa)was synthesiz...The use of CO_(2) as monomer to synthesize polymer materials is an important and potential applications topic from the viewpoint of green and sustainable chemistry.A new kind of CO_(2)-based polyurea(PUa)was synthesized by polycondensation of CO_(2) with 4,7,10-trioxa-1,13-tridecanediamine and tris(2-aminoethyl)amine(TAEA).TAEA was used as cross-link reagent.The mechanical properties of PUa were significantly improved by inserted the crosslink agent of TAEA.The formed slight cross-linked PUa exhibited excellent mechanical properties with tensile strength of 26.8 MPa,elongation at break of 34%and Young’s modulus of 351 MPa.Moreover,it could be remolded for 3 times without obvious change in the mechanical properties,which are ascribed to the hydrogen bonding interaction among the main chains and the slight cross-linked structure.In addition,the synthesized CO_(2)-based PUa is of outstanding thermal performance with an initial decomposition temperature above 300℃,besides it is tolerance for a variety of organic solvents.展开更多
基金the Natural Science Foundation of Jiangsu Province(Grant No.BK20200494)China Postdoctoral Science Foundation(Grant No.2021M701725)+3 种基金Jiangsu Postdoctoral Research Funding Program(Grant No.2021K522C)Fundamental Research Funds for the Central Universities(Grant No.30919011246)National Natural Science Foundation of China(Grant No.52278188)Natural Science Foundation of Jiangsu Province(Grant No.BK20211196)。
文摘To study the anti-explosion protection effect of polyurea coating on reinforced concrete box girder,two segmental girder specimens were made at a scale of 1:3,numbered as G(without polyurea coating)and PCG(with polyurea coating).The failure characteristics and dynamic responses of the specimens were compared through conducting explosion tests.The reliability of the numerical simulation using LS-DYNA software was verified by the test results.The effects of different scaled distances,reinforcement ratios,concrete strengths,coating thicknesses and ranges of polyurea were studied.The results show that the polyurea coating can effectively enhance the anti-explosion performance of the girder.The top plate of middle chamber in specimen G forms an elliptical penetrating hole,while that in specimen PCG only shows a very slight local dent.The peak vertical displacement and residual displacement of PCG decrease by 74.8% and 73.7%,respectively,compared with those of specimen G.For the TNT explosion with small equivalent,the polyurea coating has a more significant protective effect on reducing the size of fracture.With the increase of TNT equivalent,the protective effect of polyurea on reducing girder displacement becomes more significant.The optimal reinforcement ratio,concrete strength,thickness and range of polyurea coating were also drawn.
基金Funded by the Natural Science Foundation of Guangdong(Nos.2014A030313241,2014B090901068,and 2016A010103003)。
文摘By using 6,6-((sulfonylbis(4,1-phenylene)bis(azanediyl))bis(thiophen-2-ylm-ethylene))bis6H-di-benzo[c,e][1,2]oxaphosphinine 6-oxide(DOPO-N)as phosphorus-nitrogen flame retardant,the polyurea(PUA)with flame retardant properties(PUA/DOPO-N)was prepared.In addition,organically modified montmorillonite(OMMT)and magnesium hydroxide(MH)were used as co-effectors respectively,and the flame retardant PUA(PUA/DOPO-N/OMMT and PUA/DOPO-N/MH)were also prepared.Thermal properties,flame retardant properties,flame retardant mechanism and mechanical properties of PUA/DOPO-N,PUA/DOPO-N/OMMT and PUA/DOPO-N/MH were investigated by thermogravimetric(TG)analysis,limiting oxygen index(LOI),UL 94,cone calorimeter test,scanning electron microscopy(SEM),and tensile test.The results show that the LOI value of PUA/20%DOPO-N,PUA/18%DOPO-N/2%OMMT and PUA/15%DOPO-N/5%MH are 27.1%,27.7%,and 28.3%,respectively,and UL 94 V-0 rating is attained.Compared with PUA,the peak heat release rate(pk-HRR),total heat release(THR)and average effective heat combustion(av-EHC)of PUA/20%DOPO-N,PUA/18%DOPO-N/2%OMMT and PUA/15%DOPO-N/5%MH decrease significantly.SEM results indicate that the residual chars of PUA/20%DOPO-N,PUA/18%DOPO-N/2%OMMT and PUA/15%DOPO-N/5%MH are completer and more compact.The complex of DOPO-N/OMMT and DOPO-N/MH have synergistic flame retardancy.The mechanical properties of PUA can be improved by the addition of DOPO-N,DOPO-N/OMMT and DOPO-N/MH,respectively.The insulation performance test shows that the volume resistivity of PUA/20%DOPO-N is 6.25×10^(16)Ω.cm.Furthermore,by using modified boron nitride(MBN)as heat dissipating material,the complex of PUA/MBN was prepared,and the thermal conductivity of PUA/MBN was investigated.The thermal conductivity of PUA/8%MBN complex coating at room temperature is 0.166 W/(M·K),which is a 163%improvement over pure PUA.
基金supported by the National Natural Science Foundation of China(Grant Nos.12221002,12102233)。
文摘In recent years,explosion shock wave has been considered as a signature injury of the current military conflicts.Although strong shock wave is lethal to the human body,weak shock wave can cause many more lasting consequences.To investigate the protection ability and characteristics of flexible materials and structures under weak shock wave loading,the blast wave produced by TNT explosive is loaded on the polyurethane foam with the density of 200.0 kg/m3(F-200)and 400.0 kg/m3(F-400),polyurea with the density of 1100.0 kg/m^(3)(P-1100)and structures composed of the two materials,which are intended for individual protection.Experimental results indicate that the shock wave is attenuated to weak pressure disturbance after interacting with the flexible materials which are not damaged.The shock wave protective capability of single-layer materials is dependent on their thickness,density and microscopic characteristics.The overpressure,maximum pressure rise rate and impulse of transmitted wave decrease exponentially with increase in sample thickness.For the same thickness,F-400 provides better protective capability than F-200 while P-1100 shows the best protective capability among the three materials.In this study,as the materials are not destroyed,F-200 with a thickness more than10.0 mm,F-400 with a thickness more than 4.0 mm,and P-1100 with a thickness more than 1.0 mm can attenuate the overpressure amplitude more than 90.0%.Further,multi-layer flexible composites are designed.Different layer layouts of designed structures and layer thickness of the single-layer materials can affect the protective performance.Within the research range,the structure in which polyurea is placed on the impact side shows the optimal shock wave protective performance,and the thicknesses of polyurea and polyurethane foam are 1.0 mm and 4.0 mm respectively.The overpressure attenuation rate reached maximum value of 93.3%and impulse attenuation capacity of this structure are better than those of single-layer polyurea and polyurethane foam with higher areal density.
基金Supported by Special Project for High-quality Development of Marine Services and Fishery in Fujian Province in 2023(FJHY-YYKJ-2023-1-3)。
文摘[Objectives] This study was conducted to develop a polyurea elastomer which can be sprayed on the surface of expanded polystyrene (EPS) floating balls, so as to improve the surface strength and service life of the floating balls. [Methods] The effects of the types and amounts of isocyanate, chain extenders and polyether polyols on the gelation rate, adhesion and wear resistance of polyurea elastomer were investigated, and it was finally determined the preparation process of polyurea elastomer using liquid isophorone diisocyanate (IPDI) and amino-terminated polyether (D2000) as the main raw materials, dimethylthiotoluene diamine (E300) as the chain extender and silica as the wear resistance modifier through two-step solution polymerization of prepolymerization and chain extension. [Results] The physical properties and chemical resistance tests of spray polyurea elastomer showed that it had good physical properties and acid and alkali resistance, and could meet the requirements of spraying and protection of EPS floating ball surface in marine environment. [Conclusions] Polyurea elastomer coating can improve the aging resistance, wear resistance and acid and alkali resistance of EPS floating balls, and prevent them from being fragile and floating randomly to form marine floating garbage which results in "white pollution".
基金supported by the Science Challenge Project, No. TZ2018002National Natural Science Foundation of China, under Grant No. 11972205, 11972210 and 11921002the National Key Research Development Program of China (No. 2017YFB0702003)
文摘Fragments and blast waves generated by explosions pose a serious threat to protective structures.In this paper,the impact resistance of polyurea-coated steel plate under complex dynamic loading is analyzed and designed for improving comprehensive ballistic and blast resistance using the newly established computational evaluating model.Firstly,according to the thickness and placement effects of the coating on the impact resistance,the steel-core sandwich plates are designed,which are proved to own outstanding comprehensive ballistic and blast resistance.Besides,the distribution diagram of ballistic and blast resistance for different polyurea-coated steel plates is given to guide the design of protective structures applying in different explosion scenarios.Furthermore,the dynamic response of designed plates under two scenarios with combined fragments and blast loading is studied.The results show that the synergistic effect of the combined loading reduces both the ballistic and blast resistance of the polyurea-coated steel plate.Besides,the acting sequence of the fragments and blast affects the structural protective performance heavily.It is found that the first loading inducing structural large deformation or damage is dominant.When fragments impact first,the excellent unit-thickness ballistic performance of the structural front part is strongly needed for improving the comprehensive ballistic and blast resistance.
基金funded by National Natural Science Foundation of China(No.12002392).
文摘Five types of polyurea elastomers were synthesized by changing the isocyanate component and the mechanical properties of polyurea materials were measured. Fiber-reinforced cement boards(FRCB)strengthened by polyurea with different formulations were processed, and a series of experiments were carried out on the specimens with gas explosion devices. The results showed that the conventional mechanical properties of different types of polyureas had their own advantages. Based on the gas explosion overpressure criterion, the blast resistances of reinforced plates were quantitatively evaluated,and the best polyurea was selected to guide the formulation design. The three typical failure modes of polyurea-reinforced FRCBs were flexural, shear, and flexural-shear failure. Dynamic thermodynamics and shock wave spectral analysis revealed that the polyurea did not undergo a glass transition in the gas explosion tests but retained its elastic properties, allowing it to effectively wrap the fragments formed by the brittle substrates.
文摘Microcapsules with chlorpyrifos cores and polyurea walls were synthesized with 2,4-tolylene diisocyanate as an oil-soluble monomer and ethylenediamine as a water-soluble monomer via an interracial polycondensation reaction. The products were characterized by means of Fourier transform infrared spectrometry, ^13C NMR spectrometry and ^31p NMR spectrometry. The morphology, the particle size and the particle size distribution, and the thermal properties were also evaluated. The prepared microcapsules exhibit clear and smooth surfaces and have a mean diameter of 28. 13 μm. These microcapsules also have a good thermal stability for long-term use, and have potential applications in minimizing the toxicity of chlorpyrifos through controlled release.
基金the Provincial Basic Research Program of China(NO.2016209A003,NO·2016602B003)
文摘Polyurea is widely employed as a protective coating in many fields because of its superior ability to improve the anti-blast and anti-impact capability of structures.In this study,the mechanical properties of polyurea XS-350 were investigated via systematic experimentation over a wide range of strain rates(0.001-7000 s^-1)by using an MTS,Instron VHS,and split-Hopkinson bars.The stress-strain behavior of polyurea was obtained for various strain rates,and the effects of strain rate on the primary mechanical properties were analyzed.Additionally,a modified rate-dependent constitutive model is proposed based on the nine-parameter Mooney-Rivlin model.The results show that the stress-strain curves can be divided into three distinct regions:the linear-elastic stage,the highly elastic stage,and an approximate linear region terminating in fracture.The mechanical properties of the polyurea material were found to be highly dependent on the strain rate.Furthermore,a comparison between model predictions and the experimental stress-strain curves demonstrated that the proposed model can characterize the mechanical properties of polyurea over a wide range of strain rates.
基金Supports from the National Natural Science Foundation of China(11672130,51508567,51478465,and 51308544)the State Key Laboratory of Mechanics and Control of Mechanical Structures(MCMS-0217G03)the State Key Laboratory for Disaster Reduction in Civil Engineering(SLDRCE16-01)。
文摘Autoclaved aerated concrete(AAC) panels have ultra-light weight,excellent thermal insulation and energy absorption,so it is an ideal building material for protective structures.To improve the blast resistance of the AAC panels,three schemes are applied to strengthen the AAC panels through spraying 4 mm thick polyurea coating from top,bottom and double-sides.In three-point bending tests,the polyurea-coated AAC panels have much higher ultimate loads than the un-coated panels,but slightly lower than those strengthened by the carbon fiber reinforced plastics(CEFRPs).Close-in explosion experiments reveal the dynamic strengthening effect of the polyurea coating.Critical scaled distances of the strengthened AAC panels are acquired,which are valuable for the engineering application of the AAC panels in the extreme loading conditions.Polyurea coatings efficiently enhance the blast resistance of the bottom and double-sided polyurea-coated AAC panels.It is interesting that the polyurea-coated AAC panels have much more excellent blast resistance than the CFRP reinforced AAC panels,although the latter have better static mechanical properties.
基金supported by the Ministry of Education,Singapore(R265000533112)
文摘The present experimental study investigates shock wave mitigation capability of potentially new personal protective equipment(PPE) suspension pads made from polyurea and shear thickening fluid(STF).The shock tube test results show that when placed behind Twaron fabric systems with thickness ranging from 2 mm to 18 mm, the replacement of conventional flexible foam pad with STF and STF-infused foam pads with the same thickness of 20 mm greatly reduces the normalized peak pressure(by about 72% for each pad). However, this benefit is partially offset by a large increase in the normalized impulse(by about78% for the STF pad and 131% for the STF-infused foam pad) which may cause the shock wave mitigation performance of these two pads to become less effective. Interestingly, the use of 4 mm thick polyurea pad can greatly reduce the normalized peak pressure and impulse as well(by about 74% and 49%, respectively). These results reveal that among the potentially new suspension pads tested, the polyurea pad displays the best shock wave mitigation performance. Therefore, polyurea has potential for use as a suspension pad in personal protective equipment requiring shock wave mitigation capability such as fabric ballistic vests, bomb suits and combat helmets.
基金the financial support from the National Basic Research Program of China(No. 2009CB623200)the National Natural Science Foundation of China(No.50539040)the Scientific Research Foundation of Graduate School of Southeast University(No.YBJJ 0725).
文摘This paper gives a brief report of the preparation of hexadecane microcapsule with polyurea-melamine formaldehyde resin shell materials(HMPM).The sealing performance and thermal stability of HMPM was enhanced much more effectively than that of microcapsule with polyurea shell material(HPM).The results of microscopical imaging analysis system,DSC,TG,and laser particle analyzer were briefly introduced.
基金The authors would like to thank the State Administration of Science,Technology and Industry for National Defense of China(Grant No.WDZCKYXM20190503)Xi’an Modern Chemistry Institute for the financial support.Beijing Institute of Technology and Northwestern Polytechnical University are thanked for providing experimental equipments for this work.
文摘Polyurea is an elastomeric material that can be applied to enhance the protection ability of structures under blast and impact loading.In order to study the compressive mechanical properties of SiC/polyurea nanocomposites under quasi-static and dynamic loading,a universal testing machine and split Hopkinson pressure bar(SHPB)apparatus were used respectively.The stress-strain curves were obtained on polyurea and its composites at strain rates of 0.001e8000 s1.The results of the experiment suggested that increase in the strain rates led to the rise of the flow stress,compressive strength,strain rate sensitivity and strain energy.This indicates that all of the presented materials were dependent on strain rate.Moreover,these mechanical characters were enhanced by incorporating a small amount of SiC into polyurea matrix.The relation between yield stress and strain rates were established using the power law functions.Finally,in order to investigate the fracture surfaces and inside information of failed specimens,scanning electron microscopy(SEM)and micro X-ray computed tomography(micro-CT)were used respectively.Multiple voids,crazes,micro-cracks and cracking were observed in fracture surfaces.On the other hand,the cracking propagation was found in the micro-CT slice images.It is essential to understand the deformation and failure mechanisms in all the polyurea materials.
基金the project of State Key Laboratory of Explosion Science and Technology(Beijing Institute of Technology).The project number is NO.QNKT19-04.
文摘Nowadays, the mitigation of damage to a ship caused by the underwater explosion attracts more and more attention from the modern ship designers. In this study, two kinds of scale tests were conducted to investigate the effects of polyurea coatings on the blast resistance of hulls subjected to underwater explosion. Firstly, small-scale model tests with different polyurea coatings were carried out. Results indicate that polyurea has a better blast resistance performance when coated on the front face, which can effectively reduce the maximum deflection of the steel plate by more than 20% and reduce the deformation energy by 35.7%-45.4%. Next, a full-scale ship(approximately 50 m × 9 m) under loadings produced by the detonation of 33 kg of spherical TNT charges was tested, where a part of the ship was coated with polyurea on the front face(8 mm + 24 mm) and not on the contrast area. Damage characteristics on the bottom were statistically analyzed based on a 3D scanning technology, indicating that polyurea contributes to enhancing the blast protection of the ship. However, damage results of this test were different from those of the small-scale tests. Moreover, the deformation area of the bottom with polyurea was greatly increased by 40.1% to disperse explosion energy, a conclusion that cannot be drown from the small-scale tests.
基金This research was supported by the National Natural Science Foundation of China(Nos.51978660).
文摘In this study,the anti-penetration performance of polyurea/ASTM1405-steel composite plate subjected to high velocity projectile was analyzed.Two kinds of modified polyurea material(AMMT-053 and AMMT-055)were selected and a ballistic impact testing system including speed measuring target system and high-speed camera was designed.This experiment was conducted with a rifle and 5.8 mm projectile to explore the effects by the polyurea coating thickness,the polyurea coating position and the glass-fiber cloth on the anti-penetration performance of polyurea/ASTM1405-steel composite plate.The result showed that the effects of polyurea coating position were different between two types of polyurea,and that the effects of glass-fiber position were disparate between two types of polyurea as well.For AMMT-053 polyurea material,it was better to be on front face than on rear face;whereas for AMMT-055 polyurea,it was better to be on rear surface although the difference was very subtle.Additionally,formulas had been given to describe the relationship between the effectiveness of polyurea and the thickness of polyurea coating.In general,AMMT-055 had better anti-penetration performance than AMMT-053.Furthermore,five typical damage modes including self-healing,crack,local bulge,spallation and local fragmentation were defined and the failure mechanism was analyzed with the results of SHPB test.Additionally,the bonding strength played an important role in the anti-penetration performance of polyurea/steel composite plate.
文摘A series of novel polysiloxane polyurea-urethane blockcopolymers based on methylene bis(p-phenylisocyanate (MDI), sodium-s-1,2-dihydroxy propyl sulphonate (SDPS) and aminopropyl-terminated polydimethylsiloxane (ATPS) was synthesized with varying length of soft segments and neutralizing cation. The effect of the chemical composition and the cation on the morphology and mechanical properties of the samples were studied. It was found that the SDPS chain extender based samples have definite chemical structure (-MDI-SDPS-MDI-ATPS-). As the length of the soft segment increases, an improvement of phase separation was observed. In addition, when SO3Na was translated into SO3H or the sulphonic acid groups were neutralized with different charge cations (Na+, Zn2+ and Al3+), the morphology and mechanical properties changed greatly.
基金supported by the National Natural Science Foundation of China nos.51978660。
文摘Clay brick masonry unit(CBMU) walls are widely used in building structures,and its damage and protection under explosion loads have been a matter of concern in the field of engineering protection.In this paper,a series of full-scale experiments of the response characteristics of 24 cm CMBU walls unreinforced and reinforced with polyurea elastomer subjected to blast loading were carried out.Through setting 5.0 kg TNT charges at different stand-off distances,the damage characteristics of masonry walls at different scaled distances were obtained.The reinforcement effect of different polyurea coating thicknesses and methods on the blast resistance performance of masonry walls under single and repeated loads were also explored.Five failure grades were summarized according to the dynamic response features of masonry walls.Based on the stress wave propagation pattern in multi-media composite structures,the internal stress distribution of masonry walls were analyzed,and the division basis of the masonry walls’ failure grades was then quantified.Combined with Scanning Electron Microscope(SEM)images,the deformation characteristics of soft and hard segments of polyurea and effects of detonation products on microstructures were revealed respectively,which provides an important reference for the design and application of polyurea in the blast resistance of clay brick masonry walls.
基金the financial support from National Basic Research Program of China(2016YFA0602900)National Natural Science Foundation of China(21672204,21273222)+1 种基金Youth Innovation Promotion Association CAS(2016206)Jilin Provincial Science and Technology Program of China(20160203007GX)
文摘Activation and transformation of CO_2 is one of the important issues in the field of green and sustainable chemistry. Herein, CO_2 as a carbonoxygen resource was converted to CO_2-polyurea with 1,6-hexanediamine through a two-step polymerization. The reaction parameters such as temperature, pressure and reaction time were examined; and several kinds of catalysts were screened in the absence and presence of NMP solvent. The formed oligomer and the final polyurea were characterized by FT-IR, VT-DRIFTS, NMR, XRD, AFM and their thermal properties were examined by TGA and DSC. It was confirmed that the final polyurea has a high thermal stability; the melting temperature is 269℃ and the decomposition temperature is above 300℃. It is a brittle polymer with a tensile strength of 18.35 MPa at break length of 1.64%. The polyurea has a stronger solvent resistance due to the ordered hydrogen bond in structure. The average molecular weight should be enhanced in the postpolymerization as the appearance, hydrogen bond intensity, crystallinity, melting point and the thermal stability changed largely compared to the oligomer. The present work provides a new kind of polyurea, it is expected to have a wide application in the field of polymer materials.
基金supported by National Natural Science Foundation of China[51778622]Social Development Project of Science and Technology Department of Jiangsu Province[BE2017780]Jiangsu Natural Science Foundation Youth Project[BK20190573]。
文摘Polyurea coating and carbon fibre reinforced polymer reinforcing techniques were applied to retrofit a severely damaged urban utility tunnel(UUT).The blast responses of the retrofitted UUT were investigated through in-filed explosion experimental tests,and the displacements,strains,accelerations,and damage were compared.The retrofitted UUT exhibited comparable or even better blast resistance than the intact UUT.Although the polyurea coating was flexible,it exhibited excellent performance in improving the blast resistance of the damaged UUT.As the UUT reinforced with basalt fibre reinforce polymer(BFRP)bars has smaller damage compared with the UUT reinforced with steel bars,its retrofitting is simple,and the cost is low.The roof was simplified as an elastically simple support one-way slab.Euler beam theory was adopted to analyse the dynamic responses of UUT roof considering the interaction between soil and structure,which agree well with the experiments in the first three cases.
文摘An essential oil is the volatile lipophilic component extracted from plants. Microencapsulation systems protect the essential oil from degradation and evaporation, and, at the same time, allow a sustained release. This work analyses and characterizes the oregano and sage essential oil microcapsules prepared by interfacial polymerization technique, using polyurea as wall material. Several instrumental techniques are used: optical microscopy, size particle, Fourier transform infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), Termo gravimetric analysis (TGA), spectrophotometry, antimicrobial test and chromatography. Results show that oregano and sage oil have antimicrobial properties, and their microencapsulation allows knowing that these properties remain inside the microcapsules.
文摘The use of CO_(2) as monomer to synthesize polymer materials is an important and potential applications topic from the viewpoint of green and sustainable chemistry.A new kind of CO_(2)-based polyurea(PUa)was synthesized by polycondensation of CO_(2) with 4,7,10-trioxa-1,13-tridecanediamine and tris(2-aminoethyl)amine(TAEA).TAEA was used as cross-link reagent.The mechanical properties of PUa were significantly improved by inserted the crosslink agent of TAEA.The formed slight cross-linked PUa exhibited excellent mechanical properties with tensile strength of 26.8 MPa,elongation at break of 34%and Young’s modulus of 351 MPa.Moreover,it could be remolded for 3 times without obvious change in the mechanical properties,which are ascribed to the hydrogen bonding interaction among the main chains and the slight cross-linked structure.In addition,the synthesized CO_(2)-based PUa is of outstanding thermal performance with an initial decomposition temperature above 300℃,besides it is tolerance for a variety of organic solvents.