Minerals in Portland cement including tricalcium silicate(C_(3)S),β-dicalcium silicate(β-C_(2)S),tricalcium aluminate(C_(3)A),and tetracalcium ferroaluminate(C_(4)AF),show a significantly different activity and prod...Minerals in Portland cement including tricalcium silicate(C_(3)S),β-dicalcium silicate(β-C_(2)S),tricalcium aluminate(C_(3)A),and tetracalcium ferroaluminate(C_(4)AF),show a significantly different activity and product evolution for CO_(2)curing at various water-to-solid ratios.These pure minerals were synthesized and subject to CO_(2)curing in this study to make an in-depth understanding for the carbonation properties of cement-based materials.Results showed that the optimum water-to-solid ratios of C_(3)S,β-C_(2)S,C_(3)A and C_(4)AF were 0.25,0.15,0.30 and 0.40 for carbonation,corresponding to 2 h carbonation degree of 38.5%,38.5%,24.2%,and 21.9%,respectively.The produced calcite duringβ-C_(2)S carbonation decreased as the water-to-solid ratio increased,with an increase in content of metastable CaCO_(3)of vaterite and aragonite.The thermodynamic stability of CaCO_(3)produced during carbonation was C_(3)A>C_(4)AF>β-C_(2)S>C_(3)S.The carbonation degree of Portland cement was predicted based on the results of pure minerals and the composition of cement,and the error of predicted production of CaCO_(3)was only 1.1%,which provides a potential method to predict carbonation properties of systems with a complex mineral composition.展开更多
To improve the efficiency and stability of chloride immobilization of portland cement paste,hydrated calcium aluminate cement(HCAC)prepared by wet grinding of CAC was added into portland cement paste as an additive.Th...To improve the efficiency and stability of chloride immobilization of portland cement paste,hydrated calcium aluminate cement(HCAC)prepared by wet grinding of CAC was added into portland cement paste as an additive.The immobilized chloride ratio(ICR)was evaluated,and the mechanism of chloride immobilization was researched by XRD,DTG,NMR,and MIP tests.The analysis results demonstrated that HCAC could improve the chloride immobilization capacity of portland cement paste.The mechanism was attributed to the following aspects:chemical binding capacity was enhanced via producing more Kuzel’s salt;physical adsorption capacity was reduced by decreasing the C-S-H gel;migration resistance was enhanced through refining the pore structure.展开更多
With the great impetus of energy conservation and emission reduction policies in various countries,the proposal of concepts such as“Sponge City”and“Eco-City”,and the emphasis on restoration and governance of ecolo...With the great impetus of energy conservation and emission reduction policies in various countries,the proposal of concepts such as“Sponge City”and“Eco-City”,and the emphasis on restoration and governance of ecological environment day by day,portland cement porous concrete(PCPC),as a novel building material,has attracted more and more attention from scientific researchers and engineers.PCPC possesses the peculiar pore structure,which owns numerous functions like river embankment protection,vegetation greening as well as air-cleaning,and has been of wide application in different engineering fields.This paper reviews the salient properties of PCPC,detailedly expounds the research progress of domestic and foreign literature about this subject in the past ten years(2010–2020),conducts the statistical analysis of the distribution rule of its major properties around the world,combines with the engineering application to summarize the excellent properties of PCPC,and makes a forecast of future research direction.展开更多
The properties of low-heat Portland cement concrete（LHC） were studied in detail. The experimental results show that the LHC concrete has characteristics of a higher physical mechanical behavior, deformation and dura...The properties of low-heat Portland cement concrete（LHC） were studied in detail. The experimental results show that the LHC concrete has characteristics of a higher physical mechanical behavior, deformation and durability. Compared with moderate-heat Portland cement（MHC）, the average hydration heat of LHC concrete is reduced by about 17.5%. Under same mixing proportion, the adiabatic temperature rise of LHC concrete was reduced by 2 ℃-3 ℃,and the limits tension of LHC concrete was increased by 10× 10^-6-15×10^-6 than that of MHC. Moreover, it is indicated that LHC concrete has a better anti-crack behavior than MHC concrete.展开更多
Performances of belite-rich Portland cement, or HBC （high belite cement）, and the resultant concrete are introduced by comparing with that of alite based PC （Portland cement） and concrete. The comparison study of ...Performances of belite-rich Portland cement, or HBC （high belite cement）, and the resultant concrete are introduced by comparing with that of alite based PC （Portland cement） and concrete. The comparison study of cement properties indicates that HBC possesses the properties of less water demand for normal consistency, better compatibility with water reducer, higher later age strength after 28-day under standard curing temperature of 20 ℃, unique strength gain under elevated curing temperatures of 38-70 ℃, lower hydration heat evolution and temperature rise, lower drying shrinkage and excellent resistance to sulphate attack. These results have been demonstrated by the comparison performance evaluation of concretes prepared by HBC and PC in terms of workability, physical mechanical properties and durability when making high performance high strength concrete and massive concrete.展开更多
The effect of Portland cement （OPC） addition on the properties of high calcium fly ash geopolymer pastes was investigated in the paper. OPC partially replaced fly ash （FA） at the dosages of 0, 5%, 10%, and 15% by ...The effect of Portland cement （OPC） addition on the properties of high calcium fly ash geopolymer pastes was investigated in the paper. OPC partially replaced fly ash （FA） at the dosages of 0, 5%, 10%, and 15% by mass of binder. Sodium silicate （Na2SiO3） and sodium hydroxide （NaOH） solutions were used as the liquid portion in the mixture： NaOH 10 mol/L, Na2SiO3/NaOH with a mass ratio of 2.0, and alkaline liquid/binder （L/B） with a mass ratio of 0.6. The curing at 60℃ for 24 h was used to accelerate the geopolymerization. The setting time of all fresh pastes, porosity, and compressive strength of the pastes at the stages of 1, 7, 28, and 90 d were tested. The elastic modulus and strain capacity of the pastes at the stage of 7 d were determined. It is revealed that the use of OPC as an additive to replace part of FA results-in the decreases in the setting time, porosity, and strain capacity of the paste specimens, while the compressive strength and elastic modulus seem to increase.展开更多
China is the largest producer and user of ordinary Portland cement(OPC),and the rapid growth of infrastructure development demands more sustainable building materials for concrete structures.Alkali-activated materials...China is the largest producer and user of ordinary Portland cement(OPC),and the rapid growth of infrastructure development demands more sustainable building materials for concrete structures.Alkali-activated materials(AAMs)are a new type of energy-saving and environmentally friendly building material with a wide range of potential applications.This paper compares the durability of AAMs and 0 PC-based materials un der sulfate attack,acid corrosion,carb on ation,and chloride penetratio n.Different AAMs have shown distinct durability properties due to different compositions being formed when different raw materials are used.According to the calcium(Ca)concentration of the raw materials,this paper interprets the deterioration mechanisms of three categories of AAMs:calcium-free,low-calcium,and calcium-rich.Conflicts found in the most recent research are highlighted,as they raise concerns regarding the consistenee and long-term properties of AAMs.Nevertheless,AAMs show better durability performances than OPC-based materials in general.展开更多
Hydration heat evolution, non-evaporative water, setting time and SEM tests were peorormed to investigate the effect of fine steel slag powder on the hydration process of Portland cement and its mechanism. The results...Hydration heat evolution, non-evaporative water, setting time and SEM tests were peorormed to investigate the effect of fine steel slag powder on the hydration process of Portland cement and its mechanism. The results show that the effect of fine steel slag powder on the hydration process of Portland cement is closely related to its chemical composition, mineral phases, fineness, etc. Fine steel slag powder retards the hydration of portland cement at early age. The major reason for this phenomenon is the relative high content of MgO , MnO2, P2O5 in steel slag, and MgO solid solved in C3 S contained in steel slag.展开更多
In order to explore the serviceability and reinforcement of CaCO3 whisker in portland cement matrix, the durability of CaCO3 whisker and effect of low whisker content（0%-4.0%） on the working performance and mechanic...In order to explore the serviceability and reinforcement of CaCO3 whisker in portland cement matrix, the durability of CaCO3 whisker and effect of low whisker content（0%-4.0%） on the working performance and mechanical properties of portland cement were investigated. The experimental results show that CaCO3 whiskers have a good stability and serviceability in cement, and should not significantly alter the rheological properties of the cement paste. The flexural and compressive strength of portland cement reinforced by CaCO3 whiskers was increased by 33.3% and 12.83%, respectively.展开更多
The mining industry often uses shotcrete for ground stabilization. However, cracking within shotcrete is commonly observed, which delays production schedules and increases maintenance costs. A possible crack reduction...The mining industry often uses shotcrete for ground stabilization. However, cracking within shotcrete is commonly observed, which delays production schedules and increases maintenance costs. A possible crack reduction method is using expansive shotcrete mixture consisting of calcium sulfoaluminate cement(CSA), ordinary Portland cement(OPC), and calcium sulfate(CS) to reduce shrinkage. Furthermore, fibers can be added to the mixture to restrain expansion and impede cracking. The objective of this paper is to study the effects of nylon fiber, glass fiber, and steel fiber on an expansive shotcrete mixture that can better resist cracking. In this study, parameters such as density, water absorption, volume of permeable voids, unconfined compressive strength(UCS), splitting tensile strength(STS), and volume change of fiber-added expansive mixtures were determined at different time periods(i.e. the strengths on the 28 th day, and the volume changes on the 1 st, 7 th, 14 th, 21 st, and 28 th days). The results show that addition of fibers can improve mixture durability, in the form of decreased water absorption and reduced permeable pore space content. Moreover, the expansion of the CSA-OPC-CS mixture was restrained up to50% by glass fiber, up to 43% by nylon fiber, and up to 28% by steel fiber. The results show that the STS was improved by 57% with glass fiber addition, 43% with steel fiber addition, and 38% with nylon fiber addition. The UCS was also increased by 31% after steel fiber addition, 26% after nylon fiber addition, and16% after glass fiber addition. These results suggest that fiber additions to the expansive shotcrete mixtures can improve durability and strengths while controlling expansion.展开更多
The features of alkali activated slag（AAS） and portland cement （PC） were observed on multi-scale,the crack and fracture sections were observed with naked eyes,and SEM and AFM were used to study the structure morph...The features of alkali activated slag（AAS） and portland cement （PC） were observed on multi-scale,the crack and fracture sections were observed with naked eyes,and SEM and AFM were used to study the structure morphology differences between PC and AAS on micrometer to nano meter scale.The experimental results indicated that the AAS paste had soil like fracture texture and it was composed of mainly C-S-H gel but lacks of crystals,and it had a very strong tendency to shrink and crack.AAS paste is much denser and more homogeneous than PC,and on the nano scale C-S-H nano particle in the AAS paste is much smaller and packs much denser than PC paste.展开更多
Two kinds of CACs with different monocalcium aluminate（CA） contents were used in the PC/CAC（PAC） mixtures. Effects of CA and CACs on the properties of PAC were analyzed by setting times and the compressive strengt...Two kinds of CACs with different monocalcium aluminate（CA） contents were used in the PC/CAC（PAC） mixtures. Effects of CA and CACs on the properties of PAC were analyzed by setting times and the compressive strength tests, and also by means of calorimetry, XRD, DTA-TG and ESEM. The experimental results show that the compressive strength of the PAC mortars decreases with increasing content of CAC while it declines sharply with a higher content of CA in CAC. Compared with neat PC paste, the content of calcium hydroxide in hydrates of PAC paste decreases significantly, and the hydration time of PC is prominently prolonged. Additionally, the higher the content of CA in CAC, the more obviously the hydration of PC is delayed, confi rming that the CA phase in CAC plays an important role in the delay of PC hydration.展开更多
Cellulose ethers are widely used to mortar formulations,and it is significant to understand the interaction between cellulose ethers and cement pastes.FT-IR spectra,thermal analysis and SEM are used to investigate hyd...Cellulose ethers are widely used to mortar formulations,and it is significant to understand the interaction between cellulose ethers and cement pastes.FT-IR spectra,thermal analysis and SEM are used to investigate hydration products in the cement pastes modified by HEMC and HPMC in this article.The results show that the hydration products in modified cement pastes were finally identical with those in the unmodified cement paste,but the major hydration products,such as CH（calcium hydroxide）,ettringite and C-S-H,appeared later in the modified cement pastes than in the unmodified cement paste.The cellulose ethers decrease the outer products and increase inner products of C-S-H gels.Compared to unmodified cement pastes,no new products are found in the modified cement pastes in the present experiment.The HEMC and HPMC investigation shows almost the same influence on the hydration products of Portland cement.展开更多
The microstructural evolution of C-（A）-S-H gel in Portland cement pastes immersed in pure water and 5.0 wt% Na2SO4 solution for different ages was comparatively investigated, by means of ^（29） Si NMR spectroscopy,...The microstructural evolution of C-（A）-S-H gel in Portland cement pastes immersed in pure water and 5.0 wt% Na2SO4 solution for different ages was comparatively investigated, by means of ^（29） Si NMR spectroscopy, and SEM-EDS analysis. Additionally, molecular dynamics simulation was performed to study the aluminum coordination status and interaction of sulfate ions in C-（A）-S-H gel. The results showed significant changes in the microstructural evolution of C-（A）-S-H gel in Portland cement paste. Sulfate attack has decalcifying and dealuminizing effect on C-（A）-S-H gel which is evident from increase in mean chain length（MCL） and decrease in Ca/Si ＆ Al[4]/Si ratios of C-（A）-S-H gel. Additionally, Molecular dynamics simulation proves that Al[4] substituted in silicate chains of C-（A）-S-H gel is thermodynamically metastable, which may explain its migration from the silicate chains and transformation to Al[6], thus lowering the Al[4]/Si ratio of C-（A）-S-H gel. SO4^（2-）ions can carry the interfacial Ca^（2＋） ions into the pore solution by the diffusion-absorption-desorption process, which unravels the mechanism of sulfate attack on C-（A）-S-H gel.展开更多
The composition and structure of the inter facial zone between aggregate and paste of Portland cement as well as the orientation coefficient of portlandite ( Icn ) were preliminarily studied by XRD and SEM methods. Th...The composition and structure of the inter facial zone between aggregate and paste of Portland cement as well as the orientation coefficient of portlandite ( Icn ) were preliminarily studied by XRD and SEM methods. The main products in the zone are C -S-H gel, portlandite, AFt and pores, micro-cracks as welt as unhydrated portland cement clinker particles. Potlandite not only grows well but exists in orientating forms, and near the interface it exists in a state parallel to the surface of aggregate by its (001) lattice plane. Icn rises with the increase of cement water ratio (w/c) and the development of the cement hydration. The higher the w/c, the more the pores and micro-cracks in the zone. w/c bears an exact relation to the decrease of bond strength. Icn, is decreased when 5. 0% silica fume is added to cement. Bond strengths at early ages are reduced by adding 0. 5% FDN (one kind of water-reducing admixture) due to the retarded hydration of cement, but they will increase continually and become greater than those of other samples after 28 days.展开更多
The long-term performance of moderate heat Portland cement with double-expansive sources （DE cement） in the system of high MgO clinker and gypsum was studied by XRD, SEM/EDAX and test methods for strength and expans...The long-term performance of moderate heat Portland cement with double-expansive sources （DE cement） in the system of high MgO clinker and gypsum was studied by XRD, SEM/EDAX and test methods for strength and expansion of cement. Results indicate that the periclase particle, whose size was 5-7.5μm in DE cement clinker containing 4.8 % MgO, existed individually. The periclase hydration in hardened DE cement paste started at about 60 days and completed up to 2 000 days, and ettringite in the paste was stable from 3 days to 2 000 days. Under the conditions of 4.5%-5.0 % MgO in clinker and 2.8%-3.4 %SO3 in cement, ettringite expansion and brucite expansion in DE cement paste had a continuity, entirety and stability. At the ages of 90, 365,730 and 2 000 days the expansion of the paste reached 0.07%-0.11%, 0.16%-0.21%, 0.21%-0.27 %, and 0.29%-0.38%, respectively. The results suggest that by using this cement in mass concrete it may compensate its temperature shrinkage and autogenous shrinkage to some extent.展开更多
The reaction models and the quantitative calculation on the volume fraction of hydration products for binary ground granulated blast-furnace slag （GGBFS） cement system are presented, in which two important factors a...The reaction models and the quantitative calculation on the volume fraction of hydration products for binary ground granulated blast-furnace slag （GGBFS） cement system are presented, in which two important factors are taken into account, i e, the reactivity of GGBFS influenced by its chemical compositions and the partial replacement of aluminum phase in calcium silicate hydrate （C-S-H） gel. A simplified treatment is further suggested towards the quantification. In particular, when the replacement level of GGBFS is lower than 70%, the ratio of calcium over silica （C/S） is set at 1.5 or at 1.2 otherwise. The validity of the proposed model is addressed in terms of the contents of calcium Portlandite and non-evaporable water.展开更多
The forming temperature of Clinker melt underdifferent burning conditions has been studied by appearance examination and thermal shrinker determination, and the viscosity of melt has been discussed by studying the coo...The forming temperature of Clinker melt underdifferent burning conditions has been studied by appearance examination and thermal shrinker determination, and the viscosity of melt has been discussed by studying the coordination number of Al^(3+) and Fe^(3+) in cement clinker burned by different method with x^- ray fluorescence analysis and Moss- bauer spectroscopy. The results show that the clin- ker melt under rapid burning may come into exis- tence at lower temperature and It's viscosity is lower. So the forming processes of clinker may be different at rapid burning from ordinary burning. They are probably an important factor to promote the formation of clinker burned at lower temperature with rapid burning method.展开更多
Portland cement is the most common type of cement in general use around the world as a basic ingredient of concrete, mortar, stucco, and non-speciality grout. Dicalcium silicate （Ca2SiO4） is the primary constituent ...Portland cement is the most common type of cement in general use around the world as a basic ingredient of concrete, mortar, stucco, and non-speciality grout. Dicalcium silicate （Ca2SiO4） is the primary constituent of a number of different types of cement. The β-Ca2SiO4 phase is metastable at room temperature and will transform into β-Ca2SiO4 at 663K. In this work, Portland cement is annealed at a temperature of 950K under pressures in the range of 0-5.5 CPa. The high pressure experiments are carried out in an apparatus with six anvil tops. The effect of high pressure on the obtaining nano-size β-Ca2SiO4 （C2S） process is investigated by x-ray diffraction and transmission electron microscopy. Experimental results show that the grain size of the C2S decreases with the increase of pressure. The volume fraction of the C2S phase increases with the pressure as the pressure is below 3 CPa, and then decreases （P 〉 3 GPa）. The nano-effect is very important to the stabilization of β-Ca2SiO4. The mechanism for the effects of the high pressure on the annealing process of the Portland cement is also discussed.展开更多
基金Funded by Hainan Provincial Natural Science Foundation of China(No.522QN279)State Key Laboratory of High Performance Civil Engineering Materials(No.2023CEM004)Natural Science Foundation of Jiangsu Province(No.BK20231088)。
文摘Minerals in Portland cement including tricalcium silicate(C_(3)S),β-dicalcium silicate(β-C_(2)S),tricalcium aluminate(C_(3)A),and tetracalcium ferroaluminate(C_(4)AF),show a significantly different activity and product evolution for CO_(2)curing at various water-to-solid ratios.These pure minerals were synthesized and subject to CO_(2)curing in this study to make an in-depth understanding for the carbonation properties of cement-based materials.Results showed that the optimum water-to-solid ratios of C_(3)S,β-C_(2)S,C_(3)A and C_(4)AF were 0.25,0.15,0.30 and 0.40 for carbonation,corresponding to 2 h carbonation degree of 38.5%,38.5%,24.2%,and 21.9%,respectively.The produced calcite duringβ-C_(2)S carbonation decreased as the water-to-solid ratio increased,with an increase in content of metastable CaCO_(3)of vaterite and aragonite.The thermodynamic stability of CaCO_(3)produced during carbonation was C_(3)A>C_(4)AF>β-C_(2)S>C_(3)S.The carbonation degree of Portland cement was predicted based on the results of pure minerals and the composition of cement,and the error of predicted production of CaCO_(3)was only 1.1%,which provides a potential method to predict carbonation properties of systems with a complex mineral composition.
基金Funded by the National Natural Science Foundation of China(Nos.52278275 and 52202029)the Major Technical Innovation Project in Hubei Province of China(No.2021BAA060)。
文摘To improve the efficiency and stability of chloride immobilization of portland cement paste,hydrated calcium aluminate cement(HCAC)prepared by wet grinding of CAC was added into portland cement paste as an additive.The immobilized chloride ratio(ICR)was evaluated,and the mechanism of chloride immobilization was researched by XRD,DTG,NMR,and MIP tests.The analysis results demonstrated that HCAC could improve the chloride immobilization capacity of portland cement paste.The mechanism was attributed to the following aspects:chemical binding capacity was enhanced via producing more Kuzel’s salt;physical adsorption capacity was reduced by decreasing the C-S-H gel;migration resistance was enhanced through refining the pore structure.
基金supported by the Jiangsu Water Conservancy Science and Technology Project of China(2016036).
文摘With the great impetus of energy conservation and emission reduction policies in various countries,the proposal of concepts such as“Sponge City”and“Eco-City”,and the emphasis on restoration and governance of ecological environment day by day,portland cement porous concrete(PCPC),as a novel building material,has attracted more and more attention from scientific researchers and engineers.PCPC possesses the peculiar pore structure,which owns numerous functions like river embankment protection,vegetation greening as well as air-cleaning,and has been of wide application in different engineering fields.This paper reviews the salient properties of PCPC,detailedly expounds the research progress of domestic and foreign literature about this subject in the past ten years(2010–2020),conducts the statistical analysis of the distribution rule of its major properties around the world,combines with the engineering application to summarize the excellent properties of PCPC,and makes a forecast of future research direction.
基金the National Natural Science Foundation of China(No.50539010)
文摘The properties of low-heat Portland cement concrete（LHC） were studied in detail. The experimental results show that the LHC concrete has characteristics of a higher physical mechanical behavior, deformation and durability. Compared with moderate-heat Portland cement（MHC）, the average hydration heat of LHC concrete is reduced by about 17.5%. Under same mixing proportion, the adiabatic temperature rise of LHC concrete was reduced by 2 ℃-3 ℃,and the limits tension of LHC concrete was increased by 10× 10^-6-15×10^-6 than that of MHC. Moreover, it is indicated that LHC concrete has a better anti-crack behavior than MHC concrete.
文摘Performances of belite-rich Portland cement, or HBC （high belite cement）, and the resultant concrete are introduced by comparing with that of alite based PC （Portland cement） and concrete. The comparison study of cement properties indicates that HBC possesses the properties of less water demand for normal consistency, better compatibility with water reducer, higher later age strength after 28-day under standard curing temperature of 20 ℃, unique strength gain under elevated curing temperatures of 38-70 ℃, lower hydration heat evolution and temperature rise, lower drying shrinkage and excellent resistance to sulphate attack. These results have been demonstrated by the comparison performance evaluation of concretes prepared by HBC and PC in terms of workability, physical mechanical properties and durability when making high performance high strength concrete and massive concrete.
基金supported by the Higher Education Research Promotion and National Research University Project of ThailandThailand Research Fund (TRF) under the TRF Senior Research Scholar (No.RTA5480004)the Royal Golden Jubilee Ph.D. Program (No. PHD/0340/2552)
文摘The effect of Portland cement （OPC） addition on the properties of high calcium fly ash geopolymer pastes was investigated in the paper. OPC partially replaced fly ash （FA） at the dosages of 0, 5%, 10%, and 15% by mass of binder. Sodium silicate （Na2SiO3） and sodium hydroxide （NaOH） solutions were used as the liquid portion in the mixture： NaOH 10 mol/L, Na2SiO3/NaOH with a mass ratio of 2.0, and alkaline liquid/binder （L/B） with a mass ratio of 0.6. The curing at 60℃ for 24 h was used to accelerate the geopolymerization. The setting time of all fresh pastes, porosity, and compressive strength of the pastes at the stages of 1, 7, 28, and 90 d were tested. The elastic modulus and strain capacity of the pastes at the stage of 7 d were determined. It is revealed that the use of OPC as an additive to replace part of FA results-in the decreases in the setting time, porosity, and strain capacity of the paste specimens, while the compressive strength and elastic modulus seem to increase.
基金Financial support from the National Natural Science Foundation of China(51778003,51878263,and 51608004)Opening Foundation of State Key Laboratory of High Performance Civil Engineering Materials(2018CEM002)+1 种基金Anhui Provincial Education Department(gxfxZD2016134)Anhui Province Higher Education Revitalization Program([2014]No.11).
文摘China is the largest producer and user of ordinary Portland cement(OPC),and the rapid growth of infrastructure development demands more sustainable building materials for concrete structures.Alkali-activated materials(AAMs)are a new type of energy-saving and environmentally friendly building material with a wide range of potential applications.This paper compares the durability of AAMs and 0 PC-based materials un der sulfate attack,acid corrosion,carb on ation,and chloride penetratio n.Different AAMs have shown distinct durability properties due to different compositions being formed when different raw materials are used.According to the calcium(Ca)concentration of the raw materials,this paper interprets the deterioration mechanisms of three categories of AAMs:calcium-free,low-calcium,and calcium-rich.Conflicts found in the most recent research are highlighted,as they raise concerns regarding the consistenee and long-term properties of AAMs.Nevertheless,AAMs show better durability performances than OPC-based materials in general.
基金Funded by National 973 Project (No.2001CB610704-2)
文摘Hydration heat evolution, non-evaporative water, setting time and SEM tests were peorormed to investigate the effect of fine steel slag powder on the hydration process of Portland cement and its mechanism. The results show that the effect of fine steel slag powder on the hydration process of Portland cement is closely related to its chemical composition, mineral phases, fineness, etc. Fine steel slag powder retards the hydration of portland cement at early age. The major reason for this phenomenon is the relative high content of MgO , MnO2, P2O5 in steel slag, and MgO solid solved in C3 S contained in steel slag.
文摘In order to explore the serviceability and reinforcement of CaCO3 whisker in portland cement matrix, the durability of CaCO3 whisker and effect of low whisker content（0%-4.0%） on the working performance and mechanical properties of portland cement were investigated. The experimental results show that CaCO3 whiskers have a good stability and serviceability in cement, and should not significantly alter the rheological properties of the cement paste. The flexural and compressive strength of portland cement reinforced by CaCO3 whiskers was increased by 33.3% and 12.83%, respectively.
基金financial support from Natural Sciences and Engineering ResearchCouncil(NSERC)(NSERC EGP 501335-16) along with the donated CSA cement
文摘The mining industry often uses shotcrete for ground stabilization. However, cracking within shotcrete is commonly observed, which delays production schedules and increases maintenance costs. A possible crack reduction method is using expansive shotcrete mixture consisting of calcium sulfoaluminate cement(CSA), ordinary Portland cement(OPC), and calcium sulfate(CS) to reduce shrinkage. Furthermore, fibers can be added to the mixture to restrain expansion and impede cracking. The objective of this paper is to study the effects of nylon fiber, glass fiber, and steel fiber on an expansive shotcrete mixture that can better resist cracking. In this study, parameters such as density, water absorption, volume of permeable voids, unconfined compressive strength(UCS), splitting tensile strength(STS), and volume change of fiber-added expansive mixtures were determined at different time periods(i.e. the strengths on the 28 th day, and the volume changes on the 1 st, 7 th, 14 th, 21 st, and 28 th days). The results show that addition of fibers can improve mixture durability, in the form of decreased water absorption and reduced permeable pore space content. Moreover, the expansion of the CSA-OPC-CS mixture was restrained up to50% by glass fiber, up to 43% by nylon fiber, and up to 28% by steel fiber. The results show that the STS was improved by 57% with glass fiber addition, 43% with steel fiber addition, and 38% with nylon fiber addition. The UCS was also increased by 31% after steel fiber addition, 26% after nylon fiber addition, and16% after glass fiber addition. These results suggest that fiber additions to the expansive shotcrete mixtures can improve durability and strengths while controlling expansion.
基金Funded by the Open Foundation of National Key Laboratory of Green Building Materials(CBM-08-KF103)
文摘The features of alkali activated slag（AAS） and portland cement （PC） were observed on multi-scale,the crack and fracture sections were observed with naked eyes,and SEM and AFM were used to study the structure morphology differences between PC and AAS on micrometer to nano meter scale.The experimental results indicated that the AAS paste had soil like fracture texture and it was composed of mainly C-S-H gel but lacks of crystals,and it had a very strong tendency to shrink and crack.AAS paste is much denser and more homogeneous than PC,and on the nano scale C-S-H nano particle in the AAS paste is much smaller and packs much denser than PC paste.
基金Funded by the National Key Technology R&D Programs in the12th Five-year Plan of China(2012BA20B02)
文摘Two kinds of CACs with different monocalcium aluminate（CA） contents were used in the PC/CAC（PAC） mixtures. Effects of CA and CACs on the properties of PAC were analyzed by setting times and the compressive strength tests, and also by means of calorimetry, XRD, DTA-TG and ESEM. The experimental results show that the compressive strength of the PAC mortars decreases with increasing content of CAC while it declines sharply with a higher content of CA in CAC. Compared with neat PC paste, the content of calcium hydroxide in hydrates of PAC paste decreases significantly, and the hydration time of PC is prominently prolonged. Additionally, the higher the content of CA in CAC, the more obviously the hydration of PC is delayed, confi rming that the CA phase in CAC plays an important role in the delay of PC hydration.
基金Funded by Youth Fund of National Natural Science Foundation of China(No.50902107)the 973 Program(No.2009CB623201)from Ministry of Science and Technology of Chinathe Fundamental Research Funds for the Central Universities
文摘Cellulose ethers are widely used to mortar formulations,and it is significant to understand the interaction between cellulose ethers and cement pastes.FT-IR spectra,thermal analysis and SEM are used to investigate hydration products in the cement pastes modified by HEMC and HPMC in this article.The results show that the hydration products in modified cement pastes were finally identical with those in the unmodified cement paste,but the major hydration products,such as CH（calcium hydroxide）,ettringite and C-S-H,appeared later in the modified cement pastes than in the unmodified cement paste.The cellulose ethers decrease the outer products and increase inner products of C-S-H gels.Compared to unmodified cement pastes,no new products are found in the modified cement pastes in the present experiment.The HEMC and HPMC investigation shows almost the same influence on the hydration products of Portland cement.
基金Funded by National Natural Science Foundation of China(Nos.51778513,51578004,51608004)the Major State Basic Research Development Program of China("973"Program)(No.2015CB655101)
文摘The microstructural evolution of C-（A）-S-H gel in Portland cement pastes immersed in pure water and 5.0 wt% Na2SO4 solution for different ages was comparatively investigated, by means of ^（29） Si NMR spectroscopy, and SEM-EDS analysis. Additionally, molecular dynamics simulation was performed to study the aluminum coordination status and interaction of sulfate ions in C-（A）-S-H gel. The results showed significant changes in the microstructural evolution of C-（A）-S-H gel in Portland cement paste. Sulfate attack has decalcifying and dealuminizing effect on C-（A）-S-H gel which is evident from increase in mean chain length（MCL） and decrease in Ca/Si ＆ Al[4]/Si ratios of C-（A）-S-H gel. Additionally, Molecular dynamics simulation proves that Al[4] substituted in silicate chains of C-（A）-S-H gel is thermodynamically metastable, which may explain its migration from the silicate chains and transformation to Al[6], thus lowering the Al[4]/Si ratio of C-（A）-S-H gel. SO4^（2-）ions can carry the interfacial Ca^（2＋） ions into the pore solution by the diffusion-absorption-desorption process, which unravels the mechanism of sulfate attack on C-（A）-S-H gel.
文摘The composition and structure of the inter facial zone between aggregate and paste of Portland cement as well as the orientation coefficient of portlandite ( Icn ) were preliminarily studied by XRD and SEM methods. The main products in the zone are C -S-H gel, portlandite, AFt and pores, micro-cracks as welt as unhydrated portland cement clinker particles. Potlandite not only grows well but exists in orientating forms, and near the interface it exists in a state parallel to the surface of aggregate by its (001) lattice plane. Icn rises with the increase of cement water ratio (w/c) and the development of the cement hydration. The higher the w/c, the more the pores and micro-cracks in the zone. w/c bears an exact relation to the decrease of bond strength. Icn, is decreased when 5. 0% silica fume is added to cement. Bond strengths at early ages are reduced by adding 0. 5% FDN (one kind of water-reducing admixture) due to the retarded hydration of cement, but they will increase continually and become greater than those of other samples after 28 days.
基金Funded by National Natural Science Foundation of China (No.59493604)Zhejiang Provincial Natural Science Foundation of China (No.597082)China Yangtze River Three Gorges General
文摘The long-term performance of moderate heat Portland cement with double-expansive sources （DE cement） in the system of high MgO clinker and gypsum was studied by XRD, SEM/EDAX and test methods for strength and expansion of cement. Results indicate that the periclase particle, whose size was 5-7.5μm in DE cement clinker containing 4.8 % MgO, existed individually. The periclase hydration in hardened DE cement paste started at about 60 days and completed up to 2 000 days, and ettringite in the paste was stable from 3 days to 2 000 days. Under the conditions of 4.5%-5.0 % MgO in clinker and 2.8%-3.4 %SO3 in cement, ettringite expansion and brucite expansion in DE cement paste had a continuity, entirety and stability. At the ages of 90, 365,730 and 2 000 days the expansion of the paste reached 0.07%-0.11%, 0.16%-0.21%, 0.21%-0.27 %, and 0.29%-0.38%, respectively. The results suggest that by using this cement in mass concrete it may compensate its temperature shrinkage and autogenous shrinkage to some extent.
基金Funded by the National Natural Science Foundation of China(No.51078081)
文摘The reaction models and the quantitative calculation on the volume fraction of hydration products for binary ground granulated blast-furnace slag （GGBFS） cement system are presented, in which two important factors are taken into account, i e, the reactivity of GGBFS influenced by its chemical compositions and the partial replacement of aluminum phase in calcium silicate hydrate （C-S-H） gel. A simplified treatment is further suggested towards the quantification. In particular, when the replacement level of GGBFS is lower than 70%, the ratio of calcium over silica （C/S） is set at 1.5 or at 1.2 otherwise. The validity of the proposed model is addressed in terms of the contents of calcium Portlandite and non-evaporable water.
文摘The forming temperature of Clinker melt underdifferent burning conditions has been studied by appearance examination and thermal shrinker determination, and the viscosity of melt has been discussed by studying the coordination number of Al^(3+) and Fe^(3+) in cement clinker burned by different method with x^- ray fluorescence analysis and Moss- bauer spectroscopy. The results show that the clin- ker melt under rapid burning may come into exis- tence at lower temperature and It's viscosity is lower. So the forming processes of clinker may be different at rapid burning from ordinary burning. They are probably an important factor to promote the formation of clinker burned at lower temperature with rapid burning method.
基金Supported by the National Natural Science Foundation of China under Grant No 11674274
文摘Portland cement is the most common type of cement in general use around the world as a basic ingredient of concrete, mortar, stucco, and non-speciality grout. Dicalcium silicate （Ca2SiO4） is the primary constituent of a number of different types of cement. The β-Ca2SiO4 phase is metastable at room temperature and will transform into β-Ca2SiO4 at 663K. In this work, Portland cement is annealed at a temperature of 950K under pressures in the range of 0-5.5 CPa. The high pressure experiments are carried out in an apparatus with six anvil tops. The effect of high pressure on the obtaining nano-size β-Ca2SiO4 （C2S） process is investigated by x-ray diffraction and transmission electron microscopy. Experimental results show that the grain size of the C2S decreases with the increase of pressure. The volume fraction of the C2S phase increases with the pressure as the pressure is below 3 CPa, and then decreases （P 〉 3 GPa）. The nano-effect is very important to the stabilization of β-Ca2SiO4. The mechanism for the effects of the high pressure on the annealing process of the Portland cement is also discussed.