Tin-doped indium oxide （ITO） thin films were prepared using conventional radio frequency （RF） planar magnetron sputtering equipped with IR irradiation using a ceramic target of In2O3/SnO2 with a mass ratio of 1：1...Tin-doped indium oxide （ITO） thin films were prepared using conventional radio frequency （RF） planar magnetron sputtering equipped with IR irradiation using a ceramic target of In2O3/SnO2 with a mass ratio of 1：1 at various IR irradiation temperatures T1 （from room temperature to 400℃）. The refractive index, deposited ratio, and resistivity are functions of the sputtering Ar gas pressure. The microstructure of ITO thin films is related to IR T1, the crystalline seeds appear at T1= 300℃, and the films are amorphous at the temperature ranging from 27℃ to 400℃. AFM investigation shows that the roughness value of peak-valley of ITO thin film （Rp-v） and the surface microstructure of rio thin films have a close relation with T1. The IR irradiation results in a widening value of band-gap energy due to Burstein-Moss effect and the maximum visible transmittance shifts toward a shorter wavelength along with a decrease in the film＇s refractive index. The plasma wavelength and the refractive index of ITO thin films are relative to the T1. XPS investigation shows that the photoelectrolytic properties can be deteriorated by the sub-oxides. The deterioration can be decreased by increasing the oxygen flow rote （fo2）, and the mole ratio of Sn/In in the samples reduces with an increase info2.展开更多
Pt/Ti bottom electrodes were fabricated on SiO2/Si substrates by magnetron dual-facingtarget sputtering system. Lead zirconate titanate（PZT） thin films were deposited on Pt/Ti/SiO2/Si substrates by radio frequency ...Pt/Ti bottom electrodes were fabricated on SiO2/Si substrates by magnetron dual-facingtarget sputtering system. Lead zirconate titanate（PZT） thin films were deposited on Pt/Ti/SiO2/Si substrates by radio frequency （RF） magnetron sputtering system. The thickness of PZT thin films which were deposited for 5 h was about 800 nm. XRD spectra show that PZT thin films deposited in Ar ambience and rapid-thermal-annealed for 20 min at 700 ℃ have good crystallization behavior and perovskite structure. AFM micrographs show that mean diameter of crystallites is 70 nm and surface structures of PZT thin films are uniform and dense. Raw mean, root mean square roughness and mean roughness of PZT thin films are 34..357 rim, 2. 479 nm and 1. 954 nm respectively. As test frequency is 1 kHz, dielectric constant of PZT thin films is 327.5. Electric hysteresis loop shows that coercive field strength, residual polarization strength and spontaneous polarization strength of PZT thin films are 50 kV/cm, 10μC/cm^2 and 13μC/cm^2 respectively.展开更多
Tin-doped indium oxide （ITO） thin films were prepared using conventional radio frequency （RF） planar magnetron sputtering equipped with IR irradiation using a ceramic target of In2O3/SnO2 with a mass ratio of 1∶1...Tin-doped indium oxide （ITO） thin films were prepared using conventional radio frequency （RF） planar magnetron sputtering equipped with IR irradiation using a ceramic target of In2O3/SnO2 with a mass ratio of 1∶1 at various IR irradiation temperatures T1 （from room temperature to 400?℃）. The refractive index,deposited ratio,and resistivity are functions of the sputtering Ar gas pressure. The microstructure of ITO thin films is related to IR T1,the crystalline seeds appear at T1=300?℃,and the films are amorphous at the temperature ranging from 27?℃ to 400?℃. AFM investigation shows that the roughness value of peak-valley of ITO thin film （R p-v ） and the surface microstructure of ITO thin films have a close relation with T1. The IR irradiation results in a widening value of band-gap energy due to Burstein-Moss effect and the maximum visible transmittance shifts toward a shorter wavelength along with a decrease in the film’s refractive index. The plasma wavelength and the refractive index of ITO thin films are relative to the T1. XPS investigation shows that the photoelectrolytic properties can be deteriorated by the sub-oxides. The deterioration can be decreased by increasing the oxygen flow rate （fo2）,and the mole ratio of Sn/In in the samples reduces with an increase in fo2.展开更多
Bi_(3.25)La_(0.75)Ti_(3)O_(12)(BLT)thin films are promising materials used in non-volatile memories.In this work,BLT films were deposited on Pt(111)/Ti/SiO_(2)/Si substrates by rf-magnetron sputtering method followed ...Bi_(3.25)La_(0.75)Ti_(3)O_(12)(BLT)thin films are promising materials used in non-volatile memories.In this work,BLT films were deposited on Pt(111)/Ti/SiO_(2)/Si substrates by rf-magnetron sputtering method followed by annealing treatments.The microstructures of BLT thin films were investigated via X-ray diffraction(XRD),scanning electron microscopy(SEM)and atomic force microscopy(AFM).With the increase in annealing temperature,the grain size increased significantly and the preferred crystalline orientation changed.A well-saturated hysteresis loop with a superior remnant polarization of 15.4μC/cm^(2) was obtained for BLT thin films annealed at 700°C.The results show that the dielectric constant decreased with the increase in grain sizes.展开更多
Surface metallization of glass fiber(GF)/polyetheretherketone(PEEK)[GF/PEEK] is conducted by coating copper using electroplating and magnetron sputtering and the properties are determined by X-ray diffraction(XRD), sc...Surface metallization of glass fiber(GF)/polyetheretherketone(PEEK)[GF/PEEK] is conducted by coating copper using electroplating and magnetron sputtering and the properties are determined by X-ray diffraction(XRD), scanning electron microscopy(SEM), and electron backscatter diffraction(EBSD).The coating bonding strength is assessed by pull-out tests and scribing in accordance with GB/T 9286-1998.The results show that the Cu coating with a thickness of 30 μm deposited on GF/PEEK by magnetron sputtering has lower roughness, finer grain size, higher crystallinity, as well as better macroscopic compressive stress,bonding strength, and electrical conductivity than the Cu coating deposited by electroplating.展开更多
Pure cobalt(Co)thin films were fabricated by direct current magnetron sputtering,and the effects of sputtering power and pres-sure on the microstructure and electromagnetic properties of the films were investigated.As...Pure cobalt(Co)thin films were fabricated by direct current magnetron sputtering,and the effects of sputtering power and pres-sure on the microstructure and electromagnetic properties of the films were investigated.As the sputtering power increases from 15 to 60 W,the Co thin films transition from an amorphous to a polycrystalline state,accompanied by an increase in the intercrystal pore width.Simultaneously,the resistivity decreases from 276 to 99μΩ·cm,coercivity increases from 162 to 293 Oe,and in-plane magnetic aniso-tropy disappears.As the sputtering pressure decreases from 1.6 to 0.2 Pa,grain size significantly increases,resistivity significantly de-creases,and the coercivity significantly increases(from 67 to 280 Oe),which can be attributed to the increase in defect width.Corres-pondingly,a quantitative model for the coercivity of Co thin films was formulated.The polycrystalline films sputtered under pressures of 0.2 and 0.4 Pa exhibit significant in-plane magnetic anisotropy,which is primarily attributable to increased microstress.展开更多
Magnetron sputtering deposition with regulated Cu target power was used for depositing Cu-containing high-entropy alloy nitride(Cu-(HEA)N)films on TC4 titanium alloy substrates.The microscopic morphologies,surface com...Magnetron sputtering deposition with regulated Cu target power was used for depositing Cu-containing high-entropy alloy nitride(Cu-(HEA)N)films on TC4 titanium alloy substrates.The microscopic morphologies,surface compositions,and thicknesses of the films were characterized using SEM+EDS;the anti-corrosion,wear resistance and antibacterial properties of the films in simulated seawater were investigated.The experimental results show that all four Cu-(HEA)N films are uniformly dense and contained nanoparticles.The film with Cu doping come into contact with oxygen in the air to form cuprous oxide.The corrosion resistance of the(HEA)N film without Cu doping on titanium alloy is better than the films with Cu doping.The Cu-(HEA)N film with Cu target power of 16 W shows the best wear resistance and antibacterial performance,which is attributed to the fact that Cu can reduce the coefficient of friction and exacerbate corrosion,and the formation of cuprous oxide has antibacterial properties.The findings of this study provide insights for engineering applications of TC4 in the marine field.展开更多
This study delves into ion behavior at the substrate position within RF magnetron discharges utilizing an indium tin oxide(ITO)target.The positive ion energies exhibit an upward trajectory with increasing RF power,att...This study delves into ion behavior at the substrate position within RF magnetron discharges utilizing an indium tin oxide(ITO)target.The positive ion energies exhibit an upward trajectory with increasing RF power,attributed to heightened plasma potential and initial emergent energy.Simultaneously,the positive ion flux escalates owing to amplified sputtering rates and electron density.Conversely,negative ions exhibit broad ion energy distribution functions(IEDFs)characterized by multiple peaks.These patterns are clarified by a combination of radiofrequency oscillation of cathode voltage and plasma potential,alongside ion transport time.This elucidation finds validation in a one-dimensional model encompassing the initial ion energy.At higher RF power,negative ions surpassing 100 e V escalate in both flux and energy,posing a potential risk of sputtering damages to ITO layers.展开更多
The mechanical and frictional properties of ta-C coatings deposited on the substrate surface affect applications in the field of cutting tools and wear-resistant components.In this paper,the effect of bias parameters ...The mechanical and frictional properties of ta-C coatings deposited on the substrate surface affect applications in the field of cutting tools and wear-resistant components.In this paper,the effect of bias parameters on the performance of ta-C coatings was investigated based on high power impulse magnetron sputtering(HiPIMS)technology.The results show that bias voltage has a significant effect on the deposition rate,structure,and wear resistance of the coating.In the range of bias voltage−50 V to−200 V,the ta-C coating performance was the best under bias voltage−150 V.The thickness reached 530.4 nm,the hardness value reached 35.996 GPa,and the bonding force in-creased to 14.2 N.The maximum sp3 bond content was 59.53% at this condition.展开更多
To achieve high microwave permeability in wide-band for the micron-thick magnetic films,[Fe-Fe_(20)Ni_(80)/Cr]_(n) multilayer structure was proposed by co-sputtering Fe and FeNi to form the magnetic layers and Cr to f...To achieve high microwave permeability in wide-band for the micron-thick magnetic films,[Fe-Fe_(20)Ni_(80)/Cr]_(n) multilayer structure was proposed by co-sputtering Fe and FeNi to form the magnetic layers and Cr to form the interlayers.The multilayer structure contributes to the high permeability by reducing the coercivity and diminishing out-of-plane magnetization.The maximum imaginary permeability of[Fe-Fe_(20)Ni_(80)/Cr]_(n) multilayer film reaches a large value of 800 at 0.52 GHz even though its overall thickness exceeds 1μm.Besides,the magnetic resonance frequency of the multilayer film can be modulated from 0.52 to 1.35 GHz by adjusting the sputtering power of Fe from 0 to 86 W,and its bandwidth for μ’’>200(Δf) is as large as 2.0 GHz.The desirable broad Δf of magnetic permeability,which can be well fitted by the Landau-Lifshitz-Gilbert equations,is due to dual magnetic resonances originated from double magnetic phases of Fe and FeNi that are of different saturation magnetization.The micron-thick multilayer films with high permeability in extended waveband are promising candidate for electromagnetic noise suppression application.展开更多
Al_(1-x)In_(x)N, a Ⅲ-nitride semiconductor material, is currently of great research interest due to its remarkable physical properties and chemical stability. When the Al and In compositions are tuned, its band-gap e...Al_(1-x)In_(x)N, a Ⅲ-nitride semiconductor material, is currently of great research interest due to its remarkable physical properties and chemical stability. When the Al and In compositions are tuned, its band-gap energy varies from 0.7 eV to 6.2 eV, which shows great potential for application in photodetectors. Here, we report the fabrication and performance evaluation of integrated Al_(1-x)In_(x)N on a free-standing GaN substrate through direct radio-frequency magnetron sputtering.The optical properties of Al_(1-x)In_(x)N will be enhanced by the polarization effect of a heterostructure composed of Al_(1-x)In_(x)N and other Ⅲ-nitride materials. An Al_(1-x)In_(x)N/Ga N visible-light photodetector was prepared by semiconductor fabrication technologies such as lithography and metal deposition. The highest photoresponsivity achieved was 1.52 A·W^(-1)under 365 nm wavelength illumination and the photodetector was determined to have the composition Al0.75In0.25N/GaN.A rise time of 0.55 s was observed after transient analysis of the device. The prepared Al_(1-x)In_(x)N visible-light photodetector had a low dark current, high photoresponsivity and fast response speed. By promoting a low-cost, simple fabrication method,this study expands the application of ternary alloy Al_(1-x)In_(x)N visible-light photodetectors in optical communication.展开更多
We deposited indium-tin-oxide(ITO)films on silicon and quartz substrates by magnetron sputtering technology in pure argon.Using electrostatic quadrupole plasma diagnostic technology,we investigate the effects of disch...We deposited indium-tin-oxide(ITO)films on silicon and quartz substrates by magnetron sputtering technology in pure argon.Using electrostatic quadrupole plasma diagnostic technology,we investigate the effects of discharge power and discharge pressure on the ion flux and energy distribution function of incidence on the substrate surface,with special attention to the production of high-energy negative oxygen ions,and elucidate the mechanism behind its production.At the same time,the structure and properties of ITO films are systematically characterized to understand the potential effects of high energy oxygen ions on the growth of ITO films.Combining with the kinetic property analysis of sputtering damage mechanism of transparent conductive oxide(TCO)thin films,this study provides valuable physical understanding of optimization of TCO thin film deposition process.展开更多
Cadmium sulfide(CdS)is an n-type semiconductor with excellent electrical conductivity that is widely used as an electron transport material(ETM)in solar cells.At present,numerous methods for preparing CdS thin films h...Cadmium sulfide(CdS)is an n-type semiconductor with excellent electrical conductivity that is widely used as an electron transport material(ETM)in solar cells.At present,numerous methods for preparing CdS thin films have emerged,among which magnetron sputtering(MS)is one of the most commonly used vacuum techniques.For this type of technique,the substrate temperature is one of the key deposition parameters that affects the interfacial properties between the target film and substrate,determining the specific growth habits of the films.Herein,the effect of substrate temperature on the microstructure and electrical properties of magnetron-sputtered CdS(MS-CdS)films was studied and applied for the first time in hydrothermally deposited antimony selenosulfide(Sb_(2)(S,Se)_(3))solar cells.Adjusting the substrate temperature not only results in the design of the flat and dense film with enhanced crystallinity but also leads to the formation of an energy level arrangement with a Sb_(2)(S,Se)_(3)layer that is more favorable for electron transfer.In addition,we developed an oxygen plasma treatment for CdS,reducing the parasitic absorption of the device and resulting in an increase in the short-circuit current density of the solar cell.This study demonstrates the feasibility of MS-CdS in the fabrication of hydrothermal Sb_(2)(S,Se)_(3)solar cells and provides interface optimization strategies to improve device performance.展开更多
One-dimensional ZnO nanorods are synthesized by ox idating thin metal zinc films deposited on Si(111) substrates with radio frequen cy magnetron sputtering.The crystal structure,surface morphology,and optical pro per...One-dimensional ZnO nanorods are synthesized by ox idating thin metal zinc films deposited on Si(111) substrates with radio frequen cy magnetron sputtering.The crystal structure,surface morphology,and optical pro perties of nanorods are investigated.X-ray diffraction(XRD) pattern,scanning el ectron microscopy(SEM),and transmission electron microscopy(TEM) analyses show t hat the synthesized single-crystal ZnO nanorods develop like hairpins along dif ferent radials,with a hexagonal wurtzite structure.The diameters of nanorods ran ge between 30 and 60nm and lengths up to micrometers.Photoluminescence(PL) analy sis shows that,under 280nm light excitation,a strong and sharp near band-edge U V light emission band at 372nm and a relatively weak green deep-level light emi ssion band at 516nm are observed from the ZnO nanorods,which indicates excellent crystallization and optical quality of the fabricated ZnO nanorods.展开更多
Al-doped ZnO thin films were prepared on glass substrate using an ultra-high density target by RF magnetron sputtering at room temperature. The microstructure, surface morphology, optical and electrical properties of ...Al-doped ZnO thin films were prepared on glass substrate using an ultra-high density target by RF magnetron sputtering at room temperature. The microstructure, surface morphology, optical and electrical properties of AZO thin films were investigated by X-ray diffractometer, scanning electron microscope, UV-visible spectrophotometer, four-point probe method, and Hall-effect measurement system. The results showed that all the films obtained were polycrystalline with a hexagonal structure and average optical transmittance of AZO thin films was over 85 % at different sputtering powers. The sputtering power had a great effect on optoelectronic properties of the AZO thin films, especially on the resistivity. The lowest resistivity of 4.5×10^-4 Ω·cm combined with the transmittance of 87.1% was obtained at sputtering power of 200 W. The optical band gap varied between 3.48 and 3.68 eV.展开更多
In order to study the effect of the microstructure with Al and V added TiN coatings, TiN, TiAlN and TiAlVN coatings were deposited on AISI M2 high-speed steels by magnetron reactive sputtering. The microstructures of ...In order to study the effect of the microstructure with Al and V added TiN coatings, TiN, TiAlN and TiAlVN coatings were deposited on AISI M2 high-speed steels by magnetron reactive sputtering. The microstructures of all the coatings were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results indicate that the addition of Al into TiN coatings reduces their lattice constant, but a further addition of V into TiAlN coatings increases their lattice constant. Moreover, the growth morphologies for TiN, TiAlN, and TiAlVN indicate that adding Al and V has a tendency to improve the columnar structure. The (111) and (200) orientations of TiN, TiAlN, and TiAlVN are identified. Theε(Fe3N-Fe2N) phase occurs because a small amount of Fe is present in the coatings. The interlayers of TiAlN and TiAlVN have the preferred (01 1 0) orientation. The texture (columnar) structure of the (111) and (200) orientations is observed in the TiAlN and TiAlVN coatings. An orientation relationship of (01 1 0)α-Ti//(110)T.M occurs between the interlayer and tempered martensite (T.M) in TiAlVN.展开更多
Wurtzite aluminum nitride（AlN） films were deposited on Si（100） wafers under various sputtering pressures by radio-frequency（RF） reactive magnetron sputtering. The film properties were investigated by XRD, SEM, A...Wurtzite aluminum nitride（AlN） films were deposited on Si（100） wafers under various sputtering pressures by radio-frequency（RF） reactive magnetron sputtering. The film properties were investigated by XRD, SEM, AFM, XPS and nanoindenter techniques. It is suggested from the XRD patterns that highly c-axis oriented films grow preferentially at low pressures and the growth of（100） planes are preferred at higher pressures. The SEM and AFM images both reveal that the deposition rate and the surface roughness decrease while the average grain size increases with increasing the sputtering pressure. XPS results show that lowering the sputtering pressure is a useful way to minimize the incorporation of oxygen atoms into the AlN films and hence a film with closer stoichiometric composition is obtained. From the measurement of nanomechanical properties of AlN thin films, the largest hardness and elastic modulus are obtained at 0.30 Pa.展开更多
Nano-scaled ZrNbAlN films with different negative bias voltages（Vb） were deposited on bronze substrate and Si（100） wafers by a reactive unbalanced magnetron sputtering technique. Composition and structure properti...Nano-scaled ZrNbAlN films with different negative bias voltages（Vb） were deposited on bronze substrate and Si（100） wafers by a reactive unbalanced magnetron sputtering technique. Composition and structure properties were characterized by X-ray photoelectron spectroscopy and X-ray diffraction. It is found that mole concentrations of Zr and Nb are affected by Vb, which leads to the increase of binding energy of N 1s and Al 2p and decrease of binding energy of Zr 3d5/2 and Nb 3d5/2. Surface morphologies evolution controlled by Vb could be observed. Furthermore, X-ray diffraction patterns reveal that these films show a（111） preferred orientation. Moreover, mechanical property and corrosion behavior of ZrNbAlN films were characterized by nanoindentation test and corrosion test, respectively. A maximum value of 21.85 GPa at-70 V occurs in the ZrNbAlN- bronze system, which outperforms uncoated bronze. Corrosion experiments in 0.5 mol/L NaCl and 0.5 mol/L HCl solution show that corrosion potential and corrosion current are dependent on Vb, and better anti-corrosion property could be obtained at-90 V.展开更多
A kind of W/DLC/W-S-C composite film was fabricated by magnetron sputtering method.Effects of WSx content on the structure and the adhesion of the composite films were investigated.In addition,tribological behavior of...A kind of W/DLC/W-S-C composite film was fabricated by magnetron sputtering method.Effects of WSx content on the structure and the adhesion of the composite films were investigated.In addition,tribological behavior of the composite films was studied in the conditions of the ambient air and N2 gas atmosphere by ball-on-disk tester.The results indicate that the composite films show dense and amorphous microstructure.The WCx and WSx compounds are found in amorphous diamond like carbon matrix in the top layers of W-S-C.A proper WSx content is beneficial for improving the adhesion of the composite films.In air atmosphere,the composite films with high C content have better wear resistance and the friction coefficients range from 0.15 to 0.25.In N2 condition,high WSx content is benefit for the wear resistance and the friction coefficients of the composite films range from 0.03 to 0.1.展开更多
Zinc nitride （Zn3N2） thin films were prepared by radio frequency （RF） magnetron sputtering on quartz glass at different substrate temperatures.The structure and composition were characterized by X-ray diffraction ...Zinc nitride （Zn3N2） thin films were prepared by radio frequency （RF） magnetron sputtering on quartz glass at different substrate temperatures.The structure and composition were characterized by X-ray diffraction and Raman-scattering measurements,respectively.The polycrystalline phase Zn3N2 films appeared when the ratio of the N2 partial pressure to the total pressure reached 1/2.The effects of the substrate temperature on the electrical and optical properties of the Zn3N2 films were investigated by Hall measurements and optical transmission spectra.The electrical and optical properties of the films were highly dependent on the substrate temperature.With the substrate temperature increasing from 100 to 300℃,the resistivity of the Zn3N2 films decreased from 0.49 to 0.023Ω·cm,the carrier concentration increased from 2.7×10^16 to 8.2×10^19cm^-3,and the electron mobility decreased from 115 to 32cm^2/（V·s）.The deposited Zn3N2 films were considered to be n-type semiconductors with a direct optical band gap,which was around 1.23eV when the substrate temperature was 200℃.展开更多
基金This work was financially supported by the National Defence Science Council of China (NO. 5141002040JW0504) and the Excellent Ph.D Thesis Foundation of Huazhong University of Science and Technology (No. HUST2004-39).
文摘Tin-doped indium oxide （ITO） thin films were prepared using conventional radio frequency （RF） planar magnetron sputtering equipped with IR irradiation using a ceramic target of In2O3/SnO2 with a mass ratio of 1：1 at various IR irradiation temperatures T1 （from room temperature to 400℃）. The refractive index, deposited ratio, and resistivity are functions of the sputtering Ar gas pressure. The microstructure of ITO thin films is related to IR T1, the crystalline seeds appear at T1= 300℃, and the films are amorphous at the temperature ranging from 27℃ to 400℃. AFM investigation shows that the roughness value of peak-valley of ITO thin film （Rp-v） and the surface microstructure of rio thin films have a close relation with T1. The IR irradiation results in a widening value of band-gap energy due to Burstein-Moss effect and the maximum visible transmittance shifts toward a shorter wavelength along with a decrease in the film＇s refractive index. The plasma wavelength and the refractive index of ITO thin films are relative to the T1. XPS investigation shows that the photoelectrolytic properties can be deteriorated by the sub-oxides. The deterioration can be decreased by increasing the oxygen flow rote （fo2）, and the mole ratio of Sn/In in the samples reduces with an increase info2.
文摘Pt/Ti bottom electrodes were fabricated on SiO2/Si substrates by magnetron dual-facingtarget sputtering system. Lead zirconate titanate（PZT） thin films were deposited on Pt/Ti/SiO2/Si substrates by radio frequency （RF） magnetron sputtering system. The thickness of PZT thin films which were deposited for 5 h was about 800 nm. XRD spectra show that PZT thin films deposited in Ar ambience and rapid-thermal-annealed for 20 min at 700 ℃ have good crystallization behavior and perovskite structure. AFM micrographs show that mean diameter of crystallites is 70 nm and surface structures of PZT thin films are uniform and dense. Raw mean, root mean square roughness and mean roughness of PZT thin films are 34..357 rim, 2. 479 nm and 1. 954 nm respectively. As test frequency is 1 kHz, dielectric constant of PZT thin films is 327.5. Electric hysteresis loop shows that coercive field strength, residual polarization strength and spontaneous polarization strength of PZT thin films are 50 kV/cm, 10μC/cm^2 and 13μC/cm^2 respectively.
文摘Tin-doped indium oxide （ITO） thin films were prepared using conventional radio frequency （RF） planar magnetron sputtering equipped with IR irradiation using a ceramic target of In2O3/SnO2 with a mass ratio of 1∶1 at various IR irradiation temperatures T1 （from room temperature to 400?℃）. The refractive index,deposited ratio,and resistivity are functions of the sputtering Ar gas pressure. The microstructure of ITO thin films is related to IR T1,the crystalline seeds appear at T1=300?℃,and the films are amorphous at the temperature ranging from 27?℃ to 400?℃. AFM investigation shows that the roughness value of peak-valley of ITO thin film （R p-v ） and the surface microstructure of ITO thin films have a close relation with T1. The IR irradiation results in a widening value of band-gap energy due to Burstein-Moss effect and the maximum visible transmittance shifts toward a shorter wavelength along with a decrease in the film’s refractive index. The plasma wavelength and the refractive index of ITO thin films are relative to the T1. XPS investigation shows that the photoelectrolytic properties can be deteriorated by the sub-oxides. The deterioration can be decreased by increasing the oxygen flow rate （fo2）,and the mole ratio of Sn/In in the samples reduces with an increase in fo2.
基金supported by the Research Foundation of Liaocheng University(No.318051939)Opening Project of Beijing Key Laboratory of Digital Stomatology(PKUSS20210301)+1 种基金Natural Science Foundation of Shandong Province of China(Nos.ZR2020ME031,ZR2020ME033)Innovation Team of Higher Educational Science and Technology Program in Shandong Province(No.2019KJA025).
文摘Bi_(3.25)La_(0.75)Ti_(3)O_(12)(BLT)thin films are promising materials used in non-volatile memories.In this work,BLT films were deposited on Pt(111)/Ti/SiO_(2)/Si substrates by rf-magnetron sputtering method followed by annealing treatments.The microstructures of BLT thin films were investigated via X-ray diffraction(XRD),scanning electron microscopy(SEM)and atomic force microscopy(AFM).With the increase in annealing temperature,the grain size increased significantly and the preferred crystalline orientation changed.A well-saturated hysteresis loop with a superior remnant polarization of 15.4μC/cm^(2) was obtained for BLT thin films annealed at 700°C.The results show that the dielectric constant decreased with the increase in grain sizes.
基金Funded by Shenzhen-Hong Kong Innovative Collaborative Research and Development Program (Nos.SGLH20181109 110802117, CityU 9240014)Innovation Project of Southwestern Institute of Physics (Nos.202001XWCXYD002, 202301XWCX003)CNNC Young Talent Program (No.2023JZYF-01)。
文摘Surface metallization of glass fiber(GF)/polyetheretherketone(PEEK)[GF/PEEK] is conducted by coating copper using electroplating and magnetron sputtering and the properties are determined by X-ray diffraction(XRD), scanning electron microscopy(SEM), and electron backscatter diffraction(EBSD).The coating bonding strength is assessed by pull-out tests and scribing in accordance with GB/T 9286-1998.The results show that the Cu coating with a thickness of 30 μm deposited on GF/PEEK by magnetron sputtering has lower roughness, finer grain size, higher crystallinity, as well as better macroscopic compressive stress,bonding strength, and electrical conductivity than the Cu coating deposited by electroplating.
基金the financial support from the National Key Research and Development Program of China(No.2017YFB0305500)the State Key Laboratory of Powder Metallurgy,Central South University,Changsha,China.
文摘Pure cobalt(Co)thin films were fabricated by direct current magnetron sputtering,and the effects of sputtering power and pres-sure on the microstructure and electromagnetic properties of the films were investigated.As the sputtering power increases from 15 to 60 W,the Co thin films transition from an amorphous to a polycrystalline state,accompanied by an increase in the intercrystal pore width.Simultaneously,the resistivity decreases from 276 to 99μΩ·cm,coercivity increases from 162 to 293 Oe,and in-plane magnetic aniso-tropy disappears.As the sputtering pressure decreases from 1.6 to 0.2 Pa,grain size significantly increases,resistivity significantly de-creases,and the coercivity significantly increases(from 67 to 280 Oe),which can be attributed to the increase in defect width.Corres-pondingly,a quantitative model for the coercivity of Co thin films was formulated.The polycrystalline films sputtered under pressures of 0.2 and 0.4 Pa exhibit significant in-plane magnetic anisotropy,which is primarily attributable to increased microstress.
基金Funded by the National Natural Science Foundation of China(No.52071252)the Key Research and Development Plan of Shaanxi Province Industrial Project(Nos.2021GY-208,2022GY-407,and 2021ZDLSF03-11)the China Postdoctoral Science Foundation(No.2020M683670XB)。
文摘Magnetron sputtering deposition with regulated Cu target power was used for depositing Cu-containing high-entropy alloy nitride(Cu-(HEA)N)films on TC4 titanium alloy substrates.The microscopic morphologies,surface compositions,and thicknesses of the films were characterized using SEM+EDS;the anti-corrosion,wear resistance and antibacterial properties of the films in simulated seawater were investigated.The experimental results show that all four Cu-(HEA)N films are uniformly dense and contained nanoparticles.The film with Cu doping come into contact with oxygen in the air to form cuprous oxide.The corrosion resistance of the(HEA)N film without Cu doping on titanium alloy is better than the films with Cu doping.The Cu-(HEA)N film with Cu target power of 16 W shows the best wear resistance and antibacterial performance,which is attributed to the fact that Cu can reduce the coefficient of friction and exacerbate corrosion,and the formation of cuprous oxide has antibacterial properties.The findings of this study provide insights for engineering applications of TC4 in the marine field.
基金financial supports by National Natural Science Foundation of China(Nos.11975163 and 12175160)Nantong Basic Science Research-General Program(No.JC22022034)Natural Science Research Fund of Jiangsu College of Engineering and Technology(No.GYKY/2023/2)。
文摘This study delves into ion behavior at the substrate position within RF magnetron discharges utilizing an indium tin oxide(ITO)target.The positive ion energies exhibit an upward trajectory with increasing RF power,attributed to heightened plasma potential and initial emergent energy.Simultaneously,the positive ion flux escalates owing to amplified sputtering rates and electron density.Conversely,negative ions exhibit broad ion energy distribution functions(IEDFs)characterized by multiple peaks.These patterns are clarified by a combination of radiofrequency oscillation of cathode voltage and plasma potential,alongside ion transport time.This elucidation finds validation in a one-dimensional model encompassing the initial ion energy.At higher RF power,negative ions surpassing 100 e V escalate in both flux and energy,posing a potential risk of sputtering damages to ITO layers.
基金supported by the National Key R&D Program of China(No.2019YFE0123900)the National Natural Sci-ence Foundation of China(Grant No.51974069)the Special Fund for Basic Scientific Research of Central Colleges(N2125035).
文摘The mechanical and frictional properties of ta-C coatings deposited on the substrate surface affect applications in the field of cutting tools and wear-resistant components.In this paper,the effect of bias parameters on the performance of ta-C coatings was investigated based on high power impulse magnetron sputtering(HiPIMS)technology.The results show that bias voltage has a significant effect on the deposition rate,structure,and wear resistance of the coating.In the range of bias voltage−50 V to−200 V,the ta-C coating performance was the best under bias voltage−150 V.The thickness reached 530.4 nm,the hardness value reached 35.996 GPa,and the bonding force in-creased to 14.2 N.The maximum sp3 bond content was 59.53% at this condition.
基金Funded by the Young Top-notch Talent Cultivation Program of Hubei Provincethe Fundamental Research Funds for the Central Universities(WUT:2021IVA116 and WUT:2021CG015)。
文摘To achieve high microwave permeability in wide-band for the micron-thick magnetic films,[Fe-Fe_(20)Ni_(80)/Cr]_(n) multilayer structure was proposed by co-sputtering Fe and FeNi to form the magnetic layers and Cr to form the interlayers.The multilayer structure contributes to the high permeability by reducing the coercivity and diminishing out-of-plane magnetization.The maximum imaginary permeability of[Fe-Fe_(20)Ni_(80)/Cr]_(n) multilayer film reaches a large value of 800 at 0.52 GHz even though its overall thickness exceeds 1μm.Besides,the magnetic resonance frequency of the multilayer film can be modulated from 0.52 to 1.35 GHz by adjusting the sputtering power of Fe from 0 to 86 W,and its bandwidth for μ’’>200(Δf) is as large as 2.0 GHz.The desirable broad Δf of magnetic permeability,which can be well fitted by the Landau-Lifshitz-Gilbert equations,is due to dual magnetic resonances originated from double magnetic phases of Fe and FeNi that are of different saturation magnetization.The micron-thick multilayer films with high permeability in extended waveband are promising candidate for electromagnetic noise suppression application.
基金Project supported by the National Natural Science Foundation of China (Grant Nos. 61974144, 62004127, and 12074263)Key-Area Research and Development Program of Guangdong Province (Grant Nos. 2020B010174003 and 2020B010169001)+2 种基金Guangdong Science Foundation for Distinguished Young Scholars (Grant No. 2022B1515020073)the Science and Technology Foundation of Shenzhen (Grant No. JSGG20191129114216474)the Open Project of State Key Laboratory of Functional Materials for Informatics。
文摘Al_(1-x)In_(x)N, a Ⅲ-nitride semiconductor material, is currently of great research interest due to its remarkable physical properties and chemical stability. When the Al and In compositions are tuned, its band-gap energy varies from 0.7 eV to 6.2 eV, which shows great potential for application in photodetectors. Here, we report the fabrication and performance evaluation of integrated Al_(1-x)In_(x)N on a free-standing GaN substrate through direct radio-frequency magnetron sputtering.The optical properties of Al_(1-x)In_(x)N will be enhanced by the polarization effect of a heterostructure composed of Al_(1-x)In_(x)N and other Ⅲ-nitride materials. An Al_(1-x)In_(x)N/Ga N visible-light photodetector was prepared by semiconductor fabrication technologies such as lithography and metal deposition. The highest photoresponsivity achieved was 1.52 A·W^(-1)under 365 nm wavelength illumination and the photodetector was determined to have the composition Al0.75In0.25N/GaN.A rise time of 0.55 s was observed after transient analysis of the device. The prepared Al_(1-x)In_(x)N visible-light photodetector had a low dark current, high photoresponsivity and fast response speed. By promoting a low-cost, simple fabrication method,this study expands the application of ternary alloy Al_(1-x)In_(x)N visible-light photodetectors in optical communication.
基金supported by the National Key R&D Program of China(Grant No.2022YFE03050001)the National Natural Science Foundation of China(Grant Nos.12175160 and 12305284).The authors thank Suzhou Maxwell Technologies Co.,Ltd.for partial hardware and particle financial support to carry out the research.
文摘We deposited indium-tin-oxide(ITO)films on silicon and quartz substrates by magnetron sputtering technology in pure argon.Using electrostatic quadrupole plasma diagnostic technology,we investigate the effects of discharge power and discharge pressure on the ion flux and energy distribution function of incidence on the substrate surface,with special attention to the production of high-energy negative oxygen ions,and elucidate the mechanism behind its production.At the same time,the structure and properties of ITO films are systematically characterized to understand the potential effects of high energy oxygen ions on the growth of ITO films.Combining with the kinetic property analysis of sputtering damage mechanism of transparent conductive oxide(TCO)thin films,this study provides valuable physical understanding of optimization of TCO thin film deposition process.
基金supported by the National Natural Science Foundation of China(22275180)the National Key Research and Development Program of China(2019YFA0405600)the Collaborative Innovation Program of Hefei Science Center,CAS,and the University Synergy Innovation Program of Anhui Province(GXXT-2023-031).
文摘Cadmium sulfide(CdS)is an n-type semiconductor with excellent electrical conductivity that is widely used as an electron transport material(ETM)in solar cells.At present,numerous methods for preparing CdS thin films have emerged,among which magnetron sputtering(MS)is one of the most commonly used vacuum techniques.For this type of technique,the substrate temperature is one of the key deposition parameters that affects the interfacial properties between the target film and substrate,determining the specific growth habits of the films.Herein,the effect of substrate temperature on the microstructure and electrical properties of magnetron-sputtered CdS(MS-CdS)films was studied and applied for the first time in hydrothermally deposited antimony selenosulfide(Sb_(2)(S,Se)_(3))solar cells.Adjusting the substrate temperature not only results in the design of the flat and dense film with enhanced crystallinity but also leads to the formation of an energy level arrangement with a Sb_(2)(S,Se)_(3)layer that is more favorable for electron transfer.In addition,we developed an oxygen plasma treatment for CdS,reducing the parasitic absorption of the device and resulting in an increase in the short-circuit current density of the solar cell.This study demonstrates the feasibility of MS-CdS in the fabrication of hydrothermal Sb_(2)(S,Se)_(3)solar cells and provides interface optimization strategies to improve device performance.
文摘One-dimensional ZnO nanorods are synthesized by ox idating thin metal zinc films deposited on Si(111) substrates with radio frequen cy magnetron sputtering.The crystal structure,surface morphology,and optical pro perties of nanorods are investigated.X-ray diffraction(XRD) pattern,scanning el ectron microscopy(SEM),and transmission electron microscopy(TEM) analyses show t hat the synthesized single-crystal ZnO nanorods develop like hairpins along dif ferent radials,with a hexagonal wurtzite structure.The diameters of nanorods ran ge between 30 and 60nm and lengths up to micrometers.Photoluminescence(PL) analy sis shows that,under 280nm light excitation,a strong and sharp near band-edge U V light emission band at 372nm and a relatively weak green deep-level light emi ssion band at 516nm are observed from the ZnO nanorods,which indicates excellent crystallization and optical quality of the fabricated ZnO nanorods.
基金supported by open research fund from Guangxi Key Laboratory of New Energy and Building Energy Saving, China
文摘Al-doped ZnO thin films were prepared on glass substrate using an ultra-high density target by RF magnetron sputtering at room temperature. The microstructure, surface morphology, optical and electrical properties of AZO thin films were investigated by X-ray diffractometer, scanning electron microscope, UV-visible spectrophotometer, four-point probe method, and Hall-effect measurement system. The results showed that all the films obtained were polycrystalline with a hexagonal structure and average optical transmittance of AZO thin films was over 85 % at different sputtering powers. The sputtering power had a great effect on optoelectronic properties of the AZO thin films, especially on the resistivity. The lowest resistivity of 4.5×10^-4 Ω·cm combined with the transmittance of 87.1% was obtained at sputtering power of 200 W. The optical band gap varied between 3.48 and 3.68 eV.
文摘In order to study the effect of the microstructure with Al and V added TiN coatings, TiN, TiAlN and TiAlVN coatings were deposited on AISI M2 high-speed steels by magnetron reactive sputtering. The microstructures of all the coatings were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results indicate that the addition of Al into TiN coatings reduces their lattice constant, but a further addition of V into TiAlN coatings increases their lattice constant. Moreover, the growth morphologies for TiN, TiAlN, and TiAlVN indicate that adding Al and V has a tendency to improve the columnar structure. The (111) and (200) orientations of TiN, TiAlN, and TiAlVN are identified. Theε(Fe3N-Fe2N) phase occurs because a small amount of Fe is present in the coatings. The interlayers of TiAlN and TiAlVN have the preferred (01 1 0) orientation. The texture (columnar) structure of the (111) and (200) orientations is observed in the TiAlN and TiAlVN coatings. An orientation relationship of (01 1 0)α-Ti//(110)T.M occurs between the interlayer and tempered martensite (T.M) in TiAlVN.
基金Project(21271188)supported by the National Natural Science Foundation of ChinaProject(2012M521541)supported by the China Postdoctoral Science Foundation+2 种基金Project(2012QNZT002)supported by the Fundamental Research Funds for the Central South Universities,ChinaProject(20110933K)supported by the State Key Laboratory of Powder Metallurgy,ChinaProject(CSU2012024)supported by the Open-End Fund for Valuable and Precision Instruments of Central South University,China
文摘Wurtzite aluminum nitride（AlN） films were deposited on Si（100） wafers under various sputtering pressures by radio-frequency（RF） reactive magnetron sputtering. The film properties were investigated by XRD, SEM, AFM, XPS and nanoindenter techniques. It is suggested from the XRD patterns that highly c-axis oriented films grow preferentially at low pressures and the growth of（100） planes are preferred at higher pressures. The SEM and AFM images both reveal that the deposition rate and the surface roughness decrease while the average grain size increases with increasing the sputtering pressure. XPS results show that lowering the sputtering pressure is a useful way to minimize the incorporation of oxygen atoms into the AlN films and hence a film with closer stoichiometric composition is obtained. From the measurement of nanomechanical properties of AlN thin films, the largest hardness and elastic modulus are obtained at 0.30 Pa.
基金Project(50725413)supported by the National Natural Science Foundation of ChinaProject(2010BB4290)supported by Natural Science Foundation Project of CQ CSTC,China
文摘Nano-scaled ZrNbAlN films with different negative bias voltages（Vb） were deposited on bronze substrate and Si（100） wafers by a reactive unbalanced magnetron sputtering technique. Composition and structure properties were characterized by X-ray photoelectron spectroscopy and X-ray diffraction. It is found that mole concentrations of Zr and Nb are affected by Vb, which leads to the increase of binding energy of N 1s and Al 2p and decrease of binding energy of Zr 3d5/2 and Nb 3d5/2. Surface morphologies evolution controlled by Vb could be observed. Furthermore, X-ray diffraction patterns reveal that these films show a（111） preferred orientation. Moreover, mechanical property and corrosion behavior of ZrNbAlN films were characterized by nanoindentation test and corrosion test, respectively. A maximum value of 21.85 GPa at-70 V occurs in the ZrNbAlN- bronze system, which outperforms uncoated bronze. Corrosion experiments in 0.5 mol/L NaCl and 0.5 mol/L HCl solution show that corrosion potential and corrosion current are dependent on Vb, and better anti-corrosion property could be obtained at-90 V.
文摘A kind of W/DLC/W-S-C composite film was fabricated by magnetron sputtering method.Effects of WSx content on the structure and the adhesion of the composite films were investigated.In addition,tribological behavior of the composite films was studied in the conditions of the ambient air and N2 gas atmosphere by ball-on-disk tester.The results indicate that the composite films show dense and amorphous microstructure.The WCx and WSx compounds are found in amorphous diamond like carbon matrix in the top layers of W-S-C.A proper WSx content is beneficial for improving the adhesion of the composite films.In air atmosphere,the composite films with high C content have better wear resistance and the friction coefficients range from 0.15 to 0.25.In N2 condition,high WSx content is benefit for the wear resistance and the friction coefficients of the composite films range from 0.03 to 0.1.
文摘Zinc nitride （Zn3N2） thin films were prepared by radio frequency （RF） magnetron sputtering on quartz glass at different substrate temperatures.The structure and composition were characterized by X-ray diffraction and Raman-scattering measurements,respectively.The polycrystalline phase Zn3N2 films appeared when the ratio of the N2 partial pressure to the total pressure reached 1/2.The effects of the substrate temperature on the electrical and optical properties of the Zn3N2 films were investigated by Hall measurements and optical transmission spectra.The electrical and optical properties of the films were highly dependent on the substrate temperature.With the substrate temperature increasing from 100 to 300℃,the resistivity of the Zn3N2 films decreased from 0.49 to 0.023Ω·cm,the carrier concentration increased from 2.7×10^16 to 8.2×10^19cm^-3,and the electron mobility decreased from 115 to 32cm^2/（V·s）.The deposited Zn3N2 films were considered to be n-type semiconductors with a direct optical band gap,which was around 1.23eV when the substrate temperature was 200℃.