Pure cobalt(Co)thin films were fabricated by direct current magnetron sputtering,and the effects of sputtering power and pres-sure on the microstructure and electromagnetic properties of the films were investigated.As...Pure cobalt(Co)thin films were fabricated by direct current magnetron sputtering,and the effects of sputtering power and pres-sure on the microstructure and electromagnetic properties of the films were investigated.As the sputtering power increases from 15 to 60 W,the Co thin films transition from an amorphous to a polycrystalline state,accompanied by an increase in the intercrystal pore width.Simultaneously,the resistivity decreases from 276 to 99μΩ·cm,coercivity increases from 162 to 293 Oe,and in-plane magnetic aniso-tropy disappears.As the sputtering pressure decreases from 1.6 to 0.2 Pa,grain size significantly increases,resistivity significantly de-creases,and the coercivity significantly increases(from 67 to 280 Oe),which can be attributed to the increase in defect width.Corres-pondingly,a quantitative model for the coercivity of Co thin films was formulated.The polycrystalline films sputtered under pressures of 0.2 and 0.4 Pa exhibit significant in-plane magnetic anisotropy,which is primarily attributable to increased microstress.展开更多
We measure the time-resolved terahertz spectroscopy of GeSn thin film and studied the ultrafast dynamics of its photo-generated carriers.The experimental results show that there are photo-generated carriers in GeSn un...We measure the time-resolved terahertz spectroscopy of GeSn thin film and studied the ultrafast dynamics of its photo-generated carriers.The experimental results show that there are photo-generated carriers in GeSn under femtosecond laser excitation at 2500 nm,and its pump-induced photoconductivity can be explained by the Drude–Smith model.The carrier recombination process is mainly dominated by defect-assisted Auger processes and defect capture.The firstand second-order recombination rates are obtained by the rate equation fitting,which are(2.6±1.1)×10^(-2)ps^(-1)and(6.6±1.8)×10^(-19)cm^(3)·ps^(-1),respectively.Meanwhile,we also obtain the diffusion length of photo-generated carriers in GeSn,which is about 0.4μm,and it changes with the pump delay time.These results are important for the GeSn-based infrared optoelectronic devices,and demonstrate that Ge Sn materials can be applied to high-speed optoelectronic detectors and other applications.展开更多
AlN was used as a host material and doped with Eu grown on Si substrate by pulsed laser deposition (PLD) with low substrate temperature. The X-ray diffraction (XRD) data revealed the orientation and the composition of...AlN was used as a host material and doped with Eu grown on Si substrate by pulsed laser deposition (PLD) with low substrate temperature. The X-ray diffraction (XRD) data revealed the orientation and the composition of the thin film. The surface morphology was studied by scanning electron microscope (SEM). While raising the annealing temperatures from 300˚C to 900˚C, the emission was observed from AlN: Eu under excitation of 260 nm excitation. The photoluminescence (PL) was integrated over the visible light wavelength shifted from the blue to the red zone in the CIE 1931 chromaticity coordinates. The luminescence color coordination of AlN: Eu depending on the annealing temperatures guides the further study of Eu-doped nitrides manufacturing on white light emitting diode (LED) and full color LED devices.展开更多
Since the first report of amorphous In–Ga–Zn–O based thin film transistors,interest in oxide semiconductors has grown.They offer high mobility,low off-current,low process temperature,and wide flexibility for compos...Since the first report of amorphous In–Ga–Zn–O based thin film transistors,interest in oxide semiconductors has grown.They offer high mobility,low off-current,low process temperature,and wide flexibility for compositions and processes.Unfortunately,depositing oxide semiconductors using conventional processes like physical vapor deposition leads to problematic issues,especially for high-resolution displays and highly integrated memory devices.Conventional approaches have limited process flexibility and poor conformality on structured surfaces.Atomic layer deposition(ALD)is an advanced technique which can provide conformal,thickness-controlled,and high-quality thin film deposition.Accordingly,studies on ALD based oxide semiconductors have dramatically increased recently.Even so,the relationships between the film properties of ALD-oxide semiconductors and the main variables associated with deposition are still poorly understood,as are many issues related to applications.In this review,to introduce ALD-oxide semiconductors,we provide:(a)a brief summary of the history and importance of ALD-based oxide semiconductors in industry,(b)a discussion of the benefits of ALD for oxide semiconductor deposition(in-situ composition control in vertical distribution/vertical structure engineering/chemical reaction and film properties/insulator and interface engineering),and(c)an explanation of the challenging issues of scaling oxide semiconductors and ALD for industrial applications.This review provides valuable perspectives for researchers who have interest in semiconductor materials and electronic device applications,and the reasons ALD is important to applications of oxide semiconductors.展开更多
Amorphous oxide semiconductors(AOS)have unique advantages in transparent and flexible thin film transistors(TFTs)applications,compared to low-temperature polycrystalline-Si(LTPS).However,intrinsic AOS TFTs are difficu...Amorphous oxide semiconductors(AOS)have unique advantages in transparent and flexible thin film transistors(TFTs)applications,compared to low-temperature polycrystalline-Si(LTPS).However,intrinsic AOS TFTs are difficult to obtain field-effect mobility(μFE)higher than LTPS(100 cm^(2)/(V·s)).Here,we design ZnAlSnO(ZATO)homojunction structure TFTs to obtainμFE=113.8 cm^(2)/(V·s).The device demonstrates optimized comprehensive electrical properties with an off-current of about1.5×10^(-11)A,a threshold voltage of–1.71 V,and a subthreshold swing of 0.372 V/dec.There are two kinds of gradient coupled in the homojunction active layer,which are micro-crystallization and carrier suppressor concentration gradient distribution so that the device can reduce off-current and shift the threshold voltage positively while maintaining high field-effect mobility.Our research in the homojunction active layer points to a promising direction for obtaining excellent-performance AOS TFTs.展开更多
Biodegradable metals as electrodes, interconnectors, and device conductors are essential components in the emergence of transient electronics, either for passive implants or active electronic devices, especially in th...Biodegradable metals as electrodes, interconnectors, and device conductors are essential components in the emergence of transient electronics, either for passive implants or active electronic devices, especially in the fields of biomedical electronics. Magnesium and its alloys are strong candidates for biodegradable and implantable conducting materials because of their high conductivity and biocompatibility, in addition to their well-understood dissolution behavior. One critical drawback of Mg and its alloys is their considerably high dissolution rates originating from their low anodic potential, which disturbs the compatibility to biomedical applications. Herein, we introduce a single-phase thin film of a Mg-Zn binary alloy formed by sputtering, which enhances the corrosion resistance of the device electrode, and verify its applicability in biodegradable electronics. The formation of a homogeneous solid solution of single-phase Mg-3Zn was confirmed through X-ray diffraction and transmission electron microscopy. In addition, the dissolution behavior and chemistry was also investigated in various biological fluids by considering the effect of different ion species. Micro-tensile tests showed that the Mg-3Zn alloy electrode exhibited an enhanced yield strain and elongation in relation to a pure Mg electrode. Cell viability test revealed the high biocompatibility rate of the Mg-3Zn binary alloy thin film. Finally, the fabrication of a wireless heater demonstrated the integrability of biodegradable electrodes and highlighted the ability to prolong the lifecycle of thermotherapy-relevant electronics by enhancing the dissolution resistance of the Mg alloy.展开更多
The effects of radio frequency(RF)atmospheric pressure(AP)He/H_(2)plasma and thermal treatment on the hydrogenation of TiO_(2)thin films were investigated and compared in this work.The color of the original TiO_(2)fil...The effects of radio frequency(RF)atmospheric pressure(AP)He/H_(2)plasma and thermal treatment on the hydrogenation of TiO_(2)thin films were investigated and compared in this work.The color of the original TiO_(2)film changes from white to black after being hydrogenated in He/H_(2)plasma at160 W(gas temperature~381℃)within 5 min,while the color of the thermally treated TiO_(2)film did not change significantly even in pure H_(2)or He/H_(2)atmosphere with higher temperature(470℃)and longer time(30 min).This indicated that a more effective hydrogenation reaction happened through RF AP He/H_(2)plasma treatment than through pure H_(2)or He/H_(2)thermal treatment.The color change of TiO_(2)film was measured based on the Commission Internationale d’Eclairage L*a*b*color space system.Hydrogenated TiO_(2)film displayed improved visible light absorption with increased plasma power.The morphology of the cauliflower-like nanoparticles of the TiO_(2)film surface remained unchanged after plasma processing.X-ray photoelectron spectroscopy results showed that the contents of Ti3+species and Ti-OH bonds in the plasma-hydrogenated black TiO_(2)increased compared with those in the thermally treated TiO_(2).X-ray diffraction(XRD)patterns and Raman spectra indicated that plasma would destroy the crystal structure of the TiO_(2)surface layer,while thermal annealing would increase the overall crystallinity.The different trends of XRD and Raman spectra results suggested that plasma modification on the TiO_(2)surface layer is more drastic than on its inner layer,which was also consistent with transmission electron microscopy results.Optical emission spectra results suggest that numerous active species were generated during RF AP He/H_(2)plasma processing,while there were no peaks detected from thermal processing.A possible mechanism for the TiO_(2)hydrogenation process by plasma has been proposed.Numerous active species were generated in the bulk plasma region,accelerated in the sheath region,and bumped toward the TiO_(2)film,which will react with the TiO_(2)surface to form OVs and disordered layers.This leads to the tailoring of the band gap of black TiO_(2)and causes its light absorption to extend into the visible region.展开更多
As a thin film solar cell absorber material, antimony selenide (Sb<sub>2</sub>Se<sub>3</sub>) has become a potential candidate recently because of its unique optical and electrical properties a...As a thin film solar cell absorber material, antimony selenide (Sb<sub>2</sub>Se<sub>3</sub>) has become a potential candidate recently because of its unique optical and electrical properties and easy fabrication method. X-ray photoelectron spectroscopy (XPS) was used to determine the stoichiometry and composition of electroless Sb<sub>2</sub>Se<sub>3</sub> thin films using depth profile studies. The surface layers were analyzed nearly stoichiometric. But the abundant amount of antimony makes the inner layer electrically more conductive.展开更多
Sb<sub>2</sub>S<sub>3</sub> has gained tremendous research recently for thin film solar cell absorber material because of their easy synthesis, unique electrical and optical properties. The sto...Sb<sub>2</sub>S<sub>3</sub> has gained tremendous research recently for thin film solar cell absorber material because of their easy synthesis, unique electrical and optical properties. The stoichiometry and composition of electroless Sb<sub>2</sub>S<sub>3</sub> thin films were analyzed using XPS depth profile studies. The surface layers were found nearly stoichiometric. On the other hand, the inner layer was rich in antimony composition making it more conductive electrically.展开更多
This study reports the dosimetric response of a(ZnO)_(0.2)(TeO_(2))_(0.8)thin film sensor irradiated with high-energy X-ray radiation at various doses.The spray pyrolysis method was used for the film deposition on sod...This study reports the dosimetric response of a(ZnO)_(0.2)(TeO_(2))_(0.8)thin film sensor irradiated with high-energy X-ray radiation at various doses.The spray pyrolysis method was used for the film deposition on soda-lime glass substrate using zinc acetate dehydrate and tellurium dioxide powder as the starting precursors.The structural and morphological properties of the film were determined.The I-V characteristics measurements were performed during irradiation with a 6 MV X-ray beam from a Linac.The results revealed that the XRD pattern of the AS-deposited thin film is non-crystalline(amorphous)in nature.The FESEM image shows the non-uniform shape of nanoparticles agglomerated separately,and the EDX spectrum shows the presence of Te,Zn,and O in the film.The I-V characteristics measurements indicate that the current density increases linearly with X-ray doses(0-250 cGy)for all applied voltages(1-6 V).The sensitivity of the thin film sensor has been found to be in the range of 0.37-0.94 mA/cm^(2)/Gy.The current-voltage measurement test for fading normalised in percentage to day 0 was found in the order of day 0>day 15>day 30>day 1>day 2.These results are expected to be beneficial for fabricating cheap and practical X-ray sensors.展开更多
Spray pyrolysis method was used to deposit Lutetium Oxide (Lu<sub>2</sub>O<sub>3</sub>) thin films using lutetium (III) chloride as source material and water as oxidizer. Annealing was carried ...Spray pyrolysis method was used to deposit Lutetium Oxide (Lu<sub>2</sub>O<sub>3</sub>) thin films using lutetium (III) chloride as source material and water as oxidizer. Annealing was carried out in argon atmosphere at 450°C for 60 minutes of the films. To investigate the composition and stoichiometry of sprayed as-deposited and annealed Lu<sub>2</sub>O<sub>3</sub> thin films, depth profile studies using X-ray photoelectron spectroscopy (XPS) was done. Nearly stoichiometric was observed for both annealed and as-deposited films in inner and surface layers.展开更多
Ga<sub>2</sub>O<sub>3</sub> thin films were fabricated by spray pyrolysis method using gallium acetylacetonate as source material and water as oxidizer. The films were annealed at 450°C fo...Ga<sub>2</sub>O<sub>3</sub> thin films were fabricated by spray pyrolysis method using gallium acetylacetonate as source material and water as oxidizer. The films were annealed at 450°C for 60 minutes in argon atmosphere. X-ray photoelectron spectroscopy (XPS) depth profile studies were carried out to analyze the stoichiometry and composition of sprayed as-deposited and annealed Ga<sub>2</sub>O<sub>3</sub> thin films. Surface layers and the inner layers of as-deposited and annealed films were found nearly stoichiometric.展开更多
Cd_(1-x)Zn_(x)S thin films were deposited by chemical bath deposition(CBD)on the glass substrate to study the influence of cadmium sulfate concentration on the structural characteristics of the thin film.The SEM resul...Cd_(1-x)Zn_(x)S thin films were deposited by chemical bath deposition(CBD)on the glass substrate to study the influence of cadmium sulfate concentration on the structural characteristics of the thin film.The SEM results show that the thin film surfaces under the cadmium sulfate concentration of 0.005 M exhibit better compactness and uniformity.The distribution diagrams of thin film elements illustrate the film growth rate changes on the trend of the increase,decrease,and increase with the increase of cadmium sulfate concentration.XRD studies exhibit the crystal structure of the film is the hexagonal phase,and there are obvious diffraction peaks and better crystallinity when the concentration is 0.005 M.Spectrophotometer test results demonstrate that the relationship between zinc content x and optical band gap value E_(g) can be expressed by the equation E_(g)(x)=0.59x^(2)+0.69x+2.43.Increasing the zinc content can increase the optical band gap,and the absorbance of the thin film can be improved by decreasing the cadmium sulfate concentration,however,all of them have good transmittance.At a concentration of 0.005 M,the thin film has good absorbance in the 300-800 nm range,80%transmittance,and band gap value of 3.24 eV,which is suitable for use as a buffer layer for solar cells.展开更多
Solar energy is becoming more popular and widespread, and consequently, the materials to manufacture solar cells are becoming more limited and costly. Therefore, in order to keep solar energy affordable and available,...Solar energy is becoming more popular and widespread, and consequently, the materials to manufacture solar cells are becoming more limited and costly. Therefore, in order to keep solar energy affordable and available, we must research alternative materials such as copper oxides. Some benefits of copper oxides include being available in abundance, affordable, low toxicity, low bandgap, and a high absorption coefficient—all of which contribute to it being a valuable interest for the manufacturing of solar cells. In this study, CuO thin films were synthesized utilizing RF sputtering technique with deposition occurring at room temperature followed by thermal annealing between 100°C and 400<span style="white-space:normal;">°</span>C and using different gases, oxygen (O<sub>2</sub>) (oxidizing and reactive gas) and nitrogen (N<sub>2</sub>) (inert gas), besides air. Afterwards, these thin films were evaluated for a range of wavelengths: 200 - 400 nm (UV spectrum), 400 - 700 nm (Visible spectrum), and 700 - 800 nm (IR spectrum), for both, optical transmittance and photoluminescence. In addition, the CuO results were compared to our Cu<sub>2</sub>O results from a previous study to assess their differences. In the results of this study, the CuO thin film initially had a bandgap of 2.19 eV at room temperature, and by increasing the annealing temperature to different levels, the bandgap decreased respectively. The presence of air in the chamber allowed for the highest decrease, followed by the nitrogen (N<sub>2</sub>) and the lowest decrease was observed in the presence of oxygen (O<sub>2</sub>). This was reflected in the decrease in the bandgap values from 2.19 eV (room temperature) to 2.05 eV for the films annealed at 400<span style="white-space:normal;">°</span>C.展开更多
In attempts to fabricate thermally stable second-order nonlinear polymer thin films, we have investigated the second harmonic generation (SHG) from both nonlinear polymer and guest-host thin films. We have also invest...In attempts to fabricate thermally stable second-order nonlinear polymer thin films, we have investigated the second harmonic generation (SHG) from both nonlinear polymer and guest-host thin films. We have also investigated the role of capping on the SHG, temporal stability and relaxation of dipole alignment. Corona poling techniques were employed to orient the dopants into the noncentrosymmetric structure required to obtain the SHG. The effect of capping with a polymeric encapsulant below the glass transition temperature of the polymers on the unpoled and corona poled thin films was studied. Capping of the nonlinear polymer and guest host thin films have resulted in high SHG with good temporal stability. SHG signal falls drastically during the first 8 days after poling while no further significant decay in SHG signal was observed after about 33 days. Our investigations have identified the characteristics required for a good encapsulant on a non-con-ductive surface.展开更多
Tungsten-doped indium oxide (IWO) thin films were deposited on glass substrate by DC reactive magnetron sputtering. The effects of sputtering power and growth temperature on the structure, surface morphology, optical ...Tungsten-doped indium oxide (IWO) thin films were deposited on glass substrate by DC reactive magnetron sputtering. The effects of sputtering power and growth temperature on the structure, surface morphology, optical and electrical properties of IWO thin films were investigated. The thickness and surface morphology of the films are both closely dependent on the sputtering power and the substrate temperature. The transparency of the films decreases with the increase of the sputtering power but is not seriously influenced by substrate temperature. All the IWO thin film samples have high transmittance in near-infrared spectral range. With either the sputtering power or the growth temperature increases, the resistivity of the film decreases at the beginning and increases after the optimum parameters. The as-deposited IWO films with minimum resistivity of 6.4 10 4 cm were obtained at a growth temperature of225 C and sputteringpower of 40 W, with carrier mobility of 33.0 cm 2 V 1 s 1 and carrier concentration of 2.8 10 20 cm 3 and the average transmittance of about 81% in near-infrared region and about 87% in visible region.展开更多
Thin films and thin film devices have a ubiquitous presence in numerous conventional and emerging technologies. This is because of the recent advances in nanotechnology, the development of functional and smart materia...Thin films and thin film devices have a ubiquitous presence in numerous conventional and emerging technologies. This is because of the recent advances in nanotechnology, the development of functional and smart materials,conducting polymers, molecular semiconductors, carbon nanotubes, and graphene, and the employment of unique properties of thin films and ultrathin films, such as high surface area, controlled nanostructure for effective charge transfer, and special physical and chemical properties, to develop new thin film devices. This paper is therefore intended to provide a concise critical review and research directions on most thin film devices, including thin film transistors, data storage memory, solar cells, organic light-emitting diodes, thermoelectric devices, smart materials, sensors, and actuators. The thin film devices may consist of organic, inorganic, and composite thin layers, and share similar functionality, properties, and fabrication routes. Therefore, due to the multidisciplinary nature of thin film devices, knowledge and advances already made in one area may be applicable to other similar areas. Owing to the importance of developing low-cost, scalable, and vacuum-free fabrication routes, this paper focuses on thin film devices that may be processed and deposited from solution.展开更多
The humidity sensing properties of La3+/Ce3+-doped TiO2-20 wt.%SnO2 thin films were studied.Sol-gel method was employed to prepare the films on alumina substrates.By constructing a humidity-impedance measuring system,...The humidity sensing properties of La3+/Ce3+-doped TiO2-20 wt.%SnO2 thin films were studied.Sol-gel method was employed to prepare the films on alumina substrates.By constructing a humidity-impedance measuring system,the sensing behaviors were inspected for the films sintered at different temperatures.Experimental results showed that,0.5 wt.% of La2O3 or Ce2O3 doped films sintered at 500 °C for 2 h had the best humidity sensing properties,the impedance decreasing from 109 ? to below 104 ? in the humidity range of 15-95 RH%.Moreover,Ce3+-doping had better humidity sensing properties than La3+-doping.The doping mechanism was discussed in terms of phase composition,granularity of crystalline and segregation of rare earth ions at grain boundaries.展开更多
The magnetic properties and microstructure of diffusion annealed [Ta/Nd/NdFeB/Nd/Ta] thin films have been investigated. The films were deposited on Si substrate with various thickness ratio of Nd/NdFeB layer (R=0-3.3)...The magnetic properties and microstructure of diffusion annealed [Ta/Nd/NdFeB/Nd/Ta] thin films have been investigated. The films were deposited on Si substrate with various thickness ratio of Nd/NdFeB layer (R=0-3.3), then diffused and crystallized by annealing at 650℃ for 10 min. The film without Nd layer showed soft magnetic behavior and high content of α-Fe phase. The films with R≥1 showed good hard magnetic properties with the high coercivity of about 20 kOe.展开更多
The thickness of CoP thin films prepared by wet chemical deposition is of crucial importance on magnetic property and recording perform-ance. The coercivity of CoP films decreased with increasing film thickness. The c...The thickness of CoP thin films prepared by wet chemical deposition is of crucial importance on magnetic property and recording perform-ance. The coercivity of CoP films decreased with increasing film thickness. The coercivity was 45.37 kA m 1 at the thickness of 300 nm, and decreased to 21.65 kA m 1 at 5.7 μm. Recording performance tests indicate that, for drums with the same size, different recorded magnetic pole density have different thickness requirements. For 40 mm diameter magnetic drum, the optimal CoP thickness is 3～10 μm for 256 re-corded magnetic poles, 1～2 μm for 512 recorded magnetic poles, and 500～800 nm for 1024 recorded magnetic poles.展开更多
基金the financial support from the National Key Research and Development Program of China(No.2017YFB0305500)the State Key Laboratory of Powder Metallurgy,Central South University,Changsha,China.
文摘Pure cobalt(Co)thin films were fabricated by direct current magnetron sputtering,and the effects of sputtering power and pres-sure on the microstructure and electromagnetic properties of the films were investigated.As the sputtering power increases from 15 to 60 W,the Co thin films transition from an amorphous to a polycrystalline state,accompanied by an increase in the intercrystal pore width.Simultaneously,the resistivity decreases from 276 to 99μΩ·cm,coercivity increases from 162 to 293 Oe,and in-plane magnetic aniso-tropy disappears.As the sputtering pressure decreases from 1.6 to 0.2 Pa,grain size significantly increases,resistivity significantly de-creases,and the coercivity significantly increases(from 67 to 280 Oe),which can be attributed to the increase in defect width.Corres-pondingly,a quantitative model for the coercivity of Co thin films was formulated.The polycrystalline films sputtered under pressures of 0.2 and 0.4 Pa exhibit significant in-plane magnetic anisotropy,which is primarily attributable to increased microstress.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.12004067,11974070,62027807,and 52272137)the National Key R&D Program of China(Grant No.2022YFA1403000)。
文摘We measure the time-resolved terahertz spectroscopy of GeSn thin film and studied the ultrafast dynamics of its photo-generated carriers.The experimental results show that there are photo-generated carriers in GeSn under femtosecond laser excitation at 2500 nm,and its pump-induced photoconductivity can be explained by the Drude–Smith model.The carrier recombination process is mainly dominated by defect-assisted Auger processes and defect capture.The firstand second-order recombination rates are obtained by the rate equation fitting,which are(2.6±1.1)×10^(-2)ps^(-1)and(6.6±1.8)×10^(-19)cm^(3)·ps^(-1),respectively.Meanwhile,we also obtain the diffusion length of photo-generated carriers in GeSn,which is about 0.4μm,and it changes with the pump delay time.These results are important for the GeSn-based infrared optoelectronic devices,and demonstrate that Ge Sn materials can be applied to high-speed optoelectronic detectors and other applications.
文摘AlN was used as a host material and doped with Eu grown on Si substrate by pulsed laser deposition (PLD) with low substrate temperature. The X-ray diffraction (XRD) data revealed the orientation and the composition of the thin film. The surface morphology was studied by scanning electron microscope (SEM). While raising the annealing temperatures from 300˚C to 900˚C, the emission was observed from AlN: Eu under excitation of 260 nm excitation. The photoluminescence (PL) was integrated over the visible light wavelength shifted from the blue to the red zone in the CIE 1931 chromaticity coordinates. The luminescence color coordination of AlN: Eu depending on the annealing temperatures guides the further study of Eu-doped nitrides manufacturing on white light emitting diode (LED) and full color LED devices.
基金supported by the National Research Foundation of Korea (NRF) funded by the Ministry of Science and ICT (NRF-2020M3H4A3081867)the industry technology R&D program (20006400) funded by the Ministry of Trade,Industry and Energy (MOTIE, Korea)+2 种基金the project number 20010402 funded by the Ministry of Trade,Industry and Energy (MOTIE, Korea)the Industry Technology R&D program (#20010371) funded by the Ministry of Trade,Industry and Energy (MOTIE, Republic of Korea)the Technology Innovation Program (20017382) funded By the Ministryof Trade,Industry and Energy (MOTIE, Korea)
文摘Since the first report of amorphous In–Ga–Zn–O based thin film transistors,interest in oxide semiconductors has grown.They offer high mobility,low off-current,low process temperature,and wide flexibility for compositions and processes.Unfortunately,depositing oxide semiconductors using conventional processes like physical vapor deposition leads to problematic issues,especially for high-resolution displays and highly integrated memory devices.Conventional approaches have limited process flexibility and poor conformality on structured surfaces.Atomic layer deposition(ALD)is an advanced technique which can provide conformal,thickness-controlled,and high-quality thin film deposition.Accordingly,studies on ALD based oxide semiconductors have dramatically increased recently.Even so,the relationships between the film properties of ALD-oxide semiconductors and the main variables associated with deposition are still poorly understood,as are many issues related to applications.In this review,to introduce ALD-oxide semiconductors,we provide:(a)a brief summary of the history and importance of ALD-based oxide semiconductors in industry,(b)a discussion of the benefits of ALD for oxide semiconductor deposition(in-situ composition control in vertical distribution/vertical structure engineering/chemical reaction and film properties/insulator and interface engineering),and(c)an explanation of the challenging issues of scaling oxide semiconductors and ALD for industrial applications.This review provides valuable perspectives for researchers who have interest in semiconductor materials and electronic device applications,and the reasons ALD is important to applications of oxide semiconductors.
基金supported by National Natural Science Foundation of China(No.U20A20209)Zhejiang Provincial Natural Science Foundation of China(LD19E020001)+1 种基金Zhejiang Provincial Key Research and Development Program(2021C01030)"Pioneer"and"Leading Goose"R&D Program of Zhejiang Province(2021C01SA301612)。
文摘Amorphous oxide semiconductors(AOS)have unique advantages in transparent and flexible thin film transistors(TFTs)applications,compared to low-temperature polycrystalline-Si(LTPS).However,intrinsic AOS TFTs are difficult to obtain field-effect mobility(μFE)higher than LTPS(100 cm^(2)/(V·s)).Here,we design ZnAlSnO(ZATO)homojunction structure TFTs to obtainμFE=113.8 cm^(2)/(V·s).The device demonstrates optimized comprehensive electrical properties with an off-current of about1.5×10^(-11)A,a threshold voltage of–1.71 V,and a subthreshold swing of 0.372 V/dec.There are two kinds of gradient coupled in the homojunction active layer,which are micro-crystallization and carrier suppressor concentration gradient distribution so that the device can reduce off-current and shift the threshold voltage positively while maintaining high field-effect mobility.Our research in the homojunction active layer points to a promising direction for obtaining excellent-performance AOS TFTs.
基金supported by the Renewable Energy Technology Development (Develop technology to enhance reliability and durability for parts of hydrogen storage tank system) (2022303004020B) grant funded by the Korea Energy Technology Evaluation Planning (KETEP)the Ministry of Science and ICT (Development Project for Emerging Research Instruments Technology),(Project Number: (2022)ERIC)06_1Commercialization Promotion Agency for R&D Outcomes (COMPA)。
文摘Biodegradable metals as electrodes, interconnectors, and device conductors are essential components in the emergence of transient electronics, either for passive implants or active electronic devices, especially in the fields of biomedical electronics. Magnesium and its alloys are strong candidates for biodegradable and implantable conducting materials because of their high conductivity and biocompatibility, in addition to their well-understood dissolution behavior. One critical drawback of Mg and its alloys is their considerably high dissolution rates originating from their low anodic potential, which disturbs the compatibility to biomedical applications. Herein, we introduce a single-phase thin film of a Mg-Zn binary alloy formed by sputtering, which enhances the corrosion resistance of the device electrode, and verify its applicability in biodegradable electronics. The formation of a homogeneous solid solution of single-phase Mg-3Zn was confirmed through X-ray diffraction and transmission electron microscopy. In addition, the dissolution behavior and chemistry was also investigated in various biological fluids by considering the effect of different ion species. Micro-tensile tests showed that the Mg-3Zn alloy electrode exhibited an enhanced yield strain and elongation in relation to a pure Mg electrode. Cell viability test revealed the high biocompatibility rate of the Mg-3Zn binary alloy thin film. Finally, the fabrication of a wireless heater demonstrated the integrability of biodegradable electrodes and highlighted the ability to prolong the lifecycle of thermotherapy-relevant electronics by enhancing the dissolution resistance of the Mg alloy.
基金financially supported by National Natural Science Foundation of China(Nos.12075054,12205040,12175036,11875104)。
文摘The effects of radio frequency(RF)atmospheric pressure(AP)He/H_(2)plasma and thermal treatment on the hydrogenation of TiO_(2)thin films were investigated and compared in this work.The color of the original TiO_(2)film changes from white to black after being hydrogenated in He/H_(2)plasma at160 W(gas temperature~381℃)within 5 min,while the color of the thermally treated TiO_(2)film did not change significantly even in pure H_(2)or He/H_(2)atmosphere with higher temperature(470℃)and longer time(30 min).This indicated that a more effective hydrogenation reaction happened through RF AP He/H_(2)plasma treatment than through pure H_(2)or He/H_(2)thermal treatment.The color change of TiO_(2)film was measured based on the Commission Internationale d’Eclairage L*a*b*color space system.Hydrogenated TiO_(2)film displayed improved visible light absorption with increased plasma power.The morphology of the cauliflower-like nanoparticles of the TiO_(2)film surface remained unchanged after plasma processing.X-ray photoelectron spectroscopy results showed that the contents of Ti3+species and Ti-OH bonds in the plasma-hydrogenated black TiO_(2)increased compared with those in the thermally treated TiO_(2).X-ray diffraction(XRD)patterns and Raman spectra indicated that plasma would destroy the crystal structure of the TiO_(2)surface layer,while thermal annealing would increase the overall crystallinity.The different trends of XRD and Raman spectra results suggested that plasma modification on the TiO_(2)surface layer is more drastic than on its inner layer,which was also consistent with transmission electron microscopy results.Optical emission spectra results suggest that numerous active species were generated during RF AP He/H_(2)plasma processing,while there were no peaks detected from thermal processing.A possible mechanism for the TiO_(2)hydrogenation process by plasma has been proposed.Numerous active species were generated in the bulk plasma region,accelerated in the sheath region,and bumped toward the TiO_(2)film,which will react with the TiO_(2)surface to form OVs and disordered layers.This leads to the tailoring of the band gap of black TiO_(2)and causes its light absorption to extend into the visible region.
文摘As a thin film solar cell absorber material, antimony selenide (Sb<sub>2</sub>Se<sub>3</sub>) has become a potential candidate recently because of its unique optical and electrical properties and easy fabrication method. X-ray photoelectron spectroscopy (XPS) was used to determine the stoichiometry and composition of electroless Sb<sub>2</sub>Se<sub>3</sub> thin films using depth profile studies. The surface layers were analyzed nearly stoichiometric. But the abundant amount of antimony makes the inner layer electrically more conductive.
文摘Sb<sub>2</sub>S<sub>3</sub> has gained tremendous research recently for thin film solar cell absorber material because of their easy synthesis, unique electrical and optical properties. The stoichiometry and composition of electroless Sb<sub>2</sub>S<sub>3</sub> thin films were analyzed using XPS depth profile studies. The surface layers were found nearly stoichiometric. On the other hand, the inner layer was rich in antimony composition making it more conductive electrically.
文摘This study reports the dosimetric response of a(ZnO)_(0.2)(TeO_(2))_(0.8)thin film sensor irradiated with high-energy X-ray radiation at various doses.The spray pyrolysis method was used for the film deposition on soda-lime glass substrate using zinc acetate dehydrate and tellurium dioxide powder as the starting precursors.The structural and morphological properties of the film were determined.The I-V characteristics measurements were performed during irradiation with a 6 MV X-ray beam from a Linac.The results revealed that the XRD pattern of the AS-deposited thin film is non-crystalline(amorphous)in nature.The FESEM image shows the non-uniform shape of nanoparticles agglomerated separately,and the EDX spectrum shows the presence of Te,Zn,and O in the film.The I-V characteristics measurements indicate that the current density increases linearly with X-ray doses(0-250 cGy)for all applied voltages(1-6 V).The sensitivity of the thin film sensor has been found to be in the range of 0.37-0.94 mA/cm^(2)/Gy.The current-voltage measurement test for fading normalised in percentage to day 0 was found in the order of day 0>day 15>day 30>day 1>day 2.These results are expected to be beneficial for fabricating cheap and practical X-ray sensors.
文摘Spray pyrolysis method was used to deposit Lutetium Oxide (Lu<sub>2</sub>O<sub>3</sub>) thin films using lutetium (III) chloride as source material and water as oxidizer. Annealing was carried out in argon atmosphere at 450°C for 60 minutes of the films. To investigate the composition and stoichiometry of sprayed as-deposited and annealed Lu<sub>2</sub>O<sub>3</sub> thin films, depth profile studies using X-ray photoelectron spectroscopy (XPS) was done. Nearly stoichiometric was observed for both annealed and as-deposited films in inner and surface layers.
文摘Ga<sub>2</sub>O<sub>3</sub> thin films were fabricated by spray pyrolysis method using gallium acetylacetonate as source material and water as oxidizer. The films were annealed at 450°C for 60 minutes in argon atmosphere. X-ray photoelectron spectroscopy (XPS) depth profile studies were carried out to analyze the stoichiometry and composition of sprayed as-deposited and annealed Ga<sub>2</sub>O<sub>3</sub> thin films. Surface layers and the inner layers of as-deposited and annealed films were found nearly stoichiometric.
基金This work was supported by the Tianjin Municipal Education Commission,Horizontal subject(grant number 70304901).
文摘Cd_(1-x)Zn_(x)S thin films were deposited by chemical bath deposition(CBD)on the glass substrate to study the influence of cadmium sulfate concentration on the structural characteristics of the thin film.The SEM results show that the thin film surfaces under the cadmium sulfate concentration of 0.005 M exhibit better compactness and uniformity.The distribution diagrams of thin film elements illustrate the film growth rate changes on the trend of the increase,decrease,and increase with the increase of cadmium sulfate concentration.XRD studies exhibit the crystal structure of the film is the hexagonal phase,and there are obvious diffraction peaks and better crystallinity when the concentration is 0.005 M.Spectrophotometer test results demonstrate that the relationship between zinc content x and optical band gap value E_(g) can be expressed by the equation E_(g)(x)=0.59x^(2)+0.69x+2.43.Increasing the zinc content can increase the optical band gap,and the absorbance of the thin film can be improved by decreasing the cadmium sulfate concentration,however,all of them have good transmittance.At a concentration of 0.005 M,the thin film has good absorbance in the 300-800 nm range,80%transmittance,and band gap value of 3.24 eV,which is suitable for use as a buffer layer for solar cells.
文摘Solar energy is becoming more popular and widespread, and consequently, the materials to manufacture solar cells are becoming more limited and costly. Therefore, in order to keep solar energy affordable and available, we must research alternative materials such as copper oxides. Some benefits of copper oxides include being available in abundance, affordable, low toxicity, low bandgap, and a high absorption coefficient—all of which contribute to it being a valuable interest for the manufacturing of solar cells. In this study, CuO thin films were synthesized utilizing RF sputtering technique with deposition occurring at room temperature followed by thermal annealing between 100°C and 400<span style="white-space:normal;">°</span>C and using different gases, oxygen (O<sub>2</sub>) (oxidizing and reactive gas) and nitrogen (N<sub>2</sub>) (inert gas), besides air. Afterwards, these thin films were evaluated for a range of wavelengths: 200 - 400 nm (UV spectrum), 400 - 700 nm (Visible spectrum), and 700 - 800 nm (IR spectrum), for both, optical transmittance and photoluminescence. In addition, the CuO results were compared to our Cu<sub>2</sub>O results from a previous study to assess their differences. In the results of this study, the CuO thin film initially had a bandgap of 2.19 eV at room temperature, and by increasing the annealing temperature to different levels, the bandgap decreased respectively. The presence of air in the chamber allowed for the highest decrease, followed by the nitrogen (N<sub>2</sub>) and the lowest decrease was observed in the presence of oxygen (O<sub>2</sub>). This was reflected in the decrease in the bandgap values from 2.19 eV (room temperature) to 2.05 eV for the films annealed at 400<span style="white-space:normal;">°</span>C.
文摘In attempts to fabricate thermally stable second-order nonlinear polymer thin films, we have investigated the second harmonic generation (SHG) from both nonlinear polymer and guest-host thin films. We have also investigated the role of capping on the SHG, temporal stability and relaxation of dipole alignment. Corona poling techniques were employed to orient the dopants into the noncentrosymmetric structure required to obtain the SHG. The effect of capping with a polymeric encapsulant below the glass transition temperature of the polymers on the unpoled and corona poled thin films was studied. Capping of the nonlinear polymer and guest host thin films have resulted in high SHG with good temporal stability. SHG signal falls drastically during the first 8 days after poling while no further significant decay in SHG signal was observed after about 33 days. Our investigations have identified the characteristics required for a good encapsulant on a non-con-ductive surface.
基金supported by the National Natural Science Foundation of China (No. 50902006)the National High Technology Development 863 Program of China (No.2009AA03Z428)
文摘Tungsten-doped indium oxide (IWO) thin films were deposited on glass substrate by DC reactive magnetron sputtering. The effects of sputtering power and growth temperature on the structure, surface morphology, optical and electrical properties of IWO thin films were investigated. The thickness and surface morphology of the films are both closely dependent on the sputtering power and the substrate temperature. The transparency of the films decreases with the increase of the sputtering power but is not seriously influenced by substrate temperature. All the IWO thin film samples have high transmittance in near-infrared spectral range. With either the sputtering power or the growth temperature increases, the resistivity of the film decreases at the beginning and increases after the optimum parameters. The as-deposited IWO films with minimum resistivity of 6.4 10 4 cm were obtained at a growth temperature of225 C and sputteringpower of 40 W, with carrier mobility of 33.0 cm 2 V 1 s 1 and carrier concentration of 2.8 10 20 cm 3 and the average transmittance of about 81% in near-infrared region and about 87% in visible region.
基金Research funding from the Shanghai Municipal Education Commission in the framework of the oriental scholar and distinguished professor designationfunding from the National Natural Science Foundation of China(NSFC)
文摘Thin films and thin film devices have a ubiquitous presence in numerous conventional and emerging technologies. This is because of the recent advances in nanotechnology, the development of functional and smart materials,conducting polymers, molecular semiconductors, carbon nanotubes, and graphene, and the employment of unique properties of thin films and ultrathin films, such as high surface area, controlled nanostructure for effective charge transfer, and special physical and chemical properties, to develop new thin film devices. This paper is therefore intended to provide a concise critical review and research directions on most thin film devices, including thin film transistors, data storage memory, solar cells, organic light-emitting diodes, thermoelectric devices, smart materials, sensors, and actuators. The thin film devices may consist of organic, inorganic, and composite thin layers, and share similar functionality, properties, and fabrication routes. Therefore, due to the multidisciplinary nature of thin film devices, knowledge and advances already made in one area may be applicable to other similar areas. Owing to the importance of developing low-cost, scalable, and vacuum-free fabrication routes, this paper focuses on thin film devices that may be processed and deposited from solution.
基金supported by the Natioanl Natural Science Foundation of China (50562003)
文摘The humidity sensing properties of La3+/Ce3+-doped TiO2-20 wt.%SnO2 thin films were studied.Sol-gel method was employed to prepare the films on alumina substrates.By constructing a humidity-impedance measuring system,the sensing behaviors were inspected for the films sintered at different temperatures.Experimental results showed that,0.5 wt.% of La2O3 or Ce2O3 doped films sintered at 500 °C for 2 h had the best humidity sensing properties,the impedance decreasing from 109 ? to below 104 ? in the humidity range of 15-95 RH%.Moreover,Ce3+-doping had better humidity sensing properties than La3+-doping.The doping mechanism was discussed in terms of phase composition,granularity of crystalline and segregation of rare earth ions at grain boundaries.
文摘The magnetic properties and microstructure of diffusion annealed [Ta/Nd/NdFeB/Nd/Ta] thin films have been investigated. The films were deposited on Si substrate with various thickness ratio of Nd/NdFeB layer (R=0-3.3), then diffused and crystallized by annealing at 650℃ for 10 min. The film without Nd layer showed soft magnetic behavior and high content of α-Fe phase. The films with R≥1 showed good hard magnetic properties with the high coercivity of about 20 kOe.
基金supported by the National Natural Science Foundation of China (No. 51101013)Specialized Research Fund for the Doctoral Program of Higher Education of China(No. 20090006120013)the Fundamental Research Funds for the Central Universities (FRF-TP-12-038A)
文摘The thickness of CoP thin films prepared by wet chemical deposition is of crucial importance on magnetic property and recording perform-ance. The coercivity of CoP films decreased with increasing film thickness. The coercivity was 45.37 kA m 1 at the thickness of 300 nm, and decreased to 21.65 kA m 1 at 5.7 μm. Recording performance tests indicate that, for drums with the same size, different recorded magnetic pole density have different thickness requirements. For 40 mm diameter magnetic drum, the optimal CoP thickness is 3～10 μm for 256 re-corded magnetic poles, 1～2 μm for 512 recorded magnetic poles, and 500～800 nm for 1024 recorded magnetic poles.