The Ti/SnO2 Sb2O4 electrode has been prepared by the electroplate sinter method. The effect of SbCl3 adding amount and sintering temperature on its electrode lifetime and oxygen evolution potential were investigated b...The Ti/SnO2 Sb2O4 electrode has been prepared by the electroplate sinter method. The effect of SbCl3 adding amount and sintering temperature on its electrode lifetime and oxygen evolution potential were investigated by means of EDX, SEM and XRD analysis. The results indicated that the electrode appeared the best performance when the SbCl3 adding amounts was 0.2g and the sintering temperature was 550℃. In optimized conditions Ti substrate was entirely covered by SnO2 Sb2O4 and the combinations among them were tight. Due to the use of electroplate method, the electrical conductivity, the oxygen evolution potential and the electrode lifetime were increased, so the electro catalytic activity and the electrochemical stability of the prepared electrode were found to be superior.展开更多
Methodology for the electrochemical decomposition of imazethapyr using Ti/SnO2-Sb2O5/PbO2 anode in Na2SO4 medium is suggested in this paper. The electrolysis reaction conditions were optimized. The process of electroc...Methodology for the electrochemical decomposition of imazethapyr using Ti/SnO2-Sb2O5/PbO2 anode in Na2SO4 medium is suggested in this paper. The electrolysis reaction conditions were optimized. The process of electrochemical decomposition was monitored by ultra-violet spectrophotometry and CODCr method. The electrochemical decomposition mechanism of imazethapyr was studied primarily by UV-VIS spectrophotometry. The effectiveness of the electrochemical pretreatment was proved by the comparative aerobic biological treatment test based on the activated sludge process.展开更多
采用溶胶-凝胶法和化学沉积法制备了Li4Ti4.75Cu0.25O12/SnO2复合活性材料。通过X射线衍射（XRD）、扫描电镜（SEM）、恒流充放电测试对材料进行结构、形貌表征及电化学性能测试。结果表明：Li4Ti4.75Cu0.25O12/SnO2复合活性物质能够进...采用溶胶-凝胶法和化学沉积法制备了Li4Ti4.75Cu0.25O12/SnO2复合活性材料。通过X射线衍射（XRD）、扫描电镜（SEM）、恒流充放电测试对材料进行结构、形貌表征及电化学性能测试。结果表明：Li4Ti4.75Cu0.25O12/SnO2复合活性物质能够进一步改善倍率性能的同时,循环性能也得到了很好的保证。当电压在1~3 V时,电流密度为1C倍率条件下,Li4Ti4.75Cu0.25O12/SnO2复合材料首次放电比容量高达202.55 m A·h/g。经过50次循环后,容量仍保持在202.51 m A·h/g,容量保持率高达99.98%。展开更多
Compound Zn2Sn0.8Ti0.2O4 was synthesized by a hydrothermal method in which SnCl4-5H2O,TiCl4,ZnCl2 and N2H4-H2O were used as reactants.The composite Zn2Sn0.8Ti0.2O4/C was then prepared through a carbothermic reduction ...Compound Zn2Sn0.8Ti0.2O4 was synthesized by a hydrothermal method in which SnCl4-5H2O,TiCl4,ZnCl2 and N2H4-H2O were used as reactants.The composite Zn2Sn0.8Ti0.2O4/C was then prepared through a carbothermic reduction process using the as-prepared Zn2Sn0.8Ti0.2O4 and glucose as reactants.The structure,morphology and electrochemical properties of the as-prepared products were investigated by XRD,XPS,TEM and electrochemical measurements.In addition,electrochemical Li insertion/extraction in composite Zn2Sn0.8Ti0.2O4/C were examined by ex situ XRD and SEM.The first discharge capacity of Zn2SnO4 is about 1670.8 mA-h/g,with a capacity retain of 342.7 mA-h/g in the 40th cycle at a constant current density of 100 mA/g in the voltage range of 0.05-3.0 V.Comparing with the Zn2SnO4,some improved electrochemical properties are obtained for Zn2Sn0.8Ti0.2O4,Zn2SnO4/C and Zn2Sn0.8Ti0.2O4/C.The composite Zn2Sn0.8Ti0.2O4/C shows the best electrochemical properties,and its first discharge capacity is about 1530.0 mA-h/g,with a capacity retain of 479.1 mA-h/g the 100th cycle.展开更多
采用超声涂覆-热分解法制备稀土金属Ce掺杂Ti/SnO_2-Sb电极,利用SEM对电极表面形态进行表征,并考察了Ce掺杂量和电流密度对修饰电极电催化性能和稳定性的影响。结果表明,掺杂后电极涂层中引入了新物质CeO_2,优化了电极的表面结构和形态...采用超声涂覆-热分解法制备稀土金属Ce掺杂Ti/SnO_2-Sb电极,利用SEM对电极表面形态进行表征,并考察了Ce掺杂量和电流密度对修饰电极电催化性能和稳定性的影响。结果表明,掺杂后电极涂层中引入了新物质CeO_2,优化了电极的表面结构和形态;制备得到的电极对苯酚和对甲酚都有较好的降解效果,当Ce掺杂量为1%时降解苯酚性能最优,Ce掺杂量为2%时降解对甲酚性能最优;在最优掺杂量下,当电流密度为10 m A/cm2时降解苯酚性能最佳,电流密度为20 m A/cm2时降解对甲酚性能最佳。展开更多
文摘The Ti/SnO2 Sb2O4 electrode has been prepared by the electroplate sinter method. The effect of SbCl3 adding amount and sintering temperature on its electrode lifetime and oxygen evolution potential were investigated by means of EDX, SEM and XRD analysis. The results indicated that the electrode appeared the best performance when the SbCl3 adding amounts was 0.2g and the sintering temperature was 550℃. In optimized conditions Ti substrate was entirely covered by SnO2 Sb2O4 and the combinations among them were tight. Due to the use of electroplate method, the electrical conductivity, the oxygen evolution potential and the electrode lifetime were increased, so the electro catalytic activity and the electrochemical stability of the prepared electrode were found to be superior.
文摘Methodology for the electrochemical decomposition of imazethapyr using Ti/SnO2-Sb2O5/PbO2 anode in Na2SO4 medium is suggested in this paper. The electrolysis reaction conditions were optimized. The process of electrochemical decomposition was monitored by ultra-violet spectrophotometry and CODCr method. The electrochemical decomposition mechanism of imazethapyr was studied primarily by UV-VIS spectrophotometry. The effectiveness of the electrochemical pretreatment was proved by the comparative aerobic biological treatment test based on the activated sludge process.
文摘采用溶胶-凝胶法和化学沉积法制备了Li4Ti4.75Cu0.25O12/SnO2复合活性材料。通过X射线衍射（XRD）、扫描电镜（SEM）、恒流充放电测试对材料进行结构、形貌表征及电化学性能测试。结果表明：Li4Ti4.75Cu0.25O12/SnO2复合活性物质能够进一步改善倍率性能的同时,循环性能也得到了很好的保证。当电压在1~3 V时,电流密度为1C倍率条件下,Li4Ti4.75Cu0.25O12/SnO2复合材料首次放电比容量高达202.55 m A·h/g。经过50次循环后,容量仍保持在202.51 m A·h/g,容量保持率高达99.98%。
基金Project (51004028) supported by the National Natural Science Foundation of China
文摘Compound Zn2Sn0.8Ti0.2O4 was synthesized by a hydrothermal method in which SnCl4-5H2O,TiCl4,ZnCl2 and N2H4-H2O were used as reactants.The composite Zn2Sn0.8Ti0.2O4/C was then prepared through a carbothermic reduction process using the as-prepared Zn2Sn0.8Ti0.2O4 and glucose as reactants.The structure,morphology and electrochemical properties of the as-prepared products were investigated by XRD,XPS,TEM and electrochemical measurements.In addition,electrochemical Li insertion/extraction in composite Zn2Sn0.8Ti0.2O4/C were examined by ex situ XRD and SEM.The first discharge capacity of Zn2SnO4 is about 1670.8 mA-h/g,with a capacity retain of 342.7 mA-h/g in the 40th cycle at a constant current density of 100 mA/g in the voltage range of 0.05-3.0 V.Comparing with the Zn2SnO4,some improved electrochemical properties are obtained for Zn2Sn0.8Ti0.2O4,Zn2SnO4/C and Zn2Sn0.8Ti0.2O4/C.The composite Zn2Sn0.8Ti0.2O4/C shows the best electrochemical properties,and its first discharge capacity is about 1530.0 mA-h/g,with a capacity retain of 479.1 mA-h/g the 100th cycle.
文摘采用超声涂覆-热分解法制备稀土金属Ce掺杂Ti/SnO_2-Sb电极,利用SEM对电极表面形态进行表征,并考察了Ce掺杂量和电流密度对修饰电极电催化性能和稳定性的影响。结果表明,掺杂后电极涂层中引入了新物质CeO_2,优化了电极的表面结构和形态;制备得到的电极对苯酚和对甲酚都有较好的降解效果,当Ce掺杂量为1%时降解苯酚性能最优,Ce掺杂量为2%时降解对甲酚性能最优;在最优掺杂量下,当电流密度为10 m A/cm2时降解苯酚性能最佳,电流密度为20 m A/cm2时降解对甲酚性能最佳。
