The effects of activated sintering technology of H2 atmosphere sintering on the microstructure and properties of W-15Cu alloy using ultrafine W-15Cu composite powder fabricated by spray drying calcining-continuous red...The effects of activated sintering technology of H2 atmosphere sintering on the microstructure and properties of W-15Cu alloy using ultrafine W-15Cu composite powder fabricated by spray drying calcining-continuous reduction technology were investigated.The experimental results showed that W-15Cu alloy,consolidated by activated sintering technology of H2 atmosphere sintering for 1 h at 1300 ℃,with 98.5 % relative density,transverse rupture strength 1218 MPa,Vickers hardness HV0.5 378,average grain size about 1.2 μm and thermal conductivity 192 W/m·K,was obtained.In comparison to the normal sintering process,activated sintering process to W-15Cu alloy could be achieved at lower sintering temperature.Furthermore,better properties in activated sintered compacts were obtained,and activated sintering process resulted in finer microstructure and excellent properties.展开更多
W-15Cu composite powders prepared by mechanical alloying （MA） of raw powders were consolidated by spark plasma sintering （SPS） process at temperature ranged 1 230-1 300 ℃ for 10 min and under a pressure of 30 MPa...W-15Cu composite powders prepared by mechanical alloying （MA） of raw powders were consolidated by spark plasma sintering （SPS） process at temperature ranged 1 230-1 300 ℃ for 10 min and under a pressure of 30 MPa. By using high energy milling, particles containing very fine tungsten grains embedded in copper, called composite particles, could be produced. The W grains were homogeneously dispersed in copper phase, which was very important to obtain W-Cu alloy with high mechanical properties, fine and homogeneous microstructure. The microstructure and properties of W-15Cu alloys prepared by SPS processes at different temperature were researched. The results show that W-15Cu alloys consolidated by SPS can reach 99.6 % relative density, and transverse rupture strength （TRS） is 1 400.9 MPa, Rockwell C hardness （HRC） is 45.2, the thermal conductivity is 196 W/m-K at room temperature, the average grain size is less than 2 μm, and W-15Cu alloy with excellent properties, homogeneous and fine microstructure is obtained.展开更多
The effects of microwave sintering and conventional H2 sintering on the microstructure and properties of W-15Cu alloy using ultrafine W-15Cu composite powder fabricated by spray drying ＆ calcining-continuous reductio...The effects of microwave sintering and conventional H2 sintering on the microstructure and properties of W-15Cu alloy using ultrafine W-15Cu composite powder fabricated by spray drying ＆ calcining-continuous reduction technology were investigated. In comparison to the conventional HE sintering processing, microwave sintering to W-15Cu can be achieved at lower sintering temperature and shorter sintering time. Furthermore, higher performances in microwave sintered compacts were obtained, but high microwave sintering temperature or long microwave sintering time could result in coarser microstructures.展开更多
The precipitation behaviors of an A1-Cu-Li-Mn-Zr alloy at different ageing temperatures （120, 160 and 200 ~C） were investigated using Vickers hardness measurements and transmission electron microscopy （TEM） charac...The precipitation behaviors of an A1-Cu-Li-Mn-Zr alloy at different ageing temperatures （120, 160 and 200 ~C） were investigated using Vickers hardness measurements and transmission electron microscopy （TEM） characterization. Age hardening curves show an increase in precipitation kinetics with increasing ageing temperature. The results of TEM show that for the samples peak aged at 120 ~C, the amount of g＇ （A13Li）, GP zones/0＇ （A12Cu） and Z （A15Cu6Li2） phases is obviously higher than that of T1 （A12CuLi） precipitates; while the samples peak aged at 160 and 200 ~C are usually dominated by T1 phase with a minor fraction of GP zones/0＇ and g＇, and the Z phase almost does not form. In addition, quantitative analysis on the T1 platelets demonstrates that the samples peak aged at 200 ~C have larger plate diameter and smaller area fraction of T1, as compared to the samples peak aged at 160 ~C. Correspondingly, the possible reasons for such phenomena are discussed.展开更多
By investigating the thermal expansion properties of three quasicrystalline alloys Al 65 Cu 20 Cr 15 quenched, Al 65 Cu 20 Cr 15 cast and Al 65 Cu 20 Fe 15 cast particles reinforced Al matrix composites from 25 ℃ to ...By investigating the thermal expansion properties of three quasicrystalline alloys Al 65 Cu 20 Cr 15 quenched, Al 65 Cu 20 Cr 15 cast and Al 65 Cu 20 Fe 15 cast particles reinforced Al matrix composites from 25 ℃ to 500 ℃, the thermal expansion coefficients of three quasicrystalline alloys were theoretically estimated. The results show that the thermal expansion coefficients of the composites are much lower than that of pure Al, and the thermal expansion coefficients of the composites reinforced by Al Cu Cr quasicrystalline particles are lower than those of the composites reinforced by Al Cu Fe quasicrystalline particles. According to estimating, quasicrystalline alloys have negative thermal expansion coefficients, and the thermal expansion coefficients of Al Cu Cr quasicrystalline alloys are lower than those of Al Cu Fe quasicrystalline alloys. In the alloys, the more the qusicrystalline content, the lower the thermal expansion coefficient.展开更多
Alloys used as bearings in aircraft landing gear are required to reduce friction and wear as well as improve the load‐carrying capability due to the increased aircraft weights.Cu–15Ni–8Sn–0.8Nb alloy is well known...Alloys used as bearings in aircraft landing gear are required to reduce friction and wear as well as improve the load‐carrying capability due to the increased aircraft weights.Cu–15Ni–8Sn–0.8Nb alloy is well known for possessing good mechanical and wear properties that satisfy such requirements.In this study,the microstructure,mechanical properties,and grease‐lubricated sliding wear behavior of Cu–15Ni–8Sn–0.8Nb alloy with 0.8 wt%Nb are investigated.The nanoscale NbNi3 and NbNi2Sn compounds can strengthen the alloy through the Orowan strengthening mechanism.A Stribeck‐like curve is plotted to illustrate the relationship among friction coefficient,normal load,and sliding velocity and to analyze the grease‐lubricated mechanism.The wear rate increases with normal load and decreases with sliding velocity,except at 2.58 m/s.A wear mechanism map has been developed to exhibit the dominant wear mechanisms under various friction conditions.When the normal load is 700 N and the sliding velocity is 2.58 m/s,a chemical reaction between the lubricating grease and friction pairs occurs,resulting in the failure of lubricating grease and an increase in wear.展开更多
基金Funded by the Project for Science and Technology Plan of Wuhan City(200910321092)the Fundamental Research Funds for the Central Universities(2010-Ⅱ-020)
文摘The effects of activated sintering technology of H2 atmosphere sintering on the microstructure and properties of W-15Cu alloy using ultrafine W-15Cu composite powder fabricated by spray drying calcining-continuous reduction technology were investigated.The experimental results showed that W-15Cu alloy,consolidated by activated sintering technology of H2 atmosphere sintering for 1 h at 1300 ℃,with 98.5 % relative density,transverse rupture strength 1218 MPa,Vickers hardness HV0.5 378,average grain size about 1.2 μm and thermal conductivity 192 W/m·K,was obtained.In comparison to the normal sintering process,activated sintering process to W-15Cu alloy could be achieved at lower sintering temperature.Furthermore,better properties in activated sintered compacts were obtained,and activated sintering process resulted in finer microstructure and excellent properties.
基金Funded by the Youth Science Plan for Light of the Morning Sun of Wuhan City(No.200750731270).
文摘W-15Cu composite powders prepared by mechanical alloying （MA） of raw powders were consolidated by spark plasma sintering （SPS） process at temperature ranged 1 230-1 300 ℃ for 10 min and under a pressure of 30 MPa. By using high energy milling, particles containing very fine tungsten grains embedded in copper, called composite particles, could be produced. The W grains were homogeneously dispersed in copper phase, which was very important to obtain W-Cu alloy with high mechanical properties, fine and homogeneous microstructure. The microstructure and properties of W-15Cu alloys prepared by SPS processes at different temperature were researched. The results show that W-15Cu alloys consolidated by SPS can reach 99.6 % relative density, and transverse rupture strength （TRS） is 1 400.9 MPa, Rockwell C hardness （HRC） is 45.2, the thermal conductivity is 196 W/m-K at room temperature, the average grain size is less than 2 μm, and W-15Cu alloy with excellent properties, homogeneous and fine microstructure is obtained.
基金Funded by the Project for Science and Technology Plan of Wuhan City(200910321092)the Youth Science Plan for Light of the Morning Sun of Wuhan City (200750731270)
文摘The effects of microwave sintering and conventional H2 sintering on the microstructure and properties of W-15Cu alloy using ultrafine W-15Cu composite powder fabricated by spray drying ＆ calcining-continuous reduction technology were investigated. In comparison to the conventional HE sintering processing, microwave sintering to W-15Cu can be achieved at lower sintering temperature and shorter sintering time. Furthermore, higher performances in microwave sintered compacts were obtained, but high microwave sintering temperature or long microwave sintering time could result in coarser microstructures.
基金Project（2016YFB0300901） supported by the National Key R＆D Program of China Project（51421001） supported by the National Natural Science Foundation of China Project（2018CDJDCL0019） supported by the Fundamental Research Funds for the Central Universities, China
文摘The precipitation behaviors of an A1-Cu-Li-Mn-Zr alloy at different ageing temperatures （120, 160 and 200 ~C） were investigated using Vickers hardness measurements and transmission electron microscopy （TEM） characterization. Age hardening curves show an increase in precipitation kinetics with increasing ageing temperature. The results of TEM show that for the samples peak aged at 120 ~C, the amount of g＇ （A13Li）, GP zones/0＇ （A12Cu） and Z （A15Cu6Li2） phases is obviously higher than that of T1 （A12CuLi） precipitates; while the samples peak aged at 160 and 200 ~C are usually dominated by T1 phase with a minor fraction of GP zones/0＇ and g＇, and the Z phase almost does not form. In addition, quantitative analysis on the T1 platelets demonstrates that the samples peak aged at 200 ~C have larger plate diameter and smaller area fraction of T1, as compared to the samples peak aged at 160 ~C. Correspondingly, the possible reasons for such phenomena are discussed.
文摘By investigating the thermal expansion properties of three quasicrystalline alloys Al 65 Cu 20 Cr 15 quenched, Al 65 Cu 20 Cr 15 cast and Al 65 Cu 20 Fe 15 cast particles reinforced Al matrix composites from 25 ℃ to 500 ℃, the thermal expansion coefficients of three quasicrystalline alloys were theoretically estimated. The results show that the thermal expansion coefficients of the composites are much lower than that of pure Al, and the thermal expansion coefficients of the composites reinforced by Al Cu Cr quasicrystalline particles are lower than those of the composites reinforced by Al Cu Fe quasicrystalline particles. According to estimating, quasicrystalline alloys have negative thermal expansion coefficients, and the thermal expansion coefficients of Al Cu Cr quasicrystalline alloys are lower than those of Al Cu Fe quasicrystalline alloys. In the alloys, the more the qusicrystalline content, the lower the thermal expansion coefficient.
基金The authors would like to express their gratitude for the financial support provided by the National Key Research and Development Program of China(Grant Nos.2017YFB0306105 and 2018YFE0306100).
文摘Alloys used as bearings in aircraft landing gear are required to reduce friction and wear as well as improve the load‐carrying capability due to the increased aircraft weights.Cu–15Ni–8Sn–0.8Nb alloy is well known for possessing good mechanical and wear properties that satisfy such requirements.In this study,the microstructure,mechanical properties,and grease‐lubricated sliding wear behavior of Cu–15Ni–8Sn–0.8Nb alloy with 0.8 wt%Nb are investigated.The nanoscale NbNi3 and NbNi2Sn compounds can strengthen the alloy through the Orowan strengthening mechanism.A Stribeck‐like curve is plotted to illustrate the relationship among friction coefficient,normal load,and sliding velocity and to analyze the grease‐lubricated mechanism.The wear rate increases with normal load and decreases with sliding velocity,except at 2.58 m/s.A wear mechanism map has been developed to exhibit the dominant wear mechanisms under various friction conditions.When the normal load is 700 N and the sliding velocity is 2.58 m/s,a chemical reaction between the lubricating grease and friction pairs occurs,resulting in the failure of lubricating grease and an increase in wear.