Decomposition processes of the quenched Zn-Al alloys were studied by differential scanning calorimetry (DSC), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The results show that the stabilities o...Decomposition processes of the quenched Zn-Al alloys were studied by differential scanning calorimetry (DSC), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The results show that the stabilities of supersaturated solid solution (SSS) of Zn-Al alloy and α' phase formed by quenching would reduce with the increase of Zn content and the precipitation of η-Zn phases even when aging at ambient temperature, so that the exothermic precipitation peak in DSC curve would disappear. The activation energy of the η-Zn precipitation and the reaction enthalpy were calculated and measured. The kinetics of α' decomposition or η-Zn formation was determined by XRD. The microstructure change during aging was observed by TEM.展开更多
X-ray powder diffraction data and crystal structure of NiSbY compound were studied by X-ray powderdiffraction. The compound belongs to the space group F43 m with MgAgAs structure type, and the parameters Z=4, a=0.6307...X-ray powder diffraction data and crystal structure of NiSbY compound were studied by X-ray powderdiffraction. The compound belongs to the space group F43 m with MgAgAs structure type, and the parameters Z=4, a=0.63075(2) nm.展开更多
The compound PrNiSn was studied by X ray powder diffraction technique. The crystal structure and the X ray diffraction data for this compound at room temperature were reported. The compound PrNiSn is orthorhombic wi...The compound PrNiSn was studied by X ray powder diffraction technique. The crystal structure and the X ray diffraction data for this compound at room temperature were reported. The compound PrNiSn is orthorhombic with lattice parameters a =0.74569(3) nm, b =0.76851(5) nm, c =0.45676(8) nm, V =0.26176 nm 3, Z =4 and D x=8.076 g·cm -3 , space group Pna2 1(33). The figure of merit F N for the compound is F 30 =54 (0.0093, 60).展开更多
The compound CeNi 5Sn was studied by means of X ray powder diffraction technique and refined by Rietveld method. It has a hexagonal structure with space group P 6 3/ mmc (No.194), Z =4, the lattice constant...The compound CeNi 5Sn was studied by means of X ray powder diffraction technique and refined by Rietveld method. It has a hexagonal structure with space group P 6 3/ mmc (No.194), Z =4, the lattice constants a =0 48912(3) nm, c =1 973(2) nm and D x=8 974 g·cm -3 . The Rietveld structural refinement was performed, leading to R p=0 138 and R wp =0 185. The figure of merit F N for the XRD data is F 30 =82 1(0 0068, 54). The X ray powder diffraction data are presented.展开更多
To evaluate the residual stress in TiAl based alloys by X ray diffraction, X ray elastic constants (REC) of a γ TiAl alloy were determined. From these results, the stress state of a given phase in a duplex TiAl based...To evaluate the residual stress in TiAl based alloys by X ray diffraction, X ray elastic constants (REC) of a γ TiAl alloy were determined. From these results, the stress state of a given phase in a duplex TiAl based alloy under a uniaxial tensile loading has been characterized by X ray diffraction. The results show that the X ray elastic constants and the microscopic stresses of the given phase are different from the apparent elastic constants and the macroscopic stresses of the alloy. The reason of the different distribution of the alloy was also discussed. [展开更多
A primary study on Processing in X - ray inspection of spot weld for aluminum alloy spot welding,in- cluding for background simulation,acquisition of ideal binary image, and extraction and identifi- cation of defec...A primary study on Processing in X - ray inspection of spot weld for aluminum alloy spot welding,in- cluding for background simulation,acquisition of ideal binary image, and extraction and identifi- cation of defect features was presented.展开更多
The silicon-containing poly (amic acid)s were synthesized from bis (3, 4-dicarboxyphenyl) dimethylsilane dianhydride (SIDA), pyromellitic dianhydride (PMDA) and 4,4′-oxydianiline (4,4'-ODA) in N, N-dimethylacetam...The silicon-containing poly (amic acid)s were synthesized from bis (3, 4-dicarboxyphenyl) dimethylsilane dianhydride (SIDA), pyromellitic dianhydride (PMDA) and 4,4′-oxydianiline (4,4'-ODA) in N, N-dimethylacetamide (DMAc). The poly (amic acid) films were obtained by solution-cast method from DMAc solutions and thermally converted into transparent, flexible and tough polyimide films. The wide-angle X-ray diffraction diagrams revealed that all the polyimides possessed amorphous character, and the regulation of those polyimides were decreased with the increase of the molar ratio of SIDA to PMDA. Differential scanning calorimeter measurements showed that the introduction of SIDA to polyimide backbone would make glass transition temperature shift to lower temperature. Thermogravimetric analyses indicated that the silicon-containing polyimides lowered decomposition temperature as compared with PMDA/4, 4′-ODA polyimides. However, UV-visible transmission and reflection spectra showed that the optical transparency of silicon-containing polyimide thin films was superior to that of PMDA/4, 4'-ODA polyimide thin films.展开更多
The residual stress in a 20%SiC w/6061Al composite as extruded was investigated by using X ray stress measurement method. It was found that, high residual stress existed in the composite and residual stress distributi...The residual stress in a 20%SiC w/6061Al composite as extruded was investigated by using X ray stress measurement method. It was found that, high residual stress existed in the composite and residual stress distribution in each direction are not uniform. Relaxation process of residual stress in the composite was dynamically measured during annealing at high temperature. It is verified that the relaxation of residual stress obeys the power law at high temperature. With the creep mechanism, the relaxation behavior of residual stresses at high temperature was analyzed. The results show that, the stress exponent and activation energy for stress relaxation of the composite are obviously higher than those of the matrix alloy.展开更多
Industrial grade multi-walled carbon nanotubes(IG-MWCNTs) are a low-cost substitute for commercially purified multi-walled carbon nanotubes(P-MWCNTs). In this work, IG-MWCNTs were functionalized with tetraethylenepent...Industrial grade multi-walled carbon nanotubes(IG-MWCNTs) are a low-cost substitute for commercially purified multi-walled carbon nanotubes(P-MWCNTs). In this work, IG-MWCNTs were functionalized with tetraethylenepentamine(TEPA) for CO2capture. The TEPA impregnated IG-MWCNTs were characterized with various experimental methods including N2adsorption/desorption isotherms, elemental analysis, X-ray diffraction, Fourier transform infrared spectroscopy and thermogravimetric analysis. Both the adsorption isotherms of IGMWCNTs-n and the isosteric heats of different adsorption capacities were obtained from experiments. TEPA impregnated IG-MWCNTs were also shown to have high CO2adsorption capacity comparable to that of TEPA impregnated P-MWCNTs. The adsorption capacity of IG-MWCNTs based adsorbents was in the range of 2.145 to 3.088 mmol/g, depending on adsorption temperatures. Having the advantages of low-cost and high adsorption capacity, TEPA impregnated IG-MWCNTs seem to be a promising adsorbent for CO2capture from flue gas.展开更多
The structure of bcc-Fe80Cu20 solid solution produced by mechanical alloying of the elemental bcc-Fe and fcc-Cu powders has been studied using X-ray diffraction and the extended X-ray absorption fine structure (EXAFS)...The structure of bcc-Fe80Cu20 solid solution produced by mechanical alloying of the elemental bcc-Fe and fcc-Cu powders has been studied using X-ray diffraction and the extended X-ray absorption fine structure (EXAFS) techniques. The disappearance of elemental Fe and Cu X-ray diffraction (XRD) peaks and the presence of bcc structural XRD peaks illustrate the formation of a nanocrystalline single-phase bcc-Fe80Cu20 solid solution. From the EXAFS result, the clear observation of Cu atoms taking on bcc coordination in the solid solution and Fe atoms remaining bcc structure further verifies the reality of atomic alloying between Fe and Cu atoms and the lattice change of Cu from fcc to bcc. However, the supersaturated bcc solid solution is not chemically uniform, i.e., some regions are rich in Fe atoms and other regions rich in Cu atoms.展开更多
An Al62.5Cu25Fe12.5 quasi-crystalline alloy was prepared by are melting. X-ray diffraction and scanning electron microscopy were used to study the microstructure of the quasi-crystalline alloy. Isothermal weight gain ...An Al62.5Cu25Fe12.5 quasi-crystalline alloy was prepared by are melting. X-ray diffraction and scanning electron microscopy were used to study the microstructure of the quasi-crystalline alloy. Isothermal weight gain of the Al-Cu-Fe quasi-crystal at elevated temperature in dry air was measured by means of a thermal balance and the oxidation behavior was evaluated by oxidation kinetic curves, from which it was deduced that the quasi-crystal exhibits good oxidation resistance. The surface morphologies of the Al-Cu-Fe quasi-crystal after isothermal oxidation at 700°C and 800°C for different times were observed. The oxidation resistance of quasi-crystalline powder and normal crystalline powder in the Al-Cu-Fe system was also quantitatively compared in quantity.展开更多
Isothermal oxygen in diffusion in c textured epitaxial YBa 2Cu 3O 7- δ thin films was studied by in situ X ray diffraction. Thermal expansion coefficients of c axis length with different oxygen contents are α c (6.9...Isothermal oxygen in diffusion in c textured epitaxial YBa 2Cu 3O 7- δ thin films was studied by in situ X ray diffraction. Thermal expansion coefficients of c axis length with different oxygen contents are α c (6.91, O 2)=19.1×10 -6 K -1 and α c (6.0, N 2)=19.3×10 -6 K -1 respectively. Chemical diffusion process of oxygen was described by relaxation time. From the Arrhenius plot of relaxation time, an activation energy of lattice diffusion was obtained as 1.1?eV, which is close to the results of SIMS (0.95?eV) and internal friction (1.02?eV).展开更多
New oxometallides with the formula Ba5Y8-xMn4021-1.5x （x = 0, 1） are prepared through an atmosphere-controlled solid-state reaction. Two single-phase samples with Ba/Y/Mn atomic ratios 5/8/4 （Y8） and 5/7/4 （Y7）...New oxometallides with the formula Ba5Y8-xMn4021-1.5x （x = 0, 1） are prepared through an atmosphere-controlled solid-state reaction. Two single-phase samples with Ba/Y/Mn atomic ratios 5/8/4 （Y8） and 5/7/4 （Y7） are obtained. The crystal structures and the physical properties of the compounds are investigated by X-ray powder diffraction, magnetization, conductivity, and dielectricity measurements. The Ba5Y8-xMn4021-1.5x compound is demonstrated to be a Y-deficient solid solution. The solid solution compound Ba5Y8-xMn4021-1.5x crystallizes into tetragonal symmetry with the space group I4/m. Detailed structure analysis by Rietveld refinement of the X-ray powder diffraction data reveals that the Y vacancies occur preferentially at the Y（2） site. Thermal magnetization measurements indicate the presence of antiferromagnetic interaction between Mn ions in the compounds, and temperature-dependent resistivity measurements show that insulator-semiconductor transitions occur around 175 K and 170 K for the Y8 and Y7 samples, respectively. Strong frequency dependences of the dielectric constant are observed above -175 K for the two compounds.展开更多
文摘Decomposition processes of the quenched Zn-Al alloys were studied by differential scanning calorimetry (DSC), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The results show that the stabilities of supersaturated solid solution (SSS) of Zn-Al alloy and α' phase formed by quenching would reduce with the increase of Zn content and the precipitation of η-Zn phases even when aging at ambient temperature, so that the exothermic precipitation peak in DSC curve would disappear. The activation energy of the η-Zn precipitation and the reaction enthalpy were calculated and measured. The kinetics of α' decomposition or η-Zn formation was determined by XRD. The microstructure change during aging was observed by TEM.
文摘X-ray powder diffraction data and crystal structure of NiSbY compound were studied by X-ray powderdiffraction. The compound belongs to the space group F43 m with MgAgAs structure type, and the parameters Z=4, a=0.63075(2) nm.
文摘The compound PrNiSn was studied by X ray powder diffraction technique. The crystal structure and the X ray diffraction data for this compound at room temperature were reported. The compound PrNiSn is orthorhombic with lattice parameters a =0.74569(3) nm, b =0.76851(5) nm, c =0.45676(8) nm, V =0.26176 nm 3, Z =4 and D x=8.076 g·cm -3 , space group Pna2 1(33). The figure of merit F N for the compound is F 30 =54 (0.0093, 60).
文摘The compound CeNi 5Sn was studied by means of X ray powder diffraction technique and refined by Rietveld method. It has a hexagonal structure with space group P 6 3/ mmc (No.194), Z =4, the lattice constants a =0 48912(3) nm, c =1 973(2) nm and D x=8 974 g·cm -3 . The Rietveld structural refinement was performed, leading to R p=0 138 and R wp =0 185. The figure of merit F N for the XRD data is F 30 =82 1(0 0068, 54). The X ray powder diffraction data are presented.
文摘To evaluate the residual stress in TiAl based alloys by X ray diffraction, X ray elastic constants (REC) of a γ TiAl alloy were determined. From these results, the stress state of a given phase in a duplex TiAl based alloy under a uniaxial tensile loading has been characterized by X ray diffraction. The results show that the X ray elastic constants and the microscopic stresses of the given phase are different from the apparent elastic constants and the macroscopic stresses of the alloy. The reason of the different distribution of the alloy was also discussed. [
文摘A primary study on Processing in X - ray inspection of spot weld for aluminum alloy spot welding,in- cluding for background simulation,acquisition of ideal binary image, and extraction and identifi- cation of defect features was presented.
文摘The silicon-containing poly (amic acid)s were synthesized from bis (3, 4-dicarboxyphenyl) dimethylsilane dianhydride (SIDA), pyromellitic dianhydride (PMDA) and 4,4′-oxydianiline (4,4'-ODA) in N, N-dimethylacetamide (DMAc). The poly (amic acid) films were obtained by solution-cast method from DMAc solutions and thermally converted into transparent, flexible and tough polyimide films. The wide-angle X-ray diffraction diagrams revealed that all the polyimides possessed amorphous character, and the regulation of those polyimides were decreased with the increase of the molar ratio of SIDA to PMDA. Differential scanning calorimeter measurements showed that the introduction of SIDA to polyimide backbone would make glass transition temperature shift to lower temperature. Thermogravimetric analyses indicated that the silicon-containing polyimides lowered decomposition temperature as compared with PMDA/4, 4′-ODA polyimides. However, UV-visible transmission and reflection spectra showed that the optical transparency of silicon-containing polyimide thin films was superior to that of PMDA/4, 4'-ODA polyimide thin films.
基金financially supported by the National Key Basic Research Program of China(No.2014CB643403)the National Science Fund for Distinguished Young Scholars(No.51225401)
文摘The residual stress in a 20%SiC w/6061Al composite as extruded was investigated by using X ray stress measurement method. It was found that, high residual stress existed in the composite and residual stress distribution in each direction are not uniform. Relaxation process of residual stress in the composite was dynamically measured during annealing at high temperature. It is verified that the relaxation of residual stress obeys the power law at high temperature. With the creep mechanism, the relaxation behavior of residual stresses at high temperature was analyzed. The results show that, the stress exponent and activation energy for stress relaxation of the composite are obviously higher than those of the matrix alloy.
基金supported by Zhejiang Provincial Natural Science Foundation of China(Grant No.LZ12E08002)
文摘Industrial grade multi-walled carbon nanotubes(IG-MWCNTs) are a low-cost substitute for commercially purified multi-walled carbon nanotubes(P-MWCNTs). In this work, IG-MWCNTs were functionalized with tetraethylenepentamine(TEPA) for CO2capture. The TEPA impregnated IG-MWCNTs were characterized with various experimental methods including N2adsorption/desorption isotherms, elemental analysis, X-ray diffraction, Fourier transform infrared spectroscopy and thermogravimetric analysis. Both the adsorption isotherms of IGMWCNTs-n and the isosteric heats of different adsorption capacities were obtained from experiments. TEPA impregnated IG-MWCNTs were also shown to have high CO2adsorption capacity comparable to that of TEPA impregnated P-MWCNTs. The adsorption capacity of IG-MWCNTs based adsorbents was in the range of 2.145 to 3.088 mmol/g, depending on adsorption temperatures. Having the advantages of low-cost and high adsorption capacity, TEPA impregnated IG-MWCNTs seem to be a promising adsorbent for CO2capture from flue gas.
基金financially supported by the National Natural Science Foundation of China(Nos.51574284 and 51504293)the Science and Technology Program of Yunnan Province,China(No.2013IB020)
基金supported by the National Natural Science Foundation of China(no.21206202)Scientific and Technological Research Program of Chongqing Municipal Education Commission(no.KJ1600902)+2 种基金the Demonstration project of Chongqing"121"Scientific&Technological Support Project(CSTC2014zktjccx BX0089)Project of Key generic industry technologies of Chongqing(No.cstc2016zdcy-ztzx0020-02)Program for Innovative Research Team in Chongqing University of Technology(2015TD22)
基金Natural Science Foundation of Guangdong Province (Grant No. 20010056).
文摘The structure of bcc-Fe80Cu20 solid solution produced by mechanical alloying of the elemental bcc-Fe and fcc-Cu powders has been studied using X-ray diffraction and the extended X-ray absorption fine structure (EXAFS) techniques. The disappearance of elemental Fe and Cu X-ray diffraction (XRD) peaks and the presence of bcc structural XRD peaks illustrate the formation of a nanocrystalline single-phase bcc-Fe80Cu20 solid solution. From the EXAFS result, the clear observation of Cu atoms taking on bcc coordination in the solid solution and Fe atoms remaining bcc structure further verifies the reality of atomic alloying between Fe and Cu atoms and the lattice change of Cu from fcc to bcc. However, the supersaturated bcc solid solution is not chemically uniform, i.e., some regions are rich in Fe atoms and other regions rich in Cu atoms.
文摘An Al62.5Cu25Fe12.5 quasi-crystalline alloy was prepared by are melting. X-ray diffraction and scanning electron microscopy were used to study the microstructure of the quasi-crystalline alloy. Isothermal weight gain of the Al-Cu-Fe quasi-crystal at elevated temperature in dry air was measured by means of a thermal balance and the oxidation behavior was evaluated by oxidation kinetic curves, from which it was deduced that the quasi-crystal exhibits good oxidation resistance. The surface morphologies of the Al-Cu-Fe quasi-crystal after isothermal oxidation at 700°C and 800°C for different times were observed. The oxidation resistance of quasi-crystalline powder and normal crystalline powder in the Al-Cu-Fe system was also quantitatively compared in quantity.
文摘Isothermal oxygen in diffusion in c textured epitaxial YBa 2Cu 3O 7- δ thin films was studied by in situ X ray diffraction. Thermal expansion coefficients of c axis length with different oxygen contents are α c (6.91, O 2)=19.1×10 -6 K -1 and α c (6.0, N 2)=19.3×10 -6 K -1 respectively. Chemical diffusion process of oxygen was described by relaxation time. From the Arrhenius plot of relaxation time, an activation energy of lattice diffusion was obtained as 1.1?eV, which is close to the results of SIMS (0.95?eV) and internal friction (1.02?eV).
基金Project supported by the National Natural Science Foundation of China (Grant Nos. 50872148 and 51072225)the National Basic Research Program of China (Grant No. 2007CB925003)
文摘New oxometallides with the formula Ba5Y8-xMn4021-1.5x （x = 0, 1） are prepared through an atmosphere-controlled solid-state reaction. Two single-phase samples with Ba/Y/Mn atomic ratios 5/8/4 （Y8） and 5/7/4 （Y7） are obtained. The crystal structures and the physical properties of the compounds are investigated by X-ray powder diffraction, magnetization, conductivity, and dielectricity measurements. The Ba5Y8-xMn4021-1.5x compound is demonstrated to be a Y-deficient solid solution. The solid solution compound Ba5Y8-xMn4021-1.5x crystallizes into tetragonal symmetry with the space group I4/m. Detailed structure analysis by Rietveld refinement of the X-ray powder diffraction data reveals that the Y vacancies occur preferentially at the Y（2） site. Thermal magnetization measurements indicate the presence of antiferromagnetic interaction between Mn ions in the compounds, and temperature-dependent resistivity measurements show that insulator-semiconductor transitions occur around 175 K and 170 K for the Y8 and Y7 samples, respectively. Strong frequency dependences of the dielectric constant are observed above -175 K for the two compounds.