The formation mechanism of 'white band' and central carbon segregation of high-carbon Cr bearing steel concasting billets are discussed in this paper. The maximum oxygen content in the steel produced by concas...The formation mechanism of 'white band' and central carbon segregation of high-carbon Cr bearing steel concasting billets are discussed in this paper. The maximum oxygen content in the steel produced by concasting process was 13xl0^-6 with an average oxygen content of 9.3xl0^-6. Comparison of metallurgical quality and fatigue property between the concasting steel (CC) and ingot casting steel (IC) showed that the carbon segregation (C/C0) in former steel was 0.92～1.10 and its fatigue life was equal to that of the latter steel.展开更多
An industrial plant trial for optimizing the process parameters in a round billet continuous casting mold with electromagnetic stirring （M-EMS） was performed, in which the influences of stirring parameters with M-EM...An industrial plant trial for optimizing the process parameters in a round billet continuous casting mold with electromagnetic stirring （M-EMS） was performed, in which the influences of stirring parameters with M-EMS on the solidification macrostructure of high carbon steel were investigated. The results show that the billet quality is not well controlled under the condition of working current and frequency with EMS, in which the subsurface crack of grade 1.0-2.0 ups to 38.09%, the central pipe of grade 1.0-1.5 reaches to 14.28%, and the central porosity of grade 1.5 is 14.29%. The parameters of current 260 A and frequency 8 Hz as the final optimum scheme has a remarkable effect for improving the macroscopic quality of billet, in which the subsurface crack, central pipe and skin blowhole are all disappeared, and the central porosity and carbon segregation are also well improved.展开更多
文摘The formation mechanism of 'white band' and central carbon segregation of high-carbon Cr bearing steel concasting billets are discussed in this paper. The maximum oxygen content in the steel produced by concasting process was 13xl0^-6 with an average oxygen content of 9.3xl0^-6. Comparison of metallurgical quality and fatigue property between the concasting steel (CC) and ingot casting steel (IC) showed that the carbon segregation (C/C0) in former steel was 0.92～1.10 and its fatigue life was equal to that of the latter steel.
基金supported by the Program for New Century Excellent Talents in University from the Ministry of Education of China (No.NCET-04-0285)
文摘An industrial plant trial for optimizing the process parameters in a round billet continuous casting mold with electromagnetic stirring （M-EMS） was performed, in which the influences of stirring parameters with M-EMS on the solidification macrostructure of high carbon steel were investigated. The results show that the billet quality is not well controlled under the condition of working current and frequency with EMS, in which the subsurface crack of grade 1.0-2.0 ups to 38.09%, the central pipe of grade 1.0-1.5 reaches to 14.28%, and the central porosity of grade 1.5 is 14.29%. The parameters of current 260 A and frequency 8 Hz as the final optimum scheme has a remarkable effect for improving the macroscopic quality of billet, in which the subsurface crack, central pipe and skin blowhole are all disappeared, and the central porosity and carbon segregation are also well improved.