The properties and mechanism of concrete under water leakage corrosion were studied in terms of the dissolution of calcium oxide and silicon oxide from concrete and the variation of pH value of permeate water.The expe...The properties and mechanism of concrete under water leakage corrosion were studied in terms of the dissolution of calcium oxide and silicon oxide from concrete and the variation of pH value of permeate water.The experimental results show that the amount of calcium oxide and silicon oxide dissolved from per cubic meter of concrete gradually decrease with penetration time and ultimately stabilize at a certain value.The pH value of permeate water descend along with penetration time.The durability of concrete under leakage corrosion was analyzed by a formula fitted on the dissolved amount of calcium oxide.展开更多
基金Funded by National Key Technologies R&D Program of China(No.96-220-01-03-03, 96-221-02-04-02)
文摘The properties and mechanism of concrete under water leakage corrosion were studied in terms of the dissolution of calcium oxide and silicon oxide from concrete and the variation of pH value of permeate water.The experimental results show that the amount of calcium oxide and silicon oxide dissolved from per cubic meter of concrete gradually decrease with penetration time and ultimately stabilize at a certain value.The pH value of permeate water descend along with penetration time.The durability of concrete under leakage corrosion was analyzed by a formula fitted on the dissolved amount of calcium oxide.