This work describes thermal decomposition behaviour of plastic bonded explosives(PBXs) based on mixture of 1,3,5,7-tetranitro-1,3,5,7-tetrazocane(HMX) and 2,4,6-triamino-1,3,5-trinitrobenzene(TATB)with Viton A as poly...This work describes thermal decomposition behaviour of plastic bonded explosives(PBXs) based on mixture of 1,3,5,7-tetranitro-1,3,5,7-tetrazocane(HMX) and 2,4,6-triamino-1,3,5-trinitrobenzene(TATB)with Viton A as polymer binder. Thermal decomposition of PBXs was undertaken by applying simultaneous thermal analysis(STA) and differential scanning calorimetry(DSC) to investigate influence of the HMX amount on thermal behavior and its kinetics. Thermogravimetric analysis(TGA) indicated that the thermal decomposition of PBXs based on mixture of HMX and TATB was occurred in a three-steps. The first step was mainly due to decomposition of HMX. The second step was ascribed due to decomposition of TATB, while the third step was occurred due to decomposition of the polymer matrices. The thermal decomposition % was increased with increasing HMX amount. The kinetics related to thermal decomposition were investigated under non-isothermal for a single heating rate measurement. The variation in the activation energy of PBXs based on mixture of HMX and TATB was observed with varying the HMX amount. The kinetics from the results of TGA data at various heating rates under non-isothermal conditions were also calculated by Flynn—Wall—Ozawa(FWO) and Kissinger-Akahira-Sunose(KAS)methods. The activation energies calculated by employing FWO method were very close to those obtained by KAS method. The mean activation energy calculated by FWO and KAS methods was also a good agreement with the activation energy obtained from single heating rate measurement in the first step decomposition.展开更多
Refinement and thermal analysis of hypereutectic Al 25%Si alloy were investigated with scanning electron microscope (SEM) and differential scanning calorimeter (DSC). The results show that the average size of primary ...Refinement and thermal analysis of hypereutectic Al 25%Si alloy were investigated with scanning electron microscope (SEM) and differential scanning calorimeter (DSC). The results show that the average size of primary silicon in Al 25%Si alloy without and with phosphorus addition are 250 μm and 30 μm, respectively. But the primary and eutectic growth temperature is raised by about 17.3 ℃ and 4?℃ respectively due to phosphorus addition. The primary nucleation temperatures are 745.0 ℃ and 762.0 ℃ for untreated and treated samples and in addition, the enthalpy changes of primary and eutectic transformation are -261.0 J/g and -397.3 J/g without phosphorus addition, -294.2 J/g and -386.1 J/g with phosphorus addition, respectively. Otherwise the mechanisms of refinement and thermal transformation of Al 25%Si alloy in solidifying process are also discussed. [展开更多
基金DRDO(TBR-1251)for funding and awarding the Project
文摘This work describes thermal decomposition behaviour of plastic bonded explosives(PBXs) based on mixture of 1,3,5,7-tetranitro-1,3,5,7-tetrazocane(HMX) and 2,4,6-triamino-1,3,5-trinitrobenzene(TATB)with Viton A as polymer binder. Thermal decomposition of PBXs was undertaken by applying simultaneous thermal analysis(STA) and differential scanning calorimetry(DSC) to investigate influence of the HMX amount on thermal behavior and its kinetics. Thermogravimetric analysis(TGA) indicated that the thermal decomposition of PBXs based on mixture of HMX and TATB was occurred in a three-steps. The first step was mainly due to decomposition of HMX. The second step was ascribed due to decomposition of TATB, while the third step was occurred due to decomposition of the polymer matrices. The thermal decomposition % was increased with increasing HMX amount. The kinetics related to thermal decomposition were investigated under non-isothermal for a single heating rate measurement. The variation in the activation energy of PBXs based on mixture of HMX and TATB was observed with varying the HMX amount. The kinetics from the results of TGA data at various heating rates under non-isothermal conditions were also calculated by Flynn—Wall—Ozawa(FWO) and Kissinger-Akahira-Sunose(KAS)methods. The activation energies calculated by employing FWO method were very close to those obtained by KAS method. The mean activation energy calculated by FWO and KAS methods was also a good agreement with the activation energy obtained from single heating rate measurement in the first step decomposition.
文摘Refinement and thermal analysis of hypereutectic Al 25%Si alloy were investigated with scanning electron microscope (SEM) and differential scanning calorimeter (DSC). The results show that the average size of primary silicon in Al 25%Si alloy without and with phosphorus addition are 250 μm and 30 μm, respectively. But the primary and eutectic growth temperature is raised by about 17.3 ℃ and 4?℃ respectively due to phosphorus addition. The primary nucleation temperatures are 745.0 ℃ and 762.0 ℃ for untreated and treated samples and in addition, the enthalpy changes of primary and eutectic transformation are -261.0 J/g and -397.3 J/g without phosphorus addition, -294.2 J/g and -386.1 J/g with phosphorus addition, respectively. Otherwise the mechanisms of refinement and thermal transformation of Al 25%Si alloy in solidifying process are also discussed. [